To clarify the effect of SnO2 particle size on the arc erosion behavior of AgSnO2 contact material, Ag?4%SnO2 (mass fraction) contact materials with different sizes of SnO2 particles were fabricated by powder metallur...To clarify the effect of SnO2 particle size on the arc erosion behavior of AgSnO2 contact material, Ag?4%SnO2 (mass fraction) contact materials with different sizes of SnO2 particles were fabricated by powder metallurgy. The microstructure of Ag?4%SnO2 contact materials was characterized, and the relative density, hardness and electrical conductivity were measured. The arc erosion of Ag?4%SnO2 contact materials was tested, the arc duration and mass loss before and after arc erosion were determined, the surface morphologies and compositions of Ag?4%SnO2 contact materials after arc erosion were characterized, and the arc erosion mechanism of AgSnO2 contact materials was discussed. The results show that fine SnO2 particle is beneficial for the improvement of the relative density and hardness, but decreases the electrical conductivity. With the decrease of SnO2 particle size, Ag?4%SnO2contact material presents shorter arc duration, less mass loss, larger erosion area and shallower arc erosion pits.展开更多
Arc erosion morphologies of Ag/MeO（10） electrical contact materials after 50000 operations under direct current of 19 V and 20 A and resistive load conditions were investigated using scanning electron microscope（SE...Arc erosion morphologies of Ag/MeO（10） electrical contact materials after 50000 operations under direct current of 19 V and 20 A and resistive load conditions were investigated using scanning electron microscope（SEM） and a 3D optical profiler（3DOP）. The results indicated that 3DOP could supply clearer and more detailed arc erosion morphology information. Arc erosion resistance of Ag/SnO_2（10） electrical contact material was the best and that of Ag/CuO（10） was the worst. Arc erosion morphology of Ag/MeO（10） electrical contact materials mainly included three different types. Arc erosion morphologies of Ag/ZnO（10） and Ag/SnO_2（10） electrical contact materials were mainly liquid splash and evaporation, and those of Ag/CuO（10） and Ag/CdO（10） were mainly material transfer from anode to cathode. Arc erosion morphology of Ag/SnO_2（6）In_2O_3（4） electrical contact materials included both liquid splash, evaporation and material transfer. In addition, the formation process and mechanism on arc erosion morphology of Ag/MeO（10） electrical contact materials were discussed.展开更多
According to the principle that fiber-like arrangement of reinforcing particles SnO2 paralleling to the direction of current is propitious to the electrical and mechanical performance of the electrical contact materia...According to the principle that fiber-like arrangement of reinforcing particles SnO2 paralleling to the direction of current is propitious to the electrical and mechanical performance of the electrical contact materials, we proposed and reported a novel precursor route used to prepare Ag/SnO,. electrical contact material with fiber- like arrangement of reinforcing nanoparticles. The mechanism for the formation of fiber-like arrangement of rein- forcing nanoparticles in Ag/SnO2 electrical contact material was also discussed. The as-prepared samples were char- acterized by means of scanning electron microscope （SEM）, optical microscope （OM）, energy-dispersive X-ray spectroscopy （EDX）, MHV2000 microhardness test, and double bridge tester. The analysis showed that the as-prepared Ag/SnO,, electrical contact material with fiber-like arrangement of reinforcing nanoparticles exhibits a high elongation of 24 %, a particularly low electrical resistivity of 2.08 μΩ. cm, and low arcing energy, and thus has considerable technical, economical and environmental benefits.展开更多
Arc erosion behavior of Ag/Ni materials with different operation numbers was investigated by OM,3DOP and SEM.The results indicated that the arc erosion of Ag/10Ni electrical contact material fabricated by sintering−ex...Arc erosion behavior of Ag/Ni materials with different operation numbers was investigated by OM,3DOP and SEM.The results indicated that the arc erosion of Ag/10Ni electrical contact material fabricated by sintering−extrusion technology was more and more serious with the operation numbers increasing from 1000 to 40000.With the same operation numbers,the arc erosion on anode was more serious than that on cathode.Besides,the pores preferred to emerge around the arc effect spot during the first 10000 operations.And the morphology of the molten silver on cathode and anode was different due to the action of gravity and arc erosion.Furthermore,the relationships among arc energy,arc time,welding force,electric resistivity,temperature and mass change on contacts were discussed,which indicated that the mass loss on cathode was mainly caused by the fracture of molten bridge.展开更多
