Mo/ZSM 5 catalysts with different Mo content were prepared by impregnation method. The effect of Mo content on the property of Mo/ZSM 5 catalysts and their performance for selective catalytic reduction(SCR) of NO with...Mo/ZSM 5 catalysts with different Mo content were prepared by impregnation method. The effect of Mo content on the property of Mo/ZSM 5 catalysts and their performance for selective catalytic reduction(SCR) of NO with ammonia was investigated by XRD, ICP, XPS and NO TPD respectively. The results showed that the catalytic activity of Mo/ZSM 5 for SCR of NO is strongly influenced by the Mo loading in HZSM 5 zeolites. The NOx conversion reached the highest value of 64.2% at 375℃ when Mo content is about 10 9%, and the temperatures at which the maximum of NOx conversion obtained were declined with the increase of Mo content. From XRD results, it can be seen that it exhibits the distinct interaction between Mo and HZSM 5 when Mo content is about 10 9%. This may result in a suitable phase structure in Mo/ZSM 5 catalyst, which is advantageous for NO reduction. XPS and NO TPD results also showed that the catalytic activity of Mo/ZSM 5 may be related to the Mo percent on the surface.展开更多
The influence of AI content on the Mg-AI alloys corrosion performance during sodium chloride induced atmospheric corrosion has been studied. It was found that the corrosion rate of three Mg-AI alloys was accelerated w...The influence of AI content on the Mg-AI alloys corrosion performance during sodium chloride induced atmospheric corrosion has been studied. It was found that the corrosion rate of three Mg-AI alloys was accelerated with increasing AI content. The poor corrosion resistance was attributed to the galvanic coupling between the phase and eutectic phase or α phase and the formation of porous corrosion products.展开更多
文摘Mo/ZSM 5 catalysts with different Mo content were prepared by impregnation method. The effect of Mo content on the property of Mo/ZSM 5 catalysts and their performance for selective catalytic reduction(SCR) of NO with ammonia was investigated by XRD, ICP, XPS and NO TPD respectively. The results showed that the catalytic activity of Mo/ZSM 5 for SCR of NO is strongly influenced by the Mo loading in HZSM 5 zeolites. The NOx conversion reached the highest value of 64.2% at 375℃ when Mo content is about 10 9%, and the temperatures at which the maximum of NOx conversion obtained were declined with the increase of Mo content. From XRD results, it can be seen that it exhibits the distinct interaction between Mo and HZSM 5 when Mo content is about 10 9%. This may result in a suitable phase structure in Mo/ZSM 5 catalyst, which is advantageous for NO reduction. XPS and NO TPD results also showed that the catalytic activity of Mo/ZSM 5 may be related to the Mo percent on the surface.
基金support by the National Natural ScienceFoundation of China (Grant No. 50571105) is acknowl-edged.
文摘The influence of AI content on the Mg-AI alloys corrosion performance during sodium chloride induced atmospheric corrosion has been studied. It was found that the corrosion rate of three Mg-AI alloys was accelerated with increasing AI content. The poor corrosion resistance was attributed to the galvanic coupling between the phase and eutectic phase or α phase and the formation of porous corrosion products.