The regularities of atmospheric corrosion of A3 steel deposited with different amount of NaCl exposed to the air containing 1ppm SO2 at 80%RH and 25℃ were studied in laboratory. NaCl can accelerate the corrosion of A...The regularities of atmospheric corrosion of A3 steel deposited with different amount of NaCl exposed to the air containing 1ppm SO2 at 80%RH and 25℃ were studied in laboratory. NaCl can accelerate the corrosion of A3 steel obviously under such condition. The relationship between the weight loss of A3 steel and the amount of NaCl deposition can be well described by using a quadratic function. Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), Scanning electron microscopy and electron dispersion X-ray analysis (SEM/EDAX) were used to characterize the corrosion products. In the absence of NaCl, FeSO4 · xH2O is the dominant corrosion products, while Fe3O4, FeSO4·H2O, β-FeOOH and γ-FeOOH dominate in the presence of NaCl.展开更多
Regularity of the initial atmospheric corrosion of A3 steel in the presence of NaCI was investigated. The results showed that NaCI can accelerate the corrosion of A3 steel. Dry mass gain of A3 steel in the presence of...Regularity of the initial atmospheric corrosion of A3 steel in the presence of NaCI was investigated. The results showed that NaCI can accelerate the corrosion of A3 steel. Dry mass gain of A3 steel in the presence of NaCI deposition increases with the exposure time, which can be correlated by using exponential decay function. The relationship between dry mass gain and amount of NaCI deposition at a certain exposure time follows a quadratic function. More amount of NaCI deposition will slow down the corrosion rate to some extent after exposure for a certain time. SEM/EDAX was used to characterize the corrosion surface and products. The surfaces of the NaCI treated A3 steel were obviously uneven, and some tiny crevices appear in the corrosion products that could help O2 transmit to the inner layer. The amount of oxygen in atomic percentage in the corrosion products increases with the amount of NaCI deposition.展开更多
The morphology and corrosion behavior of Ni/Al2O3 composite coatings prepared using double-pulsed electrodepositing technique after oxidized under 800 ℃ NaCl deposit in air environment were analyzed by scanning elect...The morphology and corrosion behavior of Ni/Al2O3 composite coatings prepared using double-pulsed electrodepositing technique after oxidized under 800 ℃ NaCl deposit in air environment were analyzed by scanning electrical microscope (SEM), X-ray diffraction(XRD) and energy dispersive spectrum(EDS). The results showed that the corrosion of all composite coatings was accelerated under NaCl deposits, and the corrosion products were rather porous with poor adherence to the matrix. Al2O3 particles in the coatings can refine the grain size and improve the high temperature corrosion resistance of the coatings. Within the test scope, the more Al2O3 particles in the coatings, the lower corrosion rates could be obtained, and the corrosion mechanism was also discussed.展开更多
A laboratory study of the atmospheric corrosion of carbon steel deposited with (NH4)2SO4 in the presence of SO2 is reported. The different levels of (NH4)2SO4 (0, 15, 30, 45, 60 μg·cm-2) were added on the surfac...A laboratory study of the atmospheric corrosion of carbon steel deposited with (NH4)2SO4 in the presence of SO2 is reported. The different levels of (NH4)2SO4 (0, 15, 30, 45, 60 μg·cm-2) were added on the surface of the samples before the exposure. The corrosion was investigated by a combination of gravimetry, Fourier transform infrared spectroscope and scanning electron microscopy. A detailed knowledge about the corrosion products was acquired, both quantitatively and qualitatively. The results show that the metal loss increased and the increasing tendency of corrosion rates slowed down with the increasing exposure time. The phase constituents of the corrosion products are mainly α-FeO(OH), γ-FeO(OH), and δ-FeO(OH).展开更多
21Cr2NiMo steel is widely used to stabilize offshore oil platforms;however,it suffers from stress-corrosion cracking(SCC).Herein,we studied the SCC behavior of 21Cr2NiMo steel in SO_(2)-polluted coastal atmospheres.El...21Cr2NiMo steel is widely used to stabilize offshore oil platforms;however,it suffers from stress-corrosion cracking(SCC).Herein,we studied the SCC behavior of 21Cr2NiMo steel in SO_(2)-polluted coastal atmospheres.Electrochemical tests revealed that the addition of SO_(2) increased the corrosion current.Rust characterization showed that SO_(2) addition densified the corrosion products and promoted pitting.Furthermore,slow strain rate tests demonstrated a high susceptibility to SCC in high SO_(2) contents.Fracture morphologies revealed that the stress-corrosion cracks initiated at corrosion pits and the crack propagation showed transgranular and intergranular cracking modes.In conclusion,SCC is mix-controlled by anodic dissolution and hydrogen embrittlement mechanisms.展开更多
Fe/Al2O3 ceramic coating was made by spraying and sol-gel. The corrosion resistance between Fe/Al2O3 ceramic coating and steel 45# was studied. By microscope and X-ray diffraction, the binding and the composition of ...Fe/Al2O3 ceramic coating was made by spraying and sol-gel. The corrosion resistance between Fe/Al2O3 ceramic coating and steel 45# was studied. By microscope and X-ray diffraction, the binding and the composition of the interface were also analyzed. The results showed that Fe/Al2O3 ceramic coating had dense struc- ture, less porosity and better binding with the substrate which was effective to prevent erosive liquor immersing into the inside of ceramic coating. Some substances that distributed homogeneously in Fe/Al2O3 ceramic coating, such as α-Al2O3, FeAlO3 and Fe3Al, could improve the corrosion resistance of this material.展开更多
基金This work was financially supported by the National Natural Science Foundation of China (Project No. 59899144). The authors are grateful to Ms Wang for English diction.
