We report the detailed crystal structures and physical properties of Ru_(1-x)Mo_(x)alloys in the solid solution range of x=0.1-0.9.Structure characterizations indicate that the crystal structure changes from the hcp-M...We report the detailed crystal structures and physical properties of Ru_(1-x)Mo_(x)alloys in the solid solution range of x=0.1-0.9.Structure characterizations indicate that the crystal structure changes from the hcp-Mg-type,toβ-CrFe-type,and then bcc-W-type.The measurements of physical properties show that the Ru_(1-x)Mo_(x)samples with x≥0.2are superconductors and the superconducting transition temperature T_c as a function of Mo content exhibits a dome-like behavior.展开更多
The microstructure evolutions of two A1-Zn-Mg alloys, one of which was alloyed with Sc and Zr, and the kinetics of A13（SCl-xZrx） precipitates in the A1-Zn-Mg alloy during homogenization were investigated. Both alloy...The microstructure evolutions of two A1-Zn-Mg alloys, one of which was alloyed with Sc and Zr, and the kinetics of A13（SCl-xZrx） precipitates in the A1-Zn-Mg alloy during homogenization were investigated. Both alloys under as-cast condition with supersaturated, non-equilibrium T（Mg32（A1, Zn）49） phase and impurities phase were displayed. When the homogenization temperatures are below 350 ~C, Zn and Mg atoms precipitate from matrix; however, when the temperatures are above 400 ~C, T phase dissolves into matrix, enhancing solid-solution strengthening. Kinetics of A13（Scl.xZrx） precipitates was studied based on Jmat Pro software calculation and the difference values between the hardness of the two alloys in each homogenization condition. The calculations predict that the Sc and Zr solubilities in ct-A1 decline with the presence of Mg and Zn. Investigation of the difference values reveals that when the temperature is between 300 ~C and 350 ~C, the nucleation rate of A13（Sc1-xZrx） precipitates is the highest and the strengthening effect from A13（SCl_xZrx） precipitates is the best. After homogenization at 470℃ for 12 h, non-equilibrium T phase disappears, while impurity phase remains. The mean diameter of A13（Scl_xZrx） precipitates is around 18 urn. Ideas about better fulfilling the potentials of Sc and Zr were proposed at last.展开更多
The Sr/F co-doped CaP(Sr/F-CaP)coatings were prepared by micro-arc oxidation(MAO)under different voltages to modify the microstructure and corrosion behavior of Mg-4Zn-1Mn alloy.The surface and interface characteristi...The Sr/F co-doped CaP(Sr/F-CaP)coatings were prepared by micro-arc oxidation(MAO)under different voltages to modify the microstructure and corrosion behavior of Mg-4Zn-1Mn alloy.The surface and interface characteristics investigated using scanning electron microscopy(SEM)and energy dispersive X-ray spectrometer(EDS)showed that the MAO coatings displayed uneven crater-like holes and tiny cracks under lower voltage,while they exhibited relatively homogeneous crater-like holes without cracks under higher voltage.The thickness of MAO coatings increased with increasing voltage.The corrosion behavior of Mg-4Zn-1Mn alloy was improved by the MAO coatings.The MAO coatings prepared under 450 V and 500 V voltages possessed the best corrosion resistance with regard to the electrochemical corrosion tests and immersion corrosion tests,respectively.The MAO coatings fabricated under 450-500 V could provide a better corrosion protection effect for the substrate.展开更多
The composites of Mg_(20)Pr_(1)Sm_(3)Y_(1)Ni_(10)as-quenched alloy and 3 wt.%M(M=CoS,CoS_(2),MoS_(2))catalyst were prepared by high-speed vibration ball mill.The effects of metal sulfides on the hydrogenation and dehy...The composites of Mg_(20)Pr_(1)Sm_(3)Y_(1)Ni_(10)as-quenched alloy and 3 wt.%M(M=CoS,CoS_(2),MoS_(2))catalyst were prepared by high-speed vibration ball mill.The effects of metal sulfides on the hydrogenation and dehydrogenation dynamics of alloys were compared.The results show that the as-milled composites contain a large number of amorphous embedded by a small amount of nanocrystals,and there are many point defects.After ball milling,the crystal grain size in the composites containing CoS is relatively larger,followed by CoS_(2)and MoS_(2)again.After hydrogenation,the amorphous phase is crystallized to form Mg_(2)NiH_(4),YH_(3),Pr_(8)H_(18.96),Sm_(3)H_7,Mg,Co or Mo phases,however,Mg_(2)Ni,YH_(2),PrH_(2)and Ni_(3)Y phases appeared after dehydrogenation.The maximum hydrogenation capacity of the composites containing CoS,CoS_(2)and MoS_(2)are 3.939,4.265 and 4.507 wt.%,respectively.The hydrogenation saturation ratio of composite containing MoS_(2)is higher than that of the composites containing CoS and CoS_(2).The dehydrogenation activation energy of the composites containing CoS,CoS_(2)and MoS_(2)is 107.76,68.43 and 63.28 kJ.mol^(-1).H_(2).On the improvement of hydrogen storage performance of Mg_(20)Pr_(1)Sm_(3)Y_(1)Ni_(10)alloy,the catalytic effect of MoS_(2)sulfide is better than that of CoS_(2)sulfide,and which is better than CoS sulfide.展开更多
