A SiC/ZrSiO4？SiO2 （SZS） coating was successfully fabricated on the carbon/carbon （C/C） composites by pack cementation, slurry painting and sintering to improve the anti-oxidation property and thermal shock r...A SiC/ZrSiO4？SiO2 （SZS） coating was successfully fabricated on the carbon/carbon （C/C） composites by pack cementation, slurry painting and sintering to improve the anti-oxidation property and thermal shock resistance. The anti-oxidation properties under different oxygen partial pressures （OPP） and thermal shock resistance of the SZS coating were investigated. The results show that the SZS coated sample under low OPP, corresponding to the ambient air, during isothermal oxidation was 0.54% in mass gain after 111 h oxidation at 1500 ° C and less than 0.03% in mass loss after 50 h oxidation in high OPP, corresponding to the air flow rate of 36 L/h. Additionally, the residual compressive strengths （RCS） of the SZS coated samples after oxidation for 50 h in high OPP and 80 h in low OPP remain about 70% and 72.5% of those of original C/C samples, respectively. Moreover, the mass loss of SZS coated samples subjected to the thermal cycle from 1500 ° C in high OPP to boiling water for 30 times was merely 1.61%.展开更多
The B4C/2024Al composites were successfully produced by pressureless infiltration method, and the effects of heat treatment on phase content and mechanical properties were investigated by X-ray diffraction （XRD）, sc...The B4C/2024Al composites were successfully produced by pressureless infiltration method, and the effects of heat treatment on phase content and mechanical properties were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and mechanical properties testing. The results show that phases of BnC/2024Al composites include B4C, Al, Al3BC, AlB2 and Al2Cu. The phase species remain unchanged; however, the phase content of the composites changes significantly after heat treatment at the temperature of 660, 700, 800 or 900 ℃ for 12, 24 or 36 h. It is found that the heat treatment results in not only considerable enhancement in hardness, but also reduction in bending strength of the composites. Heat treatment at 800 ℃ for 36 h does best to hardness of the composites, while at 700 ℃ for 36 h it is the most beneficial to their comprehensive mechanical properties.展开更多
The B4C/Mg composites fabricated by metal-assisted pressureless infiltration technique were used as experimental material, and the wear behavior and mechanism of this material were studied. A pin-on-disc apparatus was...The B4C/Mg composites fabricated by metal-assisted pressureless infiltration technique were used as experimental material, and the wear behavior and mechanism of this material were studied. A pin-on-disc apparatus was used to evaluate the wear behavior where loads of 20, 40, 60 and 80 N, and a sliding velocity of 250 r/min were exerted. The results show that B4C/Mg composites possess superior wear resistance than pure Mg under various applied loads, and the content of Ti, as infiltration inducer, has an influence on the wear resistance of B4C/Mg composites. The dominant wear mechanism for pure Mg is abrasion, while that for B4C/Mg composites under low loads is adhesion and delamination. Under high loads, the wear mechanism of B4C/Mg composites can be attributed to thermal softening and melting or plastic deformation.展开更多
Modern communication technologies put forward higher requirements for electromagnetic wave(EMW)absorption materials.Metal-organic framework(MOF)derivatives have been widely concerned with its diverse advantages.To bre...Modern communication technologies put forward higher requirements for electromagnetic wave(EMW)absorption materials.Metal-organic framework(MOF)derivatives have been widely concerned with its diverse advantages.To break the mindset of magneticderivative design,and make up the shortage of monometallic non-magnetic derivatives,we first try non-magnetic bimetallic MOFs derivatives to achieve efficient EMW absorption.The porous carbon-wrapped TiO2/ZrTiO4 composites derived from PCN-415(TiZr-MOFs)are qualified with a minimum reflection loss of−67.8 dB(2.16 mm,13.0 GHz),and a maximum effective absorption bandwidth of 5.9 GHz(2.70 mm).Through in-depth discussions,the synergy of enhanced interfacial polarization and other attenuation mechanisms in the composites is revealed.Therefore,this work confirms the huge potentials of nonmagnetic bimetallic MOFs derivatives in EMW absorption applications.展开更多
