The texture evaluation of α2 phase in Ti-25Al-10Nb-3V-1Mo sheet during rolling and annealing has been investigated by means of microstructure observation and ODF analysis. From the weak initial {1010} (1210) and {000...The texture evaluation of α2 phase in Ti-25Al-10Nb-3V-1Mo sheet during rolling and annealing has been investigated by means of microstructure observation and ODF analysis. From the weak initial {1010} (1210) and {0001}(1210) textures a {1210}(1010) texture and a {0001}(uvtw)fibre texture are formed after cold rolling. The {0001} (1210) texture is also strengthened simultaneously. The activation process of slip systems is discussed concerning formation of the rolling texture. Because of the disappearance of {0001} (nvtw) fibre texture the primary recrystallization process should occur and the {1210}(1010) texture forms during annealing展开更多
In the as-cast Ti-55 alloy, the intragranular rare earth-rich phase particles are about 1. 0~14 μm in diameter, elliptical, and rich in Nd, Sn, and O. The contents of Nd and Sn on the grain boundaries are higher th...In the as-cast Ti-55 alloy, the intragranular rare earth-rich phase particles are about 1. 0~14 μm in diameter, elliptical, and rich in Nd, Sn, and O. The contents of Nd and Sn on the grain boundaries are higher than those at other sites. The intragranular phases grow preferably at the region on the grain boundaries, which causes the formation of the elliptical morphology of the intragranular phases.展开更多
文摘The texture evaluation of α2 phase in Ti-25Al-10Nb-3V-1Mo sheet during rolling and annealing has been investigated by means of microstructure observation and ODF analysis. From the weak initial {1010} (1210) and {0001}(1210) textures a {1210}(1010) texture and a {0001}(uvtw)fibre texture are formed after cold rolling. The {0001} (1210) texture is also strengthened simultaneously. The activation process of slip systems is discussed concerning formation of the rolling texture. Because of the disappearance of {0001} (nvtw) fibre texture the primary recrystallization process should occur and the {1210}(1010) texture forms during annealing
文摘In the as-cast Ti-55 alloy, the intragranular rare earth-rich phase particles are about 1. 0~14 μm in diameter, elliptical, and rich in Nd, Sn, and O. The contents of Nd and Sn on the grain boundaries are higher than those at other sites. The intragranular phases grow preferably at the region on the grain boundaries, which causes the formation of the elliptical morphology of the intragranular phases.