The effects of low-Co AB_5 type hydrogen storage alloys prepared by quenchingand annealing on the performances of MH-Ni batteries were investigated, and the characteristics ofthe low-Co AB_5 type hydrogen storage allo...The effects of low-Co AB_5 type hydrogen storage alloys prepared by quenchingand annealing on the performances of MH-Ni batteries were investigated, and the characteristics ofthe low-Co AB_5 type hydrogen storage alloys were compared with those of the high-Co AB_5 typehydrogen storage alloy as well. The results showed that the faster the cooling of the low-Cohydrogen storage alloy is, the better homogeneity of the chemical composition for the alloy and thelonger cycle life of the battery are, but the electrochemical discharge capacity and high-ratedischarge ability are reduced. The high-rate discharge ability and charge retention of MH-Nibatteries for the conventional as-cast annealed low-Co hydrogen storage alloy were superior to thosefor the rapidly quenched low-Co hydrogen storage alloy and the high-Co hydrogen storage alloy, buta little inferior in the cycle life.展开更多
Fuel cell using borohydride as the fuel has received much attention. AB5-type hydrogen storage alloy used as the anodic material instead of noble metals has been investigated. In order to restrain the generation of hy...Fuel cell using borohydride as the fuel has received much attention. AB5-type hydrogen storage alloy used as the anodic material instead of noble metals has been investigated. In order to restrain the generation of hydrogen and enhance the utilization of borohydride, Ti/Zr metal powders has been added into the parent LmNi4.78Mn0.22 (where Lm is La-richened mischmetal) alloy (LNM) by ball milling and heat treatment methods. It is found that the addition of Ti/Zr metal powders lowers the electrochemical catalytic activity of the electrodes, at the same time, restrains the generation of hydrogen and enhances the utilization of the fuel. All the results show that the hydrogen generation rate or the utilization of the fuel is directly relative to the electrochemical catalytic activity or the discharge capability of the electrodes. The utilization of the fuel increases with discharge current density. It is very important to find a balance between the discharge capability and the utilization of the fuel.展开更多
The effect of the hot-charging treatment on the performance of AB2 and AB5 hydrogen storage alloy electrodes was investigated. The result showed that the treatment can markedly improve the voltage plateau ratio (VPR),...The effect of the hot-charging treatment on the performance of AB2 and AB5 hydrogen storage alloy electrodes was investigated. The result showed that the treatment can markedly improve the voltage plateau ratio (VPR), the high rate discharge ability (HRDA), the diffusion coefficient of hydrogen DH and the discharge capacity of the AB2 hydrogen storage alloy electrode. The SEM analysis showed that the hot-charging treatment brings about a Ni-rich surface due to the dissolution of Zr oxides. It is also very helpful for the improvement of the kinetic properties of AB2 hydrogen storage alloy electrode because the microcracking of the surface results in fresh surface. This can be the basic modification treatment for NiMH battery used in electric vehicles (EVs) in the future. But for AB5 type alloys, the treatment has the disadvantage of impairing the comprehensive electrochemical properties, because the surface of the alloy may be corroded during the treatment. The mechanism of the surface modification of the electrode is also proposed.展开更多
The effect of thickness (1 similar to 10 mm) of the ingots on the electrochemical properties of as-cast and annealed strip cast LPCNi3.55Co0.75Mn0.4Al0.3 hydrogen storage alloys was investigated. It is found that the ...The effect of thickness (1 similar to 10 mm) of the ingots on the electrochemical properties of as-cast and annealed strip cast LPCNi3.55Co0.75Mn0.4Al0.3 hydrogen storage alloys was investigated. It is found that the 0.2 C discharge capacity of as-cast LPCNi3.55Co0.75Mn0.4Al0.3 alloy increases with the increase of the thickness of the ingots. As-east alloy with the thickness of 10 mm shows better activation property, higher 1C discharge capacity and better cyclic stability than others. It is mainly contributed to its larger unit cell volume and less internal stress. Annealed LPCNi3.55Co0.75Mn0.4Al0.3 alloy with the thickness of 3 mm shows much better comprehensive electrochemical properties than as-east one; The cyclic. stability of the alloy with the thickness of 6 mm and the activation properties of the alloys with the thickness of 3 similar to 6 mm are improved after annealing. It is mainly owing to the great release of internal stress and the decrease of the segregation of Mn in the alloys.展开更多