This work aimed to fabricate B4C reinforced aluminum matrix composites via blended powder semisolid forming that is an implementation of the benefits of semisolid forming to the powder metallurgy. Al7075 elements were...This work aimed to fabricate B4C reinforced aluminum matrix composites via blended powder semisolid forming that is an implementation of the benefits of semisolid forming to the powder metallurgy. Al7075 elements were incrementally added to ethanol solution under mechanical mixing. Al7075 constituents and B4C particles were blended in a high energy ball mill. Cold compacted Al7075/B4C blends were pressed at semisolid state. The effects of the size of the matrix（20, 45 and 63 μm）, reinforcing volume fraction（5%, 10% and 20%） and semisolid compaction pressure（50 and 100 MPa） on the morphology, microstructure, density, hardness, compression and bending strength were thoroughly analyzed. Experimental results revealed that the highest microstructural uniformity was achieved when large B4C particles（45 μm） were distributed within the small particles（20 μm） of the matrix phase. Composites with matrix particles larger than reinforcing phase indicated agglomerations in loadings more than 10%（volume fraction）. Agglomerated regions resisted against penetration of the liquid phase to the pores and lowered the density and strength of these composites. Composites with 20 μm Al7075 and 20%（volume fraction） 45 μm B4C powder pressed under 100 MPa exhibited the highest values of hardness（HV 190） and compressive strength（336 MPa）.展开更多
B4C/6061Al composites reinforced with nano-to micrometer-sized B4C particles were fabricated via powder metallurgy route consisting of spark plasma sintering(SPS)and hot extrusion and rolling(HER),followed by T6 treat...B4C/6061Al composites reinforced with nano-to micrometer-sized B4C particles were fabricated via powder metallurgy route consisting of spark plasma sintering(SPS)and hot extrusion and rolling(HER),followed by T6 treatment.The microstructural evolution and mechanical properties were investigated.Results showed that the status of B4C particles changed from a network after SPS to a dispersion distribution after HER.The substructured grains reached 66.5%owing to the pinning effect of nano-sized B4C,and the grain size was refined from 3.12μm to 1.56μm after HER.After T6 treatment,dispersed Mg_(2)Si precipitated phases formed,and the grain size increased to 1.87μm.Fine recrystallized grains around micro-sized B4C were smaller than those in the areas with uniform distribution of nano-sized B4C and Mg_(2)Si.The stress distributions of as-rolled and heated composites were similar,considering that the T6 heat treatment was only effective in eliminating the first internal stress.The Vickers,microhardness,and tensile strength of as-SPSed composites were greatly improved from HV 55.45,0.86 GPa,and 180 MPa to HV 77.51,1.08 GPa,and 310 MPa,respectively.Despite the precipitation strengthening,the corresponding values of as-heated composites decreased to HV 70.82,0.85 GPa,and 230 MPa owing to grain coarsening.展开更多
Polypyrrole‐modified graphitic carbon nitride composites(PPy/g‐C3N4)are fabricated using an in‐situ polymerization method to improve the visible light photocatalytic activity of g‐C3N4.The PPy/g‐C3N4 is applied t...Polypyrrole‐modified graphitic carbon nitride composites(PPy/g‐C3N4)are fabricated using an in‐situ polymerization method to improve the visible light photocatalytic activity of g‐C3N4.The PPy/g‐C3N4 is applied to the photocatalytic degradation of methylene blue(MB)under visible light irradiation.Various characterization techniques are employed to investigate the relationship between the structural properties and photoactivities of the as‐prepared composites.Results show that the specific surface area of the PPy/g‐C3N4 composites increases upon assembly of the amorphous PPy nanoparticles on the g‐C3N4 surface.Owing to the strong conductivity,the PPy can be used as a transition channel for electrons to move onto the g‐C3N4 surface,thus inhibiting the recombination of photogenerated carriers of g‐C3N4 and improving the photocatalytic performance.The elevated light adsorption of PPy/g‐C3N4 composites is attributed to the strong absorption coefficient of PPy.The composite containing 0.75 wt%PPy exhibits a photocatalytic efficiency that is 3 times higher than that of g‐C3N4 in 2 h.Moreover,the degradation kinetics follow a pseudo‐first‐order model.A detailed photocatalytic mechanism is proposed with·OH and·O2-radicals as the main reactive species.The present work provides new insights into the mechanistic understanding of PPy in PPy/g‐C3N4 composites for environmental applications.展开更多
