The preparation of SmOx/Rh(100) and CO adsorption on this model surface have been investigated with Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption spect...The preparation of SmOx/Rh(100) and CO adsorption on this model surface have been investigated with Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption spectroscopy (TDS). The oxygen adsorption on the SmRh alloy surface leads to the aggregation of Sm on the surface. The thermal treatment of this oxidized surface induces the further agglomeration of SmOx on the Rh(100) surface. Compared with CO TDS on the clean Rh(100) surface, three additional CO desorption peaks can be observed at 176,331 and 600 K on the SmOx/Rh(100) surface. The CO desorption peak at 176 K may originate from CO adsorbed on SmOx islands, while the appearance of the CO adsorption peaks at 331 and 600 K, depending on the oxidation state of Sm, is attributed to CO species located at the interface of SmOx/Rh(100).展开更多
基金This work was supported by the National Natural Science Foundation of China (Grant No. 29873042)the State Key Laboratory of Catalysis+1 种基金 Dalian Institute of Chemical Physicsthe Chinese Academy of Sciences.
文摘The preparation of SmOx/Rh(100) and CO adsorption on this model surface have been investigated with Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption spectroscopy (TDS). The oxygen adsorption on the SmRh alloy surface leads to the aggregation of Sm on the surface. The thermal treatment of this oxidized surface induces the further agglomeration of SmOx on the Rh(100) surface. Compared with CO TDS on the clean Rh(100) surface, three additional CO desorption peaks can be observed at 176,331 and 600 K on the SmOx/Rh(100) surface. The CO desorption peak at 176 K may originate from CO adsorbed on SmOx islands, while the appearance of the CO adsorption peaks at 331 and 600 K, depending on the oxidation state of Sm, is attributed to CO species located at the interface of SmOx/Rh(100).