CNTs-Ag-G electrical contact composite material was prepared by means of powder metallurgical method. The influence of the graphite content on sliding wear characteristics of electrical contact levels was examined. In...CNTs-Ag-G electrical contact composite material was prepared by means of powder metallurgical method. The influence of the graphite content on sliding wear characteristics of electrical contact levels was examined. In experiments, CNTs content was retained as 1% (mass fraction), and graphite was added at content levels of 8%, 10%, 13%, 15% and 18%, respectively. The results indicate that with the increase of graphite content, the contact resistance of electrical contacts is enhanced to a certain level then remains constant. Friction coefficient decreases gradually with the increase of graphite content. Wear mass loss decreases to the minimum value then increases. With the small content of graphite, the adhesive wear is hindered, which leads to the decrease of wear mass loss, while excessive graphite brings much more worn debris, resulting in the increase of mass loss. It is concluded that wear mass loss reaches the minimum value when the graphite mass fraction is about 13%. Compared with conventional Ag-G contact material, the wear mass loss of CNTs-Ag-G composite is much less due to the obvious increase of hardness and electrical conductivity, decline of friction surface temperature and inhibition of adhesive wear between composites and slip rings.展开更多
Because of the different ways in which contact materials work, the basic requirements for silver metal oxide contact materials are different. They are anti-welded and anti-erosion when closed, anti-erosion when broken...Because of the different ways in which contact materials work, the basic requirements for silver metal oxide contact materials are different. They are anti-welded and anti-erosion when closed, anti-erosion when broken, and arc easily moved and have smaller contact resistance. In this paper, La2O3 is used as a stable oxide in contact material to replace CdO. A new type of Ag/SnO2-La2O3-Bi2O3 contact material is first obtained through using powder metallurgical method. Then electrical contact material parameter tester is used to test the electrical contact performance of the contact material. Through experiments, the arcing voltage and current curves, arcing energy curves, fusion power curves while broken and contact resistance while closed were obtained. Analysis of the results showed that the addition of La2O3 makes the contact material have the following advantages: smaller electrical wear, smaller arc energy, smaller contact resistance and arc is more easily extinguished.展开更多
基金Project(51274163)supported by the National Natural Science Foundation of ChinaProject(13JS076)supported by the Key Laboratory Research Program of Shaanxi Province,China+1 种基金Project(2012KCT-25)supported by the Pivot Innovation Team of Shaanxi Electrical Materials and Infiltration Technique,ChinaProject(2011HBSZS009)supported by the Special Foundation of Key Disciplines,China
文摘To clarify the effect of SnO2 particle size on the arc erosion behavior of AgSnO2 contact material, Ag?4%SnO2 (mass fraction) contact materials with different sizes of SnO2 particles were fabricated by powder metallurgy. The microstructure of Ag?4%SnO2 contact materials was characterized, and the relative density, hardness and electrical conductivity were measured. The arc erosion of Ag?4%SnO2 contact materials was tested, the arc duration and mass loss before and after arc erosion were determined, the surface morphologies and compositions of Ag?4%SnO2 contact materials after arc erosion were characterized, and the arc erosion mechanism of AgSnO2 contact materials was discussed. The results show that fine SnO2 particle is beneficial for the improvement of the relative density and hardness, but decreases the electrical conductivity. With the decrease of SnO2 particle size, Ag?4%SnO2contact material presents shorter arc duration, less mass loss, larger erosion area and shallower arc erosion pits.
基金Project(2012QNZT003)supported by the Fundamental Research Funds for the Central Universities,ChinaProject(2012M521542)supported by the Postdoctoral Science Foundation of China+1 种基金Project(14JJ3014)supported by the Hunan Provincial Natural Science Foundation of ChinaProject(BSh1202)supported by the Zhejiang Provincial Postdoctoral Scientific Research Foundation of China
文摘Arc erosion morphologies of Ag/MeO（10） electrical contact materials after 50000 operations under direct current of 19 V and 20 A and resistive load conditions were investigated using scanning electron microscope（SEM） and a 3D optical profiler（3DOP）. The results indicated that 3DOP could supply clearer and more detailed arc erosion morphology information. Arc erosion resistance of Ag/SnO_2（10） electrical contact material was the best and that of Ag/CuO（10） was the worst. Arc erosion morphology of Ag/MeO（10） electrical contact materials mainly included three different types. Arc erosion morphologies of Ag/ZnO（10） and Ag/SnO_2（10） electrical contact materials were mainly liquid splash and evaporation, and those of Ag/CuO（10） and Ag/CdO（10） were mainly material transfer from anode to cathode. Arc erosion morphology of Ag/SnO_2（6）In_2O_3（4） electrical contact materials included both liquid splash, evaporation and material transfer. In addition, the formation process and mechanism on arc erosion morphology of Ag/MeO（10） electrical contact materials were discussed.
