NiFe2O4-10NiO-based cermet inert anodes for aluminium electrolysis were prepared and their properties were investigated in a lab-scale electrolysis cell. The results show that the inert anodes exhibit good performance...NiFe2O4-10NiO-based cermet inert anodes for aluminium electrolysis were prepared and their properties were investigated in a lab-scale electrolysis cell. The results show that the inert anodes exhibit good performance during electrolysis in molten salt cryolite at 960 °C, but according to the analyses of phase compositions and microstructures through XRD, SEM/EDX and metallographic analysis, the metal in the anodes is preferentially corroded and many pores are produced on the anode surface after electrolysis. The preferential dissolution of Fe in the NiFe2O4 phase may lead to the non-uniform corrosion of NiFe2O4 grains. Moreover, a dense protective layer of NiFe2O4-NiAl2O4-FeAl2O4 is formed on the anode surface, which originates from the reaction of Al2O3 dissolved in the electrolyte with NiO or FeO, the annexation of NiFe2O4-NiAl2O4-FeAl2O4 to NiO and volume expansion. Thus, the dense NiFe2O4-NiAl2O4-FeAl2O4 layer inhibits the metal loss and ceramic-phase corrosion on the surface of the cermet inert anodes.展开更多
The CaO-doped Cu/（NiFe2O4-10NiO） cermet inert anodes were prepared by the cold isostatie pressing-sintering process, and their corrosion resistance to Na3AlF6-K3AlF6-Al203 melt was studied. The results show that the...The CaO-doped Cu/（NiFe2O4-10NiO） cermet inert anodes were prepared by the cold isostatie pressing-sintering process, and their corrosion resistance to Na3AlF6-K3AlF6-Al203 melt was studied. The results show that the relative density of 5Cu/（NiFe2O4-10NiO） cermet sintered at 1 200 ℃ increases from 82.83% to 97.63% when 2% CaO （mass fraction） is added. During the electrolysis, the relative density of cermet inert anode descends owing to the chemical dissolution of additive CaO at ceramic grain boundary, which accelerates the penetration of electrolyte. Thus, the corrosion resistance to melts of Cu/（NiFe2O4-10NiO） cermet inert anode is reduced. To improve the corrosion resistance of the cermet inert anode, the content of CaO doped should be decreased and the technology of cleaning the ceramic grain boundary should be applied.展开更多
The sintering behavior of NiFe2 O4-10NiO/xNi cermet which was used as the most prospective inert anode materials for aluminum electrolysis was studied by examining the effects of raw powder particle size, sintering te...The sintering behavior of NiFe2 O4-10NiO/xNi cermet which was used as the most prospective inert anode materials for aluminum electrolysis was studied by examining the effects of raw powder particle size, sintering temperature, and the contents of Ni. The results show that fine particle size enables the powder to have high driving force for sintering. High temperature is beneficial to densification, but the ultra-high temperature does harm to the improvement of the density. The samples of NiFe2O4-10NiO/SNi has the highest relative density of 97.28 % when it is sintered at 1 350 ℃, but it decreases to 95.23 % when sintered at 1 400 ℃. Low addition of Ni has a great help to the sintering of NiFe2 O4-10NiO matrix. When the samples are sintered at 1 350 ℃ and the mass fraction of Ni is 5%, the highest relative density is gained, but the density decreases with the further increase of Ni contents. The low density of the sintered samples of NiFe2 O4-10NiO/17Ni is attributed to the high volume fraction of pores.展开更多
基金Project (2012FJ6123) supported by the Project of Science and Technology of Hunan Province,ChinaProject supported by Post-Doctoral Foundation of Central South University,China+1 种基金Project (CL12100) supported the Undergraduate Innovative Training of Central South University,ChinaProject (2282013bkso13) supported by Free Exploration Plan of Central South University,China
文摘NiFe2O4-10NiO-based cermet inert anodes for aluminium electrolysis were prepared and their properties were investigated in a lab-scale electrolysis cell. The results show that the inert anodes exhibit good performance during electrolysis in molten salt cryolite at 960 °C, but according to the analyses of phase compositions and microstructures through XRD, SEM/EDX and metallographic analysis, the metal in the anodes is preferentially corroded and many pores are produced on the anode surface after electrolysis. The preferential dissolution of Fe in the NiFe2O4 phase may lead to the non-uniform corrosion of NiFe2O4 grains. Moreover, a dense protective layer of NiFe2O4-NiAl2O4-FeAl2O4 is formed on the anode surface, which originates from the reaction of Al2O3 dissolved in the electrolyte with NiO or FeO, the annexation of NiFe2O4-NiAl2O4-FeAl2O4 to NiO and volume expansion. Thus, the dense NiFe2O4-NiAl2O4-FeAl2O4 layer inhibits the metal loss and ceramic-phase corrosion on the surface of the cermet inert anodes.
基金Project(2005CB623703) supported by the Major State Basic Research and Development Program of ChinaProject(2008AA030503) supported by Hi-Tech Research and Development Program of China
文摘The CaO-doped Cu/（NiFe2O4-10NiO） cermet inert anodes were prepared by the cold isostatie pressing-sintering process, and their corrosion resistance to Na3AlF6-K3AlF6-Al203 melt was studied. The results show that the relative density of 5Cu/（NiFe2O4-10NiO） cermet sintered at 1 200 ℃ increases from 82.83% to 97.63% when 2% CaO （mass fraction） is added. During the electrolysis, the relative density of cermet inert anode descends owing to the chemical dissolution of additive CaO at ceramic grain boundary, which accelerates the penetration of electrolyte. Thus, the corrosion resistance to melts of Cu/（NiFe2O4-10NiO） cermet inert anode is reduced. To improve the corrosion resistance of the cermet inert anode, the content of CaO doped should be decreased and the technology of cleaning the ceramic grain boundary should be applied.
基金Project(2005CB623703) supported by the National Key Fundamental Research and Development Programof China
文摘The sintering behavior of NiFe2 O4-10NiO/xNi cermet which was used as the most prospective inert anode materials for aluminum electrolysis was studied by examining the effects of raw powder particle size, sintering temperature, and the contents of Ni. The results show that fine particle size enables the powder to have high driving force for sintering. High temperature is beneficial to densification, but the ultra-high temperature does harm to the improvement of the density. The samples of NiFe2O4-10NiO/SNi has the highest relative density of 97.28 % when it is sintered at 1 350 ℃, but it decreases to 95.23 % when sintered at 1 400 ℃. Low addition of Ni has a great help to the sintering of NiFe2 O4-10NiO matrix. When the samples are sintered at 1 350 ℃ and the mass fraction of Ni is 5%, the highest relative density is gained, but the density decreases with the further increase of Ni contents. The low density of the sintered samples of NiFe2 O4-10NiO/17Ni is attributed to the high volume fraction of pores.