Al-Si pistons are frequently damaged by burning piston top surface due to elevated combustion temperature, and by rubbing the first ring groove against the engine cylinder liner. To prevent piston from these damages, ...Al-Si pistons are frequently damaged by burning piston top surface due to elevated combustion temperature, and by rubbing the first ring groove against the engine cylinder liner. To prevent piston from these damages, some technologies were invented, such as mounting high Ni cast iron ring around the first ring groove in Al alloy piston body and thermal resistant steel on piston top surface, and fabricating Al composite pistons by squeeze casting for enhancing the whole or local piston performance. In this paper, composite pistons locally reinforced with in situ primary Si and primary Mg2Si particles are fabricated by centrifugal casting. The microstructure characteristics, hardness and wear resistance of the composite piston are investigated and the motion characteristic of the in situ particles in centrifugal field is analyzed. The results of the experiments show that primary Si and Mg2Si particles mix up with each other in melt and segregate at the regions of piston top and piston ring grooves under the effect of centrifugal force. Particulate reinforced regions have a higher hardness and better wear resistance compared with the unreinforced regions and this performance increases after heat treatment. The analysis result of particle movement shows that, primary Si and primary Mg2Si particles move at approximately the same velocity in the centrifugal field, because of the growth of primary Si and fusion after colliding between primary Si particles, which compromised the velocity difference of primary Si and primary Mg2Si particles caused by the difference of their densities. Research results have some theory significance and applicative value of project in development of new aluminum matrix composites piston products.展开更多
The microstructure and rheological behavior of semi-solid Mg2Si/AM60 magnesium matrix composite at steady state were investigated.The results show that the primary α-Mg phases are knapped by mechanical stirring and t...The microstructure and rheological behavior of semi-solid Mg2Si/AM60 magnesium matrix composite at steady state were investigated.The results show that the primary α-Mg phases are knapped by mechanical stirring and the Chinese script type reinforced Mg2Si phases exist in liquid phase and grain boundary.The analysis of apparent viscosity indicates that the apparent viscosity of semi-solid Mg2Si/AM60 magnesium matrix composite at steady state increases with increasing the volume fraction of Mg2Si and solid fraction of primary α-Mg,but decreases with increasing the shearing rate and shearing time,and the apparent viscosity keeps stable when shearing time reaches 300 s.展开更多
The structure and mechanical properties of a new type of Al-based discontinuous gradient composites prepared by using the ternary AI-19Si-5Mg alloys as the raw material adopting the centrifugal casting method were inv...The structure and mechanical properties of a new type of Al-based discontinuous gradient composites prepared by using the ternary AI-19Si-5Mg alloys as the raw material adopting the centrifugal casting method were investigated. Structurally, the composites are divided into two zones： a reinforced zone with the high volume fraction of primary Si and Mg2Si particles and an unreinforced zone with no or a few particles. In the reinforced zone, the primary particles are evenly distributed, with the sizes of the primary Si particles 80-120 μm, and that of primary Mg2Si particles 20-50 μm. The properties test results show the reinforced zone has higher Rockwell hardness and better wear resistance than the unreinforced zone, due to the complementary reinforcement relationship between the primary Si and Mg2Si particles and their high volume fraction.展开更多
