Porous TiFe_(2) intermetallic compound fabricated via elemental powder reactive synthesis

Porous intermetallics show potential in the field of filtration and separation as well as in the field of catalysis.Herein,porous Ti Fe2intermetallics were fabricated by the reactive synthesis of elemental powders.The phase transformation and pore formation of porous TiFe2intermetallics were investigated,and its corrosion behavior and hydrogen evolution reaction(HER)performance in alkali solution were studied.Porous TiFe2intermetallics with porosity in the range of 34.4%-56.4%were synthesized by the diffusion reaction of Ti and Fe elements,and the pore formation of porous TiFe2intermetallic compound is the result of a combination of the bridging effect and the Kirkendall effect.The porous TiFe2samples exhibit better corrosion resistance compared with porous 316L stainless steel,which is related to the formation of uniform nanosheets on the surface that hinder further corrosion,and porous TiFe2electrode shows the overpotential of 220.6 and 295.6 mV at 10 and 100 mA·cm-2,suggesting a good catalytic performance.The synthesized porous Fe-based intermetallic has a controllable pore structure as well as excellent corrosion resistance,showing its potential in the field of filtration and separation.

Corrosion resistance of Mg-Al-LDH steam coating on AZ80 Mg alloy:Effects of citric acid pretreatment and intermetallic compounds

In this study,the effects of intermetallic compounds(Mg_(17)Al_(12)and Al_(8)Mn_(5))on the Mg-Al layered double hydroxide(LDH)formation mechanism and corrosion behavior of an in-situ LDH/Mg(OH)_(2)steam coatings on AZ80 Mg alloy were investigated.Citric acid(CA)was used to activate the alloy surface during the pretreatment process.The alloy was first pretreated with CA and then subjected to a hydrothermal process using ultrapure water to produce Mg-Al-LDH/Mg(OH)_(2)steam coating.The effect of different time of acid pretreatment on the activation of the intermetallic compounds was investigated.The microstructure and elemental composition of the obtained coatings were analyzed using FE-SEM,EDS,XRD and FT-IR.The corrosion resistance of the coated samples was evaluated using different techniques,i.e.,potentiodynamic polarization(PDP),electrochemical impedance spectrum(EIS)and hydrogen evolution test.The results indicated that the CA pretreatment significantly influenced the activity of the alloy surface by exposing the intermetallic compounds.The surface area fraction of Mg_(17)Al_(12)and Al_(8)Mn_(5)phases on the surface of the alloy was significantly higher after the CA pretreatment,and thus promoted the growth of the subsequent Mg-Al-LDH coatings.The CA pretreatment for 30 s resulted in a denser and thicker LDH coating.Increase in the CA pretreatment time significantly led to the improvement in corrosion resistance of the coated AZ80 alloy.The corrosion current density of the coated alloy was lower by three orders of magnitude as compared to the uncoated alloy.

An innovative joint interface design for reducing intermetallic compounds and improving joint strength of thick plate friction stir welded Al/Mg joints

Friction stir welding of dissimilar Al/Mg thick plates still faces severe challenges, such as poor formability, formation of thick intermetallic compounds, and low joint strength. In this work, two joint configurations, namely inclined butt(conventional butt) and serrated interlocking(innovative butt), are proposed for improving weld formation and joint quality. The results show that a continuous and straight intermetallic compound layer appears at the Mg side interface in conventional butt joint, and the maximum average thickness reaches about 60.1 μm.Additionally, the Mg side interface also partially melts, forming a eutectic structure composed of Mg solid solution and Al_(12)Mg_(17) phase.For the innovative butt joint, the Mg side interface presents the curved interlocking feature, and intermetallic compounds can be reduced to less than 10 μm. The joint strength of innovative butt joint is more than three times that of conventional butt joint. This is due to the interlocking effect and thin intermetallic compounds in the innovative joint.

