The effect of Li(2.0 wt%)addition on mechanical properties and ageing precipitation behavior of Al-3.0 Mg 0.5 Si was investigated by tensile test,dynamic elasticity modulus test,scanning electron microscopy(SEM),trans...The effect of Li(2.0 wt%)addition on mechanical properties and ageing precipitation behavior of Al-3.0 Mg 0.5 Si was investigated by tensile test,dynamic elasticity modulus test,scanning electron microscopy(SEM),transmission electron microscopy(TEM)and high-resolution transmission electron microscopy(HRTEM)images.The results show that the tensile strength of the Li-containing alloy can be significantly improved;however,the ductility is sharply decreased and the fracture mechanism changes from ductile fracture to intergranular fracture.The elasticity modulus of the Li-containing alloy increases by 11.6%compared with the base alloy.The microstructure observation shows that the Li addition can absolutely change the precipitation behavior of the base alloy,andδ′-Al_(3)Li phase becomes the main precipitates.Besides,β′′-Mg_(2)Si andδ′-Al_(3)Li dual phases precipitation can be visibly observed at 170℃ ageing for 100 h,although the quantity ofδ′-Al_(3)Li phase is more thanβ′′-Mg_(2)Si phase.The width of the precipitate-free zone(PFZ)of the Li-containing alloy is much wider at the over-ageing state than the base alloy,which has a negative impact on the ductile and results in the decrease of elongation.展开更多
ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that...ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.展开更多
Transmission electron microscopy(TEM),scanning electron microscopy(SEM),hardness tests and tensile tests were performed to investigate the effect of aging on microstructure and mechanical properties of forged Al-4.4Cu...Transmission electron microscopy(TEM),scanning electron microscopy(SEM),hardness tests and tensile tests were performed to investigate the effect of aging on microstructure and mechanical properties of forged Al-4.4Cu-0.7Mg-0.6Si alloy.The results show that the alloy exhibits splendid mechanical properties with an ultimate tensile strength of504MPa and an elongation of10.1%after aging at170°C for16h.With tensile testing temperature increasing to150°C,the strength of the alloy declines slightly to483MPa.Then,the strength drops quickly when temperature reaches over200°C.The high strength of the alloy in peak-aged condition is caused by a considerable amount ofθ'and AlMgSiCu(Q)precipitates.The relatively stable mechanical properties tested below150°C are mainly ascribed to the stability ofθ'precipitates.The growth ofθ'and Q precipitates and the generation ofθphase lead to a rapid drop of the strength when temperature is over150°C.展开更多
The effects of addition of minor amount of(0.5 wt.%) antimony(Sb) or gadolinium(Gd) and combined addition of Sb and Gd(0.5 wt.%,respectively) on the hot tearing susceptibility(HTS) of Mg-5Al-3Ca alloy were investigate...The effects of addition of minor amount of(0.5 wt.%) antimony(Sb) or gadolinium(Gd) and combined addition of Sb and Gd(0.5 wt.%,respectively) on the hot tearing susceptibility(HTS) of Mg-5Al-3Ca alloy were investigated experimentally using a “T-shaped” hot tearing measuring system. Various solidification parameters of the alloys were measured and calculated through thermal analysis experiments. The microstructure, grain size, and morphology of the crack zone were characterized by scanning electron microscopy and electron backscatter diffraction, and the crystal phases of the alloys were analyzed by X-ray diffraction and energy-dispersive X-ray spectroscopy. The results showed that the addition of 0.5 wt.% Gd resulted in the increase in the vulnerable temperature range(Tv) and reduced the eutectic structure content that could participate in feeding, thereby improving the HTS of the alloy. However, addition of 0.5 wt.% Sb or combined addition of Gd and Sb(0.5 wt.%, respectively) to the Mg-5Al-3Ca alloy shortened the Tvand improved the skeleton strength of the alloy, thereby reducing HTS. Moreover, significantly refined structure of Mg-5Al-3Ca-0.5Gd-0.5Sb alloy improved the feeding ability of the eutectic structure, thus the alloy exhibited the lowest HTS.展开更多
The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A d...The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A dense dispersion of disc-like Ca2Mg6Zn3 precipitates are formed in Mg-8Zn-4Al-1Ca alloy aged at 160 ℃ for 16 h. In addition, the lattice distortions, honeycomb-looking Moir＆#233; fringes, edge dislocations and dislocation loop also exist in the microstructure. The precipitates of alloy aged at 160 ℃ for 48 h are coarse disc-like and fine dispersed grainy. When the alloy is subjected to aging at 160 ℃ for 227 h, the microstructure consists of numerous MgZn2 precipitates and Ca2Mg6Zn3 precipitates. All the analyses show that Ca is a particularly effective trace addition in improving the age-hardening and postponing the formation of MgZn2 precipitates in Mg-8Zn-4Al alloy aged at 160 ℃.展开更多
Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure o...Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure of master alloy and its grain refining effect on Al-7Si alloy were investigated by means of OM,XRD and SEM.Experimental results show that,the size of Al3Ti particles presented in Al-3Ti-1B master alloys increases with the increase of reaction temperature and decreases with the increase of cooling rate.The grain refining efficiency of Al-3Ti-1B master alloy on Al-7Si alloy is mainly attributed to heterogeneous nucleation of Al3Ti particles,and the morphology ofα(Al)changes from coarse dendritic to fine equiaxed.As a result,Al-3Ti-1B master alloy is prepared by permanent mold,and holding at 800 ℃for 30min,which has better grain refining performance on Al-7Si alloy.展开更多
The strength of traditional Al-Mg alloys is relatively low because it mainly relies on solid solution strengthening.Adding a third component to form precipitation can improve their strength,but it usually leads to hig...The strength of traditional Al-Mg alloys is relatively low because it mainly relies on solid solution strengthening.Adding a third component to form precipitation can improve their strength,but it usually leads to high-stress corrosion cracking(SCC)sensitivity due to the formation of high-density precipitates at grain boundaries(GBs).So far,it is still challenging to improve the strength of Al-Mg alloys without re-ducing SCC resistance.Herein,a nanostructured Al-5Mg-3 Zn alloy with a good yield strength of 336 MPa and good elongation was successfully produced.By dynamic plastic deformation and appropriate anneal-ing treatment,near-equiaxed nanograins were introduced in the nanostructured Al-5Mg-3 Zn alloy with a high proportion(71%)of the low-angle grain boundary.TEM statistical investigations show that the pre-cipitation of active T’phase at GBs has been greatly suppressed in the nanostructured Al-5Mg-3 Zn alloy at sensitized conditions,and the area fraction of GB precipitates is reduced from 72%to 21%,which sig-nificantly decreases the SCC susceptibility.This study provides guidance for developing advanced Al-Mg alloy with high SCC resistance.展开更多
基金Project(2016YFB0300802)supported by the National Key Research and Development Program of China。
文摘The effect of Li(2.0 wt%)addition on mechanical properties and ageing precipitation behavior of Al-3.0 Mg 0.5 Si was investigated by tensile test,dynamic elasticity modulus test,scanning electron microscopy(SEM),transmission electron microscopy(TEM)and high-resolution transmission electron microscopy(HRTEM)images.The results show that the tensile strength of the Li-containing alloy can be significantly improved;however,the ductility is sharply decreased and the fracture mechanism changes from ductile fracture to intergranular fracture.The elasticity modulus of the Li-containing alloy increases by 11.6%compared with the base alloy.The microstructure observation shows that the Li addition can absolutely change the precipitation behavior of the base alloy,andδ′-Al_(3)Li phase becomes the main precipitates.Besides,β′′-Mg_(2)Si andδ′-Al_(3)Li dual phases precipitation can be visibly observed at 170℃ ageing for 100 h,although the quantity ofδ′-Al_(3)Li phase is more thanβ′′-Mg_(2)Si phase.The width of the precipitate-free zone(PFZ)of the Li-containing alloy is much wider at the over-ageing state than the base alloy,which has a negative impact on the ductile and results in the decrease of elongation.
基金Funded by the National Natural Science Foundation of China(No.51401155)the School Foundation(No.XAGDXJJ1012)The Open Fund of Shaanxi Key Laboratory of Photoelectric Functional Materials and Devices(No.ZSKJ201416)
文摘ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.
基金Project(51301209)supported by the National Natural Science Foundation of China
文摘Transmission electron microscopy(TEM),scanning electron microscopy(SEM),hardness tests and tensile tests were performed to investigate the effect of aging on microstructure and mechanical properties of forged Al-4.4Cu-0.7Mg-0.6Si alloy.The results show that the alloy exhibits splendid mechanical properties with an ultimate tensile strength of504MPa and an elongation of10.1%after aging at170°C for16h.With tensile testing temperature increasing to150°C,the strength of the alloy declines slightly to483MPa.Then,the strength drops quickly when temperature reaches over200°C.The high strength of the alloy in peak-aged condition is caused by a considerable amount ofθ'and AlMgSiCu(Q)precipitates.The relatively stable mechanical properties tested below150°C are mainly ascribed to the stability ofθ'precipitates.The growth ofθ'and Q precipitates and the generation ofθphase lead to a rapid drop of the strength when temperature is over150°C.
