The electroplastic effect in AZ31B magnesium alloy sheet was investigated through uniaxial tensile tests. In order to show the athermal effect of the electrical pulses, two types of uniaxial tensile tests at the same ...The electroplastic effect in AZ31B magnesium alloy sheet was investigated through uniaxial tensile tests. In order to show the athermal effect of the electrical pulses, two types of uniaxial tensile tests at the same testing temperature were carried out： uniaxial tension in environmental cabinet and uniaxial tension with electrical pulses. In addition, the distribution of temperature field in the cross-section area during uniaxial tension with electrical pulses was simulated. The results show that the distribution of temperature field along the cross-section area is homogeneous. By comparing the true stress？true strain curves of AZ31B alloy under uniaxial tensile tests, the athermal effect with electrical pulses was confirmed. The microstructure evolution after the uniaxial tension was studied by optical microscopy. The results indicate that the electrical pulses induced dynamic recrystallization plays an important role in the decrease of flow stress. Finally, a flow stress model of AZ31B sheet taking the influence of electroplastic effect into account was proposed and validated. The results demonstrate that the calculated data fit the experimental data well.展开更多
Biodegradable magnesium-based alloys are very promising materials for temporary implants. Laser welding is an important joining method in such application. In this study, the as-rolled AZ31B magnesium alloy sheets of ...Biodegradable magnesium-based alloys are very promising materials for temporary implants. Laser welding is an important joining method in such application. In this study, the as-rolled AZ31B magnesium alloy sheets of 1 mm in thickness were successfully joined by Nd ： YAG laser welding. The microstructure and properties of the welded joint were investigated. The result shows that the welded joint is characterized by a narrow heat-affected zone, finer grains and a large number of precipitates distribute in the matrix in the weld. Microhardness of the weld is significantly improved to 72 HV 0. 05 as compared to 55 HV 0. 05 of the base metal. Tensile strength of butt-welded joint is 180. 24 MPa, which is 76. 8% that of the base metal. The electrochemical corrosion experiment shows that the corrosion resistance of laser welded joint is significantly improved in a 3.5 wt. % NaCl solution.展开更多
The purpose of this research is to explore the feasibility of roller hemming of AZ31 B magnesium alloy sheet. During the test, a special experimental setup considering the current flow and insulation was designed and ...The purpose of this research is to explore the feasibility of roller hemming of AZ31 B magnesium alloy sheet. During the test, a special experimental setup considering the current flow and insulation was designed and employed. For the sake of simplicity, the flat surface-straight edge hemming style was selected. Electrical pulses were introduced in the pre-hemming and final hemming processes. The results show that when hemming at 448 K with hemming speed of 30 mm/min, AZ31 B magnesium alloy sheet was successfully hemmed with excellent perceived quality. No recoil/warp defect, cracking or springback was observed. Electrical pulses induced dynamic recrystallized grains were observed along the grain boundaries in the severely deformed area, which is of great importance to the improvement of the ductility of the material. The hardness was slightly increased after hemming with electrical pulses, and this fact could improve the friction resistance performance of the hemmed part.展开更多
基金Projects(50975174,51275297)supported by the National Natural Science Foundation of ChinaProject(20100073110044)supported by the Education Ministry of China
文摘The electroplastic effect in AZ31B magnesium alloy sheet was investigated through uniaxial tensile tests. In order to show the athermal effect of the electrical pulses, two types of uniaxial tensile tests at the same testing temperature were carried out： uniaxial tension in environmental cabinet and uniaxial tension with electrical pulses. In addition, the distribution of temperature field in the cross-section area during uniaxial tension with electrical pulses was simulated. The results show that the distribution of temperature field along the cross-section area is homogeneous. By comparing the true stress？true strain curves of AZ31B alloy under uniaxial tensile tests, the athermal effect with electrical pulses was confirmed. The microstructure evolution after the uniaxial tension was studied by optical microscopy. The results indicate that the electrical pulses induced dynamic recrystallization plays an important role in the decrease of flow stress. Finally, a flow stress model of AZ31B sheet taking the influence of electroplastic effect into account was proposed and validated. The results demonstrate that the calculated data fit the experimental data well.
基金The work was supported by the National Natural Science Foundation of China （ Grant No. 51305292 ） and the Aviation Science Foundation （ Grant No. 20105429001 ）.
文摘Biodegradable magnesium-based alloys are very promising materials for temporary implants. Laser welding is an important joining method in such application. In this study, the as-rolled AZ31B magnesium alloy sheets of 1 mm in thickness were successfully joined by Nd ： YAG laser welding. The microstructure and properties of the welded joint were investigated. The result shows that the welded joint is characterized by a narrow heat-affected zone, finer grains and a large number of precipitates distribute in the matrix in the weld. Microhardness of the weld is significantly improved to 72 HV 0. 05 as compared to 55 HV 0. 05 of the base metal. Tensile strength of butt-welded joint is 180. 24 MPa, which is 76. 8% that of the base metal. The electrochemical corrosion experiment shows that the corrosion resistance of laser welded joint is significantly improved in a 3.5 wt. % NaCl solution.
基金the National Natural Science Foundation of China(Nos.50975174 and 51275297)
文摘The purpose of this research is to explore the feasibility of roller hemming of AZ31 B magnesium alloy sheet. During the test, a special experimental setup considering the current flow and insulation was designed and employed. For the sake of simplicity, the flat surface-straight edge hemming style was selected. Electrical pulses were introduced in the pre-hemming and final hemming processes. The results show that when hemming at 448 K with hemming speed of 30 mm/min, AZ31 B magnesium alloy sheet was successfully hemmed with excellent perceived quality. No recoil/warp defect, cracking or springback was observed. Electrical pulses induced dynamic recrystallized grains were observed along the grain boundaries in the severely deformed area, which is of great importance to the improvement of the ductility of the material. The hardness was slightly increased after hemming with electrical pulses, and this fact could improve the friction resistance performance of the hemmed part.