The effect of Ce content(0–1.6 wt.%)on the modification of Mg_(2)Si phase in the as-cast Mg-5Al-2Si alloy was investigated.The original Chinese script type Mg_(2)Si phase was refined distinctly and transformed to dis...The effect of Ce content(0–1.6 wt.%)on the modification of Mg_(2)Si phase in the as-cast Mg-5Al-2Si alloy was investigated.The original Chinese script type Mg_(2)Si phase was refined distinctly and transformed to dispersive block shape gradually by adding Ce element.The length of Chinese script type Mg_(2)Si phase was reduced from 110 to 50μm with increasing Ce content to 1.6 wt.%.The results calculated by Pandat software indicated that the added Ce element first combined with Si to form CeSi_(2)phase,which could serve as the heterogeneous nucleation of Mg_(2)Si phase due to the small lattice mismatch of 7.97%.The modification of Mg_(2)Si phase was mainly attributed to the facts that Ce changed the growth steps of Mg_(2)Si phase and CeSi_(2)promoted the nucleation of Mg_(2)Si phase.With increasing Ce content from 0 wt.%to 1.6 wt.%,the YS,UTS and EL at 150℃were improved from 67.7 MPa,91.2 MPa and 1.6%to 84.2 MPa,128 MPa and 7.5%,respectively.展开更多
By adding different amounts of Ti into the electromagnetic stirred Al-18wt.%Mg_(2)Si alloy,the effect of Ti element on the microstructure and mechanical properties of the alloy was studied.The experimental results sho...By adding different amounts of Ti into the electromagnetic stirred Al-18wt.%Mg_(2)Si alloy,the effect of Ti element on the microstructure and mechanical properties of the alloy was studied.The experimental results show that the microstructure is refined after modification with Ti,which is related to the heterogeneous nucleation of TiAl_(3) particles on theα-Al matrix.With the increase of Ti content and holding time after stirring,the primary Mg_(2)Si phase is refined firstly and then coarsened,and correspondingly,the mechanical properties of the alloy show a trend of increasing at first and then decreasing.When the addition of Ti is 0.5wt.%and the holding time is about 20 min,the refinement effect of primary Mg_(2)Si phase is the most significant and the mechanical properties of the alloy are optimal.展开更多
ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that...ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.展开更多
A novel thermal-protective coating has been successfully prepared by CPED process on a cast Al-12%Si alloy with the addition of ZrO2 nano-particles in the electrolyte. The microstructures and phase composition of the ...A novel thermal-protective coating has been successfully prepared by CPED process on a cast Al-12%Si alloy with the addition of ZrO2 nano-particles in the electrolyte. The microstructures and phase composition of the coatings were analyzed by SEM and XRD, and the heat insulation performance and the thermal shock resistance of the coatings were investigated. With ZrO2 nanoparticles addition, the cathode plasma discharge on the coating surface is more obvious than that without ZrO2 nanoparticles addition, the coating is more uniform and compact, and the thickness of the coating increases. Furthermore, the content of Zr and Y elements increases and the degree of crystallization of the coating is more complete. The formation of the solid solution of yttrium stabilized zirconia is promoted by cathode plasma discharge. In addition, the thermal insulation temperature increases as ZrO2 nano-particles are added to the electrolyte. After 1 000 cycles of thermal shock, there was no cracking in the coating surface layer, which indicated that the CPED coating with ZrO2 nanoparticles addition possessed a good thermal shock resistance.展开更多
The effect of different cooling rates(2.7,5.5,17.1,and 57.5℃/s)on the solidification parameters,microstructure,and mechanical properties of Al-15Mg_(2)Si composites was studied.The results showed that a high cooling ...The effect of different cooling rates(2.7,5.5,17.1,and 57.5℃/s)on the solidification parameters,microstructure,and mechanical properties of Al-15Mg_(2)Si composites was studied.The results showed that a high cooling rate refined the Mg_(2)Si particles and changed their morphology to more compacted forms with less microcracking tendency.The average radius and fraction of primary Mg_(2)Si particles decreased from 20μm and 13.5%to about 10μm and 7.3%,respectively,as the cooling rate increased from 2.7 to 57.5℃/s.Increasing the cooling rate also improved the distribution of microconstituents and decreased the grain size and volume fraction of micropores.The mechanical properties results revealed that augmenting the cooling rate from 2.7 to about 57.5℃/s increased the hardness and quality index by 25%and245%,respectively.The high cooling rate also changed the fracture mechanism from a brittle-dominated mode to a high-energy ductile mode comprising extensive dimpled zones.展开更多
The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue cr...The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue crack initiation than the matrix at lower stress.展开更多
基金supported by the Major Science and Technology projects in Qinghai province (2018-GX-A1)Global Frontier Program through the Global Frontier Hybrid Interface Materials (GFHIM) of the National Research Foundation of Korea (NRF) funded by the Ministry of Science, ICT & Future Planning (Grant No. 2013M3A6B1078874)+1 种基金funded by Shanghai Science and Technology Committee (Grant No. 18511109302)the National Natural Science Foundation of China (Grant No. 51825101)
文摘The effect of Ce content(0–1.6 wt.%)on the modification of Mg_(2)Si phase in the as-cast Mg-5Al-2Si alloy was investigated.The original Chinese script type Mg_(2)Si phase was refined distinctly and transformed to dispersive block shape gradually by adding Ce element.The length of Chinese script type Mg_(2)Si phase was reduced from 110 to 50μm with increasing Ce content to 1.6 wt.%.The results calculated by Pandat software indicated that the added Ce element first combined with Si to form CeSi_(2)phase,which could serve as the heterogeneous nucleation of Mg_(2)Si phase due to the small lattice mismatch of 7.97%.The modification of Mg_(2)Si phase was mainly attributed to the facts that Ce changed the growth steps of Mg_(2)Si phase and CeSi_(2)promoted the nucleation of Mg_(2)Si phase.With increasing Ce content from 0 wt.%to 1.6 wt.%,the YS,UTS and EL at 150℃were improved from 67.7 MPa,91.2 MPa and 1.6%to 84.2 MPa,128 MPa and 7.5%,respectively.