The effects of partial substitution of La by Ce and Ni by Al, Fe, or Co in LaNi_5-based alloys on hydrogen storage performance were systematically studied. All samples were prepared using vacuum arc melting in an argo...The effects of partial substitution of La by Ce and Ni by Al, Fe, or Co in LaNi_5-based alloys on hydrogen storage performance were systematically studied. All samples were prepared using vacuum arc melting in an argon atmosphere. The results showed that for LaNi_(5-x)M_x(M = Al, Fe, or Co) alloys, the lattice constants and unit cell volumes increased with an increasing amount of Al and Fe. On the other hand, these parameters decreased upon partial substitution of La by Ce. In addition, the lattice constant remained almost constant in the La_(0.6)Ce_(0.4)Ni_(5–x)Cox alloys regardless of the value of x(x = 0.3, 0.6, or 0.9), as Ce might enhance the homogeneity of the CaCu_5-type phase in Co-containing alloys. The hydrogen storage properties of the alloys were investigated using pressure, composition, and temperature isotherms. The experimental results showed that the plateau pressure decreased with an increasing content of Al, Fe, or Co, but it increased with Ce addition. Furthermore, the plateau pressures of all Co-containing alloys were almost identical upon substitution with Ce. Finally, the enthalpy(ΔH) and entropy(ΔS) values for all alloys were calculated using van't Hoff plots. The relationship between the lattice parameters and enthalpy changes for hydrogenation will be discussed.展开更多
LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 hydrogen storage alloy was investigated, and the effects of thickness of its strip casting ingots(as cast) on the electrochemical performances were discussed. It was ...LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 hydrogen storage alloy was investigated, and the effects of thickness of its strip casting ingots(as cast) on the electrochemical performances were discussed. It was found that the 0.2 C discharge capacity increased with the increase of the thickness (from 1 mm to 10 mm) of the ingots, mainly due to the enlargement of the unit cell volume; Among the thickness of the ingots in our study, 10 mm sample showed a better activation property; LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 alloy with 10mm showed higher comprehensive properties than those with other thickness under 1C rate.展开更多
The structure and electrochemical characteristics of La0.7Mg0.3Ni2.875Co0.525Mn0.1-boron composite was studied systematically. The AB3 type hydrogen storage alloys La0.7Mg0.3Ni2.875Co0.525Mn0.1 were successfully synth...The structure and electrochemical characteristics of La0.7Mg0.3Ni2.875Co0.525Mn0.1-boron composite was studied systematically. The AB3 type hydrogen storage alloys La0.7Mg0.3Ni2.875Co0.525Mn0.1 were successfully synthesized by means of inter-media alloy La2Mg17. The alloys were composited with boron at different weight rate. From the XRD analyses, each alloy of this series is mainly composed of (La,Mg)Ni3 phase and the LaNi5 phase, and the phase abundance of each phase varies with the boron weight rate, moreover, after composition, the c and cell volumes of (La,Mg)Ni3 phase increase, and the LaNi5 phase keep the same, which indicate that the boron may enter (La,Mg)Ni3 phase. The electrochemical studies show that the maximum discharge capacity of the composites decreases, but the cycling life improved. And the high rate discharge ability and exchange impendence spectroscopy (EIS) of the AB3 alloys and its composite were also studied.展开更多
In order to reduce the cost of LaNi5 based hydrogen storage alloys, effect of substitution of Mn for Ni on structural and electrochemical properties of LaNi4-xFeMnx (x=0-0.8) hydrogen storage alloys was studied system...In order to reduce the cost of LaNi5 based hydrogen storage alloys, effect of substitution of Mn for Ni on structural and electrochemical properties of LaNi4-xFeMnx (x=0-0.8) hydrogen storage alloys was studied systematically. X-ray diffraction (XRD) and scanning electron microscope (SEM) showed that LaNi5 and La2Ni7 phases were invariably present in all alloy samples, and when x >= 0.4, (Fe, Ni) phase was observed. Electrochemical studies revealed that the discharge capacity reached a maximum value of 306.4 mAh/g when x=0.2 and the cycling stability decreased with the increase of x. With the increase of Mn content, hydrogen diffusion coefficient decreased, whereas high rate discharge-ability (HRD) and exchange current density first increased slowly when x <= 0.2 and then decreased markedly when x=0.8, indicating that electrochemical reaction on the surface of alloy electrodes had strong influence on kinetic property.展开更多
The electronic structures of LaNi5 hydrogen storage alloys and its micro-hydrogenated compounds with two hydrogen atoms in the center of two octahedral interstices and two tetrahedral interstices, were investigated by...The electronic structures of LaNi5 hydrogen storage alloys and its micro-hydrogenated compounds with two hydrogen atoms in the center of two octahedral interstices and two tetrahedral interstices, were investigated by the first principles discrete variational method (DVM). The results of density of states and the difference of charge distribution clearly show that the s electrons of H mainly interact with the s electrons of hydride-non-forming element Ni, despite there being a larger affinity of La for hydrogen than that of Ni in pure metal-hydrogen system. From the cohesive energy of systems, we also found two systems have almost same stability with occupation of H atoms.展开更多