The effects of Ce addition on the microstructure of Mg-6Zn-1Mn alloy during casting, homogenization, hot extrusion, T4, T6 and T4＋two-step aging were investigated. The mechanical properties of alloys with and without...The effects of Ce addition on the microstructure of Mg-6Zn-1Mn alloy during casting, homogenization, hot extrusion, T4, T6 and T4＋two-step aging were investigated. The mechanical properties of alloys with and without Ce were compared. The results showed that Ce had an obvious effect on the microstructure of ZM61-0.5Ce alloy by restricting the occurrence of dynamic recrystallization and restraining the grain growth during extrusion and heat treatment subsequently. A new binary phase Mg 12 Ce was identified in ZM61-0.5Ce alloy, which distributed at grain boundaries and was broken to small particles distributed at grain boundaries along extrusion direction during extrusion. The mechanical properties of as-extruded ZM61-0.5Ce alloy were improved with the addition of Ce. The improved tensile properties of as-extruded ZM61-0.5Ce alloy were due to the finer grain sizes as compared to ZM61 alloy. However, the UTS and YS decreased severely and the elongation increased when ZM61-0.5Ce was treated by T6 and T4＋two-step aging. Brittle Mg 12 Ce phase, which was distributed at the grain boundary areas and cannot dissolve into the Mg matrix after solution treatment, became crack source under tensile stress.展开更多
Mg-14Li-1Al （LA141）, LA141-0.3Y, LA141-0.3Sr, and LA141-0.3Y-0.3Sr alloys were prepared in an induction furnace in the argon atmosphere. The microstructures of these alloys were investigated through scanning electro...Mg-14Li-1Al （LA141）, LA141-0.3Y, LA141-0.3Sr, and LA141-0.3Y-0.3Sr alloys were prepared in an induction furnace in the argon atmosphere. The microstructures of these alloys were investigated through scanning electron microscope （SEM）, X-ray diffractometer （XRD） and energy dispersive spectrometer （EDS）. The results show that yttrium and/or strontium additions produce a strong grain refining effect in LA141 alloy. The mean grain sizes of the alloys with addition of Y and/or Sr are reduced remarkably from 600 to 500, 260, 230 μm, respectively. Al 2 Y, Al 4 Sr and Mg 17 Sr 2 phases with different morphologies are verified and exist inside the grain or at the grain boundaries, thus possibly act as heterogeneous nucleation sites and pin up grain boundaries, which restrain the grain growth.展开更多
The microstructural characteristics, mechanical properties and creep resistance of Mg-（8%-12%） Zn-（2%-6%） A1 alloys were investigated to get a better overall understanding of these series alloys. The results indic...The microstructural characteristics, mechanical properties and creep resistance of Mg-（8%-12%） Zn-（2%-6%） A1 alloys were investigated to get a better overall understanding of these series alloys. The results indicate that the microstructure of the alloys ZA82, ZA102 and ZA122 with the mass ratio of Zn to A1 of 4-6 is mainly composed of a-Mg matrix and two different morphologies of precipitates （block τ-Mg32（Al, Zn）49 and dense lamellar ε-Mg51Zn20）, the alloys ZA84, ZA104 and ZA124 with the mass ratio of 2-3 contain α-Mg matrix and only block r phases, and the alloys ZA86, ZA106 and ZA126 with the mass ratio of 1-2 consist of a-Mg matrix, block r precipitates, lamellar Ф-Al2Mg5Zn2 eutectics and flocculent β-Mg17Al12 compounds. The alloys studied with the mass ratio of Zn to A1 of 2-3 exhibit high creep resistance, and the alloy ZA124 with the continuous network of r precipitating along grain boundaries shows the highest creep resistance.展开更多