基金financially supported by the Science and Technology Development Program of Shouguang(No.2019JH14)the Science and Technology Development Program of Weifang(No.2021GX052)the Natural Science Foundation of Liaoning Province(No.080137)。
文摘By adding different amounts of Ti into the electromagnetic stirred Al-18wt.%Mg_(2)Si alloy,the effect of Ti element on the microstructure and mechanical properties of the alloy was studied.The experimental results show that the microstructure is refined after modification with Ti,which is related to the heterogeneous nucleation of TiAl_(3) particles on theα-Al matrix.With the increase of Ti content and holding time after stirring,the primary Mg_(2)Si phase is refined firstly and then coarsened,and correspondingly,the mechanical properties of the alloy show a trend of increasing at first and then decreasing.When the addition of Ti is 0.5wt.%and the holding time is about 20 min,the refinement effect of primary Mg_(2)Si phase is the most significant and the mechanical properties of the alloy are optimal.
基金Funded by the National Natural Science Foundation of China(No.51401155)the School Foundation(No.XAGDXJJ1012)The Open Fund of Shaanxi Key Laboratory of Photoelectric Functional Materials and Devices(No.ZSKJ201416)
文摘ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.
基金Funded by the Youth Innovation Team of Shaanxi Universities,Shaanxi Key Research and Development Program(No.2018GY-111)Shaanxi Provincial Department of Education Industrialization Cultivation Project(No.17JF009)Yulin Science and Technology Project(Nos.2016-16-4 and 2018-2-30)
文摘A novel thermal-protective coating has been successfully prepared by CPED process on a cast Al-12%Si alloy with the addition of ZrO2 nano-particles in the electrolyte. The microstructures and phase composition of the coatings were analyzed by SEM and XRD, and the heat insulation performance and the thermal shock resistance of the coatings were investigated. With ZrO2 nanoparticles addition, the cathode plasma discharge on the coating surface is more obvious than that without ZrO2 nanoparticles addition, the coating is more uniform and compact, and the thickness of the coating increases. Furthermore, the content of Zr and Y elements increases and the degree of crystallization of the coating is more complete. The formation of the solid solution of yttrium stabilized zirconia is promoted by cathode plasma discharge. In addition, the thermal insulation temperature increases as ZrO2 nano-particles are added to the electrolyte. After 1 000 cycles of thermal shock, there was no cracking in the coating surface layer, which indicated that the CPED coating with ZrO2 nanoparticles addition possessed a good thermal shock resistance.
文摘The effect of different cooling rates(2.7,5.5,17.1,and 57.5℃/s)on the solidification parameters,microstructure,and mechanical properties of Al-15Mg_(2)Si composites was studied.The results showed that a high cooling rate refined the Mg_(2)Si particles and changed their morphology to more compacted forms with less microcracking tendency.The average radius and fraction of primary Mg_(2)Si particles decreased from 20μm and 13.5%to about 10μm and 7.3%,respectively,as the cooling rate increased from 2.7 to 57.5℃/s.Increasing the cooling rate also improved the distribution of microconstituents and decreased the grain size and volume fraction of micropores.The mechanical properties results revealed that augmenting the cooling rate from 2.7 to about 57.5℃/s increased the hardness and quality index by 25%and245%,respectively.The high cooling rate also changed the fracture mechanism from a brittle-dominated mode to a high-energy ductile mode comprising extensive dimpled zones.
基金Project(51971106) supported by the National Natural Science Foundation of ChinaProject(GJJ191094) supported by the Education Department of Jiangxi Province,China+2 种基金Project(PA2019GDZC0096) supported by Fundamental Research Funds for the Central Universities of ChinaProject(2019-MS-171) supported by the Liaoning Natural Science Foundation,ChinaProject supported by Programs for Liaoning Innovative Talents/Groups and Liaoning Distinguished Professors,China。
文摘The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue crack initiation than the matrix at lower stress.