Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that th...Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that the weld appearance can be effectively improved when using laser welding with filler wire. The microhardness and tensile strength of joints are almost the same us those of the base metal when ER AZ31 or ER AZ61 wire is adopted. However, when the filler wire of ER 5356 aluminum alloy is used, the mechanical properties of flints become worse. For ER AZ31 and ER AZ61 filler wires, the microstructure of weld zone slws small dendrite grains. In comparison, for ER 5356 filler wire, the weld shows a structure of snowy dendrites and many intermetallic compounds and eutectic phases distribute in the dendrites. These intermetallic constituents with low melting point increase the tendency of hot crack and result in fiagile joint properties. Therefore, ER AZ31 and ER AZ61 wire are more suitable filler material than ER 5356 for CO2 laser welding of AZ31 magnesium alloys.展开更多
Effect of cerium on microstructure,mechanical and wetting properties of Ag-Cu-Ti filler alloy was researched with optical microscopy,scanning electron microscopy and X-ray diffraction.The results indicated that additi...Effect of cerium on microstructure,mechanical and wetting properties of Ag-Cu-Ti filler alloy was researched with optical microscopy,scanning electron microscopy and X-ray diffraction.The results indicated that addition of cerium accelerated alloying of the filler alloy,enlarged supercooled region,caused microstructural refinement and dispersed distribution of intermetallic compounds.It resulted in the increase in microhardness and shear strength of Ag-Cu-Ti filler alloy.At the same time,cerium improved wet...展开更多
The effects of the addition of rare earths on the properties of Ti-Zr-Cu-Ni base brazing filler alloys and the mechanical microstructure and properties were studied for the brazed-joints in the vacuum brazing of TC4 b...The effects of the addition of rare earths on the properties of Ti-Zr-Cu-Ni base brazing filler alloys and the mechanical microstructure and properties were studied for the brazed-joints in the vacuum brazing of TC4 by comparing synthetical properties of two kinds of filler metals.The results indicate that the filler metals added with rare earths have lower melting point, better wettability and higher mechanical properties in the brazing joints.展开更多
It＇ s well known welding takes the leading role in development of titanium structures. However, in number of cases technological processes of brazing are more appropriate and, sometimes, being the single possible, in...It＇ s well known welding takes the leading role in development of titanium structures. However, in number of cases technological processes of brazing are more appropriate and, sometimes, being the single possible, in particular, during production of multilayer thin-wall structures. It should be noted that brazing filler metals of Ti-Cu-Ni, Ti-Zr-Cu-Ni, Zr-Ti-Ni and Cu-Zr-Ti systems in a form of plastic foils, as well as in powder form are mainly used in world practice for brazing of titanium alloys. Present work provides the results of complex investigations of brazing filler metals of Ti-Zr-Fe, Ti-Zr-Mn and Ti-Zr-Co systems using differential thermal analysis, light and scanning microscopy, X-ray microspectrum analysis. Data on melting ranges of pilot alloys were obtained, and liquidas su^Caces of given systems using simplex-lattice method were build. Brazing filler metals covering brazing temperature range of current structural titanium materials based on solid solutions as well as intermetallics were proposed. Structure, chemical inhomogeniety and strength characteristics of brazed joints were studied. It is determined that brazing of solid solution based alloys （OT4, VT6 ） using indicated brazing fiUer metals ensures strength characteristics of joints, which are not inferior to that obtained with application of known brazing filler metals even if they are received at lower brazing temperature.展开更多
A high Fe containing aluminum matrix filler metal for hardfacing aluminum silicon alloys has been developed by using iron,nickel,and silicon as the major strengthening elements,and by measuring mechanical properties...A high Fe containing aluminum matrix filler metal for hardfacing aluminum silicon alloys has been developed by using iron,nickel,and silicon as the major strengthening elements,and by measuring mechanical properties,room temperature and high temperature wear tests,and microstructural analysis.The filler metal,which contains 3.0%-5.0% Fe and 11.0%-13.0% Si,exhibits an excellent weldability.The as cast and as welded microstructures for the filler metal are of uniformly distribution and its dispersed network of hard phase is enriched with Al Si Fe Ni.The filler metal shows high mechanical properties and wear resistance at both room temperature and high temperatures.The deposited metal has a better resistance to impact wear at 220℃ than that of substrate Al Si Mg Cu piston alloy;at room temperature,the deposited metal has an equivalent resistance to slide wear with lubrication as that of a hyper eutectic aluminum silicon alloy with 27% Si and 1% Ni.展开更多
Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Fi...Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Filler metals were titanium based 40Ti-20Zr-20Cu-20Ni,silver based Ag 5Pd,and nickel based Ni-7Cr-3.1B-4.5Si-3Fe-0.06C (BNi2) and Ni-14Cr-10P-0.06C (BNi7).To select a good filler metal for brazing process,wetting test was performed at 880-1050 °C.It was not brazed using silver based filler metals,but at the conditions using titanium and nickel based filler metals had brazed zone between titanium alloy and stainless steel.However,titanium alloy was eroded during brazing using titanium based filler metals.Nickel based filler metal has a good brazed zone between titanium alloy and stainless steel among the filler metals.展开更多
Al-6.5Si-42Zn and Al-6.5Si-42Zn-0.09Sr filler metals were used for brazing 6061 aluminum alloy. Air cooling and water cooling were applied after brazing. Si phase morphologies in the brazing alloy and the brazed joint...Al-6.5Si-42Zn and Al-6.5Si-42Zn-0.09Sr filler metals were used for brazing 6061 aluminum alloy. Air cooling and water cooling were applied after brazing. Si phase morphologies in the brazing alloy and the brazed joints were investigated. It was found that zinc in the Al-Si filler metals could reduce the formation of eutectic Al-Si phase and lower the brazing temperature at about 520℃. Adding 0.09wt% Sr element into the Al-6.5Si-42Zn alloy caused a-Al phase refinement and transformed acicular Si phase into the finely fiber-like. After water cooling, Zn element dissolved into the Al-Si eutectic area, and η-Zn phase disappeared in the brazed joints. Tensile strength testing results showed that the Sr-modified filler metal could enhance the strength of the brazed joints by 13% than Al-12Si, while water-cooling further improved the strength at 144 MPa.展开更多
Cerium and titanium were added to an A1-42Zn-5.5Si brazing alloy, and the subsequent microstructures of the brazing alloy and the 6061 AI alloy brazing seam were investigated. The microstructures of filler metals and ...Cerium and titanium were added to an A1-42Zn-5.5Si brazing alloy, and the subsequent microstructures of the brazing alloy and the 6061 AI alloy brazing seam were investigated. The microstructures of filler metals and brazed joints were characterized by scanning elec- tron microscopy and X-ray energy dispersion spectrometry. A new Ce-Ti phase formed around the silicon phase in the modified filler metal and this saturation phenomenon was analyzed. Interestingly, following brazing of the 6061 alloy, there is no evidence of the Ce--Ti phase in the brazing seam. Because of the mutual solubility of the brazing alloy and base metal, the quantity of the solvent increases, and the solute Ce and Ti atoms assume an undersaturated state.展开更多
The effects of Cu, Si, Ni and RE elements （ RE = La and Ce ） on the melting temperature of AI-Si filler metals were studied by orthogonal design method. The wettability of the filler metals and the shear strength of...The effects of Cu, Si, Ni and RE elements （ RE = La and Ce ） on the melting temperature of AI-Si filler metals were studied by orthogonal design method. The wettability of the filler metals and the shear strength of 6063 aluminum alloy joints brazed with the different filler metals were measured. The results show that the copper doping content has the most obvious effect on liquidas temperature （ TL ） of the Al-Si filler metals and the effect of RE content on TL is the least. Adding suitable Cu and Si can improve the wettability of the Al-Si filler metals. The shear strength of 6063 aluminum alloy joints brazed with the filler metals SIO, S15 and S20, respectively, is better than that of the joints brazed with HL401 due to the improvement of microstructure. It can improve the shear strength of the joints by brazing with the Ni- or RE-doped Al-Si-Cu filler metals.展开更多
Si/SiC ceramic composite and lnvar alloy were successfidly joined by vacuum brazing using Ti5OCu-W filler metals into which W was added to release the thermal stress of the brazed joint. Microstructures of the brazed ...Si/SiC ceramic composite and lnvar alloy were successfidly joined by vacuum brazing using Ti5OCu-W filler metals into which W was added to release the thermal stress of the brazed joint. Microstructures of the brazed joints were irwestigated by scanning electron micrascope （SEM） and energy dispersive spectrometer （EDS）. The mechanical properties of the brazed joints were measured by shearing tests. The results showed that the brazed joints were composed of Ti-Cu phase, W phase and Ti-Si phase. W had no effect on the wettability and mobility of the .filler metals. The growth of Ti2 Cu phase was restrained, and the reaction between ceramic composite and filler metals was weakened. The specimen, brazed at 970°C for 5 rain, had the maximum shear strength of 108 MPa at room temperature.展开更多
