A method to promote aluminum hydroxide crystal growth through pickling Al(OH)_(3)as seed in the ammonia system was proposed to overcome these defects.The experimental results show that,under the conditions of pickling...A method to promote aluminum hydroxide crystal growth through pickling Al(OH)_(3)as seed in the ammonia system was proposed to overcome these defects.The experimental results show that,under the conditions of pickling time of 15 min,the acid concentration of 10%,the addition of 70 g/L pickling-Al(OH)_(3)seed,and the coarse granular Al(OH)_(3)products(d0.5=85.667)can be obtained.The characterization results show that the phase of the product is gibbsite,consistent with the seed.Moreover,the steps and ledges can be formed on pickling Al(OH)_(3)seed surface under the ammonia system,effectively promoting crystal growth.During crystal growth,the roughness of the crystal surface was first increased and then decreased,and the lamellar structure was deposited on the crystal seed surface.The final particles are approximately round,the surface is compact and dense.The growth of the product is surface reaction controlled.In addition,the content of the AlO_(6)unit is increased and contributed to Al(OH)_(3)crystal growth.展开更多
Electro-assisted regeneration(EAR)for the mixed bed of strongly acidic cation and weakly basic anion exchange resins with the Al(OH)_(3) suspension in a three-compartment cell was investigated.The desalination experim...Electro-assisted regeneration(EAR)for the mixed bed of strongly acidic cation and weakly basic anion exchange resins with the Al(OH)_(3) suspension in a three-compartment cell was investigated.The desalination experiments were carried out to evaluate the characteristic of the regenerated mixed resins.Experimental results showed that the efficiency of resin regeneration was strictly dependent on the voltage,regeneration time,and feed regenerant flow rate.The amount of the effluent reached 50 times the volume of the resins bed,and the conductivity was less than 1.0 ms/cm.Compared to the conventional ER,the total effluent volume of EAR was about 1000 mL more than that of ER under the same conditions,and the outlet conductivity was significantly lower.The desalination and regeneration reaction mechanisms of the mixed resins indicated the regeneration efficiency of resin with Al(OH)_(3) as the regenerant was much higher than that with H2O.展开更多
基金Funded by the National Natural Science Foundation of China(No.51974188)the Liaoning Revitalization Talents Program(No.XLYC2008014)。
文摘A method to promote aluminum hydroxide crystal growth through pickling Al(OH)_(3)as seed in the ammonia system was proposed to overcome these defects.The experimental results show that,under the conditions of pickling time of 15 min,the acid concentration of 10%,the addition of 70 g/L pickling-Al(OH)_(3)seed,and the coarse granular Al(OH)_(3)products(d0.5=85.667)can be obtained.The characterization results show that the phase of the product is gibbsite,consistent with the seed.Moreover,the steps and ledges can be formed on pickling Al(OH)_(3)seed surface under the ammonia system,effectively promoting crystal growth.During crystal growth,the roughness of the crystal surface was first increased and then decreased,and the lamellar structure was deposited on the crystal seed surface.The final particles are approximately round,the surface is compact and dense.The growth of the product is surface reaction controlled.In addition,the content of the AlO_(6)unit is increased and contributed to Al(OH)_(3)crystal growth.
文摘Electro-assisted regeneration(EAR)for the mixed bed of strongly acidic cation and weakly basic anion exchange resins with the Al(OH)_(3) suspension in a three-compartment cell was investigated.The desalination experiments were carried out to evaluate the characteristic of the regenerated mixed resins.Experimental results showed that the efficiency of resin regeneration was strictly dependent on the voltage,regeneration time,and feed regenerant flow rate.The amount of the effluent reached 50 times the volume of the resins bed,and the conductivity was less than 1.0 ms/cm.Compared to the conventional ER,the total effluent volume of EAR was about 1000 mL more than that of ER under the same conditions,and the outlet conductivity was significantly lower.The desalination and regeneration reaction mechanisms of the mixed resins indicated the regeneration efficiency of resin with Al(OH)_(3) as the regenerant was much higher than that with H2O.