Mechanism of microarc oxidation on AZ91D Mg alloy induced byβ-Mg_(17)Al_(12) phase

This work proposed a strategy of indirectly inducing uniform microarc discharge by controlling the content and distribution ofβ-Mg_(17)Al_(12)phase in AZ91D Mg alloy.Two kinds of nano-particles(ZrO_(2)and TiO_(2))were designed to be added into the substrate of Mg alloy by friction stir processing(FSP).Then,Mg alloy sample designed with different precipitated morphology ofβ-Mg_(17)Al_(12)phase was treated by microarc oxidation(MAO)in Na_(3)PO_(4)/Na2SiO3electrolyte.The characteristics and performance of the MAO coating was analyzed using scanning electron microscopy(SEM),energy dispersive spectrometer(EDS),X-ray diffraction(XRD),X-ray photoelectron spectroscopy(XPS),contact angle meter,and potentiodynamic polarization.It was found that the coarseα-Mg grains in extruded AZ91D Mg alloy were refined by FSP,and theβ-Mg_(17)Al_(12)phase with reticular structure was broken and dispersed.The nano-ZrO_(2)particles were pinned at the grain boundary by FSP,which refined theα-Mg grain and promoted the precipitation ofβ-Mg_(17)Al_(12)phase in grains.It effectively inhibited the“cascade”phenomenon of microarcs,which induced the uniform distribution of discharge pores.The MAO coating on Zr-FSP sample had good wettability and corrosion resistance.However,TiO_(2)particles were hardly detected in the coating on TiFSP sample.

Microstructural evolution and mechanical properties of AZ31 Mg alloy fabricated by a novel bifurcation-equal channel angular pressing

In this work,a novel type of short-process deformation technology of Mg alloys,bifurcation-equal channel angular pressing(B-ECAP),was proposed to refine grain and improve the basal texture.The cylindrical billets were first compressed into the die cavity,then sequentially flowed downward through a 90°corner and two 120°shear steps.The total strain of B-ECAP process could reach 3.924 in a single pass.The results of microstructure observation showed that DRX occurred at upsetting process in the die cavity and completed at position D.The grains were refined to 6.3μm at being extruded at 300℃ and grew obviously with the extrusion temperature increase.The shear tress induced by 900 corner and two 120°shear steps resulted in the basal poles of most grains tilted to extrusion direction(ED)by±25°.Compared with the original billets,the extruded sheets exhibited higher yield strengths(YS),which was mainly attributed to the grain refinement.The higher Schmid factor caused by ED-tilt texture resulted in a fracture elongation(FE)more than that of the original bar in ED,while was equivalent to that in transverse direction(TD).As the extrusion temperature increased,the variation of UTS and YS in ED and TD decreased gradually without ductility obviously decrease.

Influence of pre-strain and heat treatment on subsequent deformation behavior of extruded AZ31 Mg alloy

Pre-compression and heat treatment were performed on an extruded AZ31 Mg alloy,and their effects on subsequent deformation behavior were investigated.The results show that at low temperature annealing(170 ℃ for 4 h),the extruded samples with and without annealing exhibit a nearly equivalent yield stress(~148 MPa) because their microstructures are nearly unchanged.However,under the same annealing condition,the yield stress of sample with pre-twinning and subsequent annealing(~225 MPa) is higher than that of the pre-twinned one(~200 MPa).The former sample presents a hardening effect because the solute atoms segregated on twin boundaries lead to a strengthening effect.The pre-twinned sample annealed at 400 ℃ for 1 h shows a higher ultimate elongation(~28%) than the pre-twinned one(~15%),but its yield stress(~125 MPa) is much lower than that of the pre-twinned one(~200 MPa).

Fatigue behavior of friction stir spot welded AZ31 Mg alloy sheet joints

The fatigue behavior of friction stir spot welded （FSSW） AZ31 magnesium alloy sheet joints was investigated by tension- compression of fatigue test. The results suggest that all the fatigue failures occur at the stir zone of the FSSW AZ31 sheet joints, and all cracks initiate at the stir zone outer edge between the upper and lower sheet. When the cycle force equals 1 kN, the crack propagates along the interface of heat-affected zone and thermo-mechanical zone, simultaneously across the direction of force; while the cycle force equals 3 kN, the crack propagates along the diameter of stir zone and shear failure occurs finally. Moreover, the transverse microsections indicate that there is a tongue-like region at the outer edge of stir zone between the two AZ31 sheets, and the direction of tongue-like region is toward outside of the stirred zone and all fatigue cracks initiate at the tongue-like region.

