icrostructure and mechanical properties of Al_4C_3 and Al_2O_3 dispersion strengthened aluminum composite fabricated by mechanical attrition and hotpressing consolidation method were studied. It was shown that fine we...icrostructure and mechanical properties of Al_4C_3 and Al_2O_3 dispersion strengthened aluminum composite fabricated by mechanical attrition and hotpressing consolidation method were studied. It was shown that fine well developed Al_4C_3 stick and equiaxed γAl_2O_3 dispersoids with total content of about 6.6 v% uniformly distributed within the Al grains or along the grain boundaries. The Al/Al_4C_3 and Al/Al_2O_3 interfaces are very clean and well bonded at atomic level, but have no fixed orientation relationships between the dispersoids and the aluminum matrix exists. At ambient and especially elevated temperatures, strength and stiffness of the composite are much higher than that of P/M Al and even better than that of the 15 v% SiCw/Al composite.展开更多
文摘icrostructure and mechanical properties of Al_4C_3 and Al_2O_3 dispersion strengthened aluminum composite fabricated by mechanical attrition and hotpressing consolidation method were studied. It was shown that fine well developed Al_4C_3 stick and equiaxed γAl_2O_3 dispersoids with total content of about 6.6 v% uniformly distributed within the Al grains or along the grain boundaries. The Al/Al_4C_3 and Al/Al_2O_3 interfaces are very clean and well bonded at atomic level, but have no fixed orientation relationships between the dispersoids and the aluminum matrix exists. At ambient and especially elevated temperatures, strength and stiffness of the composite are much higher than that of P/M Al and even better than that of the 15 v% SiCw/Al composite.