The bonding interface of 7B52 Al alloy laminated composite （ALC） fabricated by hot rolling was investigated using optical microscopy （OM）, transmission electron microscopy （TEM）, scanning electron microscopy （...The bonding interface of 7B52 Al alloy laminated composite （ALC） fabricated by hot rolling was investigated using optical microscopy （OM）, transmission electron microscopy （TEM）, scanning electron microscopy （SEM）, ultrasonic flaw detection （UFD）, and bonding strength tests. The results show that metallurgical bonding is achieved at the interface after composite rolling. The TEM analysis and tensile tests indicate that the 7B52 ALC plate combines high strength of the hard individual layer and good toughness of the soft individual layer. However, UFD technology and SEM analysis prove that the defects （thick oxide films, acid washed residues, air, oil and coarse particles） existing in the bonding interface are harmful to the bonding strength. To sum up, the composite roiling process is suitable for 7B52 ALC plate, and the content and size of the defects should be controlled strictly. Advanced surface treatment of each individual layer would be beneficial to further improve the bonding quality.展开更多
基金Project(51312JQ08)supported by the Pre-Research Foundation of China General Equipment DepartmentProject(NBPJ2013-4)supported by the Postdoctoral Science Foundation of Ningbo Branch of China Academy of Ordnance Science+1 种基金Project(bsh1402073)supported by the Postdoctoral Science Foundation of Zhejiang Province,ChinaProject(2014A610051)supported by the Ningbo Natural Science Foundation of China
文摘The bonding interface of 7B52 Al alloy laminated composite （ALC） fabricated by hot rolling was investigated using optical microscopy （OM）, transmission electron microscopy （TEM）, scanning electron microscopy （SEM）, ultrasonic flaw detection （UFD）, and bonding strength tests. The results show that metallurgical bonding is achieved at the interface after composite rolling. The TEM analysis and tensile tests indicate that the 7B52 ALC plate combines high strength of the hard individual layer and good toughness of the soft individual layer. However, UFD technology and SEM analysis prove that the defects （thick oxide films, acid washed residues, air, oil and coarse particles） existing in the bonding interface are harmful to the bonding strength. To sum up, the composite roiling process is suitable for 7B52 ALC plate, and the content and size of the defects should be controlled strictly. Advanced surface treatment of each individual layer would be beneficial to further improve the bonding quality.