Effects of Nd and rotary forging on mechanical properties of AZ71 Mg alloys

The effects of Nd addition on the mechanical properties and plastic deformability of AZ71 Mg alloys were investigated.0.5%-2.0%（mass fraction） Nd was added to AZ71 Mg alloys.The grain size and the amount of brittle β-Mg17Al12 phase reduce with increasing the Nd addition,while nanosized AlxNdy precipitates form.In combination with 32% rotary forging and subsequent annealing,the grain size of Nd-added AZ71 Mg alloys reduces greatly from over 350 μm to below 30 μm.Both tensile strength and ductility increase with the Nd addition up to 1.0%.The addition of Nd beyond 1.0% leads to the aggregations of rod-shaped Al11Nd3 and blocky Al2 Nd precipitates,thereby deteriorating both strength and ductility.The 1.0% Nd-added AZ71 Mg alloy shows tensile strength up to 253 MPa and elongation of 10.7%.It is concluded that adding 1.0% Nd to AZ71 Mg alloy yields the optimum toughness,whether under as-cast or rotary forging and annealing conditions.

Tailoring strength-ductility balance of caliber-rolled AZ31 Mg alloy through subsequent annealing

Recently,multi-pass caliber rolling has been shown to be effective for Mg alloys.This study investigated the effect of subsequent annealing on the mechanical properties of a caliber-rolled AZ31 Mg alloy to modulate the strength-ductility relationship.This annealing gave rise to different trends in mechanical properties depending on the temperature regime.Low-temperature annealing(T≤473 K)exhibited a typical trade-off relationship,where an increase in annealing temperature resulted in increased ductility but decreased strength and hardness.Such a heat treatment did not degrade the high strength-ductility balance of the caliber-rolled alloy,suggesting that the mechanical properties could be tailored for different potential applications.In contrast,high-temperature annealing(T>473 K)caused a simultaneous deterioration in strength,hardness,and ductility with increasing annealing temperature.These differences are discussed in terms of the varying microstructural features under the different investigated annealing regimes.

Influence of heat treatment on the machinability and corrosion behavior of AZ91 Mg alloy

In the present study,AZ91 Mg alloy was heat treated at 410℃ for 6,12 and 24 h to investigate the influence of heat treatment on machinability and corrosion behavior.The effect of soaking time on the amount and distribution of Mg 17 Al 12(β-phase)was analyzed under the optical microscope.Microhardness measurements demonstrated the increased hardness with increased heat treatment soaking time,which can be attributed to the solid solution strengthening.The influence of super saturatedα-grains on reducing the cutting force(F z)with respect to increased cutting speed was observed as prominent.The corrosion behavior of the heat treated specimens was studied by conducting electrochemical tests.Surprisingly,corrosion rate of heat treated samples was observed as increased compared with the base material.From the results,it is evident that the machinability of AZ91 Mg alloy can be improved by producing super saturatedα-grains through heat treatment but at the cost of losing corrosion resistance.

The effect of Equal Channel Angular Pressing process on the microstructure of AZ31 Mg alloy strip shaped specimens

Equal Channel Angular Pressing(ECAP)is one of the most applicable Sever Plastic Deformation(SPD)processes which leads to strength and ductility improvement through the grain refining and development of a suitable texture.In this study,after designing and manufacturing a suitable die,4 pass ECAP process at route C is done on strip shaped specimens of AZ31 magnesium alloy in order to achieve desirable microstructural and mechanical properties.Microstructure then got studied through the optical microscopy.Results show that mean grain size is decreased and grain size distribution got close to normal distribution state by increasing the pass number.However,the grain size is reduced by increasing of ECAP temperature.

