The aging process of pure copper precursors and copper-zinc binary precursorswere studied by XRD, TG-DTG and TPR techniques. The catalytic activity and stability of CuO/ZnOwere tested using fixed-bed flow reactor, and...The aging process of pure copper precursors and copper-zinc binary precursorswere studied by XRD, TG-DTG and TPR techniques. The catalytic activity and stability of CuO/ZnOwere tested using fixed-bed flow reactor, and the physical properties of the catalysts and Cuspecies were characterized with N_2 adsorption and N_2O passivation method, respectively. For theCu-Zn binary system prepared at the precipitating condition of pH=8.0 and temperature=80℃, theinitial phase was a mixture of copper nitrate hydroxide Cu_2(NO_3)(OH)_3, georgeite and hydrozinciteZn_5(CO_3)_2(OH)_6. By increasing the duration of its aging time, the phase of Cu_2(NO_3)(OH)_2first transited to georgeite, and then interdiffused into Zn_5(CO_3)_2(OH)_6 and resulted in two newphases: rosasite (Cu,Zn)_2CO_3(OH)_2 and au-richalcite (Zn,Cu)_5(CO_3)_2(OH)_6. The former phasewas much easier to be formed than the latter one, while the latter phase was more responsible forthe activity of methanol synthesis than the former one. It is found that the composition andstructure of the precursors altered obviously after the colour transition point. The experimentalresults showed that methanol synthesis is a structure-sensitive catalytic reaction.展开更多
The synthesis of ultrafine cerium dioxide precursor via homogeneous precipitation was studied. Mixed aqueous solution of anhydrous cerium nitrate and urea was first heated to 85℃ for 2 h, and the prepared suspension ...The synthesis of ultrafine cerium dioxide precursor via homogeneous precipitation was studied. Mixed aqueous solution of anhydrous cerium nitrate and urea was first heated to 85℃ for 2 h, and the prepared suspension was then aged at room temperature for various periods of time. White precipitate was finally collected by centrifuging and washed with distilled water and anhydrous ethanol. The obtained cerium dioxide (CeO2) precursor was observed with SEM. It was found that the morphology and size of the precursor were strongly affected by aging time and stirring conditions (with or without stirring). The precipitated fine spherical particles of the precursor changed their shape from ellipse to slice or directly to slice. Fine spherical monodispersed (300 nm) precursor powders could be obtained by controlling the aging time. Stirring the solution also could change the reaction process and thus the morphology and size of the precursor were changed.展开更多
Homogenous precipitation and subsequent calcination has been used tosynthesize ultrafine ceria from cerium nitrate and urea solution. The ceria calcined from theprecursor inherit the size and morphology of it. The siz...Homogenous precipitation and subsequent calcination has been used tosynthesize ultrafine ceria from cerium nitrate and urea solution. The ceria calcined from theprecursor inherit the size and morphology of it. The size and morphology of the precursor areclosely related to the preparation process. The morphology, size and distribution of the precursorcould be tailored by changing the reaction condition and the ageing time. Monodispersed 200 nm sizedspherical particles is prepared by this method. The powder is used in the chemical-mechanicalpolishing of Si wafer. The average surface roughness of the polished Si wafer is 0.171 nm measuredby AFM.展开更多
Well-crystallized high-silica NaY zeolites (Si/Al〉2.5) were prepared from a reaction mixture consisting of metakaolin, sodium silicate solution and seed solution via optimization of the mixture composition and reac...Well-crystallized high-silica NaY zeolites (Si/Al〉2.5) were prepared from a reaction mixture consisting of metakaolin, sodium silicate solution and seed solution via optimization of the mixture composition and reaction conditions. The transformation from kaolin to high-silica NaY zeolite was confirmed by XRD, SEM and IR techniques. Subsequently, the influence of synthesis parameters, i.e. initial SIO2/Al2O3, initial Na2O/SiO2, initial H2O/SiO2, aging time of the seed solution, crystallization temperature and crystallization time, on the NaY growth was investigated in terms of crystallinity and Si/Al ratio. The results showed that the effects of initial SiO2/Al2O3, initial Na2O/SiO2 and initial H2O/ SiO2 on the crystaIlinity and Si/Al ratio of NaY zeolite are similar to those observed in the conventional syntheses of NaY zeolites only using sodium silicate solution as silicon source. However, due to the use of metakaolin as the main silicon and aluminum sources in the present study, a long crystallization induction period of 20 h was achieved, which can be attributed to the dissolution of metakaolin. In addition, different from the conventional syntheses of zeolite NaY, pure NaY zeolites (i.e. without NaP zeolite impurity) were still obtained even at 120℃ because of the use of a large quantity of seed solution (23 wt%) in the reaction mixture. As the aging time of the seed solution increased from 3.5 h to 22 h, the relative crystallinity of the NaY zeolite first increased sharply and then reached a plateau, while the Si/Al ratio first increased rapidly up to a maximum value of 2.75 corresponding to an aging time of 6.5 h, and then decreased sharply with the aging time.展开更多
