A modification of Mg2Si in the hypereutectic Mg-4%Si alloy（mass fraction） with Sr was investigated.Two types of Mg2Si in the alloys were found：polygonal primary Mg2Si and Chinese script type eutectic Mg2Si.Adding A...A modification of Mg2Si in the hypereutectic Mg-4%Si alloy（mass fraction） with Sr was investigated.Two types of Mg2Si in the alloys were found：polygonal primary Mg2Si and Chinese script type eutectic Mg2Si.Adding Al-10% Sr master alloy to the Mg-4%Si alloy clearly reduced the average size of primary Mg2Si and changed the morphology of eutectic Mg2Si from Chinese script type to polyhedral or fine fibre shape.The refinement of primary Mg2Si is mainly attributed to the heterogeneous nucleation mechanism induced by the Sr-rich particles.The modification of eutectic Mg2Si results from the dissolved Sr,which alters the preferred growth manner of the eutectic.展开更多
Trace amount of Sr(0.05 wt.%)was added into the hypoeutectic Al−Si(3−12 wt.%Si)alloys to modify their microstructure and improve thermal conductivity.The results showed that the thermal conductivity of hypoeutectic Al...Trace amount of Sr(0.05 wt.%)was added into the hypoeutectic Al−Si(3−12 wt.%Si)alloys to modify their microstructure and improve thermal conductivity.The results showed that the thermal conductivity of hypoeutectic Al−Si alloys was improved by Sr modification,and the increment and increasing rate of the thermal conductivity gradually increased with Si content increasing.The improvement of thermal conductivity was primarily related to the morphology variation of eutectic Si phases.In Sr-modified Al−Si alloys,the morphology of eutectic Si phases was a mixed morphology of fiber structure and fine flaky structure,and the proportion of the fine flaky eutectic Si phases gradually decreased with Si content increasing.Under the Si content reaching 9 wt.%,the proportion of fine flaky eutectic Si phases was nearly negligible in Sr-modified alloys.Correspondingly,the increment and increasing rate of thermal conductivity of Sr-modified alloys reached the maximum and tended to be stable.展开更多
基金Project(2011BAE22B00) supported by the National Key Technology R&D Program of ChinaProjects(ZR2010EQ021,ZR2010EL013) supported by the Natural Science Foundation of Shandong Province,China
文摘A modification of Mg2Si in the hypereutectic Mg-4%Si alloy（mass fraction） with Sr was investigated.Two types of Mg2Si in the alloys were found：polygonal primary Mg2Si and Chinese script type eutectic Mg2Si.Adding Al-10% Sr master alloy to the Mg-4%Si alloy clearly reduced the average size of primary Mg2Si and changed the morphology of eutectic Mg2Si from Chinese script type to polyhedral or fine fibre shape.The refinement of primary Mg2Si is mainly attributed to the heterogeneous nucleation mechanism induced by the Sr-rich particles.The modification of eutectic Mg2Si results from the dissolved Sr,which alters the preferred growth manner of the eutectic.
基金Project(2013B090500091)supported by Industry-University-Research Combined Project of Guangdong Province,ChinaProject(20180358)supported by the Shenzhen Jiansheng Technology Inc.Cooperation Project,China。
文摘Trace amount of Sr(0.05 wt.%)was added into the hypoeutectic Al−Si(3−12 wt.%Si)alloys to modify their microstructure and improve thermal conductivity.The results showed that the thermal conductivity of hypoeutectic Al−Si alloys was improved by Sr modification,and the increment and increasing rate of the thermal conductivity gradually increased with Si content increasing.The improvement of thermal conductivity was primarily related to the morphology variation of eutectic Si phases.In Sr-modified Al−Si alloys,the morphology of eutectic Si phases was a mixed morphology of fiber structure and fine flaky structure,and the proportion of the fine flaky eutectic Si phases gradually decreased with Si content increasing.Under the Si content reaching 9 wt.%,the proportion of fine flaky eutectic Si phases was nearly negligible in Sr-modified alloys.Correspondingly,the increment and increasing rate of thermal conductivity of Sr-modified alloys reached the maximum and tended to be stable.