CO2 laser welding aluminum alloy with filler wire was studied. The results indicate that the problems in CO2 laser welding of Al alloy, such as bad appearance of weld, easily excessive penetration and low strength, ca...CO2 laser welding aluminum alloy with filler wire was studied. The results indicate that the problems in CO2 laser welding of Al alloy, such as bad appearance of weld, easily excessive penetration and low strength, can be improved effectively by using laser welding with filler wire, and the maximum tensile strength of weld can reach 94% for the base metal. It also can be found that, the linear energy have great influence on the microstructure and mechanical properties of the joint. As the heat input increases, the cellular fir-tree crystals in the weld zone become sparse and the form of tensile fracture transforms from gliding fracture to brittle fracture.展开更多
文摘Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that the weld appearance can be effectively improved when using laser welding with filler wire. The microhardness and tensile strength of joints are almost the same us those of the base metal when ER AZ31 or ER AZ61 wire is adopted. However, when the filler wire of ER 5356 aluminum alloy is used, the mechanical properties of flints become worse. For ER AZ31 and ER AZ61 filler wires, the microstructure of weld zone slws small dendrite grains. In comparison, for ER 5356 filler wire, the weld shows a structure of snowy dendrites and many intermetallic compounds and eutectic phases distribute in the dendrites. These intermetallic constituents with low melting point increase the tendency of hot crack and result in fiagile joint properties. Therefore, ER AZ31 and ER AZ61 wire are more suitable filler material than ER 5356 for CO2 laser welding of AZ31 magnesium alloys.
基金supported by Natural Basic Research Program of China (2009CB724403)Program for New Century Excellent Talents in University from Ministry of Education of China (NCET-07-0435)
文摘Effect of cerium on microstructure,mechanical and wetting properties of Ag-Cu-Ti filler alloy was researched with optical microscopy,scanning electron microscopy and X-ray diffraction.The results indicated that addition of cerium accelerated alloying of the filler alloy,enlarged supercooled region,caused microstructural refinement and dispersed distribution of intermetallic compounds.It resulted in the increase in microhardness and shear strength of Ag-Cu-Ti filler alloy.At the same time,cerium improved wet...
文摘The effects of the addition of rare earths on the properties of Ti-Zr-Cu-Ni base brazing filler alloys and the mechanical microstructure and properties were studied for the brazed-joints in the vacuum brazing of TC4 by comparing synthetical properties of two kinds of filler metals.The results indicate that the filler metals added with rare earths have lower melting point, better wettability and higher mechanical properties in the brazing joints.
文摘It＇ s well known welding takes the leading role in development of titanium structures. However, in number of cases technological processes of brazing are more appropriate and, sometimes, being the single possible, in particular, during production of multilayer thin-wall structures. It should be noted that brazing filler metals of Ti-Cu-Ni, Ti-Zr-Cu-Ni, Zr-Ti-Ni and Cu-Zr-Ti systems in a form of plastic foils, as well as in powder form are mainly used in world practice for brazing of titanium alloys. Present work provides the results of complex investigations of brazing filler metals of Ti-Zr-Fe, Ti-Zr-Mn and Ti-Zr-Co systems using differential thermal analysis, light and scanning microscopy, X-ray microspectrum analysis. Data on melting ranges of pilot alloys were obtained, and liquidas su^Caces of given systems using simplex-lattice method were build. Brazing filler metals covering brazing temperature range of current structural titanium materials based on solid solutions as well as intermetallics were proposed. Structure, chemical inhomogeniety and strength characteristics of brazed joints were studied. It is determined that brazing of solid solution based alloys （OT4, VT6 ） using indicated brazing fiUer metals ensures strength characteristics of joints, which are not inferior to that obtained with application of known brazing filler metals even if they are received at lower brazing temperature.
文摘A high Fe containing aluminum matrix filler metal for hardfacing aluminum silicon alloys has been developed by using iron,nickel,and silicon as the major strengthening elements,and by measuring mechanical properties,room temperature and high temperature wear tests,and microstructural analysis.The filler metal,which contains 3.0%-5.0% Fe and 11.0%-13.0% Si,exhibits an excellent weldability.The as cast and as welded microstructures for the filler metal are of uniformly distribution and its dispersed network of hard phase is enriched with Al Si Fe Ni.The filler metal shows high mechanical properties and wear resistance at both room temperature and high temperatures.The deposited metal has a better resistance to impact wear at 220℃ than that of substrate Al Si Mg Cu piston alloy;at room temperature,the deposited metal has an equivalent resistance to slide wear with lubrication as that of a hyper eutectic aluminum silicon alloy with 27% Si and 1% Ni.