Anisotropy of the crystallographic orientation and corrosion performance of high-strength AZ80 Mg alloy

A high-strength AZ80 Mg alloy was prepared through multi-direction forging,thermal extrusion,and peak-aged heat treatment.The microstructure,crystallographic orientation and corrosion performance of extrusion-direction,transverse-direction,and normal-direction specimens were investigated using scanning electron microscopy,electron backscatter diffraction,and atomic force microscopy,respectively.Experimental results showed that crystallographic orientation significantly influenced the corrosion performance of AZ80 Mg alloy.Corrosion rates largely increased with decreased(0001)crystallographic plane intensity,whereas the(10−10)and(2−1−10)crystallographic plane intensities increased.This study showed that the corrosion rates of alloy can be modified to some extent by controlling texture,thereby promoting the applications of high-strength AZ80 Mg alloys in the aerospace and national-defense fields.

Diffusion bonding of Al 7075 and Mg AZ31 alloys:Process parameters, microstructural analysis and mechanical properties

Al 7075 and Mg AZ31 alloys were joined by diffusion bonding method. Joining process was performed in pressure range of 10-35 MPa at temperatures of 430-450 ℃ for 60 min under a vacuum of 13.3 MPa. The microstructure evaluation, phase analysis and distribution of elements at the interface were done using scanning electron microscopy （SEM）, energy-dispersive X-ray spectroscopy （EDS） and X-ray diffraction （XRD）. The pressure of 25 MPa was determined as the optimum pressure in which the minimum amount of plastic deformation takes place at the joint. Different reaction layers containing intermetallic compounds, such as Al12Mg17, Al3Mg2 andα（Al） solid solution, were observed, in interfacial transition zone （ITZ）. Thickness of layers was increased with increasing the operating temperature. According to the results, diffusion of aluminum atoms into magnesium alloy was more and the interface movement towards the Al alloy was observed. The maximum bond strength of 38 MPa was achieved at the temperature of 440 ℃ and pressure of 25 MPa. Fractography studies indicated that the brittle fracture originated from Al3Mg2 phase.

Formability of AZ31 Mg alloy sheets within medium temperatures

The stretching tests of the commercial AZ31 Mg alloy were conducted at 130 ℃, 170 ℃, 210 ℃, at the forming speeds of 10 mm/min and 50 mm/min, respectively. The formability of AZ31 sheets at high temperature was evaluated by forming limit diagrams (FLD). The fracture morphologies were analyzed using a scanning electron microscope. The results show that the FLD of AZ31 Mg alloy is affected by the forming temperature, in another word, the formability increases with the increasing of the forming temperature. That may be because the non-basal slip system starts to move by thermal activation at high forming temperature. It is also demonstrated that the formability of the AZ31 Mg alloy is on the decline with the increasing of the forming speed. The slipping performs thoroughly to release the stress during the deformation if the forming speed decreases. In addition, the higher the forming temperature is, the more obvious the effect of the forming speed is. The forming temperature is the main dominating factor on the formability of AZ31 Mg alloy.

Grain refining and property improvement of AZ31 Mg alloy by hot rolling

Hot rolling of AZ31 Mg alloy was performed by using as-cast alloy ingot as the starting material.The microstructures and mechanical properties of the as-rolled alloy subjected to various rolling passes were investigated.The results show that the grain size of the alloy can be refined steadily with increasing rolling passes by dynamic recrystallization.With the steady refining of the grain size,both the mechanical strength and the plasticity of the alloy are improved correspondingly.In particular,when the grain size is reduced to about 5μm after 5 rolling passes,the yield strength,ultimate tensile strength and tensile fracture strain of the alloy are 211 MPa,280 MPa and 0.28 in the transverse direction,they are 200 MPa,268 MPa and 0.32 in the rolling direction,respectively.

Enhancing fatigue performance of AZ31 magnesium alloy components fabricated by cold metal transfer-based wire arc directed energy deposition through LPB

