The development of semiconductors is always accompanied by the progress in controllable doping techniques.Taking AlGaN-based ultraviolet(UV)emitters as an example,despite a peak wall-plug efficiency of 15.3%at the wav...The development of semiconductors is always accompanied by the progress in controllable doping techniques.Taking AlGaN-based ultraviolet(UV)emitters as an example,despite a peak wall-plug efficiency of 15.3%at the wavelength of 275 nm,there is still a huge gap in comparison with GaN-based visible light-emitting diodes(LEDs),mainly attributed to the inefficient doping of AlGaN with increase of the Al composition.First,p-doping of Al-rich AlGaN is a long-standing challenge and the low hole concentration seriously restricts the carrier injection efficiency.Although p-GaN cladding layers are widely adopted as a compromise,the high injection barrier of holes as well as the inevitable loss of light extraction cannot be neglected.While in terms of n-doping the main issue is the degradation of the electrical property when the Al composition exceeds 80%,resulting in a low electrical efficiency in sub-250 nm UV-LEDs.This review summarizes the recent advances and outlines the major challenges in the efficient doping of Al-rich AlGaN,meanwhile the corresponding approaches pursued to overcome the doping issues are discussed in detail.展开更多
240 nm AlGaN-based micro-LEDs with different sizes are designed and fabricated.Then,the external quantum efficiency(EQE)and light extraction efficiency(LEE)are systematically investigated by comparing size and edge ef...240 nm AlGaN-based micro-LEDs with different sizes are designed and fabricated.Then,the external quantum efficiency(EQE)and light extraction efficiency(LEE)are systematically investigated by comparing size and edge effects.Here,it is revealed that the peak optical output power increases by 81.83%with the size shrinking from 50.0 to 25.0μm.Thereinto,the LEE increases by 26.21%and the LEE enhancement mainly comes from the sidewall light extraction.Most notably,transversemagnetic(TM)mode light intensifies faster as the size shrinks due to the tilted mesa side-wall and Al reflector design.However,when it turns to 12.5μm sized micro-LEDs,the output power is lower than 25.0μm sized ones.The underlying mechanism is that even though protected by SiO2 passivation,the edge effect which leads to current leakage and Shockley-Read-Hall(SRH)recombination deteriorates rapidly with the size further shrinking.Moreover,the ratio of the p-contact area to mesa area is much lower,which deteriorates the p-type current spreading at the mesa edge.These findings show a role of thumb for the design of high efficiency micro-LEDs with wavelength below 250 nm,which will pave the way for wide applications of deep ultraviolet(DUV)micro-LEDs.展开更多
In this letter,high power density AlGaN/GaN high electron-mobility transistors(HEMTs)on a freestanding GaN substrate are reported.An asymmetricΓ-shaped 500-nm gate with a field plate of 650 nm is introduced to improv...In this letter,high power density AlGaN/GaN high electron-mobility transistors(HEMTs)on a freestanding GaN substrate are reported.An asymmetricΓ-shaped 500-nm gate with a field plate of 650 nm is introduced to improve microwave power performance.The breakdown voltage(BV)is increased to more than 200 V for the fabricated device with gate-to-source and gate-to-drain distances of 1.08 and 2.92μm.A record continuous-wave power density of 11.2 W/mm@10 GHz is realized with a drain bias of 70 V.The maximum oscillation frequency(f_(max))and unity current gain cut-off frequency(f_(t))of the AlGaN/GaN HEMTs exceed 30 and 20 GHz,respectively.The results demonstrate the potential of AlGaN/GaN HEMTs on freestanding GaN substrates for microwave power applications.展开更多
Enhancement-mode(E-mode)GaN-on-Si radio-frequency(RF)high-electron-mobility transistors(HEMTs)were fabri-cated on an ultrathin-barrier(UTB)AlGaN(<6 nm)/GaN heterostructure featuring a naturally depleted 2-D electro...Enhancement-mode(E-mode)GaN-on-Si radio-frequency(RF)high-electron-mobility transistors(HEMTs)were fabri-cated on an ultrathin-barrier(UTB)AlGaN(<6 nm)/GaN heterostructure featuring a naturally depleted 2-D electron gas(2DEG)channel.The fabricated E-mode HEMTs exhibit a relatively high threshold voltage(VTH)of+1.1 V with good uniformity.A maxi-mum current/power gain cut-off frequency(fT/fMAX)of 31.3/99.6 GHz with a power added efficiency(PAE)of 52.47%and an out-put power density(Pout)of 1.0 W/mm at 3.5 GHz were achieved on the fabricated E-mode HEMTs with 1-μm gate and Au-free ohmic contact.展开更多