文摘Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Filler metals were titanium based 40Ti-20Zr-20Cu-20Ni,silver based Ag 5Pd,and nickel based Ni-7Cr-3.1B-4.5Si-3Fe-0.06C (BNi2) and Ni-14Cr-10P-0.06C (BNi7).To select a good filler metal for brazing process,wetting test was performed at 880-1050 °C.It was not brazed using silver based filler metals,but at the conditions using titanium and nickel based filler metals had brazed zone between titanium alloy and stainless steel.However,titanium alloy was eroded during brazing using titanium based filler metals.Nickel based filler metal has a good brazed zone between titanium alloy and stainless steel among the filler metals.
基金financially supported by the Foundation of Scientist and Technician Serving the Enterprise,the Ministry of Science and Technology of China (No.2009GJC20040)
文摘Al-6.5Si-42Zn and Al-6.5Si-42Zn-0.09Sr filler metals were used for brazing 6061 aluminum alloy. Air cooling and water cooling were applied after brazing. Si phase morphologies in the brazing alloy and the brazed joints were investigated. It was found that zinc in the Al-Si filler metals could reduce the formation of eutectic Al-Si phase and lower the brazing temperature at about 520℃. Adding 0.09wt% Sr element into the Al-6.5Si-42Zn alloy caused a-Al phase refinement and transformed acicular Si phase into the finely fiber-like. After water cooling, Zn element dissolved into the Al-Si eutectic area, and η-Zn phase disappeared in the brazed joints. Tensile strength testing results showed that the Sr-modified filler metal could enhance the strength of the brazed joints by 13% than Al-12Si, while water-cooling further improved the strength at 144 MPa.
基金financially supported by the National Natural Science Foundation of China(No.51375233)
文摘Cerium and titanium were added to an A1-42Zn-5.5Si brazing alloy, and the subsequent microstructures of the brazing alloy and the 6061 AI alloy brazing seam were investigated. The microstructures of filler metals and brazed joints were characterized by scanning elec- tron microscopy and X-ray energy dispersion spectrometry. A new Ce-Ti phase formed around the silicon phase in the modified filler metal and this saturation phenomenon was analyzed. Interestingly, following brazing of the 6061 alloy, there is no evidence of the Ce--Ti phase in the brazing seam. Because of the mutual solubility of the brazing alloy and base metal, the quantity of the solvent increases, and the solute Ce and Ti atoms assume an undersaturated state.
文摘The effects of Cu, Si, Ni and RE elements （ RE = La and Ce ） on the melting temperature of AI-Si filler metals were studied by orthogonal design method. The wettability of the filler metals and the shear strength of 6063 aluminum alloy joints brazed with the different filler metals were measured. The results show that the copper doping content has the most obvious effect on liquidas temperature （ TL ） of the Al-Si filler metals and the effect of RE content on TL is the least. Adding suitable Cu and Si can improve the wettability of the Al-Si filler metals. The shear strength of 6063 aluminum alloy joints brazed with the filler metals SIO, S15 and S20, respectively, is better than that of the joints brazed with HL401 due to the improvement of microstructure. It can improve the shear strength of the joints by brazing with the Ni- or RE-doped Al-Si-Cu filler metals.
文摘Si/SiC ceramic composite and lnvar alloy were successfidly joined by vacuum brazing using Ti5OCu-W filler metals into which W was added to release the thermal stress of the brazed joint. Microstructures of the brazed joints were irwestigated by scanning electron micrascope （SEM） and energy dispersive spectrometer （EDS）. The mechanical properties of the brazed joints were measured by shearing tests. The results showed that the brazed joints were composed of Ti-Cu phase, W phase and Ti-Si phase. W had no effect on the wettability and mobility of the .filler metals. The growth of Ti2 Cu phase was restrained, and the reaction between ceramic composite and filler metals was weakened. The specimen, brazed at 970°C for 5 rain, had the maximum shear strength of 108 MPa at room temperature.
文摘CO2 laser welding aluminum alloy with filler wire was studied. The results indicate that the problems in CO2 laser welding of Al alloy, such as bad appearance of weld, easily excessive penetration and low strength, can be improved effectively by using laser welding with filler wire, and the maximum tensile strength of weld can reach 94% for the base metal. It also can be found that, the linear energy have great influence on the microstructure and mechanical properties of the joint. As the heat input increases, the cellular fir-tree crystals in the weld zone become sparse and the form of tensile fracture transforms from gliding fracture to brittle fracture.