The corrosion anisotropy of 7050-T7451 A1 alloy thick plate in NaCI solution was investigated by immersion tests, slow strain rate testing （SSRT） technique, potentiodynamic and anode polarization measurements, optic...The corrosion anisotropy of 7050-T7451 A1 alloy thick plate in NaCI solution was investigated by immersion tests, slow strain rate testing （SSRT） technique, potentiodynamic and anode polarization measurements, optical microscropy （OM） and scanning electron microscopy （SEM） observations. The results show that the thick plate exhibits severe corrosion anisotropy due to the microstructure anisotropy. The observations of immersion surfaces together with the analysis of polarization curves reveal that the differences of the corrosion morphologies on various sections in this material are mainly related to the area fraction of the remnant second phase, and higher area fraction displays worst corrosion resistance. The stress corrosion cracking （SCC） susceptibility of different directions relative to the rolling direction is assessed by SSRT technique, ranked in the order： S direction 〉 L direction 〉 T direction. The result show that the smaller the grain aspect ratio, the better the corrosion resistance to SCC.展开更多
Influence of heat treatment on the microstructures and mechanical properties of sand-cast Mg-4Y-2Nd-1Gd-0.4Zr magnesium alloy was investigated,and the tensile fracture mechanisms of the studied alloys under different ...Influence of heat treatment on the microstructures and mechanical properties of sand-cast Mg-4Y-2Nd-1Gd-0.4Zr magnesium alloy was investigated,and the tensile fracture mechanisms of the studied alloys under different conditions were also discussed.The results show that the optimum T4 and T6 heat treatment conditions for the as-cast Mg-4Y-2Nd-1Gd-0.4Zr alloy are 525°C,8 h and（525°C,8 h）＋（225°C,16 h）,respectively,with regard to the microstructure observation,DSC heating curve and mechanical properties.The hardness,yield strength,ultimate tensile strength and elongation of the Mg-4Y-2Nd-1Gd-0.4Zr alloy treated by optimum T6 heat treatment are HV91,180 MPa,297 MPa and 7.4%,respectively.Moreover,the Mg-4Y-2Nd-1Gd-0.4Zr alloys under different heat treatment conditions exhibit different tensile fracture modes.展开更多
The microstructure of the 18R-type long period stacking ordered （LPSO） phase in Mg 97 Y 2 Zn 1 alloy was investigated by the first principles calculation. The arrangement rule of Zn and Y atoms in the LPSO structure...The microstructure of the 18R-type long period stacking ordered （LPSO） phase in Mg 97 Y 2 Zn 1 alloy was investigated by the first principles calculation. The arrangement rule of Zn and Y atoms in the LPSO structure is determined theoretically. The calculation results reveal that the additive atoms are firstly located in the fault layers at the two ends of the 18R-type LPSO structure, and then extend to fault layers in the interior, which is in good agreement with the experimental observations. This feature also implies the microstructural relationship between 18R and other LPSO structures. The cohesive energy and the formation heat indicate the dependence of the stability of 18R LPSO structure on contents of Y and Zn atoms. The calculated electronic structures reveal the underlying mechanism of microstructure and the stability of 18R LPSO structure.展开更多
The hot deformation behavior of a high Ti 6061 aluminum alloy in the temperature range from 350 to 510 ℃ and strain rate range from 0.001 to 10 s^-1 was investigated using stress-strain curve analysis, processing map...The hot deformation behavior of a high Ti 6061 aluminum alloy in the temperature range from 350 to 510 ℃ and strain rate range from 0.001 to 10 s^-1 was investigated using stress-strain curve analysis, processing map, transmission electron microscopy and electron backscatter diffraction analysis. The results show that the peak stress decreases with increasing deformation temperatures and decreasing strain rate. The average deformation activation energy is 185 kJ/mol in the parameter range investigated. The flow stress model was constructed. The main softening mechanism is dynamic recovery. The processing map was obtained using dynamic material model, and the suggested processing window is 400-440℃ and 0.001-0.1 s^-1.展开更多
