The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron mi...The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).展开更多
Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mas...Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mass-efficient thin-walled body structures.For body structures that require excellent ductility and fracture toughness to be joined with steel sheet via self-piercing riveting(for instance,shock towers and hinge pillars,etc.),a costly T7 heat treatment comprising a solution heat treatment at elevated temperatures(450℃-500℃)followed by an over-ageing heat treatment is needed to optimize microstructure for meeting product requirement.To enable cost-efficient mass production of HPDC body structures,it is important to eliminate the expensive T7 heat treatment without sacrificing mechanical properties.Optimizing die cast alloy chemistry is a potential solution to improve fracture toughness and ductility of the HPDC components.The present study intends to tailor the Mg and Cu additions for a new Al-Si-Cr type die casting alloy(registered as A379 with The Aluminum Association,USA)to achieve the desired tensile properties without using T7 heat treatment.It was found that Cu addition should be avoided,as it is not effective in enhancing strength while degrades tensile ductility.Mg addition is very effective in improving strength and has minor impact on tensile ductility.The investigated Al-Si-Cr alloy with a nominal composition of Al-8.5wt.%Si-0.3wt.%Cr-0.2wt.%Fe shows comparable tensile properties with the T7 treated AlSi10MnMg alloy which is currently used for manufacturing shock towers and hinge pillars.展开更多
An Al-Si-P master alloy has been developed by an in-situ reaction and the electron probe microanalyzer (EPMA) results show that there are many pre-formed AlP particles contained in the master alloy. Silicon introduc...An Al-Si-P master alloy has been developed by an in-situ reaction and the electron probe microanalyzer (EPMA) results show that there are many pre-formed AlP particles contained in the master alloy. Silicon introduced into the system plays an important role in remarkably improving the distribution and content of AlP particles due to their similar crystal structure and lattice parameters. ZL109 alloys have shown fast modification response to the addition of 0.5% Al-15Si-3.5P master alloy at 720℃, with a mass of primary Si precipitating in size of about 15 μm. Also, coarse primary Si grains in AI-30Si alloy can be refined dramatically from 150 μm to 37 μm after the addition of 2.0% Al-15Si-3.5P master alloy at 850℃. The P recovery of the Al-15Si-3.5P master alloy is much higher than that of a Cu-8.5P master alloy due to the pre-formed AlP particles.展开更多
The effects of mixing temperature,i.e.,the temperatures of two precursor melts(pure Al and Al-12Si),on the temperature and solute fields of resultant mixture,the nucleation and growth,and the size and morphology of pr...The effects of mixing temperature,i.e.,the temperatures of two precursor melts(pure Al and Al-12Si),on the temperature and solute fields of resultant mixture,the nucleation and growth,and the size and morphology of primary grains during controlled diffusion solidification(CDS) of Al-8Si alloy were investigated by using simulation and calculation.The results indicate that a lower mixing temperature is helpful for achieving more supercooled microscale Al-rich pockets in the mixture,and increasing the width and supercooling degree of supercooling zone in the Al-rich pockets,and thus,the nucleation rate.The nuclei grow up in nondendritic mode,resulting in spheroidal,at least,nondendritic grains.In a successful CDS,the superheat degrees of the two precursor melts should be limited within several degrees,and it is not necessary to extra stipulate the superheat degree of target alloy melt(Al-8Si) when the requirement about Gibbs energies of the three melts is matched.Subsequent observation on casting microstructures shows that the employed simulation and calculation processes are reasonable and the achieved results are reliable.展开更多
To obtain the finer primary silicon crystals, the proprietary Al-P masteralloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process wasmade in the experiments. The SEM (Scanning E...To obtain the finer primary silicon crystals, the proprietary Al-P masteralloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process wasmade in the experiments. The SEM (Scanning Electron Microscope) and DSC (Differential ScanningCalorimeter) analysis indicate that the Al-P modifier has more advantages over Cu-P and Fe-Pmodifier in easily addition, no elemental alteration and less undercooling of primary silicon'ssolidification, which suggests the Al-P master alloy is an effective modifier of eutectic Al-Sialloys.展开更多