The microstructure ofthe Mg/MmNi5-x (CoAlMn )x composite hydrogen storage material preparedby the method of mechanical alloyingwas characterized by X-ray diffraction, SEM and particle size distribution analysis. By me...The microstructure ofthe Mg/MmNi5-x (CoAlMn )x composite hydrogen storage material preparedby the method of mechanical alloyingwas characterized by X-ray diffraction, SEM and particle size distribution analysis. By measuring PCTcurves, the hydrogen absorption properties of the composite was evaluated.The results show that nanocrystallinecomposite structure can be obtainedunder adequate ball milling condition. The reactive activation and hydrogen absorption capacity are improved compared with the sole MmNi5-x(CoAlMn)x alloy. The effect ofmagnesium on the microstructure andhydrogen absorption properties of thecomposite were also evaluated.展开更多
The electronic structures are calculated by the DV-Xa molecular orbital method employing small model clusters in order to clarify the roles of the hydride forming elements, A, (e.g., La, Zr Ti, Mg) and non-forming e...The electronic structures are calculated by the DV-Xa molecular orbital method employing small model clusters in order to clarify the roles of the hydride forming elements, A, (e.g., La, Zr Ti, Mg) and non-forming elements, B, (e.g., Ni, Mn, Fe) in hydrogen storage alloys. It is confirmed from this calculation that hydrogen interacts more strongly with hydride non-forming elements, B, than hydride forming elements, A, in agreement with our previous calculations. However,the B-H interaction is enhanced only when some A element exists in the neighborhood. Otherwise, such a B-H interaction never operates in the alloy. In this sense,the coexistence of A and B elements are essential in the constitution of hydrogen storage alloys. Also, it is shown that the A/B compositional ratio of hydrogen storage alloys is understood in terms of a simple parameter, 2Bo(A - B) / /Bo(A - A)+ Bo(B-B)], where the Bo(A-B), Bo(A-A) and the Bo(B-B) are the bond strengths between atoms given in the parentheses.展开更多
In order to further reduce the cost of AB5 type rare earth-based hydrogen storage alloy, a low-Co AB5 type hydrogen storage alloy were by substituting Co with Cu and Fe.The characteristics of these alloys have been in...In order to further reduce the cost of AB5 type rare earth-based hydrogen storage alloy, a low-Co AB5 type hydrogen storage alloy were by substituting Co with Cu and Fe.The characteristics of these alloys have been investigated by means of XRD, PCT, and measurement of electrochemical capacity and cycle life.The test results show that the effect of these two kinds of substituting elements on discharge capacity is Cu > Fe, and the cycle life is on the contrary.Both of them have no distinct influence on activity speed, but activity speed increases with the decrease of Co.By the order way, the high discharge rate characteristics rise with the addition of Cu and decreasing of Co.展开更多
文摘The effects of low-Co AB_5 type hydrogen storage alloys prepared by quenchingand annealing on the performances of MH-Ni batteries were investigated, and the characteristics ofthe low-Co AB_5 type hydrogen storage alloys were compared with those of the high-Co AB_5 typehydrogen storage alloy as well. The results showed that the faster the cooling of the low-Cohydrogen storage alloy is, the better homogeneity of the chemical composition for the alloy and thelonger cycle life of the battery are, but the electrochemical discharge capacity and high-ratedischarge ability are reduced. The high-rate discharge ability and charge retention of MH-Nibatteries for the conventional as-cast annealed low-Co hydrogen storage alloy were superior to thosefor the rapidly quenched low-Co hydrogen storage alloy and the high-Co hydrogen storage alloy, buta little inferior in the cycle life.
文摘Fuel cell using borohydride as the fuel has received much attention. AB5-type hydrogen storage alloy used as the anodic material instead of noble metals has been investigated. In order to restrain the generation of hydrogen and enhance the utilization of borohydride, Ti/Zr metal powders has been added into the parent LmNi4.78Mn0.22 (where Lm is La-richened mischmetal) alloy (LNM) by ball milling and heat treatment methods. It is found that the addition of Ti/Zr metal powders lowers the electrochemical catalytic activity of the electrodes, at the same time, restrains the generation of hydrogen and enhances the utilization of the fuel. All the results show that the hydrogen generation rate or the utilization of the fuel is directly relative to the electrochemical catalytic activity or the discharge capability of the electrodes. The utilization of the fuel increases with discharge current density. It is very important to find a balance between the discharge capability and the utilization of the fuel.