The corrosion behaviours of Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys prepared by as-casting and extrusion were investigated in 5% NaCl aqueous solution by immersion and electrochemical tests. The microstructure indicates ...The corrosion behaviours of Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys prepared by as-casting and extrusion were investigated in 5% NaCl aqueous solution by immersion and electrochemical tests. The microstructure indicates the mean grain size of 15 μm for the extruded and 100 μm for the as-cast Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys. The corrosion morphology of as-cast sample shows pitting corrosion and little filiform corrosion, but that of the extruded sample shows pitting corrosion at the initial stage. The corrosion rate of extruded sample is higher than that of as-cast Mg-5Y-7Gd-1Nd-0.5Zr alloy according to the immersion test. The second phases containing RE acting as cathodes improve the corrosion properties. The corrosion potentials of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr alloys are -1.658 V and -1.591 V, respectively. The origins of the distinctive corrosion behavior of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr Mg alloys were discussed.展开更多
The microstructures and mechanical properties of Mg-6Zn-1Mn-4Sn-1.5Nd alloy subjected to extrusion and T5 treatment were investigated using optical microscopy（OM）, X-ray diffractometer（XRD）, scanning electron micr...The microstructures and mechanical properties of Mg-6Zn-1Mn-4Sn-1.5Nd alloy subjected to extrusion and T5 treatment were investigated using optical microscopy（OM）, X-ray diffractometer（XRD）, scanning electron microscopy（SEM）, electron back scattered diffraction（EBSD）, transmission electron microscopy（TEM）, hardness tests and uniaxial tensile tests. The results showed that the as-cast alloy consisted of α（Mg）, Mn, Mg7Zn3, Mg2 Sn and Mg Sn Nd phases. Dynamic recrystallization has completed during the extrusion process and the average grain size was 7.2 μm. After T5 treatment, the strength increased obviously, the yield strength and ultimate tensile strength of as-extruded alloy were increased by 94 and 34 MPa, respectively. Microstructure characterization revealed that the improvement of strength was determined by the high number density of β′1 rods.展开更多
基金Project supported by Beijing Natural Science Foundation (Grant No.Z200005)the National Key R&D Program of China (Grant Nos.2018YFE0202600 and 2022YFA1403800)+1 种基金the National Natural Science Foundation of China (Grant No.12274459)Beijing National Laboratory for Condensed Matter Physics,and Collaborative Research Project of Laboratory for Materials and Structures,Institute of Innovative Research,Tokyo Institute of Technology。
文摘We report the detailed crystal structures and physical properties of Ru_(1-x)Mo_(x)alloys in the solid solution range of x=0.1-0.9.Structure characterizations indicate that the crystal structure changes from the hcp-Mg-type,toβ-CrFe-type,and then bcc-W-type.The measurements of physical properties show that the Ru_(1-x)Mo_(x)samples with x≥0.2are superconductors and the superconducting transition temperature T_c as a function of Mo content exhibits a dome-like behavior.
基金Project(JPPT-115-2-948) supported by the National Civilian Matched Project of China
文摘The microstructure evolutions of two A1-Zn-Mg alloys, one of which was alloyed with Sc and Zr, and the kinetics of A13（SCl-xZrx） precipitates in the A1-Zn-Mg alloy during homogenization were investigated. Both alloys under as-cast condition with supersaturated, non-equilibrium T（Mg32（A1, Zn）49） phase and impurities phase were displayed. When the homogenization temperatures are below 350 ~C, Zn and Mg atoms precipitate from matrix; however, when the temperatures are above 400 ~C, T phase dissolves into matrix, enhancing solid-solution strengthening. Kinetics of A13（Scl.xZrx） precipitates was studied based on Jmat Pro software calculation and the difference values between the hardness of the two alloys in each homogenization condition. The calculations predict that the Sc and Zr solubilities in ct-A1 decline with the presence of Mg and Zn. Investigation of the difference values reveals that when the temperature is between 300 ~C and 350 ~C, the nucleation rate of A13（Sc1-xZrx） precipitates is the highest and the strengthening effect from A13（SCl_xZrx） precipitates is the best. After homogenization at 470℃ for 12 h, non-equilibrium T phase disappears, while impurity phase remains. The mean diameter of A13（Scl_xZrx） precipitates is around 18 urn. Ideas about better fulfilling the potentials of Sc and Zr were proposed at last.