To obtain the finer primary silicon crystals, the proprietary Al-P master alloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process was made in the experiments. The SEM (Scanning...To obtain the finer primary silicon crystals, the proprietary Al-P master alloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process was made in the experiments. The SEM (Scanning Electron Microscope) and DSC (Differential Scanning Calorimeter) analysis indicate that the Al-P modifier has more advantages over Cu-P and Fe-P modifier in easily addition, no elemental alteration and less undercooling of primary silicon’s solidification, which suggests the Al-P master alloy is an effective modifier of eutectic Al-Si alloys.展开更多
Effects of Si content and the addition amount of Al-3B master alloy on the solidification structures of hypoeutectic Al-Si alloys were studied. The addition amounts of the master alloy were 0.2%, 0.4%, 0.7% and 1% (ma...Effects of Si content and the addition amount of Al-3B master alloy on the solidification structures of hypoeutectic Al-Si alloys were studied. The addition amounts of the master alloy were 0.2%, 0.4%, 0.7% and 1% (mass fraction, so as the follows), respectively. The Si content of Al-Si binary alloys investigated varied from 1% to 11%. The observation of macrostructures of non-refined samples showed that 3% Si constitutes a transition point at which the minimum grain size can be obtained. It was also found that Al-3B master alloy can shift the transition point towards a higher Si value when its addition amount increases, making this point appear at 4%, 5% and 6% Si as its addition amount increases up to 0.4%, 0.7% and 1%, respectively.展开更多
The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope(OM) and mechanical testing and simulation(MTS).The r...The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope(OM) and mechanical testing and simulation(MTS).The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope(SEM),and energy dispersive analysis of X-rays(EDAX) that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.展开更多
The semi-solid slurry of a hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouting temperature and stirring power on the semi-solid slurry were inve...The semi-solid slurry of a hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouting temperature and stirring power on the semi-solid slurry were investigated. The results indicated that the semi-solid slurry to satisfy rheocasting can be manufactured by low superheat pouring and weak electromagnetic stirring. The pouring temperature (or superheat) and the stirring power remarkably affected the morphology of primary α-Al and the size of primary α-Al, and there is no obvious effect of stirring time on primary α-Al. Compared with the samples made by low superheat pouring with no stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 were markedly improved by low superheat pouring and weak electromagnetic stirring. On the condition of weak electromagnetic stirring, the pouring temperature with low superheat can be suitably raised to reach the effectiveness obtained from the lower pouring temperature without stirring.展开更多
In this article, a novel Al-6Zr-2P master alloy with ZrP particles was successfully synthesized, and the refining performance of this novel master alloy for the primary Si in Cu-50Si alloys was also investigated. By m...In this article, a novel Al-6Zr-2P master alloy with ZrP particles was successfully synthesized, and the refining performance of this novel master alloy for the primary Si in Cu-50Si alloys was also investigated. By means of the fracture plane observation, it is found that the ZrP phase would precipitate first in the solidification pro- cess, and then, the ZrAl3 phase grows around them. Fur- thermore, it is observed that the refining effect can be remarkably improved by changing the addition sequence of the raw materials. After the melting of commercial Cu, the 2.0 wt% Al-6Zr-2P master alloy and crystalline Si were added in sequence, and the mean size of the primary Si in Cu-50Si alloy can be significantly refined from 255.7 to 75.3 gm. Meanwhile, the refining mechanism was dis- cussed in detail.展开更多
In this study, grain refining effect of Al-1.5℃ master alloy was examined on an AZ63B magnesium alloy, and the refining mechanism was studied through investigating the role of C and Fe in this process. The results sh...In this study, grain refining effect of Al-1.5℃ master alloy was examined on an AZ63B magnesium alloy, and the refining mechanism was studied through investigating the role of C and Fe in this process. The results show that addition of Al-1.5℃ master alloy leads to significant decrease of the mean grain size from about 270μm to 50μm at the center of the AZ63 alloy ingot. Grain refinement by carbon addition is mainly due to the heterogeneity nucleation on the Al-, C-, O-, Fe- and Mn-rich particles, but not constitutional undercooling caused by the carbon solute element. Fe plays an important role in the formation of the nucleating particles, but not acts as an inhibiting element.展开更多
