Pseudobinary Ti 1 x Al x N films were synthesized on Si (100) wafer by DC magnetron sputtering method using Ti 1 x Al x alloy targets with different Al contents. The composition of the Ti 1 x Al x N films was determin...Pseudobinary Ti 1 x Al x N films were synthesized on Si (100) wafer by DC magnetron sputtering method using Ti 1 x Al x alloy targets with different Al contents. The composition of the Ti 1 x Al x N films was determined by electron probe microanalysis (EPMA). Structural characteristic was performed by X-ray diffraction (XRD), transmission electron microscopy (TEM), and high-resolution TEM (HRTEM). First principles virtual crystal calculations for the Ti 1 x Al x N disordered alloys were used for the XRD simulations. The crystalline structure of the Ti 0.61 Al 0.39 N film was found to be a metastable single phase with NaCl (B1) structure. Its lattice constant, determined by XRD, was less than that of pure TiN. With the increase of Al content, the lattice constant of B1 phase was continually decreased, while würtzite (B4) structure was observed in the Ti 0.40 Al 0.60 N film. When x reached 0.75, the B1 phase disappeared, and only B4 phase was remained. The critical Al content for the phase transition from NaCl to würtzite structure in this paper was about 0.60, which could be explained by both the thermodynamic model and the electron theory. As-deposited Ti 1 x Al x N films exhibited excellent mechanical properties. Hardness measurements of Ti 1 x Al x N films showed a high value of 45GPa for x=0.39 and was decreased to value of 27 GPa with increasing Al at x=0.60.展开更多
The hardness, toughness and electrochemical properties of the CrN coatings were studied by the method of Ion Beam Enhanced DePosition(IBED). The results show that the fraction of CrN phase and its hardness increase wi...The hardness, toughness and electrochemical properties of the CrN coatings were studied by the method of Ion Beam Enhanced DePosition(IBED). The results show that the fraction of CrN phase and its hardness increase with increasing N2 partial pressure and N ions bombarding energy in a certain range, but the toughness decreases. When the N ions: Cr atoms ratio changes from 1. 45 × 1O-2, 3. 67 × 10-2 to 5. 87 ×10 - 2, Cr2O3 is produced. In terms of corrosion resistance, the coated specimen shows a slight improvement in comparison with substrate 52100 steel. The Cr-N coated specimen is characterized with pitting corrosion by penetrating the agent throngh the defects involved very thin coating layer.展开更多
Ternary Ti-B-N coatings were synthesized on AISI 304 and Si wafer by plasma-enhanced chemical vapor deposition (PECVD) technique using a gaseous mixture of TiCl4,BCl3,H2,N2,and Ar.By virtue of X-ray diffraction analys...Ternary Ti-B-N coatings were synthesized on AISI 304 and Si wafer by plasma-enhanced chemical vapor deposition (PECVD) technique using a gaseous mixture of TiCl4,BCl3,H2,N2,and Ar.By virtue of X-ray diffraction analysis,X-ray photoelectron spectroscopy,scanning electron microscope,and high-resolution transmission electron microscope,the influences of B content on the microstructure and properties of Ti B N coatings were investigated systematically.The results indicated that the microstructure and mechanical properties of Ti-B-N coatings largely depend on the transformation from FCC-TiN phase to HCP-TiB2 phase.With increasing B content and decreasing N content in the coatings,the coating microstructure evolves gradually from FCC-TiN/a-BN to HCP-TiB2 /a-BN via FCC-TiN+HCP-TiB2/a-BN.The highest microhardness of about 34 GPa is achieved,which corresponds to the nanocomposite Ti-63%B-N (mole fraction) coating consisting of the HCP-TiB2 nano-crystallites and amorphous BN phase.The lowest friction-coefficient was observed for the nanocomposite Ti-41%B-N (mole fraction) coating consisting of the FCC-TiN nanocrystallites and amorphous BN展开更多
