Transmission electron microscopy(TEM),scanning electron microscopy(SEM),hardness tests and tensile tests were performed to investigate the effect of aging on microstructure and mechanical properties of forged Al-4.4Cu...Transmission electron microscopy(TEM),scanning electron microscopy(SEM),hardness tests and tensile tests were performed to investigate the effect of aging on microstructure and mechanical properties of forged Al-4.4Cu-0.7Mg-0.6Si alloy.The results show that the alloy exhibits splendid mechanical properties with an ultimate tensile strength of504MPa and an elongation of10.1%after aging at170°C for16h.With tensile testing temperature increasing to150°C,the strength of the alloy declines slightly to483MPa.Then,the strength drops quickly when temperature reaches over200°C.The high strength of the alloy in peak-aged condition is caused by a considerable amount ofθ'and AlMgSiCu(Q)precipitates.The relatively stable mechanical properties tested below150°C are mainly ascribed to the stability ofθ'precipitates.The growth ofθ'and Q precipitates and the generation ofθphase lead to a rapid drop of the strength when temperature is over150°C.展开更多
基金Project(51301209)supported by the National Natural Science Foundation of China
文摘Transmission electron microscopy(TEM),scanning electron microscopy(SEM),hardness tests and tensile tests were performed to investigate the effect of aging on microstructure and mechanical properties of forged Al-4.4Cu-0.7Mg-0.6Si alloy.The results show that the alloy exhibits splendid mechanical properties with an ultimate tensile strength of504MPa and an elongation of10.1%after aging at170°C for16h.With tensile testing temperature increasing to150°C,the strength of the alloy declines slightly to483MPa.Then,the strength drops quickly when temperature reaches over200°C.The high strength of the alloy in peak-aged condition is caused by a considerable amount ofθ'and AlMgSiCu(Q)precipitates.The relatively stable mechanical properties tested below150°C are mainly ascribed to the stability ofθ'precipitates.The growth ofθ'and Q precipitates and the generation ofθphase lead to a rapid drop of the strength when temperature is over150°C.