The semi-solid slurry of hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouring temperature and stirring power on the semi-solid slurry making proc...The semi-solid slurry of hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouring temperature and stirring power on the semi-solid slurry making process were investigated. The results indicate that the semi-solid slurry to satisfy rheocasting requirement can be made by a combination of low superheat pouring and weak electromagnetic stirring. The pouring temperature (or superheat) and the stirring power significantly affect the morphology and the size of primary α-Al, while there is no obvious effect of the stirring time on primary α-Al. Compared with the samples made by low superheat pouring without stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 Al alloy are markedly improved by a process of applying both low superheat pouring and weak electromagnetic stirring. Under the condition of weak electromagnetic stirring applied, the pouring temperature with low superheat can be equivalently to reach the effectiveness obtained from the even lower pouring temperature without stirring.展开更多
The influences of preparation conditions of Al-5Ti-B (as-cast and hot-rolled) and Al-10Sr (as-cast and hotextruded) and melt treatment procedures on the grain refinement and modification performance of A356 alloy ...The influences of preparation conditions of Al-5Ti-B (as-cast and hot-rolled) and Al-10Sr (as-cast and hotextruded) and melt treatment procedures on the grain refinement and modification performance of A356 alloy are experimentally studied. For the two master alloys, the 50% reduction is sufficient to meet the demands of the efficient grain refinement and modification of A356 alloy. When Al-STi-B is introduced into the melt prior to degassing, the grain refinement efficiency of Al-5Ti-B will be greatly increased due to the better dispersity of TiB2 particles. Al-5Ti-B master alloy is less prone to affect the modification effect of Al-10Sr when they are used together.展开更多
The refining effect of Al3Ti1B1RE master alloy on Al sheets used for pressure can manufacture and the behavior of mixed rare earths in master alloy were investigated with XRD, OM, SEM and EDAX. It is found that the r...The refining effect of Al3Ti1B1RE master alloy on Al sheets used for pressure can manufacture and the behavior of mixed rare earths in master alloy were investigated with XRD, OM, SEM and EDAX. It is found that the refining effect of the refiner on the material has superiority over foreign or domestic Al5Ti1B refiner, and the refiner still retains its refining ability for 6 h after adding it to molten Al, thus improving the strength and plasticity of the material remarkably. The excellent refining effect and stability of AlTiBRE refiner result from that RE can lower the surface energy of molten Al and improve the wetting characteristics of molten Al on refinement nuclei such as TiAl 3, TiB 2, etc., thus giving full play to the effect of heterogeneous nucleation and impeding the congregating tendency of TiB 2 phase in molten Al. At the same time, RE gathering in front of solid/liquid interface are also easy to cause composition supercooling in molten Al, thus impeding the growth of α Al grains and promoting α Al nucleation on refinement nuclei. In addition, RE also play certain role in purification and grain refinement, or modification, especially their effect of purification can improve the metallurgical quality of AlTiBRE master alloy.展开更多
Previous studies have proved that the zirconium(Zr)alloying and grain refining performance of a Mg-Zr master alloy on Mg alloy is closely related to the distribution of Zr particle size,and a Mg-Zr master alloy with m...Previous studies have proved that the zirconium(Zr)alloying and grain refining performance of a Mg-Zr master alloy on Mg alloy is closely related to the distribution of Zr particle size,and a Mg-Zr master alloy with more Zr particles in size range of 1-5μm exhibits a better refining efficiency.In this paper,friction stir processing(FSP)was used to modify the Zr particles size distribution of a commercially available Mg-30 wt.%Zr master alloy,and the subsequent grain refinement ability was studied by trials on a typical Mg-3Nd-0.2Zn-0.6Zr(wt.%,NZ30K)alloy.It is found that plenty of large Zr particles in the as-received Mg-30%Zr master alloy are broken by FSP.Grain refinement tests reveal that the refining efficiency of Mg-30%Zr alloy is significantly improved by FSP,which is attributed to the better distribution of Zr particles.The refinement effect by adding 0.6%FSP-ed Mg-30%Zr is approximately equivalent to that by adding 1.0%as-received Mg-30%Zr.Due to the easy and convenient operation of FSP,this study provides a new method to develop a more efficient Mg-Zr refiner.展开更多
