The liquidus of the ternary Ag-Cd-Si alloy system in the Ag-Cu rich region was determined by DTA. The ternary Ag-Cd-Si system was divided into two ternary systems Ag-Cu-Cuo.76Si0.24 and Ag-Cu0.76Si0.24-Si by the sec...The liquidus of the ternary Ag-Cd-Si alloy system in the Ag-Cu rich region was determined by DTA. The ternary Ag-Cd-Si system was divided into two ternary systems Ag-Cu-Cuo.76Si0.24 and Ag-Cu0.76Si0.24-Si by the section of Ag-Cu0.76 Si0.24.There is one ternary eutectic point for both the systems with the composition of 12. 5at. %Ag+71. 7at.%Cu+15.8at. %Si and 30at.% Ag+44.7at.%Cu+25.3at.%Sirespectivelg and the temperatures of the eutectic points are 740 and 705℃ respectively.展开更多
The liquidus of ternary system NdCl_3-MgCl_2-LiCl has been determined by means of DTA.It was found that there are two surfaces corresponding to the primary crystallization of NdCl_3 and α-(MgCl_2,LiCl)respectively,an...The liquidus of ternary system NdCl_3-MgCl_2-LiCl has been determined by means of DTA.It was found that there are two surfaces corresponding to the primary crystallization of NdCl_3 and α-(MgCl_2,LiCl)respectively,and a univariant line related to the secondary crystallization with a minimum M(68.5 wt-% NdCl_3,2.7 wt-% MgCl_2,28.8 wt-% LiCl_2 441℃)in the system.展开更多
The diagram of Ag-Cu-Bi system was constructed from the investigation of 12 internal sec- tions by DTA heating as well as cooling curves in an atmosphere of dry N_2.The composi- tion of ternary eutectic point melting ...The diagram of Ag-Cu-Bi system was constructed from the investigation of 12 internal sec- tions by DTA heating as well as cooling curves in an atmosphere of dry N_2.The composi- tion of ternary eutectic point melting at 258℃ lies in Ag(5.0)-Cu(0.5)-Bi(94.5) at.-%.The liquiduses of Ag-Cu,Ag-Bi and Cu-Bi binaries were reinvestigated.展开更多
Abstract The as-cast microstructures and solidification paths of the Nb-Si-Ti ternary alloys in the NbsSi3-TisSi3 region were investigated. Since there exist some isomor- phous compounds in the NbsSi3-TisSi3 region, s...Abstract The as-cast microstructures and solidification paths of the Nb-Si-Ti ternary alloys in the NbsSi3-TisSi3 region were investigated. Since there exist some isomor- phous compounds in the NbsSi3-TisSi3 region, such as aNbsSi3 with B3Cr5 prototype, 13NbsSi3 with Si3W5 pro- totype, 7NbsSi3 with MnsSi3 prototype, and TisSi3 with MnsSi3 prototype, the primary solidification areas of these compounds were not typically indentified in previous experiments. In the present paper, the microstructure observation, the phase identification, and the composition measurement were performed using scanning electron microscopy （SEM）, X-ray diffraction （XRD）, and electron probe microanalysis （EPMA）, respectively. No ternary compound is found. There exist three primary solidification areas, 13Nbs_x（Ti）xSi3, ~Nbs_x（Ti）xSi3, and Tis-x（Nb）xSi3 in the NbsSi3-TisSi3 region. Together with the literaturereported experimental data and optimization results, the liquidus projection of