Brittle and ductile characteristics of intermetallic compounds in magnesium alloys: A large-scale screening guided by machine learning

In the present work,we have employed machine learning(ML)techniques to evaluate ductile-brittle(DB)behaviors in intermetallic compounds(IMCs)which can form magnesium(Mg)alloys.This procedure was mainly conducted by a proxy-based method,where the ratio of shear(G)/bulk(B)moduli was used as a proxy to identify whether the compound is ductile or brittle.Starting from compounds information(composition and crystal structure)and their moduli,as found in open databases(AFLOW),ML-based models were built,and those models were used to predict the moduli in other compounds,and accordingly,to foresee the ductile-brittle behaviors of these new compounds.The results reached in the present work showed that the built models can effectively catch the elastic moduli of new compounds.This was confirmed through moduli calculations done by density functional theory(DFT)on some compounds,where the DFT calculations were consistent with the ML prediction.A further confirmation on the reliability of the built ML models was considered through relating between the DB behavior in MgBe_(13) and MgPd_(2),as evaluated by the ML-predicted moduli,and the nature of chemical bonding in these two compounds,which in turn,was investigated by the charge density distribution(CDD)and electron localization function(ELF)obtained by DFT methodology.The ML-evaluated DB behaviors of the two compounds was also consistent with the DFT calculations of CDD and ELF.These findings and confirmations gave legitimacy to the built model to be employed in further prediction processes.Indeed,as examples,the DB characteristics were investigated in IMCs that might from in three Mg alloy series,involving AZ,ZX and WE.

PtCoNi ternary intermetallic compounds anchored on Co,Ni and N co-doped mesoporous carbon:Synergetic effect between PtCoNi nanoparticles and doped mesoporous carbon promotes the catalytic activity

Highly active and robust electrocatalysts are desired for proton exchange membrane fuel cells.Pt-based intermetallic compounds(IMCs) have been recognized as one of the most promising low-platinum catalysts for fuel cells(FCs).Herein,we report a high-performance IMCs by anchoring ordered PtCoNi ternary nanoparticles on the N,Co and Ni co-doped dodecahedral mesoporous carbon(DMC).While the introduced Co and Ni participate in the formation of PtCoNi IMCs,some of them are doped in the mesoporous carbon and coordinated by N to form Co-N_(y)/Ni-N_(z)dual active centers,which further enhances the electrocatalytic activity towards oxygen reduction reaction.Moreover,the addition of Ni results in a negative shift of the d-band center of Pt as compared to the Pt/DMC and Pt_(3)Co/DMC,making it easier to adsorb oxygen on the surface.As expected,our optimal sample Pt_(3)Co_(0.7)Ni_(0.3)/DMC exhibits excellent performance with mass activity and specific activity of 1.32 A mgPt-1and 1.98 mA cm^(-2)at 0.9 V,which are 7.33and 6.19 times that of commercial Pt/C,respectively.The Pt_(3)Co_(0.7)Ni_(0.3)/DMC also reveals much better cathodic performance in an H2-air single fuel cell than commercial Pt/C catalyst with a power density of0.802 W cm^(-2).This work provides critical sights into constructing efficient catalysts by ternary intermetallic strategy and synergetic effect between active components and support.

Effect of Si on growth kinetics of intermetallic compounds during reaction between solid iron and molten aluminum

The effect of Si on the growth kinetics of intermetallic compounds during the reaction of solid iron and molten aluminum was investigated with a scanning electron microscope coupled with an energy dispersive X-ray spectroscope, and hot-dip aluminized experiments. The results show that the intermetallic layer is composed of major Fe2Al5 and minor FeAl3. The Al-Fe-Si ternary phase, rl/rg, is formed in the Fe2Al5 layer. The tongue-like morphology of the Fe2Als layer becomes less distinct and disappears finally as the content of Si in aluminum bath increases. Si in the bath improves the prohibiting ability to the growth of Fe2Als and FeAl3. When the contents of Si are 0, 0.5%, 1.0%, 1.5%, 2.0% and 3.0%, the activation energies of Fe2Al5 are evaluated to be 207, 186, 169, 168, 167 and 172 kJ/mol, respectively. The reduction of the activation energy might result from the lattice distortion caused by Si atom penetrating into the Fe2Al5 phase. When Si atom occupies the vacancy site, it blocks easy diffusion path and results in the disappearance of tongue-like morphology.

Effect of ultrasonic vibration on Fe-containing intermetallic compounds of hypereutectic Al-Si alloys with high Fe content

The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing compounds in the alloys produced by conventional casting process are detrimental to the strength of matrix. The effect of ultrasonic vibration （USV） on the morphology change of Fe-containing intermetallic compounds in the hypereutectic Al-17Si-xFe （x=2, 3, 4, 5） alloys was systematically studied. The results show that, the Fe-containing intermetallic compounds are mainly composed of long needle-like β-Al5FeSi phase with a small amount of plate-like δ-Al4FeSi2 phase in Al-17Si-2Fe alloy produced by conventional casting process. With the increase of Fe content from 2% to 5% in the alloys, the amount of plate-like or coarse needle-like δ-Al4FeSi2 phase increases while the amount of long needle-like β-Al5FeSi phases decreases. In Al-17Si-5Fe alloy, the Fe-containing intermetallic compounds exist mainly as coarse needle-like δ-Al4FeSi2 phase. After USV treatment, the Fe-containing compounds in the Al-17Si-xFe alloys are refined and exist mainly as δ-Al4FeSi2 particles, with average grain size ranging from 26 μm to 37 μm, and only a small amount of β-Al5FeSi phases remain. The mechanism of USV on the morphology of Fe-containing intermetallic compounds was also discussed.

