Effect of slow shot speed on externally solidified crystal,porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy

The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).

Friction surfacing of hypereutectic Al-Si alloy on commercially pure aluminum : Effect of consumable rod heat treatment and heat input

This study investigated the effect of pre-friction surfacing heat treatment of consumable rods and heat input during friction surfacing on the microstructure,mechanical properties,and wear resistance of hypereutectic Al-Si alloy deposited on a commercially pure aluminum substrate.The results show that regardless of the consumable rod’s heat treatment conditions,the coating’s efficiency has increased with the increase in heat input,so the coating efficiency increases by 20%and 30%in the solid solution-treated rod and the artificially aged rod,respectively.By increasing the heat input,the average grain size in the coating fabricated by solid solution-treated rod and artificially aged rod increased from 0.1 to 0.9μm and from 0.2 to 1.3μm,respectively.At constant heat input,the average hardness and wear resistance of the coating created in the solid solution-treated rod are lower than those of the artificially aged rod.By decreasing heat input,the wear loss in the coating fabricated by solid solution-treated rod and artificially aged rod decreased by 10%and 20%,respectively,reaching 0.1 and 0.03μg/m.

Growth mechanism of primary silicon in cast hypoeutectic Al-Si alloys

The microstructural features of hypoeutectic AI-10%Si alloy were observed using optical microscopy and electron backscatter diffraction. The results show that primary silicon particles are frequently found in hypoeutectic alloys. Hence, the nucleation and growth mechanisms of the precipitation of primary silicon of hypoeutectic Al-10%Si alloy melts were investigated. It was discovered that Si atoms are easy to segregate and form Si-Si clusters, which results in the formation of primary silicon even in eutectic or hypoeutectic Al-Si alloys. In addition, solute redistribution caused by chemical driving force and large pile-ups or micro-segregation of the solute play an important role in the formation of the primary silicon, and the solute redistribution equations were derived from Jackson-Chalmers equations. Once Si solute concentration exceeds eutectic composition, primary silicon precipitates are formed at the front of solid/liquid interface.

Effect of ultrasonic vibration on Fe-containing intermetallic compounds of hypereutectic Al-Si alloys with high Fe content

The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing compounds in the alloys produced by conventional casting process are detrimental to the strength of matrix. The effect of ultrasonic vibration （USV） on the morphology change of Fe-containing intermetallic compounds in the hypereutectic Al-17Si-xFe （x=2, 3, 4, 5） alloys was systematically studied. The results show that, the Fe-containing intermetallic compounds are mainly composed of long needle-like β-Al5FeSi phase with a small amount of plate-like δ-Al4FeSi2 phase in Al-17Si-2Fe alloy produced by conventional casting process. With the increase of Fe content from 2% to 5% in the alloys, the amount of plate-like or coarse needle-like δ-Al4FeSi2 phase increases while the amount of long needle-like β-Al5FeSi phases decreases. In Al-17Si-5Fe alloy, the Fe-containing intermetallic compounds exist mainly as coarse needle-like δ-Al4FeSi2 phase. After USV treatment, the Fe-containing compounds in the Al-17Si-xFe alloys are refined and exist mainly as δ-Al4FeSi2 particles, with average grain size ranging from 26 μm to 37 μm, and only a small amount of β-Al5FeSi phases remain. The mechanism of USV on the morphology of Fe-containing intermetallic compounds was also discussed.

Nucleation and growth of eutectic cell in hypoeutectic Al-Si alloy

The nucleation and growth of eutectic cell in hypoeutectic Al-Si alloy was investigated using optical microscopy and scanning electron microscopy equipped with electron backscattering diffraction（EBSD）.By revealing the eutectic cells and analyzing the crystallographic orientation,it was found that both the eutectic Si and Al phases in an eutectic cell were not single crystal,representing an eutectic cell consisting of small ＇grains＇.It is also suggested that the eutectic nucleation mode can not be determined based on the crystallographic orientation between eutectic Al phases and the neighboring primary dendrite Al phases.However,the evolution of primary dendrite Al phases affects remarkably the following nucleation and growth of eutectic cell.The coarse flake-fine fibrous transition of eutectic Si morphology involved in impurity elements modification may be independent of eutectic nucleation.