基金financial support from Joint Research Fund Liaoning-Shenyang National Laboratory for Materials Science (2019JH3/30100014)Liaoning Bai Qian Wan Talents Program. Liaoning Revitalization Talents Program (Nos. XLYC1807021 and 1907007)+2 种基金High Level Innovation Team of Liaoning Province(XLYC1908006)Project of Liaoning Education Department(Nos. LQGD2019002, and LJGD2020008)Liaoning Nature Fund Guidance Plan (No. 2019-ZD-0210)。
文摘The effects of addition of minor amount of(0.5 wt.%) antimony(Sb) or gadolinium(Gd) and combined addition of Sb and Gd(0.5 wt.%,respectively) on the hot tearing susceptibility(HTS) of Mg-5Al-3Ca alloy were investigated experimentally using a “T-shaped” hot tearing measuring system. Various solidification parameters of the alloys were measured and calculated through thermal analysis experiments. The microstructure, grain size, and morphology of the crack zone were characterized by scanning electron microscopy and electron backscatter diffraction, and the crystal phases of the alloys were analyzed by X-ray diffraction and energy-dispersive X-ray spectroscopy. The results showed that the addition of 0.5 wt.% Gd resulted in the increase in the vulnerable temperature range(Tv) and reduced the eutectic structure content that could participate in feeding, thereby improving the HTS of the alloy. However, addition of 0.5 wt.% Sb or combined addition of Gd and Sb(0.5 wt.%, respectively) to the Mg-5Al-3Ca alloy shortened the Tvand improved the skeleton strength of the alloy, thereby reducing HTS. Moreover, significantly refined structure of Mg-5Al-3Ca-0.5Gd-0.5Sb alloy improved the feeding ability of the eutectic structure, thus the alloy exhibited the lowest HTS.
基金Project(51141007)supported by the National Natural Science Foundation of ChinaProject(E2013501096)supported by Hebei Province Natural Science Foundation,China
文摘The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A dense dispersion of disc-like Ca2Mg6Zn3 precipitates are formed in Mg-8Zn-4Al-1Ca alloy aged at 160 ℃ for 16 h. In addition, the lattice distortions, honeycomb-looking Moir＆#233; fringes, edge dislocations and dislocation loop also exist in the microstructure. The precipitates of alloy aged at 160 ℃ for 48 h are coarse disc-like and fine dispersed grainy. When the alloy is subjected to aging at 160 ℃ for 227 h, the microstructure consists of numerous MgZn2 precipitates and Ca2Mg6Zn3 precipitates. All the analyses show that Ca is a particularly effective trace addition in improving the age-hardening and postponing the formation of MgZn2 precipitates in Mg-8Zn-4Al alloy aged at 160 ℃.
文摘Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure of master alloy and its grain refining effect on Al-7Si alloy were investigated by means of OM,XRD and SEM.Experimental results show that,the size of Al3Ti particles presented in Al-3Ti-1B master alloys increases with the increase of reaction temperature and decreases with the increase of cooling rate.The grain refining efficiency of Al-3Ti-1B master alloy on Al-7Si alloy is mainly attributed to heterogeneous nucleation of Al3Ti particles,and the morphology ofα(Al)changes from coarse dendritic to fine equiaxed.As a result,Al-3Ti-1B master alloy is prepared by permanent mold,and holding at 800 ℃for 30min,which has better grain refining performance on Al-7Si alloy.
基金This research was financially supported by the National Nat-ural Science Foundation of China(Grant No.52171088)the Young Elite Scientists Sponsorship Program by CAST(grant No.2022QNRC001).We thank X.Si for assistance in sample prepara-tion.
文摘The strength of traditional Al-Mg alloys is relatively low because it mainly relies on solid solution strengthening.Adding a third component to form precipitation can improve their strength,but it usually leads to high-stress corrosion cracking(SCC)sensitivity due to the formation of high-density precipitates at grain boundaries(GBs).So far,it is still challenging to improve the strength of Al-Mg alloys without re-ducing SCC resistance.Herein,a nanostructured Al-5Mg-3 Zn alloy with a good yield strength of 336 MPa and good elongation was successfully produced.By dynamic plastic deformation and appropriate anneal-ing treatment,near-equiaxed nanograins were introduced in the nanostructured Al-5Mg-3 Zn alloy with a high proportion(71%)of the low-angle grain boundary.TEM statistical investigations show that the pre-cipitation of active T’phase at GBs has been greatly suppressed in the nanostructured Al-5Mg-3 Zn alloy at sensitized conditions,and the area fraction of GB precipitates is reduced from 72%to 21%,which sig-nificantly decreases the SCC susceptibility.This study provides guidance for developing advanced Al-Mg alloy with high SCC resistance.