A356alloy was used as the base metal to produce boron carbide(B4C)/A356composites using friction stir processing(FSP).The microstructural and mechanical properties of B4C/A356composites were optimized using artificial...A356alloy was used as the base metal to produce boron carbide(B4C)/A356composites using friction stir processing(FSP).The microstructural and mechanical properties of B4C/A356composites were optimized using artificial neural network(ANN)and non-dominated sorting genetic algorithm-II(NSGA-II).Firstly,microstructural properties of the composites fabricated in different processing conditions were investigated.Results show that FSP parameters such as rotational speed,traverse speed and tool pin profile significantly affect the size of the primary silicon(Si)particles of the base metal,as well as the dispersion quality and volume fraction of reinforcing B4C particles in the composite layer.Higher rotational to traverse speeds ratio accompanied by threaded pin profile leads to better particles distribution,finer Si particles and smaller B4C agglomerations.Secondly,hardness and tensile tests were performed to study mechanical properties of the composites.FSP changes the fracture mechanism from brittle form in the as-received metal to very ductile form in the FSPed specimens.Then,a relation between the FSP parameters and microstructural and mechanical properties of the composites was established using ANN.A modified NSGA-II by incorporating diversity preserving mechanism called theεelimination algorithm was employed to obtain the Pareto-optimal set of FSP parameters.展开更多
A Ni-B_4C macroscopic diffusion welding couple and a Ni-15 wt% B_4C composite fabricated by spark plasma sintering(SPS) were used to understand the micro-scale diffusion bonding between metals and ceramics. In the Ni-...A Ni-B_4C macroscopic diffusion welding couple and a Ni-15 wt% B_4C composite fabricated by spark plasma sintering(SPS) were used to understand the micro-scale diffusion bonding between metals and ceramics. In the Ni-B_4C macroscopic diffusion welding couple a perfect diffusion welding joint was achieved. In the Ni-15 wt% B_4C sample, microstructure analyses demonstrated that loose structures occurred around the B_4C particles. Energy dispersive X-ray spectroscopy analyses revealed that during the SPS process, the process of diffusion bonding between Ni and B_4C particles can be divided into three stages. By employing a nano-indentation test, the room-temperature fracture toughness of the Ni matrix was found to be higher than that of the interface. The micro-diffusion bonding between Ni and B_4C particles is quite different from the Ni-B_4C reaction couple.展开更多
MgAl2O4 particle-reinforced AC4C based alloy composites were fabricated by the stirring-casting method. The effects of the average sizes and the size distributions of MgAl2O4 particles on the dispersibility were inves...MgAl2O4 particle-reinforced AC4C based alloy composites were fabricated by the stirring-casting method. The effects of the average sizes and the size distributions of MgAl2O4 particles on the dispersibility were investigated, and the microstructures, strength, and fatigue properties of MgAl2O4 particle-reinforced AC4C based alloy composites were evaluated. Tensile strength in the MgAl2O4 particle-reinforced AC4C based alloy composite was increased by using the classified particles. The fatigue limit at 107 cycles in the MgA1204 particle-reinforced AC4C-Cu composite increased by 27% compared to the unreinforced alloy at 250 ~C. Dislocations were observed in the matrix around the MgAl204 particle which resulted from the mismatch of thermal expansion coefficients between MgAl2O4 and Al, and resisted failure and caused fatigue cracks to propagate around the MgAl2O4 particles, resulting in extensive crack deflection and crack bowing which contributed to the improvement of fatigue strength.展开更多
A sophisticated stir casting route to fabricate large scale AA6061-31%B4C composite was developed. Key process parameters were studied, microstructure and mechanical properties of the composite were investigated. The ...A sophisticated stir casting route to fabricate large scale AA6061-31%B4C composite was developed. Key process parameters were studied, microstructure and mechanical properties of the composite were investigated. The results indicated that vacuum stirring/casting, B4C/Mg feeding and ingots cooling were essential to the successful fabrication of AA6061-31%B4C composite. Chemical erosion examination verified the designed B4 C content; X-ray fluorescence spectrometer（XFS） showed the chemical composition of Mg and Si in the matrix conformed to industry standards; scanning electronic microscope（SEM） and X-ray diffraction（XRD） revealed that B4 C particles were evenly distributed in the composites with well dispersed Mg2Si precipitates. Tensile testing results showed that the AA6061-31%B4C composite had a tensile strength of 340 MPa, improved by 112.5% compared with AA1100-31%B4C composite, which is attributed to the enhanced strength of the matrix alloy.展开更多