The effect of high-speed direct-chill(DC) casting on the microstructure and mechanical properties of Al–Mg_2Si in situ composites and AA6061 alloy was investigated. The microstructural evolution of the Al–Mg_2Si com...The effect of high-speed direct-chill(DC) casting on the microstructure and mechanical properties of Al–Mg_2Si in situ composites and AA6061 alloy was investigated. The microstructural evolution of the Al–Mg_2Si composites and AA6061 alloy was examined by optical microscopy, field-emission scanning electron microscopy(FE-SEM) and transmission electron microscopy(TEM). The results revealed that an increase of the casting speed substantially refined the primary Mg_2Si particles(from 28 to 12 μm), the spacing of eutectic Mg_2Si(from 3 to 0.5 μm), and the grains of AA6061 alloy(from 102 to 22 μm). The morphology of the eutectic Mg_2Si transformed from lamellar to rod-like and fibrous with increasing casting speed. The tensile tests showed that the yield strength, tensile strength, and elongation improved at higher casting speeds because of refinement of the Mg_2Si phase and the grains in the Al–Mg_2Si composites and the AA6061 alloy. High-speed DC casting is demonstrated to be an effective method to improve the mechanical properties of Al–Mg_2Si composites and AA6061 alloy billets.展开更多
The semi-solid processed Mg2Si/A356 composites were fabricated using a sloping plate,and the phase and morphology evolution of the semi-solid Mg2Si/A356 slurry during the remelting process was investigated.Results ind...The semi-solid processed Mg2Si/A356 composites were fabricated using a sloping plate,and the phase and morphology evolution of the semi-solid Mg2Si/A356 slurry during the remelting process was investigated.Results indicate that compared to as-cast microstructure,the size of primaryα-Al phase and Mg2Si phase of semi-solid microstructure fabricated by using a sloping plate decreases and the morphology ofα-Al phase becomes fine and globular.With increasing the reheating temperature and prolonging the holding time,the primaryα-Al phase spheroidizes,the liquid fraction in semi-solid microstructure increases,and the Chinese script Mg2Si phase embedded in the primaryα-Al phase cannot be observed.The Chinese script Mg2Si phase is distributed in the secondaryα-Al phase and becomes smaller.The net-shaped eutectic phase also becomes finer after reheating.The optimum remelting parameters suitable for thixoforming in this study are remelting at 580℃for 30 min.展开更多
The microstructure and dry sliding wear behav- ior of cast Al-18 wt% MgaSi in-situ metal matrix com- posite modified by Nd were investigated. Experimental results show that, after introducing a proper amount of Nd, bo...The microstructure and dry sliding wear behav- ior of cast Al-18 wt% MgaSi in-situ metal matrix com- posite modified by Nd were investigated. Experimental results show that, after introducing a proper amount of Nd, both primary and eutectic Mg2Si in the Al-18 wt% Mg2Si composite are well modified. The morphology of primary Mg2Si is changed from irregular or dendritic to polyhedral shape, and its average particle size is signifi- cantly decreased. Moreover, the morphology of the eutectic MgzSi phase is altered from flake-like to very short fibrous or dot-like. The wear rates and friction coefficient of the composites with Nd are lower than those without Nd. Furthermore, the addition of 0.5 wt% Nd changes the wear mechanism of the composite from the combination of abrasive, adhesive, and delamination wear without Nd into a single mild abrasion wear with 0.5 wt% Nd.展开更多
In the present study, by adding SiC particles into Al-Si-Mg melt, Mg2Si and SiC particles hybrid reinforced Al matrix composites were fabricated through the Mg2Si in situ synthesis in melt combined with the SiC ex sit...In the present study, by adding SiC particles into Al-Si-Mg melt, Mg2Si and SiC particles hybrid reinforced Al matrix composites were fabricated through the Mg2Si in situ synthesis in melt combined with the SiC ex situ stir casting. The as-cast microstructure containing primary Mg2Si and SiC particles that distribute homogenously in Al matrix was successfully achieved. The effects of SiC particle addition on the microstructure of Mg2Si/Al composites were investigated by using scanning electron microscopy(SEM) and XRD. The results show that, with increasing the fraction of the SiC particles from 5wt.% to 10wt.%, the morphologies of the primary Mg2Si particulates in the prepared samples remain polygonal, but the size of the primary phase decreases slightly. However, when the SiC particle addition reaches 15wt.%, the morphologies of the primary Mg2Si particulates change partially from polygonal to quadrangular with a decrease in size from 50 μm to 30 μm. The size of primary Al dendrites decreases with increasing fraction of the SiC particles from 0wt.% to 15wt.%. The morphology of the eutectic Mg2Si phase changes from a fi ber-form to a short fi ber-form and/or a dot-like shape with increasing fraction of the SiC particles. Furthermore, no signifi cant change in dendrite arm spacing(DAS) was observed in the presence of SiC particles.展开更多