In order to investigate the effect of Zr addition on the precipitations of K4169 superalloy,a manual electric arc furnace was used to prepare the superalloy with different Zr addition from 0.03wt.% to 0.07wt%.After st...In order to investigate the effect of Zr addition on the precipitations of K4169 superalloy,a manual electric arc furnace was used to prepare the superalloy with different Zr addition from 0.03wt.% to 0.07wt%.After standard heat treatment and long-time aging,the microstructures of the alloys were observed using XRD,SEM and TEM.The results show that Zr not only inhibits the precipitation of Laves phase at the grain boundary,but also significantly promotes the precipitation of earlobe-like γ' and γ″ phases.After long time aging at 680℃ for 500 h,the γ″ phase grows up obviously and forms a γ'/γ'' clad microstructure when the Zr addition is 0.03 wt.%.A large number of fine orbed γ' particles precipitate in the grains and some γ″ phase transforms to disk-like δ phase when the Zr addition increases to 0.05wt.%.The nano-polycrystalline γ' phase precipitates in the grains and there is a little δ phase when the Zr addition is 0.07wt.%.As the Zr addition increases,the amount of Laves phase at the grain boundary decreases at first,and then increases and forms flaky morphology.展开更多
Cerium-zirconium composite oxides with high performance were synthesized by a co-precipitation method, using zirconium oxychloride and rare earth chloride as raw materials. The effects of precipitate aging time on the...Cerium-zirconium composite oxides with high performance were synthesized by a co-precipitation method, using zirconium oxychloride and rare earth chloride as raw materials. The effects of precipitate aging time on the properties of cerium-zirconium composite oxides were investigated. The prepared cerium-zirconium composite oxides were characterized by X-ray diffraction(XRD), BET specific surface area, pulsed oxygen chemical adsorption, H2 temperature-programmed-reduction(H2-TPR), scanning electron microscopy(SEM), etc. The results showed that the precipitate aging time caused great effects on the properties of cerium zirconium composite oxides. With the increase of aging time, the cerium zirconium composite oxides showed enhanced specific surface area, good thermal stability, and high oxygen storage capacity(OSC). The best performance sample was obtained while the precipitate aging time up to 48 h, with the specific surface area of 140.7 m2/g, and OSC of 657.24 μmolO2/g for the fresh sample. Even after thermal aged under 1000 oC for 4 h, the aged specific surface area was 41.6 m2/g, moreover with a good OSC of 569.9 μmolO2/g.展开更多
The fiber properties depending on the coating thickness and long-term time aging were investigated. The coating strip forces of optical fiber were strongly increased with secondary coating thickness. But it did not ch...The fiber properties depending on the coating thickness and long-term time aging were investigated. The coating strip forces of optical fiber were strongly increased with secondary coating thickness. But it did not change with time aging up to 90 days. The tensile strength and stress corrosion parameters of coated fiber were increased with time aging also but the increasing rate was quite different depending on the coating展开更多
In order to meet the design requirements of the aging treatment process of a 4th generation nickel-based single crystal superalloy(Ni-SX)developed independently,the effects of aging temperatures and aging times on the...In order to meet the design requirements of the aging treatment process of a 4th generation nickel-based single crystal superalloy(Ni-SX)developed independently,the effects of aging temperatures and aging times on the precipitation and morphological evolution ofγprecipitates are studied.The morphological evolution behavior ofγprecipitates during the aging process is summarized subsequently and the coarsening behavior ofγprecipitates is discussed by comparing with the Lifshitz-Slyozov-Wagner model(LSW)and the trans-interface diffusion-controlled model(TIDC).It is demonstrated that primary aging temperature and secondary aging time dominate the size and squareness ofγprecipitates respectively,a narrow primary aging temperature range and a suitable secondary aging time are allowed to obtain the optimized morphology ofγprecipitates.The optimal aging process of the Ni-SX investigated in the present work is obtained for 1100-1120°C/4 h and 870°C/16 h,confirmed by the corresponding creep tests.The coarsening growth ofγprecipitates in short-term aging also conforms to the LSW model well.Besides,the aging process design rules of various Ni-SXs of different generations are also summarized.展开更多
文摘The aging process of pure copper precursors and copper-zinc binary precursorswere studied by XRD, TG-DTG and TPR techniques. The catalytic activity and stability of CuO/ZnOwere tested using fixed-bed flow reactor, and the physical properties of the catalysts and Cuspecies were characterized with N_2 adsorption and N_2O passivation method, respectively. For theCu-Zn binary system prepared at the precipitating condition of pH=8.0 and temperature=80℃, theinitial phase was a mixture of copper nitrate hydroxide Cu_2(NO_3)(OH)_3, georgeite and hydrozinciteZn_5(CO_3)_2(OH)_6. By increasing the duration of its aging time, the phase of Cu_2(NO_3)(OH)_2first transited to georgeite, and then interdiffused into Zn_5(CO_3)_2(OH)_6 and resulted in two newphases: rosasite (Cu,Zn)_2CO_3(OH)_2 and au-richalcite (Zn,Cu)_5(CO_3)_2(OH)_6. The former phasewas much easier to be formed than the latter one, while the latter phase was more responsible forthe activity of methanol synthesis than the former one. It is found that the composition andstructure of the precursors altered obviously after the colour transition point. The experimentalresults showed that methanol synthesis is a structure-sensitive catalytic reaction.
