Blends of poly（lactic acid）（PLA） and thermoplastic acetylated starch（ATPS） were prepared by means of the melt mixing method. The results show that PLA and ATPS were partially miscible, which was confirmed with t...Blends of poly（lactic acid）（PLA） and thermoplastic acetylated starch（ATPS） were prepared by means of the melt mixing method. The results show that PLA and ATPS were partially miscible, which was confirmed with the measurement of Tg by dynamic mechanical analysis（DMA） and differrential scanning calorimetry（DSC）. The mechanical and thermal properties of the blends were improved. With increasing the ATPS content, the elongation at break and impact strength were increased. The elongation at break increased from 5% of neat PLA to 25% of the blend PLA/ATPS40. It was found that the cold crystallization behavior of PLA changed evidently by addition of ATPS. The cold crystallization temperature（Tcc） of each of PLA/ATPS blends was found to shift to a lower temperature and the width of exothermic peak became narrow compared with that of neat PLA. The thermogravimetry analysis（TGA） results showed that the peak of derivative weight for ATPS moved to higher temperature with increasing PLA content in PLA/ATPS blends. It can be concluded that PLA could increase the thermal stability of ATPS. The rheological measurement reveals the melt elasticity and viscosity of the blends decreased with the increased concentration of ATPS, which was favorable to the processing properties of PLA.展开更多
Sugar palm(Arenga pinnata)starch is considered an important renewable,biodegradable,and eco-friendly polymer,which is derived from agricultural by-products and residues,with great potential for the development of bioc...Sugar palm(Arenga pinnata)starch is considered an important renewable,biodegradable,and eco-friendly polymer,which is derived from agricultural by-products and residues,with great potential for the development of biocomposite materials.This research was aimed at investigating the development of TPS biocomposites from A.pinnata palm starch using an extrusion process.Palm starch,glycerol,and stearic acid were extruded in a twin-screw extruder.Scanning electron microscopy(SEM)analysis of TPS showed that the starch granules were damaged and gelatinized in the extrusion process.The density of TPS was 1.3695 g/mL,lower than that of palm starch,and the addition of stearic acid resulted in increased TPS density.X-ray diffraction(XRD)results showed that palm starch had a C-type pattern crystalline structure.The tensile strength,elongation at break,and modulus of elasticity of TPS were 7.19 MPa,33.95%,and 0.56 GPa,respectively.The addition of stearic acid reduced the tensile strength,elongation at break and modulus of elasticity of TPS.The rheological properties,i.e.,melt flow rate(MFR)and viscosity of TPS,were 7.13 g/10 min and 2482.19 Pa.s,respectively.The presence of stearic acid in TPS resulted in increased MFR and decreased viscosity values.The peak gelatinization temperature of A.pinnata palm starch was 70°C,while Tg of TPS was 65°C.The addition of stearic acid reduced the Tg of TPS.The thermogravimetric analysis(TGA)analysis showed that the addition of glycerol and stearic acid decreased the thermal stability,but extended the temperature range of thermal degradation.TPS derived from A.pinnata palm starch by extrusion method has the potential to be applied in industrial practice as a promising raw material for manufacturing bio-based packaging as a sustainable and green alternative to petroleum-based plastics.展开更多
In this paper,aliphatic amidediol was synthesized and mixed with glycerol used as a plasticizer for preparing thermoplastic starch（AGPTPS）.The yield of aliphatic amidediol was 91%.FF-IR expressed that the mixture of...In this paper,aliphatic amidediol was synthesized and mixed with glycerol used as a plasticizer for preparing thermoplastic starch（AGPTPS）.The yield of aliphatic amidediol was 91%.FF-IR expressed that the mixture of aliphatic amidediol and glycerol formed stronger and stable hydrogen bond with starch molecules compared to the native cornstarch.By scanning electron microscope（SEM）native cornstarch granules were proved to transfer to a homogeneous continuous system.After being stored for a period time at room temperature,the mechanical properties of AGPTPS were also studied.As a mixed plasticizer,aliphatic amidediol and glycerol would be practical to extend TPS application scopes.展开更多
