Laser powder bed fusion(LPBF)is an advanced manufacturing technology;however,inappropriate LPBF process parameters may cause printing defects in materials.In the present work,the LPBF process of Ti-6.5Al-3.5Mo-1.5Zr-0...Laser powder bed fusion(LPBF)is an advanced manufacturing technology;however,inappropriate LPBF process parameters may cause printing defects in materials.In the present work,the LPBF process of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy was investigated by a two-step optimization approach.Subsequently,heat transfer and liquid flow behaviors during LPBF were simulated by a well-tested phenomenological model,and the defect formation mechanisms in the as-fabricated alloy were discussed.The optimized process parameters for LPBF were detected as laser power changed from 195 W to 210 W,with scanning speed of 1250 mm/s.The LPBF process was divided into a laser irradiation stage,a spreading flow stage,and a solidification stage.The morphologies and defects of deposited tracks were affected by liquid flow behavior caused by rapid cooling rates.The findings of this research can provide valuable support for printing defect-free metal components.展开更多
基金Supported by Development of a Verification Platform for Product Design,Process and Information Exchange Standards in Additive Manufacturing (Grant No.2019-00899-1-1)Ministry of Science and Technology of the People’s Republic of China (Grant No.2017YFB1103000)+1 种基金National Natural Science Foundation of China (Grant No.51375242)Natural Science Foundation of Jiangsu Province (Grant No.BK20180483)。
文摘Laser powder bed fusion(LPBF)is an advanced manufacturing technology;however,inappropriate LPBF process parameters may cause printing defects in materials.In the present work,the LPBF process of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy was investigated by a two-step optimization approach.Subsequently,heat transfer and liquid flow behaviors during LPBF were simulated by a well-tested phenomenological model,and the defect formation mechanisms in the as-fabricated alloy were discussed.The optimized process parameters for LPBF were detected as laser power changed from 195 W to 210 W,with scanning speed of 1250 mm/s.The LPBF process was divided into a laser irradiation stage,a spreading flow stage,and a solidification stage.The morphologies and defects of deposited tracks were affected by liquid flow behavior caused by rapid cooling rates.The findings of this research can provide valuable support for printing defect-free metal components.