The wear resistance of austenitic stainless steels can be improved by thermo-chemical surface treatment with nitrogen and carbon. However, it is possible that the corrosion resistance will be impaired by the precipita...The wear resistance of austenitic stainless steels can be improved by thermo-chemical surface treatment with nitrogen and carbon. However, it is possible that the corrosion resistance will be impaired by the precipitation of chromiumnitrid or -carbide. The present contribution deals with investigations of the corrosion behaviour and structural characteristics of a low temperature nitrided and carburised austenitic stainless steel. The material investigated was AISI 316L (X2CrNiMol7-12-2) austenitic stainless steel. A commercial plasma-nitriding unit (pulsed dc) was used for the nitriding and carburising process. Additional samples were treated by the gasoxinitriding process for a comparison between plasma- and gasoxinitriding. The nitrided and carburised layer of austenitic stainless steel consists of the nitrogen or carbon S-phase (expanded austenite), respectively. X-ray diffraction investigations show the typical shift of the peaks to lower angles, indicating expansion of the fee lattice. Also the X-ray diffraction technique was employed to study the residual stresses in the nitrogen and carbon S-phase. The corrosion behaviour of surface engineered samples was investigated with electrochemical methods. Anodic potentiodynamic polarisation curves were recorded for testing the resistance against general corrosion (in H2SO4) and pitting corrosion (in NaCl).展开更多
Microstructure evolution and mechanical properties of 316L austenitic stainless steel with aluminum addition by warm rolling at 550 ℃ were investigated. It is found that sample is composed of an ashen austenite matri...Microstructure evolution and mechanical properties of 316L austenitic stainless steel with aluminum addition by warm rolling at 550 ℃ were investigated. It is found that sample is composed of an ashen austenite matrix, a gray black ferrite phase and a small number of NiCx. The average grain sizes are 21.62, 19.66 and 19.49 μm for samples with the rolling deformation of 30%, 50% and 70%, respectively. The yield strength and tensile strength of samples with solid solution time of 30 min and deformation of 70% are higher. The fracture modes are similar and belong to toughness fracture. The fracture surfaces of the samples are composed of relatively large equal-axis ductile dimples （5-15 μm） and fine scattered ones around the dimples （〈 5 μm）. As the rolling deformation increases, the quantity of subgrain boundary increases and the 〈 101 〉 orientation is more prominent. {001 } 〈 110 〉 rotation-cube textures are present in ferrite phase of samples and weak Goss texture is formed in austenite pole images.展开更多
基金The DFG(Deutsche Forschungsgemeinschaf)is gratefully acknowledged for the financial support(DFG-BI 418/9-1).
文摘The wear resistance of austenitic stainless steels can be improved by thermo-chemical surface treatment with nitrogen and carbon. However, it is possible that the corrosion resistance will be impaired by the precipitation of chromiumnitrid or -carbide. The present contribution deals with investigations of the corrosion behaviour and structural characteristics of a low temperature nitrided and carburised austenitic stainless steel. The material investigated was AISI 316L (X2CrNiMol7-12-2) austenitic stainless steel. A commercial plasma-nitriding unit (pulsed dc) was used for the nitriding and carburising process. Additional samples were treated by the gasoxinitriding process for a comparison between plasma- and gasoxinitriding. The nitrided and carburised layer of austenitic stainless steel consists of the nitrogen or carbon S-phase (expanded austenite), respectively. X-ray diffraction investigations show the typical shift of the peaks to lower angles, indicating expansion of the fee lattice. Also the X-ray diffraction technique was employed to study the residual stresses in the nitrogen and carbon S-phase. The corrosion behaviour of surface engineered samples was investigated with electrochemical methods. Anodic potentiodynamic polarisation curves were recorded for testing the resistance against general corrosion (in H2SO4) and pitting corrosion (in NaCl).
基金The work was supported by the National Natural Science Foundation of China （51561020）, the Gansu Provincial Science and Technology Support Program （1304GKCA027） and the China Postdoctoral Science Foundation （2015M572615, 2016T90959）.
文摘Microstructure evolution and mechanical properties of 316L austenitic stainless steel with aluminum addition by warm rolling at 550 ℃ were investigated. It is found that sample is composed of an ashen austenite matrix, a gray black ferrite phase and a small number of NiCx. The average grain sizes are 21.62, 19.66 and 19.49 μm for samples with the rolling deformation of 30%, 50% and 70%, respectively. The yield strength and tensile strength of samples with solid solution time of 30 min and deformation of 70% are higher. The fracture modes are similar and belong to toughness fracture. The fracture surfaces of the samples are composed of relatively large equal-axis ductile dimples （5-15 μm） and fine scattered ones around the dimples （〈 5 μm）. As the rolling deformation increases, the quantity of subgrain boundary increases and the 〈 101 〉 orientation is more prominent. {001 } 〈 110 〉 rotation-cube textures are present in ferrite phase of samples and weak Goss texture is formed in austenite pole images.