Influence of solution treatment on microstructure and properties of in-situ Mg_2Si/AZ91D composites

The influence of solution treatment on the microstructure and properties of Mg2Si/AZ91D composites fabricated from Mg-SiO2 system via in-situ processing method was investigated.The results show that coarse Chinese script shape Mg2Si phases can be formed by adding SiO2 into AZ91D magnesium alloy with Si content up to 1.5% of the alloy melt.During solution treatment,the morphology and distribution of the coarse Chinese script shape Mg2Si phases are modified.Meanwhile,the β-Mg17Al12 phase is dissolved into the magnesium matrix.With increasing holding time,the coarse Mg2Si phases tend to dissolve,break and spheroidize.After solution treatment at 420 ℃ for 16 h,Mg2Si phases become the finest and relatively well-distributed phase.The tensile strength and elongation are increased by 14.9% and 38.9%,respectively.It is believed that the Mg2Si phases continuously dissolve and break,and finally the spheroidized Mg2Si particles are obtained due to the interface tension of Mg2Si/Mg interface.

Microstructure and Mechanical Behavior of Squeeze Cast SiC_w/AZ91 Magnesium Matrix Composites

The interfacial microstructure and tensile properties of the squeeze cast SiCw/AZ91 Mg composites were characterized. There exist uniform, line and discrete MgO particles at the interface between SiC whisker and magnesium in the composites using acid aluminum phosphate binder. The interfacial reaction products MgO are beneficial to interfacial bonding between SiCw and the Mg matrix. resulting in an improvement of the mechanical properties of the composite.

Experimental determination of grain density function of AZ91/SiC composite with different mass fractions of SiC and undercoolings using heterogeneous nucleation model

The grain density,Nv,in the solid state after solidification of AZ91/SiC composite is a function of maximum undercooling,ΔT,of a liquid alloy.This type of function depends on the characteristics of heterogeneous nucleation sites and number of SiC present in the alloy.The aim of this paper was selection of parameters for the model describing the relationship between the grain density of primary phase and undercooling.This model in connection with model of crystallisation,which is based on chemical elements diffusion and grain interface kinetics,can be used to predict casting quality and its microstructure.Nucleation models have parameters,which exact values are usually not known and sometimes even their physical meaning is under discussion.Those parameters can be obtained after mathematical analysis of the experimental data.The composites with 0,1,2,3 and 4wt.% of SiC particles were prepared.The AZ91 alloy was a matrix of the composite reinforcement SiC particles.This composite was cast to prepare four different thickness plates.They were taken from the region near to the thermocouple,to analyze the undercooling for different composites and thickness plates and its influence on the grain size.The microstructure and thermal analysis gave set of values that connect mass fraction of SiC particles,and undercooling with grain size.These values were used to approximate nucleation model adjustment parameters.Obtained model can be very useful in modelling composites microstructure.

Effects of in-situ ZrB_2 particle on grain refinement of ZrB_2/AZ91D magnesium matrix composite

In-situ ZrB2/AZ91D magnesium matrix composite was successfully synthesized with AI/K2ZrF6＋NH4BF4 by means of Direct Melt Reaction. The fabricated ZrB2/AZ91D magnesium matrix composite through direct melt mixing method was investigated. Results from X-ray diffraction （XRD） and energy dispersive X-ray spectroscopy （EDS） confirmed the existence of ZrB2 particles in the AZ91D alloy, and most ZrB2 particles were in the size range of just several microns, some even to 100 nm. The cast specimens were studied through corrosion testing and heat treatment. The average grain size of AZ91D decreased markedly from about 250 pm to 50 IJm. In addition, the shape and size of the ,β-MglTAI12 phase as well as the morphologies of primary a-Mg in the magnesium matrix composite were greatly changed. The network structure of the β-MglTAI12 phase was broken into small blocks and the size of a-Mg decreased significantly.