Being used more and more widely in engineering,AlSi alloys comprise about 80%of all kinds of aluminum alloys,which are the most widely utilized nonferrous alloys.Although most Al-Si alloys consist of multiple componen...Being used more and more widely in engineering,AlSi alloys comprise about 80%of all kinds of aluminum alloys,which are the most widely utilized nonferrous alloys.Although most Al-Si alloys consist of multiple components,the eutectics in the structure accounts for 50%-90%of the sum volume of such alloys.Therefore,understanding the modification mechanism and function rules of the AlSi eutectic solidification is the technical key in controlling the structures and properties of such casting alloys.The present paper chiefly reviews recent investigation developments and important conclusions along the lines of the functions of modification elements and their modification mechanism in the eutectic solidification of Al-Si alloys.展开更多
This paper summarizes a process for the preparation of Al5%Zr master alloy by the reduction of K2ZrF6 with aluminium. The reduction in grain size of aluminium by addition of known quantity of master alloy is also stud...This paper summarizes a process for the preparation of Al5%Zr master alloy by the reduction of K2ZrF6 with aluminium. The reduction in grain size of aluminium by addition of known quantity of master alloy is also studied.展开更多
Effects of cooling rates on the morphology, sizes and species of primary vanadium-containing phases in Al-10V master alloys were investigated. The results show that the primary vanadium-containing phases with differen...Effects of cooling rates on the morphology, sizes and species of primary vanadium-containing phases in Al-10V master alloys were investigated. The results show that the primary vanadium-containing phases with different morphologies and compositions present in Al-10V master alloys at different cooling rates with the pouring temperature of 1,170 °C. When the Al-10V master alloy is solidified in the refractory mold at a cooling rate of 2 °C·s-1, the vanadium-containing phases are mainly plate-like Al10V phases, with the average size of 100.0 μm in the center and 93.2 μm at the edge of the ingot. When the master alloy is solidified in the graphite mold at a cooling rate of 24.3 °C·s-1, the primary vanadium-containing phases are dendritic Al3V phases, with the average length of 297.0 μm for the first dendrite in the center and 275.0 μm at the edge of the ingot. The secondary dendrite arm spacing (SDAS) is 9.5 μm in the center and 9.3 μm at the edge of the ingot, respectively. When the solidification is carried out in the copper mould at a cooling rate of 45.7 °C·s-1, the primary vanadium-containing phases are also Al3V phases but with smaller size, compared with that prepared at the cooling rate of 24.3 °C·s-1. As a result, the average length is 190.0 μm for the first dendrite in the center and 150.0 μm at the edge of the ingot. The SDAS is 9.8 μm in the center and 4.4 μm at the edge of the ingot, respectively.展开更多
Al-Ti-C-Y master alloy was prepared by combining SHS technique and melting-casting method. The microstructure of master alloy and its grain-refining effect on AZ31 alloy were investigated by means of OM, XRD, SEM and ...Al-Ti-C-Y master alloy was prepared by combining SHS technique and melting-casting method. The microstructure of master alloy and its grain-refining effect on AZ31 alloy were investigated by means of OM, XRD, SEM and EDS. Experimental results indicated that the prepared master alloy consisted of α-Al, TiAl3, TiC and Al3Y phases, and exhibited good grain-refining performance of AZ31 alloy. Morphology of α-Mg changed from coarse dendritic to free equiaxed and the average grain size of α-Mg matrix reduced from the original 580 to 170 μm after adding 1.0 wt.% master alloy. The grain refining efficiency of Al-Ti-C-Y master alloy on AZ31 alloy was mainly attributed to heterogeneous nucleation of TiC particles and grain growth restriction of Al-Y compound or TiC at grain boundaries.展开更多
基金financially supported by the National Key Research and Development Program of China(2022YFB3404201)the Major Science and Technology Project of Changchun City,Jilin Province(Grant No.20210301024GX)。
文摘The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).