文摘The regularities of atmospheric corrosion of A3 steel deposited with different amount of NaCl exposed to the air containing 1ppm SO2 at 80%RH and 25℃ were studied in laboratory. NaCl can accelerate the corrosion of A3 steel obviously under such condition. The relationship between the weight loss of A3 steel and the amount of NaCl deposition can be well described by using a quadratic function. Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), Scanning electron microscopy and electron dispersion X-ray analysis (SEM/EDAX) were used to characterize the corrosion products. In the absence of NaCl, FeSO4 · xH2O is the dominant corrosion products, while Fe3O4, FeSO4·H2O, β-FeOOH and γ-FeOOH dominate in the presence of NaCl.
基金This work was financially supported by the National Natural Science Foundation of China. The number of the project is 5989914. The authors are grateful to Ms. Ping Wan for English diction.
文摘Regularity of the initial atmospheric corrosion of A3 steel in the presence of NaCI was investigated. The results showed that NaCI can accelerate the corrosion of A3 steel. Dry mass gain of A3 steel in the presence of NaCI deposition increases with the exposure time, which can be correlated by using exponential decay function. The relationship between dry mass gain and amount of NaCI deposition at a certain exposure time follows a quadratic function. More amount of NaCI deposition will slow down the corrosion rate to some extent after exposure for a certain time. SEM/EDAX was used to characterize the corrosion surface and products. The surfaces of the NaCI treated A3 steel were obviously uneven, and some tiny crevices appear in the corrosion products that could help O2 transmit to the inner layer. The amount of oxygen in atomic percentage in the corrosion products increases with the amount of NaCI deposition.
文摘The morphology and corrosion behavior of Ni/Al2O3 composite coatings prepared using double-pulsed electrodepositing technique after oxidized under 800 ℃ NaCl deposit in air environment were analyzed by scanning electrical microscope (SEM), X-ray diffraction(XRD) and energy dispersive spectrum(EDS). The results showed that the corrosion of all composite coatings was accelerated under NaCl deposits, and the corrosion products were rather porous with poor adherence to the matrix. Al2O3 particles in the coatings can refine the grain size and improve the high temperature corrosion resistance of the coatings. Within the test scope, the more Al2O3 particles in the coatings, the lower corrosion rates could be obtained, and the corrosion mechanism was also discussed.
文摘A laboratory study of the atmospheric corrosion of carbon steel deposited with (NH4)2SO4 in the presence of SO2 is reported. The different levels of (NH4)2SO4 (0, 15, 30, 45, 60 μg·cm-2) were added on the surface of the samples before the exposure. The corrosion was investigated by a combination of gravimetry, Fourier transform infrared spectroscope and scanning electron microscopy. A detailed knowledge about the corrosion products was acquired, both quantitatively and qualitatively. The results show that the metal loss increased and the increasing tendency of corrosion rates slowed down with the increasing exposure time. The phase constituents of the corrosion products are mainly α-FeO(OH), γ-FeO(OH), and δ-FeO(OH).
基金financially supported by the Fundamental Research Funds for the Central Universities(No.FRF-MP-18-002)。
文摘21Cr2NiMo steel is widely used to stabilize offshore oil platforms;however,it suffers from stress-corrosion cracking(SCC).Herein,we studied the SCC behavior of 21Cr2NiMo steel in SO_(2)-polluted coastal atmospheres.Electrochemical tests revealed that the addition of SO_(2) increased the corrosion current.Rust characterization showed that SO_(2) addition densified the corrosion products and promoted pitting.Furthermore,slow strain rate tests demonstrated a high susceptibility to SCC in high SO_(2) contents.Fracture morphologies revealed that the stress-corrosion cracks initiated at corrosion pits and the crack propagation showed transgranular and intergranular cracking modes.In conclusion,SCC is mix-controlled by anodic dissolution and hydrogen embrittlement mechanisms.
文摘Fe/Al2O3 ceramic coating was made by spraying and sol-gel. The corrosion resistance between Fe/Al2O3 ceramic coating and steel 45# was studied. By microscope and X-ray diffraction, the binding and the composition of the interface were also analyzed. The results showed that Fe/Al2O3 ceramic coating had dense struc- ture, less porosity and better binding with the substrate which was effective to prevent erosive liquor immersing into the inside of ceramic coating. Some substances that distributed homogeneously in Fe/Al2O3 ceramic coating, such as α-Al2O3, FeAlO3 and Fe3Al, could improve the corrosion resistance of this material.