Recrystallization and grain growth in Mg-4.9Zn-0.7Zr and Mg-4.9Zn-0.9Y-0.7Zr alloys as a function of temperature on deformation were investigated with regards to hot rolling and annealing. The influence of yttrium add...Recrystallization and grain growth in Mg-4.9Zn-0.7Zr and Mg-4.9Zn-0.9Y-0.7Zr alloys as a function of temperature on deformation were investigated with regards to hot rolling and annealing. The influence of yttrium addition on the microstructure was examined by X-ray diffraction （XRD）, optical microscopy （OM）, scanning electron microscopy （SEM）, and transmission electron microscopy （TEM）. The results indicated that yttrium addition promoted nucleation of recrystallization during hot rolling process. The grain size of Mg-4.9Zn-0.7Zr alloy samples grew significantly with annealing temperature （300-400 ℃） and holding time （0-120 min）, while the microstructure of the alloy with yttrium addition remained unchanged and fine. The activation energy of grain boundary migration for Mg-4.9Zn-0.9Y-0.7Zr alloy samples （56.34 kJ/mol） was higher than that for Mg-4.9Zn-0.7Zr （42.66 kJ/mol） owing to the pinning effect of Y-containing particles. The proposed growth models of recrysta/lized grains for the two studied alloys conformed well to E. Robert＇s grain-growth equation. Besides, the ultimate strength and yield strength of the alloys with yttrium addition were improved with good plasticity.展开更多
A new rare earth magnesium alloy(Mg-6 Zn-4 Sm-0.4 Zr, wt.%) was prepared by permanent mould casting. The microstructure and mechanical properties of the alloy sample in as-cast and various heat treatment situations we...A new rare earth magnesium alloy(Mg-6 Zn-4 Sm-0.4 Zr, wt.%) was prepared by permanent mould casting. The microstructure and mechanical properties of the alloy sample in as-cast and various heat treatment situations were characterized with an optical microscope(OM), X-ray diffractometer(XRD), scanning electron microscope(SEM) equipped with energy dispersive spectroscope(EDS), transmission electron microscope(TEM) and mechanical tests at room temperature, respectively. The experimental results show that the as-cast alloy mainly consists of α-Mg, eutectic Mg_2Zn_3, MgZnSm and Mg_(41)Sm_5. These eutectic phases with continuous or semicontinuous morphology principally distribute along grain boundaries. Almost all the eutectic compounds dissolve in α-Mg and the grains have no obvious growth trend after optimum solution treatment at 490 °C for 18 h. Meanwhile, the ultimate tensile strength(UTS) of 229 MPa and elongation(EL) to rupture of 9.78% can be achieved through the optimal solution treatment, which increase by 37 MPa and 57.74%, respectively, compared with that of the as-cast alloy. Further aging treatments at 200 °C for different durations lead to the conspicuous increment of mechanical properties and prominent age-hardening response. Peak-aged alloy(treated at 200 °C for 12 h) reveals better mechanical properties(UTS 258 MPa, EL 9.42%, hardness 73.4 HV) compared with the same alloy treated in other aging conditions, which is mainly ascribed to precipitated Mg_2Zn_3 and MgZn_2 phases. Fracture analysis demonstrates that the as-cast alloy belongs to inter-granular and cleavage fracture patterns, while the solutionized alloy(treated at 490 °C for 18 h) reveals trans-granular and quasi-cleavage fracture modes. For the peak-aged alloy, the fracture pattern obeys the mixture of trans-granular and cleavage modes.展开更多
The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue cr...The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue crack initiation than the matrix at lower stress.展开更多
In this work,a new(Y,Gd)H_(2) precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that t...In this work,a new(Y,Gd)H_(2) precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that the as-cast alloy contains α-Mg,Mg_(24)(Gd,Y)_(5),and(Y,Gd)H_(2) phase.The(Y,Gd)H_(2) phase usually forms near the eutectic phase Mg_(24)(Gd,Y)_(5) or in the α-Mg grains,displaying a rectangle-shape.The Mg_(24)(Gd,Y)_(5) and(Y,Gd)H_(2) phases crystalize in bcc and fcc structure,respectively,and the(Y,Gd)H_(2) phase has a semi-coherent relationship with α-Mg matrix.The thermodynamics calculation results reveal that the hydrogen dissolved in the melt leads to the formation of hydrides.It is also found that the(Y,Gd)H_(2) hydride can form directly from the liquid phase during solidification.Additionally,it can precipitate by the decomposition of Mg_(24)(Gd,Y)_(5) phase due to absorbing hydrogen from the remaining melt.展开更多
基金the Science and Technology Program of Hunan Province (2004GK1008-2)
文摘Recrystallization and grain growth in Mg-4.9Zn-0.7Zr and Mg-4.9Zn-0.9Y-0.7Zr alloys as a function of temperature on deformation were investigated with regards to hot rolling and annealing. The influence of yttrium addition on the microstructure was examined by X-ray diffraction （XRD）, optical microscopy （OM）, scanning electron microscopy （SEM）, and transmission electron microscopy （TEM）. The results indicated that yttrium addition promoted nucleation of recrystallization during hot rolling process. The grain size of Mg-4.9Zn-0.7Zr alloy samples grew significantly with annealing temperature （300-400 ℃） and holding time （0-120 min）, while the microstructure of the alloy with yttrium addition remained unchanged and fine. The activation energy of grain boundary migration for Mg-4.9Zn-0.9Y-0.7Zr alloy samples （56.34 kJ/mol） was higher than that for Mg-4.9Zn-0.7Zr （42.66 kJ/mol） owing to the pinning effect of Y-containing particles. The proposed growth models of recrysta/lized grains for the two studied alloys conformed well to E. Robert＇s grain-growth equation. Besides, the ultimate strength and yield strength of the alloys with yttrium addition were improved with good plasticity.