文摘Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mass-efficient thin-walled body structures.For body structures that require excellent ductility and fracture toughness to be joined with steel sheet via self-piercing riveting(for instance,shock towers and hinge pillars,etc.),a costly T7 heat treatment comprising a solution heat treatment at elevated temperatures(450℃-500℃)followed by an over-ageing heat treatment is needed to optimize microstructure for meeting product requirement.To enable cost-efficient mass production of HPDC body structures,it is important to eliminate the expensive T7 heat treatment without sacrificing mechanical properties.Optimizing die cast alloy chemistry is a potential solution to improve fracture toughness and ductility of the HPDC components.The present study intends to tailor the Mg and Cu additions for a new Al-Si-Cr type die casting alloy(registered as A379 with The Aluminum Association,USA)to achieve the desired tensile properties without using T7 heat treatment.It was found that Cu addition should be avoided,as it is not effective in enhancing strength while degrades tensile ductility.Mg addition is very effective in improving strength and has minor impact on tensile ductility.The investigated Al-Si-Cr alloy with a nominal composition of Al-8.5wt.%Si-0.3wt.%Cr-0.2wt.%Fe shows comparable tensile properties with the T7 treated AlSi10MnMg alloy which is currently used for manufacturing shock towers and hinge pillars.
基金supported by the National Science Fund for Distinguished Young Scholars (No. 50625101)the Key Project of Science and Technology Research of the Ministry of Education of China (No. 106103)
文摘An Al-Si-P master alloy has been developed by an in-situ reaction and the electron probe microanalyzer (EPMA) results show that there are many pre-formed AlP particles contained in the master alloy. Silicon introduced into the system plays an important role in remarkably improving the distribution and content of AlP particles due to their similar crystal structure and lattice parameters. ZL109 alloys have shown fast modification response to the addition of 0.5% Al-15Si-3.5P master alloy at 720℃, with a mass of primary Si precipitating in size of about 15 μm. Also, coarse primary Si grains in AI-30Si alloy can be refined dramatically from 150 μm to 37 μm after the addition of 2.0% Al-15Si-3.5P master alloy at 850℃. The P recovery of the Al-15Si-3.5P master alloy is much higher than that of a Cu-8.5P master alloy due to the pre-formed AlP particles.
基金supported by the National Key Research and Development Program of China (Grant No.2018YFB2001800)。
文摘The effects of mixing temperature,i.e.,the temperatures of two precursor melts(pure Al and Al-12Si),on the temperature and solute fields of resultant mixture,the nucleation and growth,and the size and morphology of primary grains during controlled diffusion solidification(CDS) of Al-8Si alloy were investigated by using simulation and calculation.The results indicate that a lower mixing temperature is helpful for achieving more supercooled microscale Al-rich pockets in the mixture,and increasing the width and supercooling degree of supercooling zone in the Al-rich pockets,and thus,the nucleation rate.The nuclei grow up in nondendritic mode,resulting in spheroidal,at least,nondendritic grains.In a successful CDS,the superheat degrees of the two precursor melts should be limited within several degrees,and it is not necessary to extra stipulate the superheat degree of target alloy melt(Al-8Si) when the requirement about Gibbs energies of the three melts is matched.Subsequent observation on casting microstructures shows that the employed simulation and calculation processes are reasonable and the achieved results are reliable.
