Moisture Absorption and Desorption in an Ionomer-Based Encapsulant:A Type of Self-Breathing Encapsulant for CIGS Thin-Film PV Modules

As an alternative to conventional encapsulation concepts for a double glass photovoltaic(PV)module,we introduce an innovative ionomer-based multi-layer encapsulant,by which the application of additional edge sealing to prevent moisture penetration is not required.The spontaneous moisture absorption and desorption of this encapsulant and its raw materials,poly(ethylene-co-acrylic acid)and an ionomer,are analyzed under different climatic conditions in this work.The relative air humidity is thermodynamically the driving force for these inverse processes and determines the corresponding equilibrium moisture content(EMC).Higher air humidity results in a larger EMC.The homogenization of the absorbed water molecules is a diffusion-controlled process,in which temperature plays a dominant role.Nevertheless,the diffusion coefficient at a higher temperature is still relatively low.Hence,under normal climatic conditions for the application of PV modules,we believe that the investigated ionomer-based encapsulant can“breathe”the humidity:During the day,when there is higher relative humidity,it“inhales”(absorbs)moisture and restrains it within the outer edge of the module;then at night,when there is a lower relative humidity,it“exhales”(desorbs)the moisture.In this way,the encapsulant protects the cell from moisture ingress.

Study on Hydrogen Storage Properties,Anti-Oxide Ability and Rate Limiting Step of ZrCr-Based Alloy after Introducing Cobalt as Additive

In this work,the microstructure,hydrogen storage properties,anti-oxide ability and rate limiting step of Zr(Cr_(1−x)Co_(x))_(2)(x=0,0.2,0.4 and 0.6)alloys have been investigated.After studying the crystal structure,we found that all alloy samples could show C14-type phase but the alloy sample x=0 could also show a small amount of Cr phase.Rietveld fitting showed that lattice parameter and unit cell volume of C14-type phase decreased with increasing x.After further research,it was clear that the first hydrogen absorption capacity decreased with increasing x.But introducing more Co content had a positive influence on the effective hydrogen storage capacity and cyclic hydrogen absorption and desorption properties of the alloy sample.We also found that adding Co to ZrCr_(2)alloy could improve its anti-oxide ability.In addition to this,the rate limiting step model was also studied.