Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure o...Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure of master alloy and its grain refining effect on Al-7Si alloy were investigated by means of OM,XRD and SEM.Experimental results show that,the size of Al3Ti particles presented in Al-3Ti-1B master alloys increases with the increase of reaction temperature and decreases with the increase of cooling rate.The grain refining efficiency of Al-3Ti-1B master alloy on Al-7Si alloy is mainly attributed to heterogeneous nucleation of Al3Ti particles,and the morphology ofα(Al)changes from coarse dendritic to fine equiaxed.As a result,Al-3Ti-1B master alloy is prepared by permanent mold,and holding at 800 ℃for 30min,which has better grain refining performance on Al-7Si alloy.展开更多
The mechanical properties of castings depend on the grain size.There is evidence that titanium and boron(Al-5Ti-1B master alloy)affect the grain size of magnesium alloys.Here,the influence of the addition of 0-1 wt.%o...The mechanical properties of castings depend on the grain size.There is evidence that titanium and boron(Al-5Ti-1B master alloy)affect the grain size of magnesium alloys.Here,the influence of the addition of 0-1 wt.%of Al-5Ti-1B master alloy on the grain size of AZ91 magnesium alloy was investigated.Melting of the alloy was performed in steel and corundum crucibles.To study the effect of cooling rate on grain size,cylindrical samples were cast in steel and fireclay molds.The Al-5Ti-1B master alloy addition did not change the phase composition of the AZ91 alloy.This study demonstrates that the addition of Al-5Ti-1B did not contribute to the grain refinement of the AZ91 alloy,but rather led to its coarsening for samples cast in both the steel and fireclay molds.Increasing the holding time after the addition of the Al-5Ti-1B master alloy from 15 to 110 minutes also did not lead to significant grain coarsening.The mechanical properties of the AZ91 alloy samples slightly improved after Al-5Ti-1B addition.展开更多
文摘Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure of master alloy and its grain refining effect on Al-7Si alloy were investigated by means of OM,XRD and SEM.Experimental results show that,the size of Al3Ti particles presented in Al-3Ti-1B master alloys increases with the increase of reaction temperature and decreases with the increase of cooling rate.The grain refining efficiency of Al-3Ti-1B master alloy on Al-7Si alloy is mainly attributed to heterogeneous nucleation of Al3Ti particles,and the morphology ofα(Al)changes from coarse dendritic to fine equiaxed.As a result,Al-3Ti-1B master alloy is prepared by permanent mold,and holding at 800 ℃for 30min,which has better grain refining performance on Al-7Si alloy.
文摘The mechanical properties of castings depend on the grain size.There is evidence that titanium and boron(Al-5Ti-1B master alloy)affect the grain size of magnesium alloys.Here,the influence of the addition of 0-1 wt.%of Al-5Ti-1B master alloy on the grain size of AZ91 magnesium alloy was investigated.Melting of the alloy was performed in steel and corundum crucibles.To study the effect of cooling rate on grain size,cylindrical samples were cast in steel and fireclay molds.The Al-5Ti-1B master alloy addition did not change the phase composition of the AZ91 alloy.This study demonstrates that the addition of Al-5Ti-1B did not contribute to the grain refinement of the AZ91 alloy,but rather led to its coarsening for samples cast in both the steel and fireclay molds.Increasing the holding time after the addition of the Al-5Ti-1B master alloy from 15 to 110 minutes also did not lead to significant grain coarsening.The mechanical properties of the AZ91 alloy samples slightly improved after Al-5Ti-1B addition.