In this study, the effects of 1 MeV electron radiation on the D-mode GaN-based high electron mobility transistors(HEMTs) were investigated after different radiation doses. The changes in electrical properties of the d...In this study, the effects of 1 MeV electron radiation on the D-mode GaN-based high electron mobility transistors(HEMTs) were investigated after different radiation doses. The changes in electrical properties of the device were obtained, and the related physical mechanisms were analyzed. It indicated that under the radiation dose of 5 × 10^(14) cm^(-2), the channel current cannot be completely pinched off even if the negative gate voltage was lower than the threshold voltage, and the gate leakage current increased significantly. The emission microscopy and scanning electron microscopy were used to determine the damage location. Besides, the radiation dose was adjusted ranging from 5 × 10^(12) to 1 × 10^(14) cm^(-2), and we noticed that the drain-source current increased and the threshold voltage presented slightly negative shift. By calculations, it suggested that the carrier density and electron mobility gradually increased. It provided a reference for the development of device radiation reinforcement technology.展开更多
In this paper, we explore the electrical characteristics of high-electron-mobility transistors(HEMTs) using a TaN/AlGaN/GaN metal insulating semiconductor(MIS) structure. The high-resistance tantalum nitride(TaN) film...In this paper, we explore the electrical characteristics of high-electron-mobility transistors(HEMTs) using a TaN/AlGaN/GaN metal insulating semiconductor(MIS) structure. The high-resistance tantalum nitride(TaN) film prepared by magnetron sputtering as the gate dielectric layer of the device achieved an effective reduction of electronic states at the TaN/AlGaN interface, and reducing the gate leakage current of the MIS HEMT, its performance was enhanced. The HEMT exhibited a low gate leakage current of 2.15 × 10^(-7) mA/mm and a breakdown voltage of 1180 V. Furthermore, the MIS HEMT displayed exceptional operational stability during dynamic tests, with dynamic resistance remaining only 1.39 times even under 400 V stress.展开更多
基金This work was supported by the National Key Research and Development Program of China(No.2022YFB3605100)the National Natural Science Foundation of China(Nos.62234001,61927806,61974002,62135013,and 62075081)+1 种基金the Key-Area Research and Development Program of Guangdong Province(No.2020B010172001)the Major Scientific and Technological Innovation Project(MSTIP)of Shandong Province(No.2019JZZY010209).
文摘The development of semiconductors is always accompanied by the progress in controllable doping techniques.Taking AlGaN-based ultraviolet(UV)emitters as an example,despite a peak wall-plug efficiency of 15.3%at the wavelength of 275 nm,there is still a huge gap in comparison with GaN-based visible light-emitting diodes(LEDs),mainly attributed to the inefficient doping of AlGaN with increase of the Al composition.First,p-doping of Al-rich AlGaN is a long-standing challenge and the low hole concentration seriously restricts the carrier injection efficiency.Although p-GaN cladding layers are widely adopted as a compromise,the high injection barrier of holes as well as the inevitable loss of light extraction cannot be neglected.While in terms of n-doping the main issue is the degradation of the electrical property when the Al composition exceeds 80%,resulting in a low electrical efficiency in sub-250 nm UV-LEDs.This review summarizes the recent advances and outlines the major challenges in the efficient doping of Al-rich AlGaN,meanwhile the corresponding approaches pursued to overcome the doping issues are discussed in detail.
基金This work was supported by National Key R&D Program of China(2022YFB3605103)the National Natural Science Foundation of China(62204241,U22A2084,62121005,and 61827813)+3 种基金the Natural Science Foundation of Jilin Province(20230101345JC,20230101360JC,and 20230101107JC)the Youth Innovation Promotion Association of CAS(2023223)the Young Elite Scientist Sponsorship Program By CAST(YESS20200182)the CAS Talents Program(E30122E4M0).
文摘240 nm AlGaN-based micro-LEDs with different sizes are designed and fabricated.Then,the external quantum efficiency(EQE)and light extraction efficiency(LEE)are systematically investigated by comparing size and edge effects.Here,it is revealed that the peak optical output power increases by 81.83%with the size shrinking from 50.0 to 25.0μm.Thereinto,the LEE increases by 26.21%and the LEE enhancement mainly comes from the sidewall light extraction.Most notably,transversemagnetic(TM)mode light intensifies faster as the size shrinks due to the tilted mesa side-wall and Al reflector design.However,when it turns to 12.5μm sized micro-LEDs,the output power is lower than 25.0μm sized ones.The underlying mechanism is that even though protected by SiO2 passivation,the edge effect which leads to current leakage and Shockley-Read-Hall(SRH)recombination deteriorates rapidly with the size further shrinking.Moreover,the ratio of the p-contact area to mesa area is much lower,which deteriorates the p-type current spreading at the mesa edge.These findings show a role of thumb for the design of high efficiency micro-LEDs with wavelength below 250 nm,which will pave the way for wide applications of deep ultraviolet(DUV)micro-LEDs.