The microstructure and mechanical properties of TiB_2 /B_4C composites have been investi- gated.It was found that both the strength and hardness for TiB_2 greatly increase with the ad- dition of 20 to 30 wt-% B_4C,and...The microstructure and mechanical properties of TiB_2 /B_4C composites have been investi- gated.It was found that both the strength and hardness for TiB_2 greatly increase with the ad- dition of 20 to 30 wt-% B_4C,and the fracture toughness K_(IC) value remaines on the original high level.The flexure strength,Vicker's hardness and fracture toughness are 782 MPa,26.2 GPa and 7.2 MPam^(1/2),respectively,for the TiB_2-30 wt-% B_4C composite,compared to 450 MPa,21 GPa and 7.0 MPam^(1/2) for monolithic TiB_2.The toughening and strengthening mechanisms,have also been discussed.展开更多
基金Project supported by the Nonferrous Metal Oriented Advanced Structural Materials and Manufacturing Cooperative Innovation Center,ChinaProject(51205417)supported by the National Natural Science Foundation of China
文摘A SiC/ZrSiO4？SiO2 （SZS） coating was successfully fabricated on the carbon/carbon （C/C） composites by pack cementation, slurry painting and sintering to improve the anti-oxidation property and thermal shock resistance. The anti-oxidation properties under different oxygen partial pressures （OPP） and thermal shock resistance of the SZS coating were investigated. The results show that the SZS coated sample under low OPP, corresponding to the ambient air, during isothermal oxidation was 0.54% in mass gain after 111 h oxidation at 1500 ° C and less than 0.03% in mass loss after 50 h oxidation in high OPP, corresponding to the air flow rate of 36 L/h. Additionally, the residual compressive strengths （RCS） of the SZS coated samples after oxidation for 50 h in high OPP and 80 h in low OPP remain about 70% and 72.5% of those of original C/C samples, respectively. Moreover, the mass loss of SZS coated samples subjected to the thermal cycle from 1500 ° C in high OPP to boiling water for 30 times was merely 1.61%.
基金Project(2011CB605805)supported by the National Basic Research Program of China
文摘The B4C/2024Al composites were successfully produced by pressureless infiltration method, and the effects of heat treatment on phase content and mechanical properties were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and mechanical properties testing. The results show that phases of BnC/2024Al composites include B4C, Al, Al3BC, AlB2 and Al2Cu. The phase species remain unchanged; however, the phase content of the composites changes significantly after heat treatment at the temperature of 660, 700, 800 or 900 ℃ for 12, 24 or 36 h. It is found that the heat treatment results in not only considerable enhancement in hardness, but also reduction in bending strength of the composites. Heat treatment at 800 ℃ for 36 h does best to hardness of the composites, while at 700 ℃ for 36 h it is the most beneficial to their comprehensive mechanical properties.
基金Project(51271051)supported by the National Natural Sciecne Foundation of China
文摘The B4C/Mg composites fabricated by metal-assisted pressureless infiltration technique were used as experimental material, and the wear behavior and mechanism of this material were studied. A pin-on-disc apparatus was used to evaluate the wear behavior where loads of 20, 40, 60 and 80 N, and a sliding velocity of 250 r/min were exerted. The results show that B4C/Mg composites possess superior wear resistance than pure Mg under various applied loads, and the content of Ti, as infiltration inducer, has an influence on the wear resistance of B4C/Mg composites. The dominant wear mechanism for pure Mg is abrasion, while that for B4C/Mg composites under low loads is adhesion and delamination. Under high loads, the wear mechanism of B4C/Mg composites can be attributed to thermal softening and melting or plastic deformation.
基金The authors acknowledge funding from the National Natural Science Foundation of China(Nos.51572157,21902085,and 51702188)Natural Science Foundation of Shandong Province(No.ZR2019QF012)+1 种基金Fundamental Research Funds for the Central Universities(No.2018JC036 and No.2018JC046)Young Scholars Program of Shandong University(No.2018WLJH25).
文摘Modern communication technologies put forward higher requirements for electromagnetic wave(EMW)absorption materials.Metal-organic framework(MOF)derivatives have been widely concerned with its diverse advantages.To break the mindset of magneticderivative design,and make up the shortage of monometallic non-magnetic derivatives,we first try non-magnetic bimetallic MOFs derivatives to achieve efficient EMW absorption.The porous carbon-wrapped TiO2/ZrTiO4 composites derived from PCN-415(TiZr-MOFs)are qualified with a minimum reflection loss of−67.8 dB(2.16 mm,13.0 GHz),and a maximum effective absorption bandwidth of 5.9 GHz(2.70 mm).Through in-depth discussions,the synergy of enhanced interfacial polarization and other attenuation mechanisms in the composites is revealed.Therefore,this work confirms the huge potentials of nonmagnetic bimetallic MOFs derivatives in EMW absorption applications.
