Dissimilar metal joining between 5A02 aluminum alloy and H62 brass sheets was conducted by gas tungsten arc welding with Zn-15% Al and Al-12% Si flux-cored filler wires. The microstructure in the weld and distribution...Dissimilar metal joining between 5A02 aluminum alloy and H62 brass sheets was conducted by gas tungsten arc welding with Zn-15% Al and Al-12% Si flux-cored filler wires. The microstructure in the weld and distribution of major alloying elements in the intelfacial layer were examined, and the tensile strength of the resultant joints was measured. Pores appeared in the weld made with Zn-15% Al flax-cored filler wire, the interracial layer mainly consisted of AlCu phase, and the specimens fractured through the weld with tensile strength of 129 MPa. When Al-12% Si flux-cored filler wire was used, Cu diffused into the weld and Al2 Cu phase formed, and the specimens fractured along the interfacial layer with tensile strength of 122 MPa.展开更多
In order to achieve a high-quality joining of aluminum(Al)and copper(Cu)dissimilar metals,a new friction stir doubleriveting welding(FSDRW)with a Cu rod as the rivet was proposed,and the rotating tool with a large con...In order to achieve a high-quality joining of aluminum(Al)and copper(Cu)dissimilar metals,a new friction stir doubleriveting welding(FSDRW)with a Cu rod as the rivet was proposed,and the rotating tool with a large concave angle shoulder was specially designed.The results showed that under the thermal–mechanical effect of rotating tool,the Cu rod was deformed to be a double riveting heads structure with a Cu anchor at the upper surface of Al plate and an Al anchor above the lap interface of joint,and these two anchors greatly enhanced the mechanical interlocking of Al/Cu joint.The effective bonding interfaces were formed among the double riveting heads structure,the upper Al plate and the lower Cu plate,which contained the Cu/Cu interface and the Al/Cu interface.The Cu/Cu interface without the kissing bond and the Al/Cu interface with the rationally thin AlCu and Al_(2)Cu intermetallic compounds(IMCs)layers were beneficial to heightening the joint tensile shear strength.The maximum tensile shear load of the FSDRW joint achieved 5.52 kN,and the joint under different plunging depths of rotating tool presented a mixed mode of ductile fracture and brittle fracture.This novel FSDRW technique owns the advantages of strong mechanical interlocking and superb metallurgical bonding,and provides a new approach to acquiring a high-quality Al/Cu dissimilar metals joint.展开更多
基金Acknowledgements This work was financially supported by the National Natural Science Foundation of China （ Grant No. 50904012 ） and Natural Science Foundation of Liaoning Province （Grant No. 20092152）.
文摘Dissimilar metal joining between 5A02 aluminum alloy and H62 brass sheets was conducted by gas tungsten arc welding with Zn-15% Al and Al-12% Si flux-cored filler wires. The microstructure in the weld and distribution of major alloying elements in the intelfacial layer were examined, and the tensile strength of the resultant joints was measured. Pores appeared in the weld made with Zn-15% Al flax-cored filler wire, the interracial layer mainly consisted of AlCu phase, and the specimens fractured through the weld with tensile strength of 129 MPa. When Al-12% Si flux-cored filler wire was used, Cu diffused into the weld and Al2 Cu phase formed, and the specimens fractured along the interfacial layer with tensile strength of 122 MPa.
基金financially supported by the National Natural Science Foundation of China(Nos.51874201 and 52074184).
文摘In order to achieve a high-quality joining of aluminum(Al)and copper(Cu)dissimilar metals,a new friction stir doubleriveting welding(FSDRW)with a Cu rod as the rivet was proposed,and the rotating tool with a large concave angle shoulder was specially designed.The results showed that under the thermal–mechanical effect of rotating tool,the Cu rod was deformed to be a double riveting heads structure with a Cu anchor at the upper surface of Al plate and an Al anchor above the lap interface of joint,and these two anchors greatly enhanced the mechanical interlocking of Al/Cu joint.The effective bonding interfaces were formed among the double riveting heads structure,the upper Al plate and the lower Cu plate,which contained the Cu/Cu interface and the Al/Cu interface.The Cu/Cu interface without the kissing bond and the Al/Cu interface with the rationally thin AlCu and Al_(2)Cu intermetallic compounds(IMCs)layers were beneficial to heightening the joint tensile shear strength.The maximum tensile shear load of the FSDRW joint achieved 5.52 kN,and the joint under different plunging depths of rotating tool presented a mixed mode of ductile fracture and brittle fracture.This novel FSDRW technique owns the advantages of strong mechanical interlocking and superb metallurgical bonding,and provides a new approach to acquiring a high-quality Al/Cu dissimilar metals joint.