采用金相显微镜分析了30 t EAF-LF-VD-Φ200 mm电极-Φ360 mm ESR锭-120 mm×120 mm锻坯-Φ50 mm轧材的冶炼和加工工艺对不锈轴承钢9Cr18共晶碳化物的影响,结果表明,模铸电极浇注温度由1500~1510℃降至1485~1495℃,电渣重熔熔速由4....采用金相显微镜分析了30 t EAF-LF-VD-Φ200 mm电极-Φ360 mm ESR锭-120 mm×120 mm锻坯-Φ50 mm轧材的冶炼和加工工艺对不锈轴承钢9Cr18共晶碳化物的影响,结果表明,模铸电极浇注温度由1500~1510℃降至1485~1495℃,电渣重熔熔速由4.5 kg/min降至3.5 kg/min,增强电渣重熔冷却条件,可以有效减少冶炼过程中的共晶碳化物原始形成。采用锻透力强、大变形开坯,可使大颗粒碳化物破碎、减小颗粒尺寸,降低碳化物条带和网状聚集程度,能够有效改善不锈轴承钢共晶碳化物评级,减小碳化物颗粒尺寸。展开更多
Wear and corrosion are the main failure mechanisms of bearings and some measures have been proposed to prolong the working lifetime. Possible approaches include the use of more expensive materials, ion implantation, s...Wear and corrosion are the main failure mechanisms of bearings and some measures have been proposed to prolong the working lifetime. Possible approaches include the use of more expensive materials, ion implantation, surface finish enhancement, and ion beam assisted deposition. Among them ion implantation is used extensively for the modification of surface and properties of materials and many studies have disclosed that the beating steel surface can be strengthened by ion implantation of different elements such as N, Mo, N and Mo, and so on.展开更多
文摘Wear and corrosion are the main failure mechanisms of bearings and some measures have been proposed to prolong the working lifetime. Possible approaches include the use of more expensive materials, ion implantation, surface finish enhancement, and ion beam assisted deposition. Among them ion implantation is used extensively for the modification of surface and properties of materials and many studies have disclosed that the beating steel surface can be strengthened by ion implantation of different elements such as N, Mo, N and Mo, and so on.