the whole Nb-Si-Ti ternary system is constructed, and totally ten primary solidification areas-- diamond-Si, Nb1-x（Ti）xSi2, Ti1-x（Nb）xSi2, Ti1-x（Nb）xSi, Ti5-x（Nb）xSi4, βNb5-x（Ti）xSi3,αNb5-x（Ti）xSi3, Ti5-x （Nb）xSi3, （Nb,Ti）3Si, and BCC--and nine transitional invariant reactions-L ＋ Nb1-x（Ti）xSi2 → Ti1-x（Nb）x Si2 ＋ Si, L ＋ Nb1-x（Ti）xSi2 → Ti1-x（Nb）xSi2 ＋ Ti5- （Nb）xSi4, L ＋ Ti5-x（Nb）xSi4 → Ti1-x（Nb）xSi2 ＋ Ti1-x （Nb）xSi, L ＋ 13Nb5-x（Ti）5Si3→ Nb1-x（Ti）xSi2 ＋ Ti5-x （Nb）xSi4, L ＋ βNb5-x（Ti）xSi3→b5-x（Ti）xSi3 ＋Ti5-x （Nb）xSi4, L ＋ αNb5-x（Ti）αSi3 → Ti5-x（Nb）xSi3 ＋ Ti5-x（Nb）x Si4, L ＋ αNb5-x（Ti）xSi3 →βNb5-x（Ti）xSi3 ＋ Ti5-x（Nb）xSi3, L ＋ βNb5-xTb-xSi3 → Ti5-x（Nb）xSi3 ＋ （Nb,Ti）3Si, and L ＋ （Nb,Ti）3Si → Ti5-x（Nb）xSi3 ＋ BCC are confirmed.展开更多
Nine limiting binaries of Al 2O 3 SiO 2 Re 2O 3 (Re=Nd,Sm,Gd and La) system are assessed. The binary diagrams or experimental information from Toropov, Mizuno, Aramaki, Bondar, Rolin and Coutures are optimized ...Nine limiting binaries of Al 2O 3 SiO 2 Re 2O 3 (Re=Nd,Sm,Gd and La) system are assessed. The binary diagrams or experimental information from Toropov, Mizuno, Aramaki, Bondar, Rolin and Coutures are optimized with the substitutional model of Kaufman and Nesor and the approximate formula of fusion free energy for rare earth element oxides of Wu and Pelton. The extracted Gibbs free energies of pure solid oxides and stoichiometric phases and the solution parameters are used to estimate the corresponding binaries, liquidus surfaces and a series of isothermal sections of four ternaries Al 2O 3 SiO 2 Nd 2O 3, Al 2O 3 SiO 2 Sm 2O 3, Al 2O 3 SiO 2 Gd 2O 3, and Al 2O 3 SiO 2 La 2O 3. In the Al 2O 3 SiO 2 Gd 2O 3 system samples as fired at exact temperature with different compositions were analyzed by X ray diffractometer and the detected results are fitted with the calculation of isothermal sections.展开更多
文摘The liquidus of the ternary Ag-Cd-Si alloy system in the Ag-Cu rich region was determined by DTA. The ternary Ag-Cd-Si system was divided into two ternary systems Ag-Cu-Cuo.76Si0.24 and Ag-Cu0.76Si0.24-Si by the section of Ag-Cu0.76 Si0.24.There is one ternary eutectic point for both the systems with the composition of 12. 5at. %Ag+71. 7at.%Cu+15.8at. %Si and 30at.% Ag+44.7at.%Cu+25.3at.%Sirespectivelg and the temperatures of the eutectic points are 740 and 705℃ respectively.
文摘The liquidus of ternary system NdCl_3-MgCl_2-LiCl has been determined by means of DTA.It was found that there are two surfaces corresponding to the primary crystallization of NdCl_3 and α-(MgCl_2,LiCl)respectively,and a univariant line related to the secondary crystallization with a minimum M(68.5 wt-% NdCl_3,2.7 wt-% MgCl_2,28.8 wt-% LiCl_2 441℃)in the system.
文摘The diagram of Ag-Cu-Bi system was constructed from the investigation of 12 internal sec- tions by DTA heating as well as cooling curves in an atmosphere of dry N_2.The composi- tion of ternary eutectic point melting at 258℃ lies in Ag(5.0)-Cu(0.5)-Bi(94.5) at.-%.The liquiduses of Ag-Cu,Ag-Bi and Cu-Bi binaries were reinvestigated.