Effects of Fe-Al intermetallic compounds on interfacial bonding of clad materials

The growth of intermetallic compounds at the interface between solid Al and Fe and the effects of intermetallic compound layers on the interfacial bonding of clad materials were investigated. The results showed that the interface between the solid Fe and Al formed by heat-treatment consisted of Fe2Al5 and FeAl3 intermetallic compound layers, which deteriorated the interfacial bonding strength. Fractures occurred in the intermetallic compound layer during the shear testing. The location of the fracture depended on the defects of microcracks or voids in the intermetallic compound layers. The microcracks in the intermetallic compound layer were caused by the mismatch of thermal expansion coefficients of materials during cooling, and the voids were consistent with the Kirkendall effect. The work will lay an important foundation for welding and joining of aluminum and steel, especially for fabrication of Al-Fe clad materials.

Effects of heat treatment on the intermetallic compounds and mechanical properties of the stainless steel 321–aluminum 1230 explosive-welding interface

The effects of heat treatment on the microstructure and mechanical properties of intermetallic compounds in the interface of stainless steel 321 explosively bonded to aluminum 1230 were investigated in this study. Experimental investigations were performed by optical microscopy, scanning electron microscopy, and microhardness and shear tensile strength testing. Prior to heat treatment, increasing the stand-off distance between samples from 1 to 2.5 mm caused their interface to become wavy and the thickness of intermetallic layers to increase from 3.5 to 102.3 μm. The microhardness increased from HV 766 in the sample prepared at a stand-off distance of 1 mm to HV 927 in the sample prepared at a stand-off distance of 2.5 mm; in addition, the sample strength increased from 103.2 to 214.5 MPa. Heat treatment at 450°C for 6 h increased the thickness of intermetallic compound layers to 4.4 and 118.5 μm in the samples prepared at stand-off distances of 1 and 2.5 mm, respectively. These results indicated that increasing the duration and temperature of heat treatment decreased the microhardness and strength of the interface of explosively welded stainless steel 321-Al 1230 and increased the thickness of the intermetallic region.

Effect of intermetallic compounds on the fracture behavior of dissimilar friction stir welding joints of Mg and Al alloys

Joining Mg to Al is challenging because of the deterioration of mechanical properties caused by the formation of intermetallic compounds(IMCs) at the Mg/Al interface. This study aims to improve the mechanical properties of welded samples by preventing the fracture location at the Mg/Al interface. Friction stir welding was performed to join Mg to Al at different rotational and travel speeds. The microstructure of the welded samples showed the IMCs layers containing Al12Mg17(γ) and Al3Mg2(β) at the welding zone with a thickness(< 3.5 μm). Mechanical properties were mainly affected by the thickness of the IMCs, which was governed by welding parameters. The highest tensile strength was obtained at 600 r/min and 40 mm/min with a welding efficiency of 80%. The specimens could fracture along the boundary at the thermo-mechanically affected zone in the Mg side of the welded joint.

Review of magnetic properties and magnetocaloric effect in the intermetallic compounds of rare earth with low boiling point metals

The magnetocaloric effect （MCE） in many rare earth （RE） based intermetallic compounds has been extensively in- vestigated during the last two decades, not only due to their potential applications for magnetic refrigeration but also for better understanding of the fundamental problems of the materials. This paper reviews our recent progress on studying the magnetic properties and MCE in some binary or ternary intermetallic compounds of RE with low boiling point metal（s） （Zn, Mg, and Cd）. Some of them exhibit promising MCE properties, which make them attractive for low temperature magnetic refrigeration. Characteristics of the magnetic transition, origin of large MCE, as well as the potential application of these compounds are thoroughly discussed. Additionally, a brief review of the magnetic and magnetocaloric properties in the quaternary rare earth nickel boroncarbides RENi2B2C superconductors is also presented.

Twinning in Intermetallic Compounds Are Long Shear Vectors and/or Shuffles Really Necessary?

