MORPHOLOGY OF MARTENSITE IN 7CrSiMnMoV STEEL AND ITS STRENGTH-TOUGHNESS

The morphology and substructure of martensites in 7CrSMnMoV steel were observed under optical or electron microscope,and martensitic transformation with its morphology was also analysed.In the normally quenched steel three types of martensites are found,including the wide lath one of dislocation substructure formed preferentially along grain boundaries,the thinner inner laths and the twinning martensite plate in interior of grain.Therefore,an at- tempt was made to substitute lower bainite,formed by short-term isothermal quenching.for intergranular martensite,it is believed that the morphology would be very influential to the stength-toughness of the steel.

7CrSiMnMoV钢的马氏体形态及其强韧性研究

本文用金相及电子显微分析研究了7CrSiMnMoV钢的马氏体形态及亚结构,并对不同形态的马氏体转化规律进行了分析。研究发现该钢冷却产生的马氏体有三种类型,包括晶界上优先产生的具有位错亚结构的宽大板条马氏体,晶内较细小的板条马氏体以及内部少量的孪晶马氏体片。基于上述结果,本工作试用短时等温淬火形成的下贝氏体来代替晶界马氏体,证明晶界组织形态对材料的强韧性有着很大的影响。

7CrSiMnMoV钢电火花线切割电参数优化及变质层研究

通过电火花线切割加工7CrSiMnMoV模具钢,对线切割加工电参数和工件表面的变质层进行了研究。利用正交试验的方法对加工电参数进行了优化,电参数优化后的工件表面质量得到提高。在此基础上观察分析了7CrSiMnMoV模具钢线切割后变质层的微观形貌和显微组织,并利用X射线衍射仪对线切割加工试样表面变质层的物相进行了分析。

7CrSiMnMoV钢贝氏体、马氏体混合组织的力学性能

本文研究贝氏体含量与贝氏体-马氏体(B/M)混合组织力学性能的关系。研究了工艺参数对混合组织强韧性的影响。实验得知,低温回火态的B/M混合组织中含有20～40%下贝氏体时的最佳强韧性。最佳淬火温度是900℃。采用80～100℃的热油淬火可以防止淬裂。

激光热处理对7CrSiMnMoV模具钢组织与性能的影响

激光热处理是一种高效、清洁的表面强化工艺,以7CrSiMnMoV模具钢为研究对象,进行了不同工艺参数下的激光热处理工艺实验,研究了激光功率和激光扫描速度对淬硬层微观组织和性能的影响规律。结果表明:7CrSiMnMoV模具钢自表层至淬硬层和热影响层均产生了大量针状马氏体,马氏体含量及其晶粒尺寸均随层深的增加而减小。通过控制激光能量密度即可使材料获得一定深度的淬硬层,拟合得到了淬硬层深度与激光能量密度的关系式,实现了淬硬层深度的预测。通过室温摩擦磨损实验,发现淬后试样的耐磨性显著增强,且试样的耐磨性随激光能量密度的增大而提升。