In order to modify in-situ synthesized Mg_2Si particles in Mg_2Si/Mg-4Si composite, the modif ication effect of calcium-magnesia phosphate fertilizer on primary Mg_2Si phase in Mg_2Si/Mg-4Si composite was investigated...In order to modify in-situ synthesized Mg_2Si particles in Mg_2Si/Mg-4Si composite, the modif ication effect of calcium-magnesia phosphate fertilizer on primary Mg_2Si phase in Mg_2Si/Mg-4Si composite was investigated by means of X-ray diffraction(XRD), optical microscopy(OM), scanning electron microscopy(SEM) and energy dispersive spectroscopy(EDS) analysis. The results indicate that the morphology of the primary Mg_2Si phase apparently changes from coarse dendrites to f ine dispersive polygonal particles, and the mean size is decreased from 277 μm to 17 μm. With the addition of 4.0wt.% calcium-magnesia phosphate fertilizer as a modif ier, the ultimate tensile strength and elongation of the Mg_2Si/Mg-4Si composite are increased from 78.7 MPa and 2.1% to 105.2 MPa and 2.6%, as compared to those of the base composite, which is probably attributed to the formation of the phosphorous compound and the cluster of Ca compounds that acted as the heterogeneous nucleation substrates of the primary Mg_2Si particles, resulting in a ref ined distribution of these precipitates.展开更多
To control the morphology and size of the primary and eutectic Mg2Si phases in in situ Mg2Si/Al-Si composite and achieve a feasible and reliable technique to produce appropriate feedstock for the thixo-casting and rhe...To control the morphology and size of the primary and eutectic Mg2Si phases in in situ Mg2Si/Al-Si composite and achieve a feasible and reliable technique to produce appropriate feedstock for the thixo-casting and rheo-casting of this type of material,three Al-Si matrix composites reinforced by 5wt.%,9wt.%and 17wt.%Mg2Si with hypoeutectic,eutectic and hypereutectic compositions were prepared by the low superheat pouring(LSP)process.The effects of the pouring temperature(superheat)on the morphology and size distribution of primary phases(primaryα-Al and Mg2Si),binary(α-Al+Mg2Si)eutectic cell and eutectic Mg2Si were investigated.The experimental results show that low pouring temperature(superheat)not only refines the grain structure of the primaryα-Al and binary(α-Al+Mg2Si)eutectic cell in three composites and promotes the formation of more nondendritic structural semi-solid metal(SSM)slurry of these phases;but also refines the primary and eutectic Mg2Si phases,which seems to be attributed to the creation of an ideal condition for the nucleation and the acquisition of a high survival of nuclei caused by the LSP process.展开更多
Cylindrical components of in situ functionally gradient composite materials of Al-19Si-5Mg alloy were manufactured by centrifugal casting. Microstructure characteristics of the manufactured components were observed an...Cylindrical components of in situ functionally gradient composite materials of Al-19Si-5Mg alloy were manufactured by centrifugal casting. Microstructure characteristics of the manufactured components were observed and the effects of the used process factors on these characteristics were analyzed. The results of observations shows that, in thickness, the components possess microstructures accumulating lots of Mg2Si particles and a portion of primary silicon particles in the inner layer, a little MgzSi and primary silicon particles in the outer layer, and without any Mg2Si and primary silicon particle in the middle layer. The results of the analysis indicate that the rotation rate of centrifugal casting, mould temperature, and melt pouring temperature have evidently affected the accumulation of the second phase particles. Also, the higher the centrifugal rotation rate, mould temperature, and melt pouring temperature are, the more evident in the inner layer the degree of accumulation of Mg2Si and primary silicon particles is.展开更多
