The microstructure evolution of the Mg 5Zn 0.63Er（mass fraction,%） alloy containing quasicrystalline phase（I-phase） under the as-cast condition was investigated via different heat treatments.The results show that ...The microstructure evolution of the Mg 5Zn 0.63Er（mass fraction,%） alloy containing quasicrystalline phase（I-phase） under the as-cast condition was investigated via different heat treatments.The results show that apart from the precipitation of the W-phase particles,the I-phase almost dissolves into the matrix after solid solution treatment at 480℃ for 10 h（T4 state）.The solution-treated alloy was aged at 175℃ for 6-100 h（T6 state）.The ultimate tensile strength of the peak-aged alloy is approximately 261 MPa companying with an elongation of 10.5%.The improvement of the tensile strength is mainly attributed to the presence of the rod-like MgZn 2 particles.展开更多
Rat Liver Cd5Zn2-metallothionein isoforms were titrated with cuprous ion and monitored by 1H NMR Initial replacement occurred in β-domain followed by α-domain.MT exhibited well-defined structure under 10 mole equiva...Rat Liver Cd5Zn2-metallothionein isoforms were titrated with cuprous ion and monitored by 1H NMR Initial replacement occurred in β-domain followed by α-domain.MT exhibited well-defined structure under 10 mole equivalents cuprous ion.展开更多
基金Project(2007CB613706) supported by the National Basic Research Program of ChinaProjects(151071004,51101002) supported by the National Natural Science Foundation of China
文摘The microstructure evolution of the Mg 5Zn 0.63Er（mass fraction,%） alloy containing quasicrystalline phase（I-phase） under the as-cast condition was investigated via different heat treatments.The results show that apart from the precipitation of the W-phase particles,the I-phase almost dissolves into the matrix after solid solution treatment at 480℃ for 10 h（T4 state）.The solution-treated alloy was aged at 175℃ for 6-100 h（T6 state）.The ultimate tensile strength of the peak-aged alloy is approximately 261 MPa companying with an elongation of 10.5%.The improvement of the tensile strength is mainly attributed to the presence of the rod-like MgZn 2 particles.
文摘Rat Liver Cd5Zn2-metallothionein isoforms were titrated with cuprous ion and monitored by 1H NMR Initial replacement occurred in β-domain followed by α-domain.MT exhibited well-defined structure under 10 mole equivalents cuprous ion.