The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue cr...The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue crack initiation than the matrix at lower stress.展开更多
Al-4. 5Cu-5Pb alloy was prepared by sand and chill casting. The same alloy was also spray deposited at a gas pressure of 1.6 MPa. The microstructural features exhibit a coarse to fine dendritic morphology for sand ...Al-4. 5Cu-5Pb alloy was prepared by sand and chill casting. The same alloy was also spray deposited at a gas pressure of 1.6 MPa. The microstructural features exhibit a coarse to fine dendritic morphology for sand and chill cast alloys. Equiaxed grains were observed for spray formed alloys. Wear testing employing a pin-on-disc type set-up, reveals considerably lower wear of spray deposited alloy compared to that of chill and sand cast alloys. The morphological features of wear track on specimen and debris indicated a mixed oxidative-cum-adhesive wear mechanisms for these alloys tested in the present investigation. (Edited author abstract) 36 Refs.展开更多
In situ synchrotron X-radiography was carried out on Al-13 Cu and Al-13 Cu-7 Si alloys with and without addition of Al-5 Ti-1 B master alloy.The effects of Si content on grain growth and the solute-suppressed nucleati...In situ synchrotron X-radiography was carried out on Al-13 Cu and Al-13 Cu-7 Si alloys with and without addition of Al-5 Ti-1 B master alloy.The effects of Si content on grain growth and the solute-suppressed nucleation zone(SSNZ)were quantitatively studied.The average grain size can be refined to 164μm of Al-13 Cu alloy inoculated by Al-5 Ti-1B.After addition of 7%Si content,a large number of TiB 2 sites in the melt lost the inoculating ability due to"Si poisoning."The radius of the dendrite tip curvature of Al-13 Cu is more than two times as large as that of Al-13 Cu-7 Si.The sharper tip is able to disperse the solute more effectively and thus grains can grow more rapidly.This causes that the dendrite arm growth rate with addition of 7%Si solute is about 2.6 times that of no Si addition.In addition,the solute enrichment in the SSNZ of Al-13 Cu is faster,and the area change of SSNZ is slower than that of Al-13 Cu-7 Si.Thus more nucleation sites in the SSNZ cannot be activated with addition of Si.This study will shed light on the understanding of Si poisoning in casting Al-Cu-Si alloys.展开更多
文摘The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue crack initiation than the matrix at lower stress.
文摘Al-4. 5Cu-5Pb alloy was prepared by sand and chill casting. The same alloy was also spray deposited at a gas pressure of 1.6 MPa. The microstructural features exhibit a coarse to fine dendritic morphology for sand and chill cast alloys. Equiaxed grains were observed for spray formed alloys. Wear testing employing a pin-on-disc type set-up, reveals considerably lower wear of spray deposited alloy compared to that of chill and sand cast alloys. The morphological features of wear track on specimen and debris indicated a mixed oxidative-cum-adhesive wear mechanisms for these alloys tested in the present investigation. (Edited author abstract) 36 Refs.
基金supported by the GDAS’Project of Science and Technology Development(No.2020GDASYL-20200103140)the Fundamental and Applied Fundamental Research Foundation of Guangdong Province(No.2020B1515120065)the National Natural Science Foundation of China(No.U1832183)。
文摘In situ synchrotron X-radiography was carried out on Al-13 Cu and Al-13 Cu-7 Si alloys with and without addition of Al-5 Ti-1 B master alloy.The effects of Si content on grain growth and the solute-suppressed nucleation zone(SSNZ)were quantitatively studied.The average grain size can be refined to 164μm of Al-13 Cu alloy inoculated by Al-5 Ti-1B.After addition of 7%Si content,a large number of TiB 2 sites in the melt lost the inoculating ability due to"Si poisoning."The radius of the dendrite tip curvature of Al-13 Cu is more than two times as large as that of Al-13 Cu-7 Si.The sharper tip is able to disperse the solute more effectively and thus grains can grow more rapidly.This causes that the dendrite arm growth rate with addition of 7%Si solute is about 2.6 times that of no Si addition.In addition,the solute enrichment in the SSNZ of Al-13 Cu is faster,and the area change of SSNZ is slower than that of Al-13 Cu-7 Si.Thus more nucleation sites in the SSNZ cannot be activated with addition of Si.This study will shed light on the understanding of Si poisoning in casting Al-Cu-Si alloys.