This work investigated the microstructure evolution, tensile, impact, hardness, and sliding wear properties of an Al–20Mg2Si–2Cu in situ composite treated with different Bi contents. The desired modification of prim...This work investigated the microstructure evolution, tensile, impact, hardness, and sliding wear properties of an Al–20Mg2Si–2Cu in situ composite treated with different Bi contents. The desired modification of primary Mg2 Si particles was achieved with the addition of 0.4 wt% Bi. Increasing Bi beyond 0.4 wt%resulted in a loss of modification, possibly due to the formation of Al8 MgB iS i4 compound before the precipitation of the primary Mg2 Si. Additionally, the structure of the pseudo-eutectic Mg2 Si was transformed from plate to fibrous, which was consistent with decrease of growth temperature extracted from the cooling curve thermal analysis. Addition of Bi had an effect on the morphology of Al5 Fe Si（β）, Al2Cu（θ） and Al5Cu2Mg8Si6（Q） intermetallic compounds. The tensile strength, elongation percentage, impact toughness, and hardness increased by 6%, 13%, 75%, and 23%, respectively, due to modification of both the primary and eutectic Mg2 Si crystals. The tensile and impact fracture surfaces showed fewer decohered particles in the Bi-treated composite. The enhancement in wear resistance of the Bi-treated composite could be attributed to solid lubricant function of insoluble soft Bi phase and modification effects on Mg2 Si particles.展开更多
The influence of Nd on the microstructures, tensile properties and fracture behavior of cast Al-18 wt.%Mg2Si/n situ metal matrix composite was investigated. Experimental results showed that, after introducing a proper...The influence of Nd on the microstructures, tensile properties and fracture behavior of cast Al-18 wt.%Mg2Si/n situ metal matrix composite was investigated. Experimental results showed that, after introducing a proper amount of Nd, both primary and eutectic Mg2Si in the Al-18 wt.%Mg2Si composite were well modified. The morphology of primary MgaSi was changed fi＇om irregular or dendritic to polyhedral shape, and its average particle size was significantly decreased from 47.5 to 13.0 μm. Moreover, the morphology of the eutectic Mg2Si phase was altered from flake-like to a thin laminar, short fibrous or dot-like structure. Tensile tests revealed that Nd addition improved the tensile strength and ductility of the material. Compared with those of unmodified composite, the ultimate tensile strength and percentage elongation with 0.5% Nd were increased by 32.4% and 200%, respectively. At the same time, Nd addition changed the fracture behavior from brittle to ductile.展开更多
文摘Al-Si pistons are frequently damaged by burning piston top surface due to elevated combustion temperature, and by rubbing the first ring groove against the engine cylinder liner. To prevent piston from these damages, some technologies were invented, such as mounting high Ni cast iron ring around the first ring groove in Al alloy piston body and thermal resistant steel on piston top surface, and fabricating Al composite pistons by squeeze casting for enhancing the whole or local piston performance. In this paper, composite pistons locally reinforced with in situ primary Si and primary Mg2Si particles are fabricated by centrifugal casting. The microstructure characteristics, hardness and wear resistance of the composite piston are investigated and the motion characteristic of the in situ particles in centrifugal field is analyzed. The results of the experiments show that primary Si and Mg2Si particles mix up with each other in melt and segregate at the regions of piston top and piston ring grooves under the effect of centrifugal force. Particulate reinforced regions have a higher hardness and better wear resistance compared with the unreinforced regions and this performance increases after heat treatment. The analysis result of particle movement shows that, primary Si and primary Mg2Si particles move at approximately the same velocity in the centrifugal field, because of the growth of primary Si and fusion after colliding between primary Si particles, which compromised the velocity difference of primary Si and primary Mg2Si particles caused by the difference of their densities. Research results have some theory significance and applicative value of project in development of new aluminum matrix composites piston products.