Magnetron sputtered (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings grown on cemented carbide substrates were studied by using energy dispersive X-ray spectroscopy (EDX), scanning electron microscopy(SEM), n...Magnetron sputtered (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings grown on cemented carbide substrates were studied by using energy dispersive X-ray spectroscopy (EDX), scanning electron microscopy(SEM), nanoindentation, Rockwell A indentation test, strength measurements and cutting tests. The results show that the (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings perform good affinity to substrate, and the TiN/(Ti, Al)N multilayer coating exhibits higher hardness, higher toughness and better cutting performance compared with the (Ti, Al)N monolayer coating. Moreover, the strength measurement indicates that the physical vapour deposition (PVD) coating has no effect on the substrate strength.展开更多
(Ti, Al)N gradient nano-coating was deposited on the surface of 1Cr11Ni2W2MoV stainless steel by the MTP-8-800 arc ion plating equipment. And the oxidation performance at high temperature for 500h was tested under t...(Ti, Al)N gradient nano-coating was deposited on the surface of 1Cr11Ni2W2MoV stainless steel by the MTP-8-800 arc ion plating equipment. And the oxidation performance at high temperature for 500h was tested under the condition of the surrounding air temperature 700℃. The test results show that, because of the structural features of the （Ti, Al）N coating, the coating becomes the compact and continuous Al2O3 film, which can protect the basis material effectively in the process of the high temperature oxidizing. The oxidation kinetics of the coating accord with parabolic law.展开更多
CrN and Cr-Al-N coatings were deposited by reactive magnetron sputtering on the glass substrate,and their corrosion behavior was studied. The electrochemical tests using both DC(polarization curves) and AC techniques(...CrN and Cr-Al-N coatings were deposited by reactive magnetron sputtering on the glass substrate,and their corrosion behavior was studied. The electrochemical tests using both DC(polarization curves) and AC techniques(EIS) were carried out on Potentiostat/Galvanstat(EG&G) in 3.5%(mass fraction) NaCl solution. After immersed into NaCl solution for 1 h,the mass of the CrN coating keeps constant with the time continuing. This can be explained by the passivation of the coating. The comparison between the corrosion potential(φcorr) of the Cr-Al-N coatings with different aluminum contents reveals that the corrosion potentials of the aluminum contain coatings are nobler than that of the CrN coatings. This means that the addition of aluminum shifts the corrosion potential to more positive potential value. Among these coatings,CrN in NaCl solution exhibits the worst corrosion resistance,while the corrosion resistance of Cr0.63Al0.37N in NaCl solution is the best. The polarization data and EIS data suggest that addition of aluminum can improve the corrosion resistance of CrN coating.展开更多
基金supported by "University Innovation and Research Training Program (China)" (No. 2009003)the Natural Science Foundation of Jiangsu Province (No.BK2011252)the Industry Science and Technology Supported Plan of Changzhou (No. CE20110012)
文摘Pseudobinary Ti 1 x Al x N films were synthesized on Si (100) wafer by DC magnetron sputtering method using Ti 1 x Al x alloy targets with different Al contents. The composition of the Ti 1 x Al x N films was determined by electron probe microanalysis (EPMA). Structural characteristic was performed by X-ray diffraction (XRD), transmission electron microscopy (TEM), and high-resolution TEM (HRTEM). First principles virtual crystal calculations for the Ti 1 x Al x N disordered alloys were used for the XRD simulations. The crystalline structure of the Ti 0.61 Al 0.39 N film was found to be a metastable single phase with NaCl (B1) structure. Its lattice constant, determined by XRD, was less than that of pure TiN. With the increase of Al content, the lattice constant of B1 phase was continually decreased, while würtzite (B4) structure was observed in the Ti 0.40 Al 0.60 N film. When x reached 0.75, the B1 phase disappeared, and only B4 phase was remained. The critical Al content for the phase transition from NaCl to würtzite structure in this paper was about 0.60, which could be explained by both the thermodynamic model and the electron theory. As-deposited Ti 1 x Al x N films exhibited excellent mechanical properties. Hardness measurements of Ti 1 x Al x N films showed a high value of 45GPa for x=0.39 and was decreased to value of 27 GPa with increasing Al at x=0.60.