基金supported by the National Natural Science Foundation of China (No. 51271027)the National High Technology Research and Development Program of China (No. 2013AA031601)
文摘Abstract The as-cast microstructures and solidification paths of the Nb-Si-Ti ternary alloys in the NbsSi3-TisSi3 region were investigated. Since there exist some isomor- phous compounds in the NbsSi3-TisSi3 region, such as aNbsSi3 with B3Cr5 prototype, 13NbsSi3 with Si3W5 pro- totype, 7NbsSi3 with MnsSi3 prototype, and TisSi3 with MnsSi3 prototype, the primary solidification areas of these compounds were not typically indentified in previous experiments. In the present paper, the microstructure observation, the phase identification, and the composition measurement were performed using scanning electron microscopy （SEM）, X-ray diffraction （XRD）, and electron probe microanalysis （EPMA）, respectively. No ternary compound is found. There exist three primary solidification areas, 13Nbs_x（Ti）xSi3, ~Nbs_x（Ti）xSi3, and Tis-x（Nb）xSi3 in the NbsSi3-TisSi3 region. Together with the literaturereported experimental data and optimization results, the liquidus projection of the whole Nb-Si-Ti ternary system is constructed, and totally ten primary solidification areas-- diamond-Si, Nb1-x（Ti）xSi2, Ti1-x（Nb）xSi2, Ti1-x（Nb）xSi, Ti5-x（Nb）xSi4, βNb5-x（Ti）xSi3,αNb5-x（Ti）xSi3, Ti5-x （Nb）xSi3, （Nb,Ti）3Si, and BCC--and nine transitional invariant reactions-L ＋ Nb1-x（Ti）xSi2 → Ti1-x（Nb）x Si2 ＋ Si, L ＋ Nb1-x（Ti）xSi2 → Ti1-x（Nb）xSi2 ＋ Ti5- （Nb）xSi4, L ＋ Ti5-x（Nb）xSi4 → Ti1-x（Nb）xSi2 ＋ Ti1-x （Nb）xSi, L ＋ 13Nb5-x（Ti）5Si3→ Nb1-x（Ti）xSi2 ＋ Ti5-x （Nb）xSi4, L ＋ βNb5-x（Ti）xSi3→b5-x（Ti）xSi3 ＋Ti5-x （Nb）xSi4, L ＋ αNb5-x（Ti）αSi3 → Ti5-x（Nb）xSi3 ＋ Ti5-x（Nb）x Si4, L ＋ αNb5-x（Ti）xSi3 →βNb5-x（Ti）xSi3 ＋ Ti5-x（Nb）xSi3, L ＋ βNb5-xTb-xSi3 → Ti5-x（Nb）xSi3 ＋ （Nb,Ti）3Si, and L ＋ （Nb,Ti）3Si → Ti5-x（Nb）xSi3 ＋ BCC are confirmed.
文摘Nine limiting binaries of Al 2O 3 SiO 2 Re 2O 3 (Re=Nd,Sm,Gd and La) system are assessed. The binary diagrams or experimental information from Toropov, Mizuno, Aramaki, Bondar, Rolin and Coutures are optimized with the substitutional model of Kaufman and Nesor and the approximate formula of fusion free energy for rare earth element oxides of Wu and Pelton. The extracted Gibbs free energies of pure solid oxides and stoichiometric phases and the solution parameters are used to estimate the corresponding binaries, liquidus surfaces and a series of isothermal sections of four ternaries Al 2O 3 SiO 2 Nd 2O 3, Al 2O 3 SiO 2 Sm 2O 3, Al 2O 3 SiO 2 Gd 2O 3, and Al 2O 3 SiO 2 La 2O 3. In the Al 2O 3 SiO 2 Gd 2O 3 system samples as fired at exact temperature with different compositions were analyzed by X ray diffractometer and the detected results are fitted with the calculation of isothermal sections.