文摘In this letter,high power density AlGaN/GaN high electron-mobility transistors(HEMTs)on a freestanding GaN substrate are reported.An asymmetricΓ-shaped 500-nm gate with a field plate of 650 nm is introduced to improve microwave power performance.The breakdown voltage(BV)is increased to more than 200 V for the fabricated device with gate-to-source and gate-to-drain distances of 1.08 and 2.92μm.A record continuous-wave power density of 11.2 W/mm@10 GHz is realized with a drain bias of 70 V.The maximum oscillation frequency(f_(max))and unity current gain cut-off frequency(f_(t))of the AlGaN/GaN HEMTs exceed 30 and 20 GHz,respectively.The results demonstrate the potential of AlGaN/GaN HEMTs on freestanding GaN substrates for microwave power applications.
基金supported in part by the National Key Research and Development Program of China under Grant 2022YFB3604400in part by the Youth Innovation Promotion Association of Chinese Academy Sciences(CAS)+4 种基金in part by CAS-Croucher Funding Scheme under Grant CAS22801in part by National Natural Science Foundation of China under Grant 62074161,Grant 62004213,and Grant U20A20208in part by the Beijing Municipal Science and Technology Commission project under Grant Z201100008420009 and Grant Z211100007921018in part by the University of CASin part by IMECAS-HKUST-Joint Laboratory of Microelectronics.
文摘Enhancement-mode(E-mode)GaN-on-Si radio-frequency(RF)high-electron-mobility transistors(HEMTs)were fabri-cated on an ultrathin-barrier(UTB)AlGaN(<6 nm)/GaN heterostructure featuring a naturally depleted 2-D electron gas(2DEG)channel.The fabricated E-mode HEMTs exhibit a relatively high threshold voltage(VTH)of+1.1 V with good uniformity.A maxi-mum current/power gain cut-off frequency(fT/fMAX)of 31.3/99.6 GHz with a power added efficiency(PAE)of 52.47%and an out-put power density(Pout)of 1.0 W/mm at 3.5 GHz were achieved on the fabricated E-mode HEMTs with 1-μm gate and Au-free ohmic contact.
基金supported by the Key Program of the National Natural Science Foundation of China (Grant No. 62334002)the National Natural Science Foundation of China (Grant No. 62174008)。
文摘In this study, the effects of 1 MeV electron radiation on the D-mode GaN-based high electron mobility transistors(HEMTs) were investigated after different radiation doses. The changes in electrical properties of the device were obtained, and the related physical mechanisms were analyzed. It indicated that under the radiation dose of 5 × 10^(14) cm^(-2), the channel current cannot be completely pinched off even if the negative gate voltage was lower than the threshold voltage, and the gate leakage current increased significantly. The emission microscopy and scanning electron microscopy were used to determine the damage location. Besides, the radiation dose was adjusted ranging from 5 × 10^(12) to 1 × 10^(14) cm^(-2), and we noticed that the drain-source current increased and the threshold voltage presented slightly negative shift. By calculations, it suggested that the carrier density and electron mobility gradually increased. It provided a reference for the development of device radiation reinforcement technology.
基金supported by the National Natural Science Foundation of China(Grant No.1237310)The Youth Innovation Promotion Association of the Chinese Academy of Sciences(Grant No.2020321)+1 种基金the National Natural Science Foundation of China(Grant No.92163204)The Key Research and Development Program of Jiangsu Province(Grant No.BE2022057-1)。
文摘In this paper, we explore the electrical characteristics of high-electron-mobility transistors(HEMTs) using a TaN/AlGaN/GaN metal insulating semiconductor(MIS) structure. The high-resistance tantalum nitride(TaN) film prepared by magnetron sputtering as the gate dielectric layer of the device achieved an effective reduction of electronic states at the TaN/AlGaN interface, and reducing the gate leakage current of the MIS HEMT, its performance was enhanced. The HEMT exhibited a low gate leakage current of 2.15 × 10^(-7) mA/mm and a breakdown voltage of 1180 V. Furthermore, the MIS HEMT displayed exceptional operational stability during dynamic tests, with dynamic resistance remaining only 1.39 times even under 400 V stress.