Grain refining mechanism of Al-3B master alloy on hypoeutectic Al-Si alloys

Al-3B master alloy is a kind of efficient grain refiner for hypoeutectic Al-Si alloys. Experiments were carried out to evaluate the effect of undissolved AlB2 particles in Al-3B master alloy on the grain refinement of Al-7Si. It is found that the number and the settlement of AlB2 particles in the melt all have effect on the grain refining efficiency. On the basis of experiments and theoretical analysis, a new grain refinement mechanism was proposed to explain the grain refinement action of Al-3B on hypoeutectic Al-Si alloys. The formation of ＇Al-AlB2＇ shell structure is the direct reason for grain refinement and the undissolved AlB2 particles is the indirect nucleating base for subsequent α（Al） phase.

Overflowing phenomenon during ultrasonic treatment in Al-Si alloys

At the late stage of solidification with ultrasonic treatment （UST） in Al-Si alloys, a part of semisolid overflows and climbs along the probe. The interesting phenomenon and its influence on the solidification microstructure were investigated in order to better study the mechanism of UST. It is considered that the overflowing phenomenon occurs due to the changes of vibration and flow in the remaining semisolid. Because the overflowed portion comes from the region with intense UST effect and vibrates with the probe during solidification, great modification of primary and euteetic Si （about 10 pm in length） and refinement of primary a（Al） （about 70 μm in size） are observed in this portion.

Microstructure evolution of spray-formed hypereutectic Al-Si alloys in semisolid reheating process

The Al-27%Si alloy was prepared by the spray forming process,and its microstructure evolution during the semisolid reheating process was investigated.The results show that,the primary Si phase coarsens during the reheating process and the coarsening rate increases with the increase of reheating temperature.The eutectic phase is produced in the molten region when quenched in the cold water.The microstructure evolution in the semisolid state can be divided into three stages.The remarkable characteristic of the first stage is only a solid-state phase transformation process.However,the region around the α（Al） matrix gradually melts in the second stage.The primary Si in the liquid phase coarsens obviously,and the eutectic phase is produced in the molten region when the specimens are quenched in cold water.In the last stage,the same thing as that in the second stage happens except that all the α（Al） matrixes are melted.

Dry sliding wear behavior of rheocast hypereutectic Al-Si alloys with different Fe contents

The effect of iron content on wear behavior of hypereutectic Al?17Si?2Cu?1Ni alloy produced by rheocasting process was investigated. The dry sliding wear tests were carried out with a pin-on-disk wear tester. The results show that the wear rate of the rheocast alloy is lower than that of the alloy produced by conventional casting process under the same applied load. The fine particle-likeδ-Al4(Fe,Mn)Si2 and polygonalα-Al15(Fe,Mn)3Si2 phases help to improve the wear resistance of rheocast alloys. As the volume fraction of fine Fe-bearing compounds increases, the wear rate of the rheocast alloy decreases. Moreover, the wear rate of rheocast alloy increases with the increase of applied load from 50 to 200 N. For the rheocast alloy with 3% Fe, oxidation wear is the main mechanism at low applied load (50 N). At higher applied loads, a combination of delamination and oxidation wear is the dominant wear mechanism.

Variation of the second-phase morphology and its influence on fracture behavior of Al-Si alloy

Using an optical microscope and scanning electron microscope (SEM), the variation of eutectic Si morphology of Al-Si alloy in solution treatment was observed to study its influence on mechanical properties and fracture behavior. The results show that eutectic Si undergoes stubbing, necking, fragmentation, and growth in the initial stage (250 min); in the middle solution stage (250 to 400 min), the eutectic Si morphology has no significant change, only the degree of spheroidizing becomes higher; after 600 min, the growth of eutectic Si is a coarsening process controlled by diffusion and follows the Liftshitz-Slyozov-Wangner (LSW) model, and the eutectic Si morphology deteriorates due to the occurrence of facets and lap. Based on the quantitative measure and regression analysis, the eutectic Si morphology has a remarkable influence on mechanical properties and fracture behavior.

