Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on...Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on the catalytic performance were studied. Characterizations by TPR, XRD, NH3-TPD, XPS, and TGA indicated that catalysts 30Ni5Cu/Al2O3-MgO and 30Ni5Cu/Al2O3-ZnO have much higher H2 selectivity than 30Ni5Cu/Al2O3-SiO2, as well as good coke resistance. H2 selectivity for 30Ni5Cu/Al2O3-MgO catalyst was 73.3% at 450 ℃ and increased to 94.0% at 600℃, whereas for 30Ni5Cu/Al2O3-ZnO catalyst, the H2 selectivity was 63.6% at 450 ℃ and 95.2% at 600℃. TheseAl2O3-MgO and Al2O3-ZnO supported Ni-Cu bimetallic catalysts may have important applications in the production of hydrogen by ethanol steam reforming reactions.展开更多
TiO_2 modified Al_2O_3 binary oxide was prepared by a wet-impregnation method and used as the support for ruthenium catalyst. The catalytic performance of Ru/TiO_2–Al_2O_3catalyst in CO_2 methanation reaction was inv...TiO_2 modified Al_2O_3 binary oxide was prepared by a wet-impregnation method and used as the support for ruthenium catalyst. The catalytic performance of Ru/TiO_2–Al_2O_3catalyst in CO_2 methanation reaction was investigated. Compared with Ru/Al_2O_3 catalyst, the Ru/TiO_2–Al_2O_3catalytic system exhibited a much higher activity in CO_2 methanation reaction. The reaction rate over Ru/TiO_2–Al_2O_3 was 0.59 mol CO_2·(g Ru)1·h-1, 3.1 times higher than that on Ru/Al_2O_3[0.19 mol CO_2·(gRu)-1·h-1]. The effect of TiO_2 content and TiO_2–Al_2O_3calcination temperature on catalytic performance was addressed. The corresponding structures of each catalyst were characterized by means of H_2-TPR, XRD, and TEM. Results indicated that the averaged particle size of the Ru on TiO_2–Al_2O_3support is 2.8 nm, smaller than that on Al_2O_3 support of 4.3 nm. Therefore, we conclude that the improved activity over Ru/TiO_2–Al_2O_3catalyst is originated from the smaller particle size of ruthenium resulting from a strong interaction between Ru and the rutile-TiO_2 support, which hindered the aggregation of Ru nanoparticles.展开更多
Alumina membranes without pinholes and cracks were prepared by the sol-gel process using anunordum aluminium sulphate as the starting material. The effects of different preparing conditions on morphology characteristi...Alumina membranes without pinholes and cracks were prepared by the sol-gel process using anunordum aluminium sulphate as the starting material. The effects of different preparing conditions on morphology characteristics of the membrane were investigated by scanning electron microscopy and 3D rotational microscopy. The preparing conditions include the amounts of drying control chemical additives （DCCA）, sintering procedure and sol-gel concentration. The results showed that PVA is a good crack-preventing reagent and the morphology of supported membranes was affected by ninny factors, including Al2O3 concentration, PVA/Al2O3 ratio, heating rate, membrane thickness and intrinsic defects of the substrate surface.展开更多
基金973 Program (2006CB202500)the National Natural Science Foundation of China (20676096)New Century Excellent Talents in University.9gram (2006CB202500)
文摘Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on the catalytic performance were studied. Characterizations by TPR, XRD, NH3-TPD, XPS, and TGA indicated that catalysts 30Ni5Cu/Al2O3-MgO and 30Ni5Cu/Al2O3-ZnO have much higher H2 selectivity than 30Ni5Cu/Al2O3-SiO2, as well as good coke resistance. H2 selectivity for 30Ni5Cu/Al2O3-MgO catalyst was 73.3% at 450 ℃ and increased to 94.0% at 600℃, whereas for 30Ni5Cu/Al2O3-ZnO catalyst, the H2 selectivity was 63.6% at 450 ℃ and 95.2% at 600℃. TheseAl2O3-MgO and Al2O3-ZnO supported Ni-Cu bimetallic catalysts may have important applications in the production of hydrogen by ethanol steam reforming reactions.
基金Supported by the National Natural Science Foundation of China(211031735127108721476226 and 51471076)DICP Fundamental Research Program for Clean Energy(DICPM201307)
文摘TiO_2 modified Al_2O_3 binary oxide was prepared by a wet-impregnation method and used as the support for ruthenium catalyst. The catalytic performance of Ru/TiO_2–Al_2O_3catalyst in CO_2 methanation reaction was investigated. Compared with Ru/Al_2O_3 catalyst, the Ru/TiO_2–Al_2O_3catalytic system exhibited a much higher activity in CO_2 methanation reaction. The reaction rate over Ru/TiO_2–Al_2O_3 was 0.59 mol CO_2·(g Ru)1·h-1, 3.1 times higher than that on Ru/Al_2O_3[0.19 mol CO_2·(gRu)-1·h-1]. The effect of TiO_2 content and TiO_2–Al_2O_3calcination temperature on catalytic performance was addressed. The corresponding structures of each catalyst were characterized by means of H_2-TPR, XRD, and TEM. Results indicated that the averaged particle size of the Ru on TiO_2–Al_2O_3support is 2.8 nm, smaller than that on Al_2O_3 support of 4.3 nm. Therefore, we conclude that the improved activity over Ru/TiO_2–Al_2O_3catalyst is originated from the smaller particle size of ruthenium resulting from a strong interaction between Ru and the rutile-TiO_2 support, which hindered the aggregation of Ru nanoparticles.
基金Project supported by National Natural Science Foundation ofChina (Grant No .20373040) Science Foundation of Science andTechnology Commission of Zhejiang Province ( Grant No .0252nm101) Science Foundation of Shanghai MunicipalCommission of Science and Technology (Grant No .0452nm019)
文摘Alumina membranes without pinholes and cracks were prepared by the sol-gel process using anunordum aluminium sulphate as the starting material. The effects of different preparing conditions on morphology characteristics of the membrane were investigated by scanning electron microscopy and 3D rotational microscopy. The preparing conditions include the amounts of drying control chemical additives （DCCA）, sintering procedure and sol-gel concentration. The results showed that PVA is a good crack-preventing reagent and the morphology of supported membranes was affected by ninny factors, including Al2O3 concentration, PVA/Al2O3 ratio, heating rate, membrane thickness and intrinsic defects of the substrate surface.