文摘The Sr/F co-doped CaP(Sr/F-CaP)coatings were prepared by micro-arc oxidation(MAO)under different voltages to modify the microstructure and corrosion behavior of Mg-4Zn-1Mn alloy.The surface and interface characteristics investigated using scanning electron microscopy(SEM)and energy dispersive X-ray spectrometer(EDS)showed that the MAO coatings displayed uneven crater-like holes and tiny cracks under lower voltage,while they exhibited relatively homogeneous crater-like holes without cracks under higher voltage.The thickness of MAO coatings increased with increasing voltage.The corrosion behavior of Mg-4Zn-1Mn alloy was improved by the MAO coatings.The MAO coatings prepared under 450 V and 500 V voltages possessed the best corrosion resistance with regard to the electrochemical corrosion tests and immersion corrosion tests,respectively.The MAO coatings fabricated under 450-500 V could provide a better corrosion protection effect for the substrate.
基金the financial support provided by the Natural Science Foundations in Hebei Province(No.E2018201235)Baoding Science and Technology Planning Project(No.2074P019)+2 种基金Higher Education in Hebei Province School Science and Technology Research Project(No.QN2019209)Horizontal project(horizontal 20230048)2022 Hebei Province and Hebei University College Students Innovation and Entrepreneurship Training Program(Nos.2022265 and 2022266)。
文摘The composites of Mg_(20)Pr_(1)Sm_(3)Y_(1)Ni_(10)as-quenched alloy and 3 wt.%M(M=CoS,CoS_(2),MoS_(2))catalyst were prepared by high-speed vibration ball mill.The effects of metal sulfides on the hydrogenation and dehydrogenation dynamics of alloys were compared.The results show that the as-milled composites contain a large number of amorphous embedded by a small amount of nanocrystals,and there are many point defects.After ball milling,the crystal grain size in the composites containing CoS is relatively larger,followed by CoS_(2)and MoS_(2)again.After hydrogenation,the amorphous phase is crystallized to form Mg_(2)NiH_(4),YH_(3),Pr_(8)H_(18.96),Sm_(3)H_7,Mg,Co or Mo phases,however,Mg_(2)Ni,YH_(2),PrH_(2)and Ni_(3)Y phases appeared after dehydrogenation.The maximum hydrogenation capacity of the composites containing CoS,CoS_(2)and MoS_(2)are 3.939,4.265 and 4.507 wt.%,respectively.The hydrogenation saturation ratio of composite containing MoS_(2)is higher than that of the composites containing CoS and CoS_(2).The dehydrogenation activation energy of the composites containing CoS,CoS_(2)and MoS_(2)is 107.76,68.43 and 63.28 kJ.mol^(-1).H_(2).On the improvement of hydrogen storage performance of Mg_(20)Pr_(1)Sm_(3)Y_(1)Ni_(10)alloy,the catalytic effect of MoS_(2)sulfide is better than that of CoS_(2)sulfide,and which is better than CoS sulfide.
基金Project(2007CB613700)supported by the National Basic Research Program of ChinaProject(2007BAG06B04)supported by the National Key Technology R&D Program+2 种基金Project(CSTC,2009AB4008)supported by the Chongqing Sci&Tech ProgramProject(50725413)supported by the National Natural Science Foundation of ChinaProject(CDJXS10132202)supported by the Fundamental Research Funds for the Central Universities, China
文摘The effects of Ce addition on the microstructure of Mg-6Zn-1Mn alloy during casting, homogenization, hot extrusion, T4, T6 and T4＋two-step aging were investigated. The mechanical properties of alloys with and without Ce were compared. The results showed that Ce had an obvious effect on the microstructure of ZM61-0.5Ce alloy by restricting the occurrence of dynamic recrystallization and restraining the grain growth during extrusion and heat treatment subsequently. A new binary phase Mg 12 Ce was identified in ZM61-0.5Ce alloy, which distributed at grain boundaries and was broken to small particles distributed at grain boundaries along extrusion direction during extrusion. The mechanical properties of as-extruded ZM61-0.5Ce alloy were improved with the addition of Ce. The improved tensile properties of as-extruded ZM61-0.5Ce alloy were due to the finer grain sizes as compared to ZM61 alloy. However, the UTS and YS decreased severely and the elongation increased when ZM61-0.5Ce was treated by T6 and T4＋two-step aging. Brittle Mg 12 Ce phase, which was distributed at the grain boundary areas and cannot dissolve into the Mg matrix after solution treatment, became crack source under tensile stress.
