A set of uniaxial tensile creep tests at different pre-deformations, aging temperatures and stress levels were carried out for Al-Li-S4 alloy, and the creep behavior and the effects of pre-deformation on mechanical pr...A set of uniaxial tensile creep tests at different pre-deformations, aging temperatures and stress levels were carried out for Al-Li-S4 alloy, and the creep behavior and the effects of pre-deformation on mechanical properties and microstructures were determined under basic thermodynamics conditions of aging forming. The results show that pre-deformation shortens the time of primary creep and raises the second steady-state creep rate. Then, the total creep strain is greater, but in the range of test parameters it is still smaller than that without pre-deformation. In addition, transmission electron microscopy（TEM） observation shows that pre-deformation promotes the formation of T1 phase and θ′ phase and makes them distribute more dispersively, while inhibits the generation of δ′ phase, which leads to the improvement of mechanical properties of the alloy. A unified constitutive model reflecting the effects of aging mechanism, stress levels and different pre-deformations was established. The fitting results agree with the experimental data well.展开更多
Creep age forming techniques have been widely used in aerospace industries. In this study, we investigated the effect of aging temperature(143 °C-163 °C) on the creep behavior of Al-Li-S4 aluminum alloy and ...Creep age forming techniques have been widely used in aerospace industries. In this study, we investigated the effect of aging temperature(143 °C-163 °C) on the creep behavior of Al-Li-S4 aluminum alloy and their mechanical properties at room temperature. The mechanical properties were tested by tensile testing, and the microstructural evolution at different aging temperatures was examined by transmission electron microscopy. Results show that the creep strains and the room-temperature mechanical properties after creep aging increase with the aging temperature. As the aging temperature increases, the creep strain increases from 0.018% at 143 °C to 0.058% at 153 °C, and then to 0.094% at 163 °C. Within 25 h aging, the number of creep steps increases and the duration time of the same steps is shortened with the growth of aging temperatures. Therefore, the increase in aging temperatures accelerates the progress of the entire creep. Two main strengthening precipitates θ′(Al2 Cu) and T1(Al2 Cu Li) phases were characterized. This work indicates that the creep strain and mechanical properties of Al-Li-S4 alloys can be improved by controlling aging temperatures.展开更多
基金Project(2014CB046602)supported by the National Basic Research Program of ChinaProject(51235010)supported by the National Natural Science Foundation of China
文摘A set of uniaxial tensile creep tests at different pre-deformations, aging temperatures and stress levels were carried out for Al-Li-S4 alloy, and the creep behavior and the effects of pre-deformation on mechanical properties and microstructures were determined under basic thermodynamics conditions of aging forming. The results show that pre-deformation shortens the time of primary creep and raises the second steady-state creep rate. Then, the total creep strain is greater, but in the range of test parameters it is still smaller than that without pre-deformation. In addition, transmission electron microscopy（TEM） observation shows that pre-deformation promotes the formation of T1 phase and θ′ phase and makes them distribute more dispersively, while inhibits the generation of δ′ phase, which leads to the improvement of mechanical properties of the alloy. A unified constitutive model reflecting the effects of aging mechanism, stress levels and different pre-deformations was established. The fitting results agree with the experimental data well.
基金Project(2017YFB0306300)supported by National key R&D Program of ChinaProject(zzyikt2015-05)supported by the Project of State Key Laboratory of High Performance Complex Manufacture,China。
文摘Creep age forming techniques have been widely used in aerospace industries. In this study, we investigated the effect of aging temperature(143 °C-163 °C) on the creep behavior of Al-Li-S4 aluminum alloy and their mechanical properties at room temperature. The mechanical properties were tested by tensile testing, and the microstructural evolution at different aging temperatures was examined by transmission electron microscopy. Results show that the creep strains and the room-temperature mechanical properties after creep aging increase with the aging temperature. As the aging temperature increases, the creep strain increases from 0.018% at 143 °C to 0.058% at 153 °C, and then to 0.094% at 163 °C. Within 25 h aging, the number of creep steps increases and the duration time of the same steps is shortened with the growth of aging temperatures. Therefore, the increase in aging temperatures accelerates the progress of the entire creep. Two main strengthening precipitates θ′(Al2 Cu) and T1(Al2 Cu Li) phases were characterized. This work indicates that the creep strain and mechanical properties of Al-Li-S4 alloys can be improved by controlling aging temperatures.