基金The work was financially supported by National Natural Science Foundation of China (No.50071028) Nature Science Foundation of Shandong Province of China (No.L2000F01).
文摘To obtain the finer primary silicon crystals, the proprietary Al-P masteralloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process wasmade in the experiments. The SEM (Scanning Electron Microscope) and DSC (Differential ScanningCalorimeter) analysis indicate that the Al-P modifier has more advantages over Cu-P and Fe-Pmodifier in easily addition, no elemental alteration and less undercooling of primary silicon'ssolidification, which suggests the Al-P master alloy is an effective modifier of eutectic Al-Sialloys.
文摘To obtain the finer primary silicon crystals, the proprietary Al-P master alloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process was made in the experiments. The SEM (Scanning Electron Microscope) and DSC (Differential Scanning Calorimeter) analysis indicate that the Al-P modifier has more advantages over Cu-P and Fe-P modifier in easily addition, no elemental alteration and less undercooling of primary silicon’s solidification, which suggests the Al-P master alloy is an effective modifier of eutectic Al-Si alloys.
基金The work was financially supported by the Open Funds sponsored by Tsinghua University.
文摘Effects of Si content and the addition amount of Al-3B master alloy on the solidification structures of hypoeutectic Al-Si alloys were studied. The addition amounts of the master alloy were 0.2%, 0.4%, 0.7% and 1% (mass fraction, so as the follows), respectively. The Si content of Al-Si binary alloys investigated varied from 1% to 11%. The observation of macrostructures of non-refined samples showed that 3% Si constitutes a transition point at which the minimum grain size can be obtained. It was also found that Al-3B master alloy can shift the transition point towards a higher Si value when its addition amount increases, making this point appear at 4%, 5% and 6% Si as its addition amount increases up to 0.4%, 0.7% and 1%, respectively.
文摘The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope(OM) and mechanical testing and simulation(MTS).The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope(SEM),and energy dispersive analysis of X-rays(EDAX) that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.
基金The project was financially supported by the Hi-tech Research and Development Program of China (No. G2002AA336080) and the National Natural Science Foundation of China (No. 50374012)
文摘The semi-solid slurry of a hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouting temperature and stirring power on the semi-solid slurry were investigated. The results indicated that the semi-solid slurry to satisfy rheocasting can be manufactured by low superheat pouring and weak electromagnetic stirring. The pouring temperature (or superheat) and the stirring power remarkably affected the morphology of primary α-Al and the size of primary α-Al, and there is no obvious effect of stirring time on primary α-Al. Compared with the samples made by low superheat pouring with no stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 were markedly improved by low superheat pouring and weak electromagnetic stirring. On the condition of weak electromagnetic stirring, the pouring temperature with low superheat can be suitably raised to reach the effectiveness obtained from the lower pouring temperature without stirring.
基金financially supported by the National Natural Science Foundation of China (No. 51202088)the Shandong Doctoral Foundation (BS2010CL005)+1 种基金the Doctoral Foundation (No. XBS1106)the Research Foundation of the University of Jinan (No. XKY1106)
文摘In this article, a novel Al-6Zr-2P master alloy with ZrP particles was successfully synthesized, and the refining performance of this novel master alloy for the primary Si in Cu-50Si alloys was also investigated. By means of the fracture plane observation, it is found that the ZrP phase would precipitate first in the solidification pro- cess, and then, the ZrAl3 phase grows around them. Fur- thermore, it is observed that the refining effect can be remarkably improved by changing the addition sequence of the raw materials. After the melting of commercial Cu, the 2.0 wt% Al-6Zr-2P master alloy and crystalline Si were added in sequence, and the mean size of the primary Si in Cu-50Si alloy can be significantly refined from 255.7 to 75.3 gm. Meanwhile, the refining mechanism was dis- cussed in detail.
基金supported by the National Natural Science Foundation of China(No.50171037)Natural Science Foundation of Shandong Province of China(No.Z2004F03).