文摘The hardness, toughness and electrochemical properties of the CrN coatings were studied by the method of Ion Beam Enhanced DePosition(IBED). The results show that the fraction of CrN phase and its hardness increase with increasing N2 partial pressure and N ions bombarding energy in a certain range, but the toughness decreases. When the N ions: Cr atoms ratio changes from 1. 45 × 1O-2, 3. 67 × 10-2 to 5. 87 ×10 - 2, Cr2O3 is produced. In terms of corrosion resistance, the coated specimen shows a slight improvement in comparison with substrate 52100 steel. The Cr-N coated specimen is characterized with pitting corrosion by penetrating the agent throngh the defects involved very thin coating layer.
基金funded by a grant from the National Core Research Center(NCRC)Program through the National Research Foundation of Korea funded by the Ministry of Education,Science and Technology(No.2012-0000-957)by a grant from the Fundamental R&D Program for Core Technology of Materials funded by the Ministry of Knowledge Economy,Republic of Korea
文摘Ternary Ti-B-N coatings were synthesized on AISI 304 and Si wafer by plasma-enhanced chemical vapor deposition (PECVD) technique using a gaseous mixture of TiCl4,BCl3,H2,N2,and Ar.By virtue of X-ray diffraction analysis,X-ray photoelectron spectroscopy,scanning electron microscope,and high-resolution transmission electron microscope,the influences of B content on the microstructure and properties of Ti B N coatings were investigated systematically.The results indicated that the microstructure and mechanical properties of Ti-B-N coatings largely depend on the transformation from FCC-TiN phase to HCP-TiB2 phase.With increasing B content and decreasing N content in the coatings,the coating microstructure evolves gradually from FCC-TiN/a-BN to HCP-TiB2 /a-BN via FCC-TiN+HCP-TiB2/a-BN.The highest microhardness of about 34 GPa is achieved,which corresponds to the nanocomposite Ti-63%B-N (mole fraction) coating consisting of the HCP-TiB2 nano-crystallites and amorphous BN phase.The lowest friction-coefficient was observed for the nanocomposite Ti-41%B-N (mole fraction) coating consisting of the FCC-TiN nanocrystallites and amorphous BN
文摘Magnetron sputtered (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings grown on cemented carbide substrates were studied by using energy dispersive X-ray spectroscopy (EDX), scanning electron microscopy(SEM), nanoindentation, Rockwell A indentation test, strength measurements and cutting tests. The results show that the (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings perform good affinity to substrate, and the TiN/(Ti, Al)N multilayer coating exhibits higher hardness, higher toughness and better cutting performance compared with the (Ti, Al)N monolayer coating. Moreover, the strength measurement indicates that the physical vapour deposition (PVD) coating has no effect on the substrate strength.
文摘(Ti, Al)N gradient nano-coating was deposited on the surface of 1Cr11Ni2W2MoV stainless steel by the MTP-8-800 arc ion plating equipment. And the oxidation performance at high temperature for 500h was tested under the condition of the surrounding air temperature 700℃. The test results show that, because of the structural features of the （Ti, Al）N coating, the coating becomes the compact and continuous Al2O3 film, which can protect the basis material effectively in the process of the high temperature oxidizing. The oxidation kinetics of the coating accord with parabolic law.
基金Project (50371095) supported by the National Natural Science Foundation of China
文摘CrN and Cr-Al-N coatings were deposited by reactive magnetron sputtering on the glass substrate,and their corrosion behavior was studied. The electrochemical tests using both DC(polarization curves) and AC techniques(EIS) were carried out on Potentiostat/Galvanstat(EG&G) in 3.5%(mass fraction) NaCl solution. After immersed into NaCl solution for 1 h,the mass of the CrN coating keeps constant with the time continuing. This can be explained by the passivation of the coating. The comparison between the corrosion potential(φcorr) of the Cr-Al-N coatings with different aluminum contents reveals that the corrosion potentials of the aluminum contain coatings are nobler than that of the CrN coatings. This means that the addition of aluminum shifts the corrosion potential to more positive potential value. Among these coatings,CrN in NaCl solution exhibits the worst corrosion resistance,while the corrosion resistance of Cr0.63Al0.37N in NaCl solution is the best. The polarization data and EIS data suggest that addition of aluminum can improve the corrosion resistance of CrN coating.