基金Project(50765005) supported by the National Natural Science Foundation of Chinasupported by Key Laboratory of Ministry of Education for Conveyance and Equipment (East China Jiaotong University),China
文摘The microstructure and rheological behavior of semi-solid Mg2Si/AM60 magnesium matrix composite at steady state were investigated.The results show that the primary α-Mg phases are knapped by mechanical stirring and the Chinese script type reinforced Mg2Si phases exist in liquid phase and grain boundary.The analysis of apparent viscosity indicates that the apparent viscosity of semi-solid Mg2Si/AM60 magnesium matrix composite at steady state increases with increasing the volume fraction of Mg2Si and solid fraction of primary α-Mg,but decreases with increasing the shearing rate and shearing time,and the apparent viscosity keeps stable when shearing time reaches 300 s.
基金Funded by the National Natural Science Foundation of China(No.51201140)the Fundamental Research Funds for the Central Universities(No.XDJK2010C007)
文摘The structure and mechanical properties of a new type of Al-based discontinuous gradient composites prepared by using the ternary AI-19Si-5Mg alloys as the raw material adopting the centrifugal casting method were investigated. Structurally, the composites are divided into two zones： a reinforced zone with the high volume fraction of primary Si and Mg2Si particles and an unreinforced zone with no or a few particles. In the reinforced zone, the primary particles are evenly distributed, with the sizes of the primary Si particles 80-120 μm, and that of primary Mg2Si particles 20-50 μm. The properties test results show the reinforced zone has higher Rockwell hardness and better wear resistance than the unreinforced zone, due to the complementary reinforcement relationship between the primary Si and Mg2Si particles and their high volume fraction.
基金financially supported by the Science and Technology Program of Guangzhou,China(No.2015B090926013)Postdoctoral Science Foundation of China(No.2015M581348)+1 种基金Postdoctoral Science Foundation of Northeastern University(No.20150302)the Doctoral Foundation of Chinese Ministry of Education(No.20130042130001)
文摘The effect of high-speed direct-chill(DC) casting on the microstructure and mechanical properties of Al–Mg_2Si in situ composites and AA6061 alloy was investigated. The microstructural evolution of the Al–Mg_2Si composites and AA6061 alloy was examined by optical microscopy, field-emission scanning electron microscopy(FE-SEM) and transmission electron microscopy(TEM). The results revealed that an increase of the casting speed substantially refined the primary Mg_2Si particles(from 28 to 12 μm), the spacing of eutectic Mg_2Si(from 3 to 0.5 μm), and the grains of AA6061 alloy(from 102 to 22 μm). The morphology of the eutectic Mg_2Si transformed from lamellar to rod-like and fibrous with increasing casting speed. The tensile tests showed that the yield strength, tensile strength, and elongation improved at higher casting speeds because of refinement of the Mg_2Si phase and the grains in the Al–Mg_2Si composites and the AA6061 alloy. High-speed DC casting is demonstrated to be an effective method to improve the mechanical properties of Al–Mg_2Si composites and AA6061 alloy billets.
基金the National Natural Science Foundation of China(Grant No.51865011)the Natural Science Foundation of Jiangxi Province,China(Grant No.20171BAB216031).
文摘The semi-solid processed Mg2Si/A356 composites were fabricated using a sloping plate,and the phase and morphology evolution of the semi-solid Mg2Si/A356 slurry during the remelting process was investigated.Results indicate that compared to as-cast microstructure,the size of primaryα-Al phase and Mg2Si phase of semi-solid microstructure fabricated by using a sloping plate decreases and the morphology ofα-Al phase becomes fine and globular.With increasing the reheating temperature and prolonging the holding time,the primaryα-Al phase spheroidizes,the liquid fraction in semi-solid microstructure increases,and the Chinese script Mg2Si phase embedded in the primaryα-Al phase cannot be observed.The Chinese script Mg2Si phase is distributed in the secondaryα-Al phase and becomes smaller.The net-shaped eutectic phase also becomes finer after reheating.The optimum remelting parameters suitable for thixoforming in this study are remelting at 580℃for 30 min.