Cold Metal Transfer-Based Wire Arc Directed Energy Deposition(CMT-WA-DED)presents a promising avenue for the rapid fabrication of components crucial to automotive,shipbuilding,and aerospace industries.However,the susceptibility to fatigue of CMT-WA-DED-produced AZ31 Mg alloy components has impeded their widespread adoption for critical load-bearing applications.In this study,a comprehensive investigation into the fatigue behaviour of WA-DED-fabricated AZ31 Mg alloy has been carried out and compared to commercially available wrought AZ31 alloy.Our findings indicate that the as-deposited parts exhibit a lower fatigue life than wrought Mg alloy,primarily due to poor surface finish,tensile residual stress,porosity,and coarse grain microstructure inherent in the WA-DED process.Low Plasticity Burnishing(LPB)treatment is applied to mitigate these issues,which induce significant plastic deformation on the surface.This treatment resulted in a remarkable improvement of fatigue life by 42%,accompanied by a reduction in surface roughness,grain refinement and enhancement of compressive residual stress levels.Furthermore,during cyclic deformation,WA-DED specimens exhibited higher plasticity and dislocation density compared to both wrought and WA-DED+LPB specimens.A higher fraction of Low Angle Grain Boundaries(LAGBs)in WA-DED specimens contributed to multiple crack initiation sites and convoluted crack paths,ultimately leading to premature failure.In contrast,wrought and WA-DED+LPB specimens displayed a higher percentage of High Angle Grain Boundaries(HAGBs),which hindered dislocation movement and resulted in fewer crack initiation sites and less complex crack paths,thereby extending fatigue life.These findings underscore the effectiveness of LPB as a post-processing technique to enhance the fatigue performance of WA-DED-fabricated AZ31 Mg alloy components.Our study highlights the importance of LPB surface treatment on AZ31 Mg components produced by CMT-WA-DED to remove surface defects,enabling their widespread use in load-bearing applications.

Development of anti-corrosive coating on AZ31 Mg alloy subjected to plasma electrolytic oxidation at sub-zero temperature

Plasma electrolytic oxidation(PEO)is a promising surface treatment to generate adherent and thick anti-corrosive coating on light-weight metals(Al,Mg,Ti,etc.)using an eco-friendly alkaline electrolyte.High energy plasma,however,inevitably generates porous structures that limit their practical performance.The present study proposes a straight-forward simple method by utilizing sub-zero electrolyte(268 K)to alter the plasma characteristics during formation of the protective coating on AZ31 Mg alloy via PEO with a comparison to the electrolyte at room temperature(298 K).In refrigerated electrolyte,the formation of micro-defects is suppressed relatively at the expense of low coating growth,which is measured to be twice lower than that at 298 K due to the temperature-dependent soft plasma discharges contributing to the development of the present coating.As a consequence,corrosion resistance of the sample processed at 268 K is superior to that of 298K,implying that the effect of coating thickness is less dominant than that of compactness.This phenomenon is interpreted in relation to the ionic movement and oxide solidification controlled by soft plasma discharges arising from the temperature gradient between electrolyte and surface of the substrate during PEO.

Fabrication of chitosan/silica hybrid coating on AZ31 Mg alloy for orthopaedic applications

Biocompatible conversion of chitosan and chitosan/silica hybrid coating were prepared to enhance the biocompatibility and corrosion resistance of biodegradable AZ31 Mg alloy. The coatings were optimized and analysed with potentiodynamic polarization, SEM, ATR-IR and XPS studies. Potentiodynamic polarization studies, revealed that the coatings exhibited high corrosion resistance. The surface morphology of the Ch-3/Si coating showed small globular rough structure. The presence of functional groups was confirmed by ATR-IR. For a better understanding of chitosan/silica hybrid coating, the chemical states were examined by XPS studies. The in-vitro bioactivity of the coated samples was evaluated in Earle’s solution, which formed a dense layer of coral-like structure and calcium-deficient apatite with less stoichiometric ratio than the hydroxyapatite. In-vitro cell culture studies exhibited a good cell proliferation rate and the fabricated Ch-3/Si coating was found to be non-hemolytic. The bacterial studies proved that Ch-3/Si coating possessed inherent antibacterial activity.

Shear behavior of AZ80 Mg alloy using experimental, theoretical and numerical techniques

The shear punch test(SPT)is a suitable experiment for characterizing the shear behavior of various materials,especially where there are volume limitations.In the present investigation,the relations among various parameters such as clearance,die diameter and sample thickness,and the yield and ultimate shear strengths of AZ80Mg alloy were studied.Moreover,based on the Mohr-Coulomb theory,relatively optimum conditions were introduced for the shear punch test.With this regard,a range of2%-10%is found to be suitable for the clearance/sheet thickness ratio.To provide a simple shear stress state during a shear punch test,it is also necessary to select the die diameter/sheet thickness ratio between2:1and10:1.Based on the predictions of the Mohr-Coulomb theory,it is better to conduct a room-temperature shear punch test with a sample thickness of0.5mm,a clearance of25μm and a die diameter of2mm.Finally,the mean conversion factors to gain the tensile and compressive yield strengths of the cast AZ80from its shear one are found to be1.70and3.09,respectively.