Effect of pre-annealing on microstructure and compactibility of gas-atomized Al-Si alloy powders

Effect of pre-annealing treatment temperature on compactibility of gas-atomized Al-27%Si alloy powders was investigated. Microstructure and hardness of the annealed powders were characterized. Pre-annealing results in decreasing Al matrix hardness, dissolving of needle-like eutectic Si phase, precipitation and growth of supersaturated Si atoms, and spheroidisation of primary Si phase. Compactibility of the alloy powders is gradually improved with increasing the annealing temperature to 400 ℃. However, it decreases when the temperature is above 400 ℃ owing to the existence of Si-Si phase clusters and the densely distributed Si particles. A maximum relative density of 96.1% is obtained after annealing at 400 ℃ for 4 h. In addition, the deviation of compactibility among the pre-annealed powders reaches a maximum at a pressure of 175 MPa. Therefore, a proper pre-annealing treatment can significantly enhance the cold compactibility of gas-atomized Al-Si alloy powders.

Effects of Mg content on primary Mg_2Si phase in hypereutectic Al-Si alloys

Hypereutectic Al-Si alloy with variant Mg contents were fabricated by casting,and the effects of Mg content on the microstructure of primary Mg2Si particles in hypereutectic Al-Si alloys were investigated.The results show that the volume fraction of primary Mg2Si particles increases linearly with raising the Mg content,but the average size of Mg2Si particles does not exhibit a corresponding change.When the Mg content is 3%,á1 0 0？ directions have the fastest growth velocity,so that Mg2Si particles are likely to form octahedron shape.When gradually increasing the Mg content,the distributions of Mg and Si atoms on the solid-liquid interface become inhomogeneous,which results in the formation of irregular octahedron structures.Finally,when the Mg content is about 10%,the morphology of primary Mg2Si particles changes from the octahedron shape into various complex structures with a large size.

Microstructure and mechanical properties of hypereutectic Al-Si alloy modified with Cu-P

The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope（SEM）,and energy dispersive analysis of X-rays（EDAX） that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.

Research on semi-solid slurry of a hypoeutectic Al-Si alloy prepared by low superheat pouring and weak electromagnetic stirring

The semi-solid slurry of a hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouting temperature and stirring power on the semi-solid slurry were investigated. The results indicated that the semi-solid slurry to satisfy rheocasting can be manufactured by low superheat pouring and weak electromagnetic stirring. The pouring temperature （or superheat） and the stirring power remarkably affected the morphology of primary α-Al and the size of primary α-Al, and there is no obvious effect of stirring time on primary α-Al. Compared with the samples made by low superheat pouring with no stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 were markedly improved by low superheat pouring and weak electromagnetic stirring. On the condition of weak electromagnetic stirring, the pouring temperature with low superheat can be suitably raised to reach the effectiveness obtained from the lower pouring temperature without stirring.

Al-Si-P master alloy and its modification and refinement performance on Al-Si alloys

An Al-Si-P master alloy has been developed by an in-situ reaction and the electron probe microanalyzer （EPMA） results show that there are many pre-formed AlP particles contained in the master alloy. Silicon introduced into the system plays an important role in remarkably improving the distribution and content of AlP particles due to their similar crystal structure and lattice parameters. ZL109 alloys have shown fast modification response to the addition of 0.5% Al-15Si-3.5P master alloy at 720℃, with a mass of primary Si precipitating in size of about 15 μm. Also, coarse primary Si grains in AI-30Si alloy can be refined dramatically from 150 μm to 37 μm after the addition of 2.0% Al-15Si-3.5P master alloy at 850℃. The P recovery of the Al-15Si-3.5P master alloy is much higher than that of a Cu-8.5P master alloy due to the pre-formed AlP particles.