文摘In this study, grain refining effect of Al-1.5℃ master alloy was examined on an AZ63B magnesium alloy, and the refining mechanism was studied through investigating the role of C and Fe in this process. The results show that addition of Al-1.5℃ master alloy leads to significant decrease of the mean grain size from about 270μm to 50μm at the center of the AZ63 alloy ingot. Grain refinement by carbon addition is mainly due to the heterogeneity nucleation on the Al-, C-, O-, Fe- and Mn-rich particles, but not constitutional undercooling caused by the carbon solute element. Fe plays an important role in the formation of the nucleating particles, but not acts as an inhibiting element.
基金The paper is supported by the Hi-tech Research and Develop-ment Program of China (Authorized No.: G2002AA336080), andthe National Natural Science Foundation of China (AuthorizedNo.: 50374012).
文摘The semi-solid slurry of hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouring temperature and stirring power on the semi-solid slurry making process were investigated. The results indicate that the semi-solid slurry to satisfy rheocasting requirement can be made by a combination of low superheat pouring and weak electromagnetic stirring. The pouring temperature (or superheat) and the stirring power significantly affect the morphology and the size of primary α-Al, while there is no obvious effect of the stirring time on primary α-Al. Compared with the samples made by low superheat pouring without stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 Al alloy are markedly improved by a process of applying both low superheat pouring and weak electromagnetic stirring. Under the condition of weak electromagnetic stirring applied, the pouring temperature with low superheat can be equivalently to reach the effectiveness obtained from the even lower pouring temperature without stirring.
文摘The influences of preparation conditions of Al-5Ti-B (as-cast and hot-rolled) and Al-10Sr (as-cast and hotextruded) and melt treatment procedures on the grain refinement and modification performance of A356 alloy are experimentally studied. For the two master alloys, the 50% reduction is sufficient to meet the demands of the efficient grain refinement and modification of A356 alloy. When Al-STi-B is introduced into the melt prior to degassing, the grain refinement efficiency of Al-5Ti-B will be greatly increased due to the better dispersity of TiB2 particles. Al-5Ti-B master alloy is less prone to affect the modification effect of Al-10Sr when they are used together.
文摘The refining effect of Al3Ti1B1RE master alloy on Al sheets used for pressure can manufacture and the behavior of mixed rare earths in master alloy were investigated with XRD, OM, SEM and EDAX. It is found that the refining effect of the refiner on the material has superiority over foreign or domestic Al5Ti1B refiner, and the refiner still retains its refining ability for 6 h after adding it to molten Al, thus improving the strength and plasticity of the material remarkably. The excellent refining effect and stability of AlTiBRE refiner result from that RE can lower the surface energy of molten Al and improve the wetting characteristics of molten Al on refinement nuclei such as TiAl 3, TiB 2, etc., thus giving full play to the effect of heterogeneous nucleation and impeding the congregating tendency of TiB 2 phase in molten Al. At the same time, RE gathering in front of solid/liquid interface are also easy to cause composition supercooling in molten Al, thus impeding the growth of α Al grains and promoting α Al nucleation on refinement nuclei. In addition, RE also play certain role in purification and grain refinement, or modification, especially their effect of purification can improve the metallurgical quality of AlTiBRE master alloy.
基金This work is supported by National Natural Science Foundation of China(No.51401125,No.51201103)SJTU Special Funds for Science and Technology Innovation(No.13X100030018).