In this paper the geometric description and general theory of mechanical twinning are reviewed, the twins in general lattices and superlattices are summarized, and the kinetic process by which mechanical twins form is revisited. A case study of mechanical twinning of HfV2+Nb, (cubic) Laves phase, is presented and the synchroshear of selected atomic layers is proposed to explain the physical process of twin formation. If the twins form in this way, then long shear vectors and / or atomicshuffles are not really necessary.

STUDY OF THE EFFECT OF BORON CONTENT ON THE ORDERED EXTENT OF THE Ni_3Al INTERMETALLICS COMPOUND BY AP-FIM

By using AP-FIM the varity of the ordered degree of Ni_3Al with L1_2 structure with B content was studied. The possibility of boron improving ductility was also discussed from bonding between Ni and Al atoms, and antisite defects in Ni_3Al. The extent of ordering is reduced with an increase in boron content and the autisite defects are most obvious for 0.52at.K B-doped sample that has the best ductility. Some results were verified by X-ray diffraction non. The addition of boron not only influences electron environment at grain boundary but also in the interior of Ni_3Al gm ins, the latter is favorable to improve the ductility of Ni_3Al grains.

Remarkably reducing carbon loss and H2 consumption on Ni–Ga intermetallic compounds in deoxygenation of methyl esters to hydrocarbons

Ni–Ga alloy(Ni/Ga atomic ratio of 8),Ni3Ga and Ni5Ga3 intermetallic compounds(IMCs)catalysts were prepared from Ni–Mg-Al-Ga layered double hydroxides(LDHs)for the deoxygenation of methyl esters to hydrocarbons.In the alloy and IMCs,the presence of Ga reduced the surface Ni atom density,and the charge transfer from Ga to Ni increased the electron density of Ni.In the deoxygenation of methyl laurate,the Ni catalyst gave a complete hydrogenolysis of methyl laurate to CH4at 330°C and 3.0 MPa,while the presence of Ga promoted the HDO pathway and suppressed C–C bond hydrogenolysis and methanation.The Ni5Ga3 catalyst exhibited the best desired performance.Even at 400°C,it gave the yield of C11 and C12 hydrocarbons of ~99%,and the selectivity to CH4(SCH4) was only 2.4%.In the deoxygenation of methyl octanoate and methyl palmitate,the Ni5Ga3 catalyst also gave the yield of hydrocarbons above95%.Reactivity evaluation and methyl propionate-TPD and TPSR results indicate that the C–OCH3 bond instead of the O–CH3 one was cleaved on both Ni and bimetallic Ni–Ga catalysts.It is highlighted that methanol,derived from the C–OCH3 bond hydrogenolysis,mainly decomposed to CO and H2 on IMCs,while it was converted to methane on metallic Ni and alloy.It is of great significance that H2 could be yielded from the methyl ester itself.In short,the utilization of Ni–Ga IMCs can effectively reduce carbon loss and H2 consumption,all of which are ascribed to the geometric and electronic effects of Ga.

ONE-CELL-STATE METHOD FOR DETERMINATION OF ELECTRONIC STRUCTURE OF INTERMETALLIC COMPOUNDS

ＩＮＴＲＯＤＵＣＴＩＯＮＩｎｒｅｃｅｎｔｙｅａｒｓ，ｔｈｅＰａｕｌｉｎｇ’ｓｖａｌｅｎｃｅｂｏｎｄ（ＶＢ）ｔｈｅｏｒｙｈａｓｂｅｎｍａｄｅａｇｒｅａｔｐｒｏｇｒｅｓｉｎｄｅｓｉｇｎｉｎｇａｎｄｄｅｔｅｒｍｉｎｉｎｇｔｈｅａｔｏｍｉｃｓｔａｔｅ，ａｎｄ...

Crystallographic Characteristic of Intermetallic Compounds in Al-Si-Mg Casting Alloys Using Electron Backscatter Diffraction