基金Project(50725413)supported by the National Natural Science Foundation of ChinaProject(2010CSTC-BJLKR)supported by Chongqing Science and Technology Commission, ChinaProject(CDJXS10132203)supported by the Fundamental Research Funds for the Central Universities,China
文摘Mg-14Li-1Al （LA141）, LA141-0.3Y, LA141-0.3Sr, and LA141-0.3Y-0.3Sr alloys were prepared in an induction furnace in the argon atmosphere. The microstructures of these alloys were investigated through scanning electron microscope （SEM）, X-ray diffractometer （XRD） and energy dispersive spectrometer （EDS）. The results show that yttrium and/or strontium additions produce a strong grain refining effect in LA141 alloy. The mean grain sizes of the alloys with addition of Y and/or Sr are reduced remarkably from 600 to 500, 260, 230 μm, respectively. Al 2 Y, Al 4 Sr and Mg 17 Sr 2 phases with different morphologies are verified and exist inside the grain or at the grain boundaries, thus possibly act as heterogeneous nucleation sites and pin up grain boundaries, which restrain the grain growth.
基金Project(10KJB430012) supported by the Natural Science Foundation of the Jiangsu Higher Education Institutions of ChinaProject (BK2011063) supported by the Nantong Science and Technology Commission of China
文摘The microstructural characteristics, mechanical properties and creep resistance of Mg-（8%-12%） Zn-（2%-6%） A1 alloys were investigated to get a better overall understanding of these series alloys. The results indicate that the microstructure of the alloys ZA82, ZA102 and ZA122 with the mass ratio of Zn to A1 of 4-6 is mainly composed of a-Mg matrix and two different morphologies of precipitates （block τ-Mg32（Al, Zn）49 and dense lamellar ε-Mg51Zn20）, the alloys ZA84, ZA104 and ZA124 with the mass ratio of 2-3 contain α-Mg matrix and only block r phases, and the alloys ZA86, ZA106 and ZA126 with the mass ratio of 1-2 consist of a-Mg matrix, block r precipitates, lamellar Ф-Al2Mg5Zn2 eutectics and flocculent β-Mg17Al12 compounds. The alloys studied with the mass ratio of Zn to A1 of 2-3 exhibit high creep resistance, and the alloy ZA124 with the continuous network of r precipitating along grain boundaries shows the highest creep resistance.
基金Project(2012CB619502)supported by the National Basic Research Program of China
文摘The corrosion anisotropy of 7050-T7451 A1 alloy thick plate in NaCI solution was investigated by immersion tests, slow strain rate testing （SSRT） technique, potentiodynamic and anode polarization measurements, optical microscropy （OM） and scanning electron microscopy （SEM） observations. The results show that the thick plate exhibits severe corrosion anisotropy due to the microstructure anisotropy. The observations of immersion surfaces together with the analysis of polarization curves reveal that the differences of the corrosion morphologies on various sections in this material are mainly related to the area fraction of the remnant second phase, and higher area fraction displays worst corrosion resistance. The stress corrosion cracking （SCC） susceptibility of different directions relative to the rolling direction is assessed by SSRT technique, ranked in the order： S direction 〉 L direction 〉 T direction. The result show that the smaller the grain aspect ratio, the better the corrosion resistance to SCC.
基金Project(0502)supported by the Aerospace Science and Technology Innovation Fund of China Aerospace Science and Technology CorporationProject(2007CB613701)supported by the National Basic Research Program of ChinaProject(2009AA033501)supported by the National High-tech Research and Development Program of China
文摘Influence of heat treatment on the microstructures and mechanical properties of sand-cast Mg-4Y-2Nd-1Gd-0.4Zr magnesium alloy was investigated,and the tensile fracture mechanisms of the studied alloys under different conditions were also discussed.The results show that the optimum T4 and T6 heat treatment conditions for the as-cast Mg-4Y-2Nd-1Gd-0.4Zr alloy are 525°C,8 h and（525°C,8 h）＋（225°C,16 h）,respectively,with regard to the microstructure observation,DSC heating curve and mechanical properties.The hardness,yield strength,ultimate tensile strength and elongation of the Mg-4Y-2Nd-1Gd-0.4Zr alloy treated by optimum T6 heat treatment are HV91,180 MPa,297 MPa and 7.4%,respectively.Moreover,the Mg-4Y-2Nd-1Gd-0.4Zr alloys under different heat treatment conditions exhibit different tensile fracture modes.
