TiO2 nanotube precursor was synthesized by the hydrothermal reaction of TiO2 powders with NaOH solution and the properties of the nanotube materials were tuned using different post-treatments. Transmission electron mi...TiO2 nanotube precursor was synthesized by the hydrothermal reaction of TiO2 powders with NaOH solution and the properties of the nanotube materials were tuned using different post-treatments. Transmission electron microscopic (TEM) observation revealed that the nanotube could be obtained by either a direct rinse with acid solution or rinse with distilled water followed by acid solution. The results of X-ray diffraction (XRD) and inductively coupled plasma (ICP) analysis indicated that the nanotube material was composed of H2Ti2O5·H2O. In addition, the photocatalytic activities of the resulting catalysts were found to be strongly dependent on the post-treatment. The results of the photocatalytic reaction showed that the degradation of Acid-red 3B dye fitted pseudo-zero-order kinetics and TiO2 nanotube prepared under direct rinse with acid solution exhibited a higher catalytic efficiency compared to other catalysts.展开更多
在冰乙酸介质中,利用亚硝酸根催化条件下,溴酸钾氧化茜素红的褪色反应,建立催化动力学光度法,对痕量NO_(2)^(-)进行测定.通过单因素实验得到了各种成分的加入量、反应温度和反应时间等最佳条件.结果发现,在反应体系中,茜素红浓度与NO_(2...在冰乙酸介质中,利用亚硝酸根催化条件下,溴酸钾氧化茜素红的褪色反应,建立催化动力学光度法,对痕量NO_(2)^(-)进行测定.通过单因素实验得到了各种成分的加入量、反应温度和反应时间等最佳条件.结果发现,在反应体系中,茜素红浓度与NO_(2)^(-)含量之间线性关系良好,在0.02~0.14μg/mL范围内,线性回归方程为ln(A_(0)/A)=1.43 c NO_(3)^(-)(μg/mL)+0.00859,相关系数r^(2)为0.9970,检出限为5.25×10^(-3)μg/mL.该方法操作简单、稳定性好.展开更多
文摘TiO2 nanotube precursor was synthesized by the hydrothermal reaction of TiO2 powders with NaOH solution and the properties of the nanotube materials were tuned using different post-treatments. Transmission electron microscopic (TEM) observation revealed that the nanotube could be obtained by either a direct rinse with acid solution or rinse with distilled water followed by acid solution. The results of X-ray diffraction (XRD) and inductively coupled plasma (ICP) analysis indicated that the nanotube material was composed of H2Ti2O5·H2O. In addition, the photocatalytic activities of the resulting catalysts were found to be strongly dependent on the post-treatment. The results of the photocatalytic reaction showed that the degradation of Acid-red 3B dye fitted pseudo-zero-order kinetics and TiO2 nanotube prepared under direct rinse with acid solution exhibited a higher catalytic efficiency compared to other catalysts.
文摘在冰乙酸介质中,利用亚硝酸根催化条件下,溴酸钾氧化茜素红的褪色反应,建立催化动力学光度法,对痕量NO_(2)^(-)进行测定.通过单因素实验得到了各种成分的加入量、反应温度和反应时间等最佳条件.结果发现,在反应体系中,茜素红浓度与NO_(2)^(-)含量之间线性关系良好,在0.02~0.14μg/mL范围内,线性回归方程为ln(A_(0)/A)=1.43 c NO_(3)^(-)(μg/mL)+0.00859,相关系数r^(2)为0.9970,检出限为5.25×10^(-3)μg/mL.该方法操作简单、稳定性好.