基金financially supported by the National Nature Science Foundations of China(51464032)National Basic Research Program of China(Grant No.2010CB635106)
文摘A new rare earth magnesium alloy(Mg-6 Zn-4 Sm-0.4 Zr, wt.%) was prepared by permanent mould casting. The microstructure and mechanical properties of the alloy sample in as-cast and various heat treatment situations were characterized with an optical microscope(OM), X-ray diffractometer(XRD), scanning electron microscope(SEM) equipped with energy dispersive spectroscope(EDS), transmission electron microscope(TEM) and mechanical tests at room temperature, respectively. The experimental results show that the as-cast alloy mainly consists of α-Mg, eutectic Mg_2Zn_3, MgZnSm and Mg_(41)Sm_5. These eutectic phases with continuous or semicontinuous morphology principally distribute along grain boundaries. Almost all the eutectic compounds dissolve in α-Mg and the grains have no obvious growth trend after optimum solution treatment at 490 °C for 18 h. Meanwhile, the ultimate tensile strength(UTS) of 229 MPa and elongation(EL) to rupture of 9.78% can be achieved through the optimal solution treatment, which increase by 37 MPa and 57.74%, respectively, compared with that of the as-cast alloy. Further aging treatments at 200 °C for different durations lead to the conspicuous increment of mechanical properties and prominent age-hardening response. Peak-aged alloy(treated at 200 °C for 12 h) reveals better mechanical properties(UTS 258 MPa, EL 9.42%, hardness 73.4 HV) compared with the same alloy treated in other aging conditions, which is mainly ascribed to precipitated Mg_2Zn_3 and MgZn_2 phases. Fracture analysis demonstrates that the as-cast alloy belongs to inter-granular and cleavage fracture patterns, while the solutionized alloy(treated at 490 °C for 18 h) reveals trans-granular and quasi-cleavage fracture modes. For the peak-aged alloy, the fracture pattern obeys the mixture of trans-granular and cleavage modes.
文摘The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue crack initiation than the matrix at lower stress.
基金financially supported by the Key Project of Equipment Pre-research Field Fund under Grant No.61409230407the National Natural Science Foundation of China(NSFC)under Grant No.51601054the Central Government Guides Local Science and Technology Development Fund Projects under Grant No.206Z1005G。
文摘In this work,a new(Y,Gd)H_(2) precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that the as-cast alloy contains α-Mg,Mg_(24)(Gd,Y)_(5),and(Y,Gd)H_(2) phase.The(Y,Gd)H_(2) phase usually forms near the eutectic phase Mg_(24)(Gd,Y)_(5) or in the α-Mg grains,displaying a rectangle-shape.The Mg_(24)(Gd,Y)_(5) and(Y,Gd)H_(2) phases crystalize in bcc and fcc structure,respectively,and the(Y,Gd)H_(2) phase has a semi-coherent relationship with α-Mg matrix.The thermodynamics calculation results reveal that the hydrogen dissolved in the melt leads to the formation of hydrides.It is also found that the(Y,Gd)H_(2) hydride can form directly from the liquid phase during solidification.Additionally,it can precipitate by the decomposition of Mg_(24)(Gd,Y)_(5) phase due to absorbing hydrogen from the remaining melt.