文摘The effect of the hot-charging treatment on the performance of AB2 and AB5 hydrogen storage alloy electrodes was investigated. The result showed that the treatment can markedly improve the voltage plateau ratio (VPR), the high rate discharge ability (HRDA), the diffusion coefficient of hydrogen DH and the discharge capacity of the AB2 hydrogen storage alloy electrode. The SEM analysis showed that the hot-charging treatment brings about a Ni-rich surface due to the dissolution of Zr oxides. It is also very helpful for the improvement of the kinetic properties of AB2 hydrogen storage alloy electrode because the microcracking of the surface results in fresh surface. This can be the basic modification treatment for NiMH battery used in electric vehicles (EVs) in the future. But for AB5 type alloys, the treatment has the disadvantage of impairing the comprehensive electrochemical properties, because the surface of the alloy may be corroded during the treatment. The mechanism of the surface modification of the electrode is also proposed.
文摘The effect of thickness (1 similar to 10 mm) of the ingots on the electrochemical properties of as-cast and annealed strip cast LPCNi3.55Co0.75Mn0.4Al0.3 hydrogen storage alloys was investigated. It is found that the 0.2 C discharge capacity of as-cast LPCNi3.55Co0.75Mn0.4Al0.3 alloy increases with the increase of the thickness of the ingots. As-east alloy with the thickness of 10 mm shows better activation property, higher 1C discharge capacity and better cyclic stability than others. It is mainly contributed to its larger unit cell volume and less internal stress. Annealed LPCNi3.55Co0.75Mn0.4Al0.3 alloy with the thickness of 3 mm shows much better comprehensive electrochemical properties than as-east one; The cyclic. stability of the alloy with the thickness of 6 mm and the activation properties of the alloys with the thickness of 3 similar to 6 mm are improved after annealing. It is mainly owing to the great release of internal stress and the decrease of the segregation of Mn in the alloys.
基金partially supported by International Academic Exchange Program of Muroran Institute of Technology,Muroran(Japan)University of Science and Technology Beijing,Beijing(China)+1 种基金Environmentally Friendly Materials Education Program provided by Muroran MATERIAsupported by Beijing Key Laboratory of Energy Conservation and Emission Reduction for Metallurgical Industry,Beijing,China
文摘The effects of partial substitution of La by Ce and Ni by Al, Fe, or Co in LaNi_5-based alloys on hydrogen storage performance were systematically studied. All samples were prepared using vacuum arc melting in an argon atmosphere. The results showed that for LaNi_(5-x)M_x(M = Al, Fe, or Co) alloys, the lattice constants and unit cell volumes increased with an increasing amount of Al and Fe. On the other hand, these parameters decreased upon partial substitution of La by Ce. In addition, the lattice constant remained almost constant in the La_(0.6)Ce_(0.4)Ni_(5–x)Cox alloys regardless of the value of x(x = 0.3, 0.6, or 0.9), as Ce might enhance the homogeneity of the CaCu_5-type phase in Co-containing alloys. The hydrogen storage properties of the alloys were investigated using pressure, composition, and temperature isotherms. The experimental results showed that the plateau pressure decreased with an increasing content of Al, Fe, or Co, but it increased with Ce addition. Furthermore, the plateau pressures of all Co-containing alloys were almost identical upon substitution with Ce. Finally, the enthalpy(ΔH) and entropy(ΔS) values for all alloys were calculated using van't Hoff plots. The relationship between the lattice parameters and enthalpy changes for hydrogenation will be discussed.
文摘LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 hydrogen storage alloy was investigated, and the effects of thickness of its strip casting ingots(as cast) on the electrochemical performances were discussed. It was found that the 0.2 C discharge capacity increased with the increase of the thickness (from 1 mm to 10 mm) of the ingots, mainly due to the enlargement of the unit cell volume; Among the thickness of the ingots in our study, 10 mm sample showed a better activation property; LPCNi 3.55 Co 0.75 Mn 0.4 Al 0.3 alloy with 10mm showed higher comprehensive properties than those with other thickness under 1C rate.
基金This work was financially supported by the National Natural Science Foundation of China (No.20573058).