基金National Major Scientific&Technological Achievement Transformation Project
文摘According to the principle that fiber-like arrangement of reinforcing particles SnO2 paralleling to the direction of current is propitious to the electrical and mechanical performance of the electrical contact materials, we proposed and reported a novel precursor route used to prepare Ag/SnO,. electrical contact material with fiber- like arrangement of reinforcing nanoparticles. The mechanism for the formation of fiber-like arrangement of rein- forcing nanoparticles in Ag/SnO2 electrical contact material was also discussed. The as-prepared samples were char- acterized by means of scanning electron microscope （SEM）, optical microscope （OM）, energy-dispersive X-ray spectroscopy （EDX）, MHV2000 microhardness test, and double bridge tester. The analysis showed that the as-prepared Ag/SnO,, electrical contact material with fiber-like arrangement of reinforcing nanoparticles exhibits a high elongation of 24 %, a particularly low electrical resistivity of 2.08 μΩ. cm, and low arcing energy, and thus has considerable technical, economical and environmental benefits.
基金supported by the National Natural Science Foundation of China (No.51601225)Hunan Provincial Natural Science Foundation,China (No.2020JJ5742)。
文摘Arc erosion behavior of Ag/Ni materials with different operation numbers was investigated by OM,3DOP and SEM.The results indicated that the arc erosion of Ag/10Ni electrical contact material fabricated by sintering−extrusion technology was more and more serious with the operation numbers increasing from 1000 to 40000.With the same operation numbers,the arc erosion on anode was more serious than that on cathode.Besides,the pores preferred to emerge around the arc effect spot during the first 10000 operations.And the morphology of the molten silver on cathode and anode was different due to the action of gravity and arc erosion.Furthermore,the relationships among arc energy,arc time,welding force,electric resistivity,temperature and mass change on contacts were discussed,which indicated that the mass loss on cathode was mainly caused by the fracture of molten bridge.
基金Project(50271021) supported by the National Natural Science Foundation of ChinaProject(ZD2008003) supported by Key Science Foundation of the Education Department of Anhui Province, China+2 种基金Project(CF07-10) supported by the Innovation Center for Postgraduates at HFNL (USTC), ChinaProject(KF0702) supported by the Open Project Program of Ministry of Education of ChinaProject supported by Nippon Sheet Glass Foundation of Japan for Materials Science and Engineering
文摘CNTs-Ag-G electrical contact composite material was prepared by means of powder metallurgical method. The influence of the graphite content on sliding wear characteristics of electrical contact levels was examined. In experiments, CNTs content was retained as 1% (mass fraction), and graphite was added at content levels of 8%, 10%, 13%, 15% and 18%, respectively. The results indicate that with the increase of graphite content, the contact resistance of electrical contacts is enhanced to a certain level then remains constant. Friction coefficient decreases gradually with the increase of graphite content. Wear mass loss decreases to the minimum value then increases. With the small content of graphite, the adhesive wear is hindered, which leads to the decrease of wear mass loss, while excessive graphite brings much more worn debris, resulting in the increase of mass loss. It is concluded that wear mass loss reaches the minimum value when the graphite mass fraction is about 13%. Compared with conventional Ag-G contact material, the wear mass loss of CNTs-Ag-G composite is much less due to the obvious increase of hardness and electrical conductivity, decline of friction surface temperature and inhibition of adhesive wear between composites and slip rings.
基金Project (No. 502048) supported by the Natural Science Foundation of Hebei Province, China
文摘Because of the different ways in which contact materials work, the basic requirements for silver metal oxide contact materials are different. They are anti-welded and anti-erosion when closed, anti-erosion when broken, and arc easily moved and have smaller contact resistance. In this paper, La2O3 is used as a stable oxide in contact material to replace CdO. A new type of Ag/SnO2-La2O3-Bi2O3 contact material is first obtained through using powder metallurgical method. Then electrical contact material parameter tester is used to test the electrical contact performance of the contact material. Through experiments, the arcing voltage and current curves, arcing energy curves, fusion power curves while broken and contact resistance while closed were obtained. Analysis of the results showed that the addition of La2O3 makes the contact material have the following advantages: smaller electrical wear, smaller arc energy, smaller contact resistance and arc is more easily extinguished.