Strength and plasticity improvement induced by strong grain refinement after Zr alloying in selective laser-melted AlSiMg1.4 alloy

In order to enhance the mechanical properties of the selective laser-melted(SLM) high-Mg content AlSiMg1.4 alloy,the Zr element was introduced.The influence of Zr alloying on the processability,microstructure,and mechanical properties of the alloy was systematically investigated through performing microstructure analysis and tensile testing.It was demonstrated that the SLM-fabricated AlSiMg1.4-Zr alloy exhibited high process stability with a relative density of over 99.5% at various process parameters.Besides,the strong grain refinement induced by the primary Al3Zr particle during the melt solidification process simultaneously enhanced both the strength and plasticity of the alloy.The values for the yield strength,ultimate tensile strength,and elongation of the SLM-fabricated AlSiMg1.4-Zr were(343±3) MPa,(485±4) MPa,and(10.2±0.2)%,respectively,demonstrating good strengthplasticity synergy in comparison to the AlSiMg1.4 and other Al-Si-based alloys fabricated by SLM.

Grain refinement of Mg-Ca alloys by native MgO particles

In Mg-Ca alloys the grain refining mechanism,in particular regarding the role of nucleant substrates,remains the object of debates.Although native MgO is being recognised as a nucleating substrate accounting for grain refinement of Mg alloys,the possible interactions of MgO with alloying elements that may alter the nucleation potency have not been elucidated yet.Herein,we design casting experiments of Mg-xCa alloys varied qualitatively in number density of native MgO,which are then comprehensively studied by advanced electron microscopy.The results show that grain refinement is enhanced as the particle number density of MgO increases.The native MgO particles are modified by interfacial layers due to the co-segregation of Ca and N solute atoms at the MgO/Mg interface.Using aberration-corrected scanning transmission electron microscopy and electron energy loss spectroscopy,we reveal the nature of these Ca/N interfacial layers at the atomic scale.Irrespective of the crystallographic termination of MgO,Ca and N co-segregate at the MgO/Mg interface and occupy Mg and O sites,respectively,forming an interfacial structure of a few atomic layers.The interfacial structure is slightly expanded,less ordered and defective compared to the MgO matrix due to compositional deviations,whereby the MgO substrate is altered as a poorer template to nucleate Mg solid.Upon solidification in a TP-1 mould,the impotent MgO particles account for the grain refining mechanism,where they are suggested to participate into nucleation and grain initiation processes in an explosive manner.This work not only reveals the atomic engineering of a substrate through interfacial segregation but also demonstrates the effectiveness of a strategy whereby native MgO particles can be harnessed for grain refinement in Mg-Ca alloys.

Effect of addition temperature on dispersion behavior and grain refinement efficiency of MgO introduced into Mg alloy

The effect of addition temperature of MgO particles(MgOp)on their dispersion behavior and the efficiency of grain refinement in AZ31 Mg alloy was investigated.In addition,the grain refinement mechanism was systematically studied by microstructure characterization,thermodynamic calculation,and analysis of solidification curves.The results show that the