Butt friction stir welding between pure copper and AA5754 alloy was carried out.Reinforcing SiC nanoparticles were utilized in friction stir welded(FSW)joints to decline the harmful effects of intermetallic compounds....Butt friction stir welding between pure copper and AA5754 alloy was carried out.Reinforcing SiC nanoparticles were utilized in friction stir welded(FSW)joints to decline the harmful effects of intermetallic compounds.Tensile tests,micro-hardness experiments,scanning electron microscopy and X-ray diffraction analysis were applied to studying the properties of welded joints.The joints with a travel speed of 50 mm/min and a rotation speed of 1000 r/min showed the best results.The presence of nano-sized SiC particles reduced the grain size of aluminum and copper in the stir zone(SZ)from 38.3 and 12.4μm to 12.9 and 5.1μm,respectively.The tensile strength of the joint in the presence of reinforcing SiC nano-particles was~240 MPa,which is~90%of that for the aluminum base.Furthermore,the highest microhardness of the weld zone was significantly increased from HV 160 to HV 320 upon the addition of SiC nano-particles.The results also showed that raising the heat generation in FSW joints increased the amount of Al_(4)Cu_(9) and Al_(2)Cu intermetallic compounds.展开更多
In this study,friction stir lap welding(FSLW)was performed for the welding test of 6061 aluminium alloy and T2 pure copper.The effect of process parameters containing rotation rate and travel speed on interfacial micr...In this study,friction stir lap welding(FSLW)was performed for the welding test of 6061 aluminium alloy and T2 pure copper.The effect of process parameters containing rotation rate and travel speed on interfacial microstructure evolution and mechanical properties of Al/Cu dissimilar joints were explored.The experiments were carried out under the rotation rates of 600,900 and 1200 r/min and with the travel speeds of 30,70 and 100 mm/min.The characteristic of interface transition zones(ITZs)and the species of intermetallic compounds(IMCs)were investigated.The Al/Cu interface showed a layered structure composed of Al-Cu IMCs,which will affect the mechanical property.The layer consisting of Al2Cu was formed at lower heat input,and as heat input increased the Al4Cu9 phase started to form.Excessive heat input will increase the thickness of the interface and raise the brittleness of the joints.The thickness of the IMCs layers changed from0.89μm to 3.96μm as the heat input increased.The maximum value of tensile shear loading of 4.65 kN was obtained at the rotation rate of900 r/min and travel speed of 100 mm/min with the interface thickness of 2.89μm.The fracture mode of the joints was a mix of ductile and brittle fracture.展开更多
In order to achieve a high-quality joining of aluminum(Al)and copper(Cu)dissimilar metals,a new friction stir doubleriveting welding(FSDRW)with a Cu rod as the rivet was proposed,and the rotating tool with a large con...In order to achieve a high-quality joining of aluminum(Al)and copper(Cu)dissimilar metals,a new friction stir doubleriveting welding(FSDRW)with a Cu rod as the rivet was proposed,and the rotating tool with a large concave angle shoulder was specially designed.The results showed that under the thermal–mechanical effect of rotating tool,the Cu rod was deformed to be a double riveting heads structure with a Cu anchor at the upper surface of Al plate and an Al anchor above the lap interface of joint,and these two anchors greatly enhanced the mechanical interlocking of Al/Cu joint.The effective bonding interfaces were formed among the double riveting heads structure,the upper Al plate and the lower Cu plate,which contained the Cu/Cu interface and the Al/Cu interface.The Cu/Cu interface without the kissing bond and the Al/Cu interface with the rationally thin AlCu and Al_(2)Cu intermetallic compounds(IMCs)layers were beneficial to heightening the joint tensile shear strength.The maximum tensile shear load of the FSDRW joint achieved 5.52 kN,and the joint under different plunging depths of rotating tool presented a mixed mode of ductile fracture and brittle fracture.This novel FSDRW technique owns the advantages of strong mechanical interlocking and superb metallurgical bonding,and provides a new approach to acquiring a high-quality Al/Cu dissimilar metals joint.展开更多
利用AlSi5焊丝作为填充材料对6061铝合金和T2纯铜进行冷金属过渡（Cold Metal Transfer,CMT）熔钎焊.通过拉伸试验评定搭接接头力学性能并采用SEM,EDS分析搭接接头的微观组织及化学成分,利用XRD进一步确定了钎焊界面产物.研究结果表明...利用AlSi5焊丝作为填充材料对6061铝合金和T2纯铜进行冷金属过渡（Cold Metal Transfer,CMT）熔钎焊.通过拉伸试验评定搭接接头力学性能并采用SEM,EDS分析搭接接头的微观组织及化学成分,利用XRD进一步确定了钎焊界面产物.研究结果表明：送丝速度在6.5 ～ 7.5 m/min焊接时,焊接过程稳定,焊缝成形美观.搭接接头主要断裂在钎焊面处,最大拉剪载荷为154 N/mm.钎焊界面产物主要为CuAl,CuAl2,厚度在150μm左右,显微硬度在400 HV0.1左右.钎焊界面处形成的脆硬金属间化合物是铝铜搭接接头断裂于钎焊面处的主要原因.展开更多
文摘Butt friction stir welding between pure copper and AA5754 alloy was carried out.Reinforcing SiC nanoparticles were utilized in friction stir welded(FSW)joints to decline the harmful effects of intermetallic compounds.Tensile tests,micro-hardness experiments,scanning electron microscopy and X-ray diffraction analysis were applied to studying the properties of welded joints.The joints with a travel speed of 50 mm/min and a rotation speed of 1000 r/min showed the best results.The presence of nano-sized SiC particles reduced the grain size of aluminum and copper in the stir zone(SZ)from 38.3 and 12.4μm to 12.9 and 5.1μm,respectively.The tensile strength of the joint in the presence of reinforcing SiC nano-particles was~240 MPa,which is~90%of that for the aluminum base.Furthermore,the highest microhardness of the weld zone was significantly increased from HV 160 to HV 320 upon the addition of SiC nano-particles.The results also showed that raising the heat generation in FSW joints increased the amount of Al_(4)Cu_(9) and Al_(2)Cu intermetallic compounds.
基金supported by the Key project of Education Department of Hebei Province(Grant No.ZD2019102)。
文摘In this study,friction stir lap welding(FSLW)was performed for the welding test of 6061 aluminium alloy and T2 pure copper.The effect of process parameters containing rotation rate and travel speed on interfacial microstructure evolution and mechanical properties of Al/Cu dissimilar joints were explored.The experiments were carried out under the rotation rates of 600,900 and 1200 r/min and with the travel speeds of 30,70 and 100 mm/min.The characteristic of interface transition zones(ITZs)and the species of intermetallic compounds(IMCs)were investigated.The Al/Cu interface showed a layered structure composed of Al-Cu IMCs,which will affect the mechanical property.The layer consisting of Al2Cu was formed at lower heat input,and as heat input increased the Al4Cu9 phase started to form.Excessive heat input will increase the thickness of the interface and raise the brittleness of the joints.The thickness of the IMCs layers changed from0.89μm to 3.96μm as the heat input increased.The maximum value of tensile shear loading of 4.65 kN was obtained at the rotation rate of900 r/min and travel speed of 100 mm/min with the interface thickness of 2.89μm.The fracture mode of the joints was a mix of ductile and brittle fracture.
基金financially supported by the National Natural Science Foundation of China(Nos.51874201 and 52074184).
文摘In order to achieve a high-quality joining of aluminum(Al)and copper(Cu)dissimilar metals,a new friction stir doubleriveting welding(FSDRW)with a Cu rod as the rivet was proposed,and the rotating tool with a large concave angle shoulder was specially designed.The results showed that under the thermal–mechanical effect of rotating tool,the Cu rod was deformed to be a double riveting heads structure with a Cu anchor at the upper surface of Al plate and an Al anchor above the lap interface of joint,and these two anchors greatly enhanced the mechanical interlocking of Al/Cu joint.The effective bonding interfaces were formed among the double riveting heads structure,the upper Al plate and the lower Cu plate,which contained the Cu/Cu interface and the Al/Cu interface.The Cu/Cu interface without the kissing bond and the Al/Cu interface with the rationally thin AlCu and Al_(2)Cu intermetallic compounds(IMCs)layers were beneficial to heightening the joint tensile shear strength.The maximum tensile shear load of the FSDRW joint achieved 5.52 kN,and the joint under different plunging depths of rotating tool presented a mixed mode of ductile fracture and brittle fracture.This novel FSDRW technique owns the advantages of strong mechanical interlocking and superb metallurgical bonding,and provides a new approach to acquiring a high-quality Al/Cu dissimilar metals joint.