基金Tabriz Branch,Islamic Azad University for the financial support of this research,which is based on a research project contract
文摘This work aimed to fabricate B4C reinforced aluminum matrix composites via blended powder semisolid forming that is an implementation of the benefits of semisolid forming to the powder metallurgy. Al7075 elements were incrementally added to ethanol solution under mechanical mixing. Al7075 constituents and B4C particles were blended in a high energy ball mill. Cold compacted Al7075/B4C blends were pressed at semisolid state. The effects of the size of the matrix（20, 45 and 63 μm）, reinforcing volume fraction（5%, 10% and 20%） and semisolid compaction pressure（50 and 100 MPa） on the morphology, microstructure, density, hardness, compression and bending strength were thoroughly analyzed. Experimental results revealed that the highest microstructural uniformity was achieved when large B4C particles（45 μm） were distributed within the small particles（20 μm） of the matrix phase. Composites with matrix particles larger than reinforcing phase indicated agglomerations in loadings more than 10%（volume fraction）. Agglomerated regions resisted against penetration of the liquid phase to the pores and lowered the density and strength of these composites. Composites with 20 μm Al7075 and 20%（volume fraction） 45 μm B4C powder pressed under 100 MPa exhibited the highest values of hardness（HV 190） and compressive strength（336 MPa）.
基金Projects(51775366,51805358)supported by the National Natural Science Foundation of ChinaProject(20130321024)supported by the Key Science and Technology Program of Shanxi Province,China。
文摘B4C/6061Al composites reinforced with nano-to micrometer-sized B4C particles were fabricated via powder metallurgy route consisting of spark plasma sintering(SPS)and hot extrusion and rolling(HER),followed by T6 treatment.The microstructural evolution and mechanical properties were investigated.Results showed that the status of B4C particles changed from a network after SPS to a dispersion distribution after HER.The substructured grains reached 66.5%owing to the pinning effect of nano-sized B4C,and the grain size was refined from 3.12μm to 1.56μm after HER.After T6 treatment,dispersed Mg_(2)Si precipitated phases formed,and the grain size increased to 1.87μm.Fine recrystallized grains around micro-sized B4C were smaller than those in the areas with uniform distribution of nano-sized B4C and Mg_(2)Si.The stress distributions of as-rolled and heated composites were similar,considering that the T6 heat treatment was only effective in eliminating the first internal stress.The Vickers,microhardness,and tensile strength of as-SPSed composites were greatly improved from HV 55.45,0.86 GPa,and 180 MPa to HV 77.51,1.08 GPa,and 310 MPa,respectively.Despite the precipitation strengthening,the corresponding values of as-heated composites decreased to HV 70.82,0.85 GPa,and 230 MPa owing to grain coarsening.
文摘Polypyrrole‐modified graphitic carbon nitride composites(PPy/g‐C3N4)are fabricated using an in‐situ polymerization method to improve the visible light photocatalytic activity of g‐C3N4.The PPy/g‐C3N4 is applied to the photocatalytic degradation of methylene blue(MB)under visible light irradiation.Various characterization techniques are employed to investigate the relationship between the structural properties and photoactivities of the as‐prepared composites.Results show that the specific surface area of the PPy/g‐C3N4 composites increases upon assembly of the amorphous PPy nanoparticles on the g‐C3N4 surface.Owing to the strong conductivity,the PPy can be used as a transition channel for electrons to move onto the g‐C3N4 surface,thus inhibiting the recombination of photogenerated carriers of g‐C3N4 and improving the photocatalytic performance.The elevated light adsorption of PPy/g‐C3N4 composites is attributed to the strong absorption coefficient of PPy.The composite containing 0.75 wt%PPy exhibits a photocatalytic efficiency that is 3 times higher than that of g‐C3N4 in 2 h.Moreover,the degradation kinetics follow a pseudo‐first‐order model.A detailed photocatalytic mechanism is proposed with·OH and·O2-radicals as the main reactive species.The present work provides new insights into the mechanistic understanding of PPy in PPy/g‐C3N4 composites for environmental applications.