Influence of high pressure and manganese addition on Fe-rich phases and mechanical properties of hypereutectic Al-Si alloy with rheo-squeeze casting

The influence of high pressure and manganese addition on Fe-rich phases(FRPs)and mechanical properties of Al-14Si-2Fe alloy with rheo-squeeze casting(RSC)was investigated.The semi-solid alloy melt was treated by ultrasonic vibration(UV)firstly,and then formed by squeeze casting(SC).Results show that the FRPs in as-cast SC alloys are composed of coarseβ-Al5(Fe,Mn)Si,δ-Al4(Fe,Mn)Si2 and bone-shapedα-Al15(Fe,Mn)3Si2 phases when the pressure is 0 MPa.With RSC process,the FRPs are first refined by UV,and then the solidification under pressure further causes the grains to become smaller.The peritectic transformation occurs during the formation ofαphase.For the alloy with the same composition,the ultimate tensile strength(UTS)of RSC sample is higher than that of the SC sample.With the same forming process,the UTS of Al-14Si-2Fe-0.8Mn alloy is higher than that of Al-14Si-2Fe-0.4Mn alloy.

Microstructure and performance of Al-Si alloy with high Si content by high temperature diffusion treatment

The Al-Si alloy with high Si content was prepared by pressure infiltration. Microstructure observation shows that three-dimensional structure （3D-structure） is obtained from irregular sharp Si particles via high temperature diffusion treatment （HTDT）. Flat Si-Al interfaces transform to smooth curves, and Si phases precipitate in Al and Si-Al interface. The bonding of Si-Al interface is improved by HTDT, which improves the mechanical performance of Al-Si alloy. The bending strength of 3D-Al-Si alloy increases by 6% compared with that of Al-Si alloy, but the elastic modulus changes a little. The coefficient of thermal expansion （CTE） of the 3D-Al-Si alloy is 7.7×10^-6/℃ from 20℃ to 100 ℃, which decreases by 7% compared with that of Al-Si alloy. However, HTDT has little effect on the thermal conductivity of Al-Si alloy.

Functions and mechanism of modification elements in eutectic solidification of Al-Si alloys:A brief review

Being used more and more widely in engineering,AlSi alloys comprise about 80%of all kinds of aluminum alloys,which are the most widely utilized nonferrous alloys.Although most Al-Si alloys consist of multiple components,the eutectics in the structure accounts for 50%-90%of the sum volume of such alloys.Therefore,understanding the modification mechanism and function rules of the AlSi eutectic solidification is the technical key in controlling the structures and properties of such casting alloys.The present paper chiefly reviews recent investigation developments and important conclusions along the lines of the functions of modification elements and their modification mechanism in the eutectic solidification of Al-Si alloys.

Simulation on microstructure evolution of Al-Si alloy under effect of natural convection during solidification

The solidification microstructure of Al-Si alloy was observed in the experiment,the second dendrite arm spacing(SDAS)was measured,and the effect of temperature on the microstructure was analyzed.Phase-field(PF)model incorporating natural convection caused by gravity was employed to simulate the microstructure evolution of Al-Si alloy under the experimental conditions.Good agreements between the experimental and simulation results verified the reliability of the simulation approach proposed in this study.Based on the proposed model,a series of simulation cases(2D and 3D)were performed to investigate the evolution of columnar and equiaxed dendritic structures.It was found that the solute content of the alloy had little impact on the microstructure evolution,while the solute expansion coefficient had obvious effect on the dendrite tip velocities.Significant improvement of computational efficiency was achieved via novel algorithms,making it possible to perform massive simulation for studying the evolution of solidification microstructures,which is hard to be directly observed in experiments via synchrotron radiation for Al-Si alloy.

Solidification structure of eutectic Al-Si alloy under a high magnetic field-aid-electromagnetic vibration

An electromagnetic vibration was generated by simultaneously imposing a strong static magnetic field （up to 10 T） and an alternative electricity current to the metal. Its effects on the solidification structure of eutectic Al-Si alloy have been investigated experimentally. It is found that the eutectic structure has been refined by solely imposing high magnetic field while it is coarsened under the electromagnetic vibration. Furthermore, polyhedral Si grains and non-dendritic α-Al appeared when the electromagnetic vibration strength was strong enough. The refining of eutectic structure is attributed to the decrease of diffusion coefficient caused by the strong magnetic field. The coarseness of eutectic structure may be attributed to the convection caused by electromagnetic vibration. Strong convection may break co-operative growth of eutectic phases to form polyhedral Si grains and non-dendritic α-Al.