基金Supported by the Chinese Academy of Sciences Direction Project(No.KTCX-YW-208)
文摘Blends of poly（lactic acid）（PLA） and thermoplastic acetylated starch（ATPS） were prepared by means of the melt mixing method. The results show that PLA and ATPS were partially miscible, which was confirmed with the measurement of Tg by dynamic mechanical analysis（DMA） and differrential scanning calorimetry（DSC）. The mechanical and thermal properties of the blends were improved. With increasing the ATPS content, the elongation at break and impact strength were increased. The elongation at break increased from 5% of neat PLA to 25% of the blend PLA/ATPS40. It was found that the cold crystallization behavior of PLA changed evidently by addition of ATPS. The cold crystallization temperature（Tcc） of each of PLA/ATPS blends was found to shift to a lower temperature and the width of exothermic peak became narrow compared with that of neat PLA. The thermogravimetry analysis（TGA） results showed that the peak of derivative weight for ATPS moved to higher temperature with increasing PLA content in PLA/ATPS blends. It can be concluded that PLA could increase the thermal stability of ATPS. The rheological measurement reveals the melt elasticity and viscosity of the blends decreased with the increased concentration of ATPS, which was favorable to the processing properties of PLA.
基金from The Hitachi Global Foundation Asia Innovation Award 2020.Also,the authors thank the facilities,scientific and technical support from Advanced Characterization Laboratories Serpong and Cibinong,National Research and Innovation Institute through E-Layanan Sains,Badan Riset dan Inovasi Nasional(BRIN).
文摘Sugar palm(Arenga pinnata)starch is considered an important renewable,biodegradable,and eco-friendly polymer,which is derived from agricultural by-products and residues,with great potential for the development of biocomposite materials.This research was aimed at investigating the development of TPS biocomposites from A.pinnata palm starch using an extrusion process.Palm starch,glycerol,and stearic acid were extruded in a twin-screw extruder.Scanning electron microscopy(SEM)analysis of TPS showed that the starch granules were damaged and gelatinized in the extrusion process.The density of TPS was 1.3695 g/mL,lower than that of palm starch,and the addition of stearic acid resulted in increased TPS density.X-ray diffraction(XRD)results showed that palm starch had a C-type pattern crystalline structure.The tensile strength,elongation at break,and modulus of elasticity of TPS were 7.19 MPa,33.95%,and 0.56 GPa,respectively.The addition of stearic acid reduced the tensile strength,elongation at break and modulus of elasticity of TPS.The rheological properties,i.e.,melt flow rate(MFR)and viscosity of TPS,were 7.13 g/10 min and 2482.19 Pa.s,respectively.The presence of stearic acid in TPS resulted in increased MFR and decreased viscosity values.The peak gelatinization temperature of A.pinnata palm starch was 70°C,while Tg of TPS was 65°C.The addition of stearic acid reduced the Tg of TPS.The thermogravimetric analysis(TGA)analysis showed that the addition of glycerol and stearic acid decreased the thermal stability,but extended the temperature range of thermal degradation.TPS derived from A.pinnata palm starch by extrusion method has the potential to be applied in industrial practice as a promising raw material for manufacturing bio-based packaging as a sustainable and green alternative to petroleum-based plastics.
文摘In this paper,aliphatic amidediol was synthesized and mixed with glycerol used as a plasticizer for preparing thermoplastic starch（AGPTPS）.The yield of aliphatic amidediol was 91%.FF-IR expressed that the mixture of aliphatic amidediol and glycerol formed stronger and stable hydrogen bond with starch molecules compared to the native cornstarch.By scanning electron microscope（SEM）native cornstarch granules were proved to transfer to a homogeneous continuous system.After being stored for a period time at room temperature,the mechanical properties of AGPTPS were also studied.As a mixed plasticizer,aliphatic amidediol and glycerol would be practical to extend TPS application scopes.