文摘A356alloy was used as the base metal to produce boron carbide(B4C)/A356composites using friction stir processing(FSP).The microstructural and mechanical properties of B4C/A356composites were optimized using artificial neural network(ANN)and non-dominated sorting genetic algorithm-II(NSGA-II).Firstly,microstructural properties of the composites fabricated in different processing conditions were investigated.Results show that FSP parameters such as rotational speed,traverse speed and tool pin profile significantly affect the size of the primary silicon(Si)particles of the base metal,as well as the dispersion quality and volume fraction of reinforcing B4C particles in the composite layer.Higher rotational to traverse speeds ratio accompanied by threaded pin profile leads to better particles distribution,finer Si particles and smaller B4C agglomerations.Secondly,hardness and tensile tests were performed to study mechanical properties of the composites.FSP changes the fracture mechanism from brittle form in the as-received metal to very ductile form in the FSPed specimens.Then,a relation between the FSP parameters and microstructural and mechanical properties of the composites was established using ANN.A modified NSGA-II by incorporating diversity preserving mechanism called theεelimination algorithm was employed to obtain the Pareto-optimal set of FSP parameters.
基金financially supported by the National Natural Science Foundation of China (No. 51775366)
文摘A Ni-B_4C macroscopic diffusion welding couple and a Ni-15 wt% B_4C composite fabricated by spark plasma sintering(SPS) were used to understand the micro-scale diffusion bonding between metals and ceramics. In the Ni-B_4C macroscopic diffusion welding couple a perfect diffusion welding joint was achieved. In the Ni-15 wt% B_4C sample, microstructure analyses demonstrated that loose structures occurred around the B_4C particles. Energy dispersive X-ray spectroscopy analyses revealed that during the SPS process, the process of diffusion bonding between Ni and B_4C particles can be divided into three stages. By employing a nano-indentation test, the room-temperature fracture toughness of the Ni matrix was found to be higher than that of the interface. The micro-diffusion bonding between Ni and B_4C particles is quite different from the Ni-B_4C reaction couple.
文摘MgAl2O4 particle-reinforced AC4C based alloy composites were fabricated by the stirring-casting method. The effects of the average sizes and the size distributions of MgAl2O4 particles on the dispersibility were investigated, and the microstructures, strength, and fatigue properties of MgAl2O4 particle-reinforced AC4C based alloy composites were evaluated. Tensile strength in the MgAl2O4 particle-reinforced AC4C based alloy composite was increased by using the classified particles. The fatigue limit at 107 cycles in the MgA1204 particle-reinforced AC4C-Cu composite increased by 27% compared to the unreinforced alloy at 250 ~C. Dislocations were observed in the matrix around the MgAl204 particle which resulted from the mismatch of thermal expansion coefficients between MgAl2O4 and Al, and resisted failure and caused fatigue cracks to propagate around the MgAl2O4 particles, resulting in extensive crack deflection and crack bowing which contributed to the improvement of fatigue strength.
基金founded by Joint Laboratory of Nuclear Materials and Service Safety (2013966003),China
文摘A sophisticated stir casting route to fabricate large scale AA6061-31%B4C composite was developed. Key process parameters were studied, microstructure and mechanical properties of the composite were investigated. The results indicated that vacuum stirring/casting, B4C/Mg feeding and ingots cooling were essential to the successful fabrication of AA6061-31%B4C composite. Chemical erosion examination verified the designed B4 C content; X-ray fluorescence spectrometer（XFS） showed the chemical composition of Mg and Si in the matrix conformed to industry standards; scanning electronic microscope（SEM） and X-ray diffraction（XRD） revealed that B4 C particles were evenly distributed in the composites with well dispersed Mg2Si precipitates. Tensile testing results showed that the AA6061-31%B4C composite had a tensile strength of 340 MPa, improved by 112.5% compared with AA1100-31%B4C composite, which is attributed to the enhanced strength of the matrix alloy.
文摘The microstructure and mechanical properties of TiB_2 /B_4C composites have been investi- gated.It was found that both the strength and hardness for TiB_2 greatly increase with the ad- dition of 20 to 30 wt-% B_4C,and the fracture toughness K_(IC) value remaines on the original high level.The flexure strength,Vicker's hardness and fracture toughness are 782 MPa,26.2 GPa and 7.2 MPam^(1/2),respectively,for the TiB_2-30 wt-% B_4C composite,compared to 450 MPa,21 GPa and 7.0 MPam^(1/2) for monolithic TiB_2.The toughening and strengthening mechanisms,have also been discussed.