On the cold rolling of AZ31 Mg alloy after Equal Channel Angular Pressing

Among the various Severe Plastic Deformation(SPD)processes,Equal Channel Angular Pressing(ECAP)is one of the most applicable one which improves strength and ductility due to grain refinement and suitable texture development.In this study,cold rolling were carried out on the 4 pass ECAPed(in route A and C)strip shaped specimens of AZ31 magnesium alloy to investigate the ECAP effects on the roll-ability.Results showed that reduction in area which can be concerned as an index for roll-ability increased after ECAP.It was also seen that ECAP in route C enhanced roll-ability more than route A.

Effect of electrolyte on mechanical properties of AZ31B Mg alloy in electrolytic plasma processing

Coatings on Mg alloys were prepared using NaOH + Na2SiO3 as basic electrolyte containing electrolyte of Na2SiF6 or NaF. EPP treatment was carried out on AZ31 Mg alloys matrix under a hybrid voltage of AC of 200 V combined with DC of 260 V for 30 min. Structural and morphological analyses of ceramic coatings were analyzed by XRD and SEM. Wear and hardness of coatings were measured by pin-on disk test and Vickers hardness test. The coatings formed in Na2SiF6 and NaF electrolytes were mainly composed of MgO and Mg2SiO4. The measured micro-hardness of coating formed in Na2SiF6 electrolyte was found to be over HV 1100, while, coating formed in NaF electrolyte possessed micro-hardness of HV ~900. These results show that the mechanical properties of AZ31 B Mg alloys can be enhanced by the proper selection of electrolyte agent.

Quasi-in vivo corrosion behavior of AZ31B Mg alloy with hybrid MWCNTs-PEO/PCL based coatings

This study investigated the effects of multi-walled carbon nanotubes(MWCNTs) and polycaprolactone(PCL) on the quasi-in vivo corrosion behavior of AZ31B Mg alloy treated by plasma electrolytic oxidation(PEO). Thin(~2 μm, PCTPCL4) and thick(~60 μm, PCTPCL6) PCL layers were applied only onto the MWCNTs-PEO coating(PCT) as it showed better corrosion performance. Findings reveal that incorporation of MWCNTs induced several structural and functional modifications in the PEO coating, such as increased roughness, a thicker inner barrier layer, and reduced hydrophilicity.Quasi-in vivo corrosion testing was carried out under controlled temperature, p H, and fluid flow in simulated body fluid(SBF) by electrochemical impedance spectroscopy(EIS) and hydrogen evolution experiments. EIS results revealed that, after 48 h immersion, a diffusion process controlled hydration of the ceramic coatings. Comparison of the collected hydrogen after 15 days of immersion in the quasi-in vivo environment revealed that the PEO and PCT ceramic coatings decreased hydrogen generation by up to 74% and 91%, respectively, compared to non-coated alloy.PCTPCL6 coating exhibited the lowest amount of collected hydrogen(0.2 m L/cm^(2)). The thick PCL layer delayed the onset of substrate corrosion for at least 120 h, reducing the corrosion rate by 85% compared with the PCT.

Paint-bake response of AZ80 and AZ31 Mg alloys

Aging behaviors of extruded and rolled AZ80 and AZ31 Mg alloys were investigated under conditions similar to the paint-bake cycle currently used in automotive industry.Artificial aging at 170℃ from 0.5 to 12 h was conducted on solution-treated specimens to study the effects of aging on mechanical properties.SEM observations and EDS data show thatβ-phase of Al12Mg17 precipitates continuously or discontinuously fromα-Mg matrix and distributes along grain boundaries of the AZ80 alloy during artificial aging.Data of tensile tests and Vickers hardness tests show that an optimum mechanical property is achieved after baking at 170℃ for 6-8 h when Vickers hardness,tensile strength,and elongation are increased by 6.35%,15.30%,and 7.88%,respectively, while the AZ31 alloy does not exhibit significant hardening behavior over the aging period.