基金the Natural Science Foundation of Jiangsu Province under pro ject No.BK2002010.
文摘The synthesis of ultrafine cerium dioxide precursor via homogeneous precipitation was studied. Mixed aqueous solution of anhydrous cerium nitrate and urea was first heated to 85℃ for 2 h, and the prepared suspension was then aged at room temperature for various periods of time. White precipitate was finally collected by centrifuging and washed with distilled water and anhydrous ethanol. The obtained cerium dioxide (CeO2) precursor was observed with SEM. It was found that the morphology and size of the precursor were strongly affected by aging time and stirring conditions (with or without stirring). The precipitated fine spherical particles of the precursor changed their shape from ellipse to slice or directly to slice. Fine spherical monodispersed (300 nm) precursor powders could be obtained by controlling the aging time. Stirring the solution also could change the reaction process and thus the morphology and size of the precursor were changed.
基金This project is supported by Provincial Natural Science Foundation of Jiangsu (No.BK2002010).
文摘Homogenous precipitation and subsequent calcination has been used tosynthesize ultrafine ceria from cerium nitrate and urea solution. The ceria calcined from theprecursor inherit the size and morphology of it. The size and morphology of the precursor areclosely related to the preparation process. The morphology, size and distribution of the precursorcould be tailored by changing the reaction condition and the ageing time. Monodispersed 200 nm sizedspherical particles is prepared by this method. The powder is used in the chemical-mechanicalpolishing of Si wafer. The average surface roughness of the polished Si wafer is 0.171 nm measuredby AFM.
基金supported by Beijing Natural Science Foundation (Grant No.2093043)the National Natural Science Foundation of China (Grant No.20606038)
文摘Well-crystallized high-silica NaY zeolites (Si/Al〉2.5) were prepared from a reaction mixture consisting of metakaolin, sodium silicate solution and seed solution via optimization of the mixture composition and reaction conditions. The transformation from kaolin to high-silica NaY zeolite was confirmed by XRD, SEM and IR techniques. Subsequently, the influence of synthesis parameters, i.e. initial SIO2/Al2O3, initial Na2O/SiO2, initial H2O/SiO2, aging time of the seed solution, crystallization temperature and crystallization time, on the NaY growth was investigated in terms of crystallinity and Si/Al ratio. The results showed that the effects of initial SiO2/Al2O3, initial Na2O/SiO2 and initial H2O/ SiO2 on the crystaIlinity and Si/Al ratio of NaY zeolite are similar to those observed in the conventional syntheses of NaY zeolites only using sodium silicate solution as silicon source. However, due to the use of metakaolin as the main silicon and aluminum sources in the present study, a long crystallization induction period of 20 h was achieved, which can be attributed to the dissolution of metakaolin. In addition, different from the conventional syntheses of zeolite NaY, pure NaY zeolites (i.e. without NaP zeolite impurity) were still obtained even at 120℃ because of the use of a large quantity of seed solution (23 wt%) in the reaction mixture. As the aging time of the seed solution increased from 3.5 h to 22 h, the relative crystallinity of the NaY zeolite first increased sharply and then reached a plateau, while the Si/Al ratio first increased rapidly up to a maximum value of 2.75 corresponding to an aging time of 6.5 h, and then decreased sharply with the aging time.