基金financially supported by the National Natural Youth Science Foundation of China (No. 50901038)the Key Laboratory Foundation of Liaoning Provincial Committee of Education (Nos. 20060394 and 2009S053)
文摘The microstructure and dry sliding wear behav- ior of cast Al-18 wt% MgaSi in-situ metal matrix com- posite modified by Nd were investigated. Experimental results show that, after introducing a proper amount of Nd, both primary and eutectic Mg2Si in the Al-18 wt% Mg2Si composite are well modified. The morphology of primary Mg2Si is changed from irregular or dendritic to polyhedral shape, and its average particle size is signifi- cantly decreased. Moreover, the morphology of the eutectic MgzSi phase is altered from flake-like to very short fibrous or dot-like. The wear rates and friction coefficient of the composites with Nd are lower than those without Nd. Furthermore, the addition of 0.5 wt% Nd changes the wear mechanism of the composite from the combination of abrasive, adhesive, and delamination wear without Nd into a single mild abrasion wear with 0.5 wt% Nd.
基金supported by the National Natural Science Foundation of China(No.50671044)the Sci-tech Development Project of Jilin Province of China(No.20070506)
文摘In the present study, by adding SiC particles into Al-Si-Mg melt, Mg2Si and SiC particles hybrid reinforced Al matrix composites were fabricated through the Mg2Si in situ synthesis in melt combined with the SiC ex situ stir casting. The as-cast microstructure containing primary Mg2Si and SiC particles that distribute homogenously in Al matrix was successfully achieved. The effects of SiC particle addition on the microstructure of Mg2Si/Al composites were investigated by using scanning electron microscopy(SEM) and XRD. The results show that, with increasing the fraction of the SiC particles from 5wt.% to 10wt.%, the morphologies of the primary Mg2Si particulates in the prepared samples remain polygonal, but the size of the primary phase decreases slightly. However, when the SiC particle addition reaches 15wt.%, the morphologies of the primary Mg2Si particulates change partially from polygonal to quadrangular with a decrease in size from 50 μm to 30 μm. The size of primary Al dendrites decreases with increasing fraction of the SiC particles from 0wt.% to 15wt.%. The morphology of the eutectic Mg2Si phase changes from a fi ber-form to a short fi ber-form and/or a dot-like shape with increasing fraction of the SiC particles. Furthermore, no signifi cant change in dendrite arm spacing(DAS) was observed in the presence of SiC particles.
基金financially supported by the Fundamental Research Funds for Central Universities(Grant No.:XDJK2015B001)
文摘In order to modify in-situ synthesized Mg_2Si particles in Mg_2Si/Mg-4Si composite, the modif ication effect of calcium-magnesia phosphate fertilizer on primary Mg_2Si phase in Mg_2Si/Mg-4Si composite was investigated by means of X-ray diffraction(XRD), optical microscopy(OM), scanning electron microscopy(SEM) and energy dispersive spectroscopy(EDS) analysis. The results indicate that the morphology of the primary Mg_2Si phase apparently changes from coarse dendrites to f ine dispersive polygonal particles, and the mean size is decreased from 277 μm to 17 μm. With the addition of 4.0wt.% calcium-magnesia phosphate fertilizer as a modif ier, the ultimate tensile strength and elongation of the Mg_2Si/Mg-4Si composite are increased from 78.7 MPa and 2.1% to 105.2 MPa and 2.6%, as compared to those of the base composite, which is probably attributed to the formation of the phosphorous compound and the cluster of Ca compounds that acted as the heterogeneous nucleation substrates of the primary Mg_2Si particles, resulting in a ref ined distribution of these precipitates.
