Constitutive equations for high temperature flow stress prediction of 6063 Al alloy considering compensation of strain

In order to develop the appropriate constitutive equation which can precisely model high temperature flow stress of 6063 Al alloy, a series of isothermal hot compression tests were performed at temperatures from 573 to 773 K and strain rates from 0.5 to 50 s?1 on a Gleeble?1500 thermo-simulation machine. Zener–Hollomon parameter in an exponent-type equation was used to describe the combined effects of temperature and strain rate on hot deformation behaviour of 6063 Al alloy, whereas the influence of strain was incorporated in the developed constitutive equation by considering material constants (α,n,Q andA) to be 4th order polynomial functions of strain. The results show that the developed constitutive equation can accurately predict high temperature flow stress of 6063 Al alloy, which demonstrates that it can be suitable for simulating hot deformation processes such as extrusion and forging, and for properly designing the deformation parameters in engineering practice.

Effects of extrusion speed of continuous extrusion with double billets on welding performance of 6063 Al alloy

During continuous extrusion,the welds were formed at the confluence of two billets.Influences of extrusion wheel rotational speed on micromorphology and properties of welds of 6063 Al alloy were investigated through microstructure observation,tensile test,and SEM analyses.Welding parameters were analyzed using finite element simulation.Results indicated that metal welding was remarkably affected by oxide on outer surface of the double billets during continuous extrusion.Degree of oxide breakage on the welding surface increased due to the evident increase in effective strain rate with increasing extrusion speed.The high temperature induced by increased extrusion speed accelerated the formation of metallurgical bonding.A portion of weld seam lines slowly disappeared,and the proportion of the welding interface that failed to reach metallurgical bonding was also gradually reduced.Tensile strength and elongation of the weld specimen increased with the increase of extrusion speed.

Deformation simulation of low-temperature high-speed extrusion for 6063 Al alloy

The hot compression test of 6063 Al alloy was performed on a Gleeble-1500 thermo-simulation machine, and the forming of 6063 rod cxtrudate in low-temperature high-speed extrusion was simulated with extrusion ratio of 25 on the platform of DEFORM 2D successfully. From the compression experimental results, the flow stress model of this Al alloy is obtained which could be the constitutive equation in the simulation of low-temperature high-speed extrusion process. From the numerical simulation results, there is a higher strain concentration at the entrance of the die and the exit temperature reaches up to 522 ℃ in low-temperature high-speed extrusion, which approaches to the quenching temperature of the 6063 Al alloy. The results show that the low-temperature high-speed extrusion method as a promsing one can reduce energy consumption effectively.

Deformation Behavior of 6063 Aluminum Alloy During High-Speed Compression

The deformation behavior characteristics of 6063 aluminum alloy were studied experimentally by isothermal compression tests on a Gleeble- 1500 thermal-mechanical simulator. Cylindrical specimens of 14mm in height and 10mm in diameter were compressed dynamically at temperatures ranging from 473 to 723K and at higher strain rntes from 5 to 30s^-1. It is fouud that the flow curves not only depend on the strain rate and temperature but nlso on the dynamic recovery aud recrystallization behavior. The results show that the flow stress decreased with the increase of temperature, while increased with the increase of strain rate. The discontinuous dynamic recrystallization （DDRX） may take place at a high strain rate of 20s^-1 under the tested conditions. At 30s^-1 , the flow curve can exhibit,flow softening due to the effect of temperature rise that raised the temperature by aboat 32K in less than 0.05s.

Migrating behaviors of interfacial elements and oxide layers during diffusion bonding of 6063Al alloys using Zn interlayer in air

The oxide layer on the surface has always been a key obstacle to achieving the diffusion bonding of Al alloys.It is a challenge for performing diffusion bonding without removing oxide layers.Herein,diffusion bonding of Al alloy retaining continuous oxide layers was successfully achieved in the air by a low-temperature and low-pressure diffusion bonding mothed using a Zn interlayer.During the bonding processes,conducted at 360℃ and 3 MPa,Zn diffused into Al through cracks of thin oxide layers to form the joint composed Al/(diffusion layer)/(oxide layer)/(Zn)/(oxide layer)/(diffusion layer)/Al.The diffusion layers were composed of Zn-Al eutectoid,and the oxide layer included nanocrystals and amorphous Al_(2)O_(3).The shear strength of joints containing continuous oxide layers was about 30 MPa.Interestingly,the migration behavior toward the joint center of the interfacial oxide layers was observed with consuming of the Zn interlayer.The cracking phenomenon,the“subcutaneous diffusion”and the migration behavior of oxide layers were verified and analyzed by the diffusion bonding of anodized 6063Al-6063Al.Subsequently,the dynamic migration mechanism of oxide layers with elements diffusion and bonding interface strengths were discussed in detail.The ability to join Al alloys in the air at low temperatures and low pressure suggests a highly practical and economic method for diffusion bonding.