基金financially supported by the Natural Science Foundation of Gansu Province,China (No.3ZS042-B25-028)
文摘In order to investigate the effect of Zr addition on the precipitations of K4169 superalloy,a manual electric arc furnace was used to prepare the superalloy with different Zr addition from 0.03wt.% to 0.07wt%.After standard heat treatment and long-time aging,the microstructures of the alloys were observed using XRD,SEM and TEM.The results show that Zr not only inhibits the precipitation of Laves phase at the grain boundary,but also significantly promotes the precipitation of earlobe-like γ' and γ″ phases.After long time aging at 680℃ for 500 h,the γ″ phase grows up obviously and forms a γ'/γ'' clad microstructure when the Zr addition is 0.03 wt.%.A large number of fine orbed γ' particles precipitate in the grains and some γ″ phase transforms to disk-like δ phase when the Zr addition increases to 0.05wt.%.The nano-polycrystalline γ' phase precipitates in the grains and there is a little δ phase when the Zr addition is 0.07wt.%.As the Zr addition increases,the amount of Laves phase at the grain boundary decreases at first,and then increases and forms flaky morphology.
基金Project supported by the Twelfth Five-Year National Science and Technology Pillar Program(2012BAE01B02)National Development and Reform Commission Fund:Development and commercialization of the rare earth based automotive catalytic converter for national V automotive emission standard
文摘Cerium-zirconium composite oxides with high performance were synthesized by a co-precipitation method, using zirconium oxychloride and rare earth chloride as raw materials. The effects of precipitate aging time on the properties of cerium-zirconium composite oxides were investigated. The prepared cerium-zirconium composite oxides were characterized by X-ray diffraction(XRD), BET specific surface area, pulsed oxygen chemical adsorption, H2 temperature-programmed-reduction(H2-TPR), scanning electron microscopy(SEM), etc. The results showed that the precipitate aging time caused great effects on the properties of cerium zirconium composite oxides. With the increase of aging time, the cerium zirconium composite oxides showed enhanced specific surface area, good thermal stability, and high oxygen storage capacity(OSC). The best performance sample was obtained while the precipitate aging time up to 48 h, with the specific surface area of 140.7 m2/g, and OSC of 657.24 μmolO2/g for the fresh sample. Even after thermal aged under 1000 oC for 4 h, the aged specific surface area was 41.6 m2/g, moreover with a good OSC of 569.9 μmolO2/g.
文摘The fiber properties depending on the coating thickness and long-term time aging were investigated. The coating strip forces of optical fiber were strongly increased with secondary coating thickness. But it did not change with time aging up to 90 days. The tensile strength and stress corrosion parameters of coated fiber were increased with time aging also but the increasing rate was quite different depending on the coating
基金supported by the National Natural Science Foundation of China(No.91960201)the Zhejiang Provincial Natural Science Foundation of China(Nos.LR22E010003,LY20E010004)+3 种基金the Key Basic Research Program of Zhejiang Province(No.2020C01002)the Fundamental Research Funds for the Central Universities(No.226-2022-00050)the Fundamental Research Funds of the Zhejiang Provincial Universities(No.2021XZZX011)National Science and Technology Major Project of China(No.J2019-Ⅲ-0008-0051)。
文摘In order to meet the design requirements of the aging treatment process of a 4th generation nickel-based single crystal superalloy(Ni-SX)developed independently,the effects of aging temperatures and aging times on the precipitation and morphological evolution ofγprecipitates are studied.The morphological evolution behavior ofγprecipitates during the aging process is summarized subsequently and the coarsening behavior ofγprecipitates is discussed by comparing with the Lifshitz-Slyozov-Wagner model(LSW)and the trans-interface diffusion-controlled model(TIDC).It is demonstrated that primary aging temperature and secondary aging time dominate the size and squareness ofγprecipitates respectively,a narrow primary aging temperature range and a suitable secondary aging time are allowed to obtain the optimized morphology ofγprecipitates.The optimal aging process of the Ni-SX investigated in the present work is obtained for 1100-1120°C/4 h and 870°C/16 h,confirmed by the corresponding creep tests.The coarsening growth ofγprecipitates in short-term aging also conforms to the LSW model well.Besides,the aging process design rules of various Ni-SXs of different generations are also summarized.
基金supported by the"Thousands Talents"program for pioneer researcher and his innovation team,Chinathe National Natural Science Foundation of China(51374029 and 91433102)+1 种基金the Program for New Century Excellent Talents in the University(NCET-13-0668)the Fundamental Research Funds for the Central Universities(FRF-TP-14-008C1)