文摘Previous studies have proved that the zirconium(Zr)alloying and grain refining performance of a Mg-Zr master alloy on Mg alloy is closely related to the distribution of Zr particle size,and a Mg-Zr master alloy with more Zr particles in size range of 1-5μm exhibits a better refining efficiency.In this paper,friction stir processing(FSP)was used to modify the Zr particles size distribution of a commercially available Mg-30 wt.%Zr master alloy,and the subsequent grain refinement ability was studied by trials on a typical Mg-3Nd-0.2Zn-0.6Zr(wt.%,NZ30K)alloy.It is found that plenty of large Zr particles in the as-received Mg-30%Zr master alloy are broken by FSP.Grain refinement tests reveal that the refining efficiency of Mg-30%Zr alloy is significantly improved by FSP,which is attributed to the better distribution of Zr particles.The refinement effect by adding 0.6%FSP-ed Mg-30%Zr is approximately equivalent to that by adding 1.0%as-received Mg-30%Zr.Due to the easy and convenient operation of FSP,this study provides a new method to develop a more efficient Mg-Zr refiner.
文摘Being used more and more widely in engineering,AlSi alloys comprise about 80%of all kinds of aluminum alloys,which are the most widely utilized nonferrous alloys.Although most Al-Si alloys consist of multiple components,the eutectics in the structure accounts for 50%-90%of the sum volume of such alloys.Therefore,understanding the modification mechanism and function rules of the AlSi eutectic solidification is the technical key in controlling the structures and properties of such casting alloys.The present paper chiefly reviews recent investigation developments and important conclusions along the lines of the functions of modification elements and their modification mechanism in the eutectic solidification of Al-Si alloys.
文摘This paper summarizes a process for the preparation of Al5%Zr master alloy by the reduction of K2ZrF6 with aluminium. The reduction in grain size of aluminium by addition of known quantity of master alloy is also studied.
基金financially supported by the Electromagnetic Processing of Materials (EPM) Lab Foundation in Northeastern University in China(No.NEU-EPM-005)the National Natural Science Foundation of China(Nos.51374067 and 51804010)the Training Program Foundation for the Talents by Beijing(No.2015000020124G023)
文摘Effects of cooling rates on the morphology, sizes and species of primary vanadium-containing phases in Al-10V master alloys were investigated. The results show that the primary vanadium-containing phases with different morphologies and compositions present in Al-10V master alloys at different cooling rates with the pouring temperature of 1,170 °C. When the Al-10V master alloy is solidified in the refractory mold at a cooling rate of 2 °C·s-1, the vanadium-containing phases are mainly plate-like Al10V phases, with the average size of 100.0 μm in the center and 93.2 μm at the edge of the ingot. When the master alloy is solidified in the graphite mold at a cooling rate of 24.3 °C·s-1, the primary vanadium-containing phases are dendritic Al3V phases, with the average length of 297.0 μm for the first dendrite in the center and 275.0 μm at the edge of the ingot. The secondary dendrite arm spacing (SDAS) is 9.5 μm in the center and 9.3 μm at the edge of the ingot, respectively. When the solidification is carried out in the copper mould at a cooling rate of 45.7 °C·s-1, the primary vanadium-containing phases are also Al3V phases but with smaller size, compared with that prepared at the cooling rate of 24.3 °C·s-1. As a result, the average length is 190.0 μm for the first dendrite in the center and 150.0 μm at the edge of the ingot. The SDAS is 9.8 μm in the center and 4.4 μm at the edge of the ingot, respectively.
基金the Natural Science Foundation of Shanxi Province (2007011067)Patent Generalization Project of Shanxi Province (051025)
文摘Al-Ti-C-Y master alloy was prepared by combining SHS technique and melting-casting method. The microstructure of master alloy and its grain-refining effect on AZ31 alloy were investigated by means of OM, XRD, SEM and EDS. Experimental results indicated that the prepared master alloy consisted of α-Al, TiAl3, TiC and Al3Y phases, and exhibited good grain-refining performance of AZ31 alloy. Morphology of α-Mg changed from coarse dendritic to free equiaxed and the average grain size of α-Mg matrix reduced from the original 580 to 170 μm after adding 1.0 wt.% master alloy. The grain refining efficiency of Al-Ti-C-Y master alloy on AZ31 alloy was mainly attributed to heterogeneous nucleation of TiC particles and grain growth restriction of Al-Y compound or TiC at grain boundaries.