The effects of the pre-deformation on the microstructure, mechanical properties and corrosion resistance of Al–Cu–Mg–Ag alloys were investigated by means of hardness tests, tensile tests, intergranullar corrosion(I...The effects of the pre-deformation on the microstructure, mechanical properties and corrosion resistance of Al–Cu–Mg–Ag alloys were investigated by means of hardness tests, tensile tests, intergranullar corrosion(IGC) tests and transmission electron microscopy(TEM), respectively. The results show that with the increase of deformation amount, the aging hardening rate increases while the strength of the alloy decreases and then increases. The sample with a pre-deformation of 6% possesses the highest tensile strength due to the refinedly and homogeneously distributed precipitations. The pre-deformation aging accelerates the heterogeneous nucleation of ? and θ′ phases at dislocations, and also refines the precipitations both in the grains and along the grain boundaries. The precipitation of ? phase is restrained while that of θ′ phase is accelerated in pre-deformed Al–Cu–Mg–Ag alloy compared with the sample without pre-deformation. In addition, the width of the precipitate free zone decreases with increasing the pre-deformation amount, leading to a narrower IGC passageway. This results in an enhanced IGC resistance of Al–Cu–Mg–Ag alloy treated by pre-deformation aging.展开更多
This study investigated the influence of graded Zn content on the evolution of precipitated and iron-rich phases and grain struc-ture of the alloys,designed and developed the Al–8.0Zn–1.5Mg–1.5Cu–0.2Fe(wt%)alloy w...This study investigated the influence of graded Zn content on the evolution of precipitated and iron-rich phases and grain struc-ture of the alloys,designed and developed the Al–8.0Zn–1.5Mg–1.5Cu–0.2Fe(wt%)alloy with high strength and formability.With the increase of Zn content,forming the coupling distribution of multiscale precipitates and iron-rich phases with a reasonable matching ratio and dispersion distribution characteristics is easy.This phenomenon induces the formation of cell-like structures with alternate distribu-tion of coarse and fine grains,and the average plasticity–strain ratio(characterizing the formability)of the pre-aged alloy with a high strength is up to 0.708.Results reveal the evolution and influence mechanisms of multiscale second-phase particles and the corresponding high formability mechanism of the alloys.The developed coupling control process exhibits considerable potential,revealing remarkable improvements in the room temperature formability of high-strength Al–Zn–Mg–Cu alloys.展开更多
基金Project(E2013402056)supported by the Natural Science Foundation of Hebei Province,ChinaProject(QN2014002)supported by the Science and Technology Research Foundation of Hebei Education Department for Young Teachers in University,ChinaProject(51601053)supported by the National Natural Science Foundation of China
文摘The effects of the pre-deformation on the microstructure, mechanical properties and corrosion resistance of Al–Cu–Mg–Ag alloys were investigated by means of hardness tests, tensile tests, intergranullar corrosion(IGC) tests and transmission electron microscopy(TEM), respectively. The results show that with the increase of deformation amount, the aging hardening rate increases while the strength of the alloy decreases and then increases. The sample with a pre-deformation of 6% possesses the highest tensile strength due to the refinedly and homogeneously distributed precipitations. The pre-deformation aging accelerates the heterogeneous nucleation of ? and θ′ phases at dislocations, and also refines the precipitations both in the grains and along the grain boundaries. The precipitation of ? phase is restrained while that of θ′ phase is accelerated in pre-deformed Al–Cu–Mg–Ag alloy compared with the sample without pre-deformation. In addition, the width of the precipitate free zone decreases with increasing the pre-deformation amount, leading to a narrower IGC passageway. This results in an enhanced IGC resistance of Al–Cu–Mg–Ag alloy treated by pre-deformation aging.
基金support from the National Science Foundation of China (No.51971249)the Natural Science Foundation of Shandong Province,China (No.ZR2020KE012)the Science and Technology Planning Project of Longkou City,China (No.2021KJJH025).
基金financially supported by the National Key Research and Development Program of China(No.2020YFB0311201)the National Natural Science Foundation of China(No.51627802)。
基金supported by the National Key Research and Development Program of China(No.2021YFE0115900)the National Natural Science Foundation of China(Nos.52371016,51871029,and 51571023)the Opening Project of State Key Laboratory for Advanced Metals and Materials(Nos.2020-ZD02 and No.2022-Z03).
文摘This study investigated the influence of graded Zn content on the evolution of precipitated and iron-rich phases and grain struc-ture of the alloys,designed and developed the Al–8.0Zn–1.5Mg–1.5Cu–0.2Fe(wt%)alloy with high strength and formability.With the increase of Zn content,forming the coupling distribution of multiscale precipitates and iron-rich phases with a reasonable matching ratio and dispersion distribution characteristics is easy.This phenomenon induces the formation of cell-like structures with alternate distribu-tion of coarse and fine grains,and the average plasticity–strain ratio(characterizing the formability)of the pre-aged alloy with a high strength is up to 0.708.Results reveal the evolution and influence mechanisms of multiscale second-phase particles and the corresponding high formability mechanism of the alloys.The developed coupling control process exhibits considerable potential,revealing remarkable improvements in the room temperature formability of high-strength Al–Zn–Mg–Cu alloys.