The Al-Si-Mg alloy which can be strengthened by heat treatment is widely applied to the key components of aerospace and aeronautics. Iron-rich intermetallic compounds are well known to be strongly influential on mechanical properties in Al-Si-Mg alloys. But intermetallic compounds in cast Al-Si-Mg alloy intermetallics are often misidentified in previous metallurgical studies. It was described as many different compounds, such as AlFeSi, Al8Fe2Si, Al5（Fe, Mn）3Si2 and so on. For the purpose of solving this problem, the intermetallic compounds in cast Al-Si alloys containing 0.5% Mg were investigated in this study. The iron-rich compounds in Al-Si-Mg casting alloys were characterized by optical microscope（OM）, scanning electron microscope（SEM）, energy dispersive X-ray spectrometer（EDS）, electron backscatter diffraction（EBSD） and X-ray powder diffraction（XRD）. The electron backscatter diffraction patterns were used to assess the crystallographic characteristics of intermetallic compounds. The compound which contains Fe/Mg-rich particles with coarse morphologies was Al8FeMg3Si6 in the alloy by using EBSD. The compound belongs to hexagonal system, space group P6_2m, with the lattice parameter a=0.662 nm, c=0.792 nm. The β-phase is indexed as tetragonal Al3FeSi2, space group I4/mcm, a=0.607 nm and c=0.950 nm. The XRD data indicate that Al8FeMg3Si6 and Al3FeSi2 are present in the microstructure of Al-7Si-Mg alloy, which confirms the identification result of EBSD. The present study identified the iron-rich compound in Al-Si-Mg alloy, which provides a reliable method to identify the intermetallic compounds in short time in Al-Si-Mg alloy. Study results are helpful for identification of complex compounds in alloys.

Evolution of AuSnx intermetallic compounds in laser reflowed micro-solder joints

To investigate the effect of Au thickness on evolution of AuSnx IMCs, pads with 0. 1, 0. 5 and 4. 0 μm thickness of Au surface finish were utilized. Laser reflowed solder joints were aged in 125℃ isothermal ovens. Results indicated that little IMC formed at the interface of solder and pad with 0. 1 μm thickness of Au. Even in condition of 744 hours aging, thickness of lMCs did not increase obviously. As for the joints with 0. 5 μm thickness of Au, most of AuSn4 IMCs stayed at the inteornce and were in needle-like or dendritic morphology. With the increase of aging time, AuSn4 IMCs beeame flat and changed to a continuous layer. In the joints with 4. 0 μm thickness of Au on pads, AuSn, AuSn2, AuSn4 IMCs and Au2Sn phase formed at the interface. As aging time was increased, more Sn rich IMCs formed at the interface, and evolved to AuSn4 IMCs in condition of long time aging. Thickness of AuSn4 IMCs reached about 30μm.

Computational Modeling of Intergranular Crack Propagation in an Intermetallic Compound Layer

A micromechanical model is presented to study the initiation and propagation of microcracks of intermetallic compounds(IMCs)in solder joints.The effects of the grain aggregate morphology,the grain boundary defects and the sensitivity of the various cohesive zone parameters in predicting the overall mechanical response are investigated.The overall strength is predominantly determined by the weak grain interfaces;both the grain aggregate morphology and the weak grain interfaces control the crack configuration;the different normal and tangential strengths of grain interfaces result in different intergranular cracking behaviors and play a critical role in determining the macroscopic mechanical response of the system.

ANOMALOUS STRAIN RATE DEPENDENCE OF FLOW STRESS IN TiAl INTERMETALLIC COMPOUNDS

Plastic deformation of TiAI and TiAI-V intermetallic compounds has been studied by com- pression experiment at various temperatures and strain rates.Results show that the plastic deformation in distinct temperature range is principally controlled by the mechanisms of Peierls-Nabarro,cross slip and creep of dislocations.For TiAI-V alloy deformed at a range of 600—700 K,the negative strain rate dependence of flow stress was observed,i.e.,the more the plastic strain is.the more the negative dependence will be.A possible mechanism of the anomaly could be interpreted by thermal activation of dislocation cross slipping.The effects of temperature and strain rate on work-hardening exponent were also studied and discussed.

Sub-nanometer Pt_(2)In_(3) intermetallics as ultra-stable catalyst for propane dehydrogenation

Pt-based catalysts are the typical industrial catalysts for propane dehydrogenation(PDH),which still suffer from insufficient lo ng-term durability due to the structu ral instability and coke deposition.A commercial γ-Al_(2)O_(3) supported thermally robust sub-nanometer Pt2In3intermetallic catalyst with atomically ordered structure and rigorously separated Pt single atoms was fabricated,which showed outstanding robustness in 240 h long-term operation at 600℃ with the deactivation rate constant kdas low as0.00078 h^(-1), ranking among the lowest reported values.Based on various in situ characterizations and theoretical calculations,it was proved that the catalyst stability not only resulted from the separated Pt single-atom sites but also significantly affected by the distance of adjacent Pt atoms.An increasing distance to 3.25 A in the Pt_(2)In_(3)could induce a weak π-adsorption configuration of propylene on Pt sites,which facilitated the desorption of propylene and restrained the side reactions like coking.