In areas where hot mix asphalt(HMA)is likely to be exposed by any form of mineral oil the layer has to withstand the attack of these substances in order not to damage the construction.The European Standard EN 12697-43...In areas where hot mix asphalt(HMA)is likely to be exposed by any form of mineral oil the layer has to withstand the attack of these substances in order not to damage the construction.The European Standard EN 12697-43 provides a test procedure to determine the resistance of HMA to fuel.The paper reviews this method thoroughly.A completely revised and simplified test device for the brush test was developed meeting the requirements of the standard and creating results with a high repeatability at the same time.The test conditions given by the standard such as the exposure to fuel,cleaning of the specimen after exposure or the contact pressure of the brush were varied to isolate those test conditions with a substantial influence on the result.The research revealed that in the standard some conditions with a rather small influence are set quite strictly while other conditions with a distinct influence on the result are not defined with the required accuracy to obtain comparable and repeatable results.The paper presents suggestions for the improvement of the test method and the standard itself in respect to the layout of the test device and the definition of important test conditions to enhance the outcome of the EN 12697-43.展开更多
Abradable seal rubber has been widely used in aero-engine fans to improve their efficiency by reducing the clearance between rotating and stationary components. To investigate the high-speed scraping behavior between ...Abradable seal rubber has been widely used in aero-engine fans to improve their efficiency by reducing the clearance between rotating and stationary components. To investigate the high-speed scraping behavior between a vulcanized silicone rubber and a Ti-6Al-4V fan blade and evaluate the abradable performance of seal rubber, abrasion tests were conducted at a blade tip velocity of 50–300 m/s with an incursion rate of 100 lm/s. The influences of the blade tip velocity on the wear mechanism and interaction forces were specially analyzed. It is shown that abrasive wear and pattern wear are the predominant wear mechanisms, and pattern wear can be seen as the emergence and propagation of cracks. With an increase of the blade tip velocity, both of the final incursion depth and wear mass loss of seal rubber exhibit growth trends. The gradual changes of rubbing forces with an increase of rubbing time are the characteristic of abrasive wear, and force curves with unstable mutations are a reflection of pattern wear. At a constant incursion rate of 100 lm/s, the maximum values of interaction forces decrease first and then grow with an increase of the blade tip velocity, and the blade tip velocity of 150 m/s becomes the cut-off point between abrasive wear and pattern wear.展开更多
文摘In areas where hot mix asphalt(HMA)is likely to be exposed by any form of mineral oil the layer has to withstand the attack of these substances in order not to damage the construction.The European Standard EN 12697-43 provides a test procedure to determine the resistance of HMA to fuel.The paper reviews this method thoroughly.A completely revised and simplified test device for the brush test was developed meeting the requirements of the standard and creating results with a high repeatability at the same time.The test conditions given by the standard such as the exposure to fuel,cleaning of the specimen after exposure or the contact pressure of the brush were varied to isolate those test conditions with a substantial influence on the result.The research revealed that in the standard some conditions with a rather small influence are set quite strictly while other conditions with a distinct influence on the result are not defined with the required accuracy to obtain comparable and repeatable results.The paper presents suggestions for the improvement of the test method and the standard itself in respect to the layout of the test device and the definition of important test conditions to enhance the outcome of the EN 12697-43.
基金supported by the Fundamental Research Funds for the Central Universities (No. 2013XZZX005)
文摘Abradable seal rubber has been widely used in aero-engine fans to improve their efficiency by reducing the clearance between rotating and stationary components. To investigate the high-speed scraping behavior between a vulcanized silicone rubber and a Ti-6Al-4V fan blade and evaluate the abradable performance of seal rubber, abrasion tests were conducted at a blade tip velocity of 50–300 m/s with an incursion rate of 100 lm/s. The influences of the blade tip velocity on the wear mechanism and interaction forces were specially analyzed. It is shown that abrasive wear and pattern wear are the predominant wear mechanisms, and pattern wear can be seen as the emergence and propagation of cracks. With an increase of the blade tip velocity, both of the final incursion depth and wear mass loss of seal rubber exhibit growth trends. The gradual changes of rubbing forces with an increase of rubbing time are the characteristic of abrasive wear, and force curves with unstable mutations are a reflection of pattern wear. At a constant incursion rate of 100 lm/s, the maximum values of interaction forces decrease first and then grow with an increase of the blade tip velocity, and the blade tip velocity of 150 m/s becomes the cut-off point between abrasive wear and pattern wear.