基金Projects(50861002,51071053)supported by the National Natural Science Foundation of ChinaProject(0991051)supported by NaturalScience Foundation of Guangxi Province,China+1 种基金Project(KF0803)supported by Open Project of Key Laboratory of Materials Design and Preparation Technology of Hunan Province,ChinaProject(X071117)supported by Scientific Research Foundation of Guangxi University,China
文摘The microstructure of the 18R-type long period stacking ordered （LPSO） phase in Mg 97 Y 2 Zn 1 alloy was investigated by the first principles calculation. The arrangement rule of Zn and Y atoms in the LPSO structure is determined theoretically. The calculation results reveal that the additive atoms are firstly located in the fault layers at the two ends of the 18R-type LPSO structure, and then extend to fault layers in the interior, which is in good agreement with the experimental observations. This feature also implies the microstructural relationship between 18R and other LPSO structures. The cohesive energy and the formation heat indicate the dependence of the stability of 18R LPSO structure on contents of Y and Zn atoms. The calculated electronic structures reveal the underlying mechanism of microstructure and the stability of 18R LPSO structure.
文摘The hot deformation behavior of a high Ti 6061 aluminum alloy in the temperature range from 350 to 510 ℃ and strain rate range from 0.001 to 10 s^-1 was investigated using stress-strain curve analysis, processing map, transmission electron microscopy and electron backscatter diffraction analysis. The results show that the peak stress decreases with increasing deformation temperatures and decreasing strain rate. The average deformation activation energy is 185 kJ/mol in the parameter range investigated. The flow stress model was constructed. The main softening mechanism is dynamic recovery. The processing map was obtained using dynamic material model, and the suggested processing window is 400-440℃ and 0.001-0.1 s^-1.
基金Project (2011BAE22B01) supported by the National Key Technology R&D Program of China
文摘The corrosion behaviours of Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys prepared by as-casting and extrusion were investigated in 5% NaCl aqueous solution by immersion and electrochemical tests. The microstructure indicates the mean grain size of 15 μm for the extruded and 100 μm for the as-cast Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys. The corrosion morphology of as-cast sample shows pitting corrosion and little filiform corrosion, but that of the extruded sample shows pitting corrosion at the initial stage. The corrosion rate of extruded sample is higher than that of as-cast Mg-5Y-7Gd-1Nd-0.5Zr alloy according to the immersion test. The second phases containing RE acting as cathodes improve the corrosion properties. The corrosion potentials of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr alloys are -1.658 V and -1.591 V, respectively. The origins of the distinctive corrosion behavior of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr Mg alloys were discussed.
基金Project(2013CB632200)supported by the National Great Theoretic Research,ChinaProject(2011BAE22B01-3)supported by the National Sci&Tech Support Program,ChinaProject(2010DFR50010)supported by the International Cooperation,Sharing Fund of Chongqing University’s Large-scale Equipment,China
文摘The microstructures and mechanical properties of Mg-6Zn-1Mn-4Sn-1.5Nd alloy subjected to extrusion and T5 treatment were investigated using optical microscopy（OM）, X-ray diffractometer（XRD）, scanning electron microscopy（SEM）, electron back scattered diffraction（EBSD）, transmission electron microscopy（TEM）, hardness tests and uniaxial tensile tests. The results showed that the as-cast alloy consisted of α（Mg）, Mn, Mg7Zn3, Mg2 Sn and Mg Sn Nd phases. Dynamic recrystallization has completed during the extrusion process and the average grain size was 7.2 μm. After T5 treatment, the strength increased obviously, the yield strength and ultimate tensile strength of as-extruded alloy were increased by 94 and 34 MPa, respectively. Microstructure characterization revealed that the improvement of strength was determined by the high number density of β′1 rods.