文摘To control the morphology and size of the primary and eutectic Mg2Si phases in in situ Mg2Si/Al-Si composite and achieve a feasible and reliable technique to produce appropriate feedstock for the thixo-casting and rheo-casting of this type of material,three Al-Si matrix composites reinforced by 5wt.%,9wt.%and 17wt.%Mg2Si with hypoeutectic,eutectic and hypereutectic compositions were prepared by the low superheat pouring(LSP)process.The effects of the pouring temperature(superheat)on the morphology and size distribution of primary phases(primaryα-Al and Mg2Si),binary(α-Al+Mg2Si)eutectic cell and eutectic Mg2Si were investigated.The experimental results show that low pouring temperature(superheat)not only refines the grain structure of the primaryα-Al and binary(α-Al+Mg2Si)eutectic cell in three composites and promotes the formation of more nondendritic structural semi-solid metal(SSM)slurry of these phases;but also refines the primary and eutectic Mg2Si phases,which seems to be attributed to the creation of an ideal condition for the nucleation and the acquisition of a high survival of nuclei caused by the LSP process.
文摘Cylindrical components of in situ functionally gradient composite materials of Al-19Si-5Mg alloy were manufactured by centrifugal casting. Microstructure characteristics of the manufactured components were observed and the effects of the used process factors on these characteristics were analyzed. The results of observations shows that, in thickness, the components possess microstructures accumulating lots of Mg2Si particles and a portion of primary silicon particles in the inner layer, a little MgzSi and primary silicon particles in the outer layer, and without any Mg2Si and primary silicon particle in the middle layer. The results of the analysis indicate that the rotation rate of centrifugal casting, mould temperature, and melt pouring temperature have evidently affected the accumulation of the second phase particles. Also, the higher the centrifugal rotation rate, mould temperature, and melt pouring temperature are, the more evident in the inner layer the degree of accumulation of Mg2Si and primary silicon particles is.
文摘This work investigated the microstructure evolution, tensile, impact, hardness, and sliding wear properties of an Al–20Mg2Si–2Cu in situ composite treated with different Bi contents. The desired modification of primary Mg2 Si particles was achieved with the addition of 0.4 wt% Bi. Increasing Bi beyond 0.4 wt%resulted in a loss of modification, possibly due to the formation of Al8 MgB iS i4 compound before the precipitation of the primary Mg2 Si. Additionally, the structure of the pseudo-eutectic Mg2 Si was transformed from plate to fibrous, which was consistent with decrease of growth temperature extracted from the cooling curve thermal analysis. Addition of Bi had an effect on the morphology of Al5 Fe Si（β）, Al2Cu（θ） and Al5Cu2Mg8Si6（Q） intermetallic compounds. The tensile strength, elongation percentage, impact toughness, and hardness increased by 6%, 13%, 75%, and 23%, respectively, due to modification of both the primary and eutectic Mg2 Si crystals. The tensile and impact fracture surfaces showed fewer decohered particles in the Bi-treated composite. The enhancement in wear resistance of the Bi-treated composite could be attributed to solid lubricant function of insoluble soft Bi phase and modification effects on Mg2 Si particles.
基金Project supported by Key Laboratory Foundation of Liaoning Provincial Committee of Education (2009S053)
文摘The influence of Nd on the microstructures, tensile properties and fracture behavior of cast Al-18 wt.%Mg2Si/n situ metal matrix composite was investigated. Experimental results showed that, after introducing a proper amount of Nd, both primary and eutectic Mg2Si in the Al-18 wt.%Mg2Si composite were well modified. The morphology of primary MgaSi was changed fi＇om irregular or dendritic to polyhedral shape, and its average particle size was significantly decreased from 47.5 to 13.0 μm. Moreover, the morphology of the eutectic Mg2Si phase was altered from flake-like to a thin laminar, short fibrous or dot-like structure. Tensile tests revealed that Nd addition improved the tensile strength and ductility of the material. Compared with those of unmodified composite, the ultimate tensile strength and percentage elongation with 0.5% Nd were increased by 32.4% and 200%, respectively. At the same time, Nd addition changed the fracture behavior from brittle to ductile.