The objective of this research is to prepare specially designed surface texture on hard steel surface by electrochemical micromachining (EM) and to incorporate electroless plated Ag/MoS2 solid lubricant coating into t...The objective of this research is to prepare specially designed surface texture on hard steel surface by electrochemical micromachining (EM) and to incorporate electroless plated Ag/MoS2 solid lubricant coating into the dimples of EM textured steel surface to effectively reduce friction and wear of steel-steel contacts. The friction and wear behavior of the Ag/MoS2 solid lubricant coating on EM textured steel surface was evaluated in relation to the size and spacing of the dimples thereon. The microstructure of as-plated Ag/MoS2 solid lubricant coating and the morphology and elemental composition of the worn coating surface and counterface steel surface were analyzed by means of optical microscopy, scanning electron microscopy, and energy dispersive spectrometry. It is found that electroless plated Ag/MoS2 coating is able to greatly reduce the friction and wear of the EM textured steel disc coupled with GCr15 steel ring, mainly because of the formation of solid self-lubricating layer on the EM textured steel surface and of transferred lubricating film on counterface steel surface. The diameter and spacing of the dimples are suggested as 500 μm for acquiring the best wear resistance of the hard steel discs after electrochemical micromachining treatment and electroless plating of Ag/MoS2 solid lubricating coating.展开更多
Silver matrix composite brushes were fabricated by means of powder metallurgy, which included pressing at 300 MPa and then sintering for 1 h in pure H2 protective atmosphere at 700 ℃ and repressing at 500 MPa. Four k...Silver matrix composite brushes were fabricated by means of powder metallurgy, which included pressing at 300 MPa and then sintering for 1 h in pure H2 protective atmosphere at 700 ℃ and repressing at 500 MPa. Four kinds composites with different compositions were produced, and the mechanical properties and electrical wear performance were investigated. The results showed that the composite added with carbon nanotubes had a higher hardness and strength, a lower contact voltage drop and an excellent anti-wear property in electrical sliding wear, because of the reinforcement ability of carbon nanotubes. Adding graphite to the composite also decreased the wear loss and contact voltage drop, because graphite had an electrical current conducting ability which not only made the current pass the lubricating films easily but also eliminated and reduced the arc and spark effectively.展开更多
基金Supported by National Natural Science Foundation of China (50741003)Key Project of Science and Technology of Ministry of Education of China (107066)Anhui Provincial Natural Science Foundation (070414181)
基金supported by the the National NaturalScience Foundation of China(No.51205001)Foundation for Young Talents in College of Anhui Province(No.2012SQRL083ZD)the Talent Innovation Fund of An-hui Polytechnic University(No.S05305)
文摘The objective of this research is to prepare specially designed surface texture on hard steel surface by electrochemical micromachining (EM) and to incorporate electroless plated Ag/MoS2 solid lubricant coating into the dimples of EM textured steel surface to effectively reduce friction and wear of steel-steel contacts. The friction and wear behavior of the Ag/MoS2 solid lubricant coating on EM textured steel surface was evaluated in relation to the size and spacing of the dimples thereon. The microstructure of as-plated Ag/MoS2 solid lubricant coating and the morphology and elemental composition of the worn coating surface and counterface steel surface were analyzed by means of optical microscopy, scanning electron microscopy, and energy dispersive spectrometry. It is found that electroless plated Ag/MoS2 coating is able to greatly reduce the friction and wear of the EM textured steel disc coupled with GCr15 steel ring, mainly because of the formation of solid self-lubricating layer on the EM textured steel surface and of transferred lubricating film on counterface steel surface. The diameter and spacing of the dimples are suggested as 500 μm for acquiring the best wear resistance of the hard steel discs after electrochemical micromachining treatment and electroless plating of Ag/MoS2 solid lubricating coating.
基金supported by National Natural Science Foundation of China(No50741003)Key Project of Science and Technology of Ministry of Education of China (No107066)Anhui Provincial Natural Science Foundation(No070414181)
文摘Silver matrix composite brushes were fabricated by means of powder metallurgy, which included pressing at 300 MPa and then sintering for 1 h in pure H2 protective atmosphere at 700 ℃ and repressing at 500 MPa. Four kinds composites with different compositions were produced, and the mechanical properties and electrical wear performance were investigated. The results showed that the composite added with carbon nanotubes had a higher hardness and strength, a lower contact voltage drop and an excellent anti-wear property in electrical sliding wear, because of the reinforcement ability of carbon nanotubes. Adding graphite to the composite also decreased the wear loss and contact voltage drop, because graphite had an electrical current conducting ability which not only made the current pass the lubricating films easily but also eliminated and reduced the arc and spark effectively.