文摘The structure and electrochemical characteristics of La0.7Mg0.3Ni2.875Co0.525Mn0.1-boron composite was studied systematically. The AB3 type hydrogen storage alloys La0.7Mg0.3Ni2.875Co0.525Mn0.1 were successfully synthesized by means of inter-media alloy La2Mg17. The alloys were composited with boron at different weight rate. From the XRD analyses, each alloy of this series is mainly composed of (La,Mg)Ni3 phase and the LaNi5 phase, and the phase abundance of each phase varies with the boron weight rate, moreover, after composition, the c and cell volumes of (La,Mg)Ni3 phase increase, and the LaNi5 phase keep the same, which indicate that the boron may enter (La,Mg)Ni3 phase. The electrochemical studies show that the maximum discharge capacity of the composites decreases, but the cycling life improved. And the high rate discharge ability and exchange impendence spectroscopy (EIS) of the AB3 alloys and its composite were also studied.
基金Project supported by the National Nature Science Foundation of China (NSFC50571072)GD-MOE Coordination Project of Industry Academic and Research (2008B090500274)
文摘In order to reduce the cost of LaNi5 based hydrogen storage alloys, effect of substitution of Mn for Ni on structural and electrochemical properties of LaNi4-xFeMnx (x=0-0.8) hydrogen storage alloys was studied systematically. X-ray diffraction (XRD) and scanning electron microscope (SEM) showed that LaNi5 and La2Ni7 phases were invariably present in all alloy samples, and when x >= 0.4, (Fe, Ni) phase was observed. Electrochemical studies revealed that the discharge capacity reached a maximum value of 306.4 mAh/g when x=0.2 and the cycling stability decreased with the increase of x. With the increase of Mn content, hydrogen diffusion coefficient decreased, whereas high rate discharge-ability (HRD) and exchange current density first increased slowly when x <= 0.2 and then decreased markedly when x=0.8, indicating that electrochemical reaction on the surface of alloy electrodes had strong influence on kinetic property.
基金Project supported bythe National Natural Science Foundations of China (50131040 and 50071050)
文摘The electronic structures of LaNi5 hydrogen storage alloys and its micro-hydrogenated compounds with two hydrogen atoms in the center of two octahedral interstices and two tetrahedral interstices, were investigated by the first principles discrete variational method (DVM). The results of density of states and the difference of charge distribution clearly show that the s electrons of H mainly interact with the s electrons of hydride-non-forming element Ni, despite there being a larger affinity of La for hydrogen than that of Ni in pure metal-hydrogen system. From the cohesive energy of systems, we also found two systems have almost same stability with occupation of H atoms.
文摘The microstructure ofthe Mg/MmNi5-x (CoAlMn )x composite hydrogen storage material preparedby the method of mechanical alloyingwas characterized by X-ray diffraction, SEM and particle size distribution analysis. By measuring PCTcurves, the hydrogen absorption properties of the composite was evaluated.The results show that nanocrystallinecomposite structure can be obtainedunder adequate ball milling condition. The reactive activation and hydrogen absorption capacity are improved compared with the sole MmNi5-x(CoAlMn)x alloy. The effect ofmagnesium on the microstructure andhydrogen absorption properties of thecomposite were also evaluated.
文摘The electronic structures are calculated by the DV-Xa molecular orbital method employing small model clusters in order to clarify the roles of the hydride forming elements, A, (e.g., La, Zr Ti, Mg) and non-forming elements, B, (e.g., Ni, Mn, Fe) in hydrogen storage alloys. It is confirmed from this calculation that hydrogen interacts more strongly with hydride non-forming elements, B, than hydride forming elements, A, in agreement with our previous calculations. However,the B-H interaction is enhanced only when some A element exists in the neighborhood. Otherwise, such a B-H interaction never operates in the alloy. In this sense,the coexistence of A and B elements are essential in the constitution of hydrogen storage alloys. Also, it is shown that the A/B compositional ratio of hydrogen storage alloys is understood in terms of a simple parameter, 2Bo(A - B) / /Bo(A - A)+ Bo(B-B)], where the Bo(A-B), Bo(A-A) and the Bo(B-B) are the bond strengths between atoms given in the parentheses.
文摘In order to further reduce the cost of AB5 type rare earth-based hydrogen storage alloy, a low-Co AB5 type hydrogen storage alloy were by substituting Co with Cu and Fe.The characteristics of these alloys have been investigated by means of XRD, PCT, and measurement of electrochemical capacity and cycle life.The test results show that the effect of these two kinds of substituting elements on discharge capacity is Cu > Fe, and the cycle life is on the contrary.Both of them have no distinct influence on activity speed, but activity speed increases with the decrease of Co.By the order way, the high discharge rate characteristics rise with the addition of Cu and decreasing of Co.