The behavior of eutectic liquid penetrating into the Al base during Al/Cu contact reactive brazing process was studied. Analysis results show that the eutectic liquid prefers to expand along the grain boundary in the ...The behavior of eutectic liquid penetrating into the Al base during Al/Cu contact reactive brazing process was studied. Analysis results show that the eutectic liquid prefers to expand along the grain boundary in the depth direction. Meanwhile, dissolution of solid Al and Cu into the eutectic liquid promotes the eutectic reaction and the continuously formed eutectic liquid leads to the reactive penetrating.展开更多
The reactive spread behaviour of Cu particles on the surJace of Al has been studied.The role of oxide film and the .formation mechanism of the joint during Al/Cu contacting reaction brazing have been discussed.
To design a promising Al−Si filler alloy with a relatively low melting-point,good strength and plasticity for the Cu/Al joint,the Cu,Ni,Zr and Er elements were innovatively added to modify the traditional Al−Si eutect...To design a promising Al−Si filler alloy with a relatively low melting-point,good strength and plasticity for the Cu/Al joint,the Cu,Ni,Zr and Er elements were innovatively added to modify the traditional Al−Si eutectic filler.The microstructure and mechanical properties of filler alloys and Cu/Al joints were investigated.The result indicated that the Al−Si−Ni−Cu filler alloys mainly consisted of Al(s,s),Al_(2)(Cu,Ni)and Si(s,s).The Al−10Si−2Ni−6Cu filler alloy exhibited relatively low solidus(521℃)and liquidus(577℃)temperature,good tensile strength(305.8 MPa)and fracture elongation(8.5%).The corresponding Cu/Al joint brazed using Al−10Si−2Ni−6Cu filler was mainly composed of Al_(8)(Mn,Fe)_(2)Si,Al_(2)(Cu,Ni)3,Al(Cu,Ni),Al_(2)(Cu,Ni)and Al(s,s),yielding a shear strength of(90.3±10.7)MPa.The joint strength was further improved to(94.6±2.5)MPa when the joint was brazed using the Al−10Si−2Ni−6Cu−0.2Er−0.2Zr filler alloy.Consequently,the(Cu,Ni,Zr,Er)-modified Al−Si filler alloy was suitable for obtaining high-quality Cu/Al brazed joints.展开更多
文摘The behavior of eutectic liquid penetrating into the Al base during Al/Cu contact reactive brazing process was studied. Analysis results show that the eutectic liquid prefers to expand along the grain boundary in the depth direction. Meanwhile, dissolution of solid Al and Cu into the eutectic liquid promotes the eutectic reaction and the continuously formed eutectic liquid leads to the reactive penetrating.
文摘The reactive spread behaviour of Cu particles on the surJace of Al has been studied.The role of oxide film and the .formation mechanism of the joint during Al/Cu contacting reaction brazing have been discussed.
基金the financial support from the Primary Research&Development Plan of Zhejiang Province,China(No.2021C01178)the National MCF Energy R&D Program,China(No.2019YFE03100400)+1 种基金the National Natural Science Foundation of China(Nos.51705457,51975530,52005445,52175368)the Natural Science Foundation of Zhejiang Province,China(Nos.LQ21E050015,LQ21E050018).
文摘To design a promising Al−Si filler alloy with a relatively low melting-point,good strength and plasticity for the Cu/Al joint,the Cu,Ni,Zr and Er elements were innovatively added to modify the traditional Al−Si eutectic filler.The microstructure and mechanical properties of filler alloys and Cu/Al joints were investigated.The result indicated that the Al−Si−Ni−Cu filler alloys mainly consisted of Al(s,s),Al_(2)(Cu,Ni)and Si(s,s).The Al−10Si−2Ni−6Cu filler alloy exhibited relatively low solidus(521℃)and liquidus(577℃)temperature,good tensile strength(305.8 MPa)and fracture elongation(8.5%).The corresponding Cu/Al joint brazed using Al−10Si−2Ni−6Cu filler was mainly composed of Al_(8)(Mn,Fe)_(2)Si,Al_(2)(Cu,Ni)3,Al(Cu,Ni),Al_(2)(Cu,Ni)and Al(s,s),yielding a shear strength of(90.3±10.7)MPa.The joint strength was further improved to(94.6±2.5)MPa when the joint was brazed using the Al−10Si−2Ni−6Cu−0.2Er−0.2Zr filler alloy.Consequently,the(Cu,Ni,Zr,Er)-modified Al−Si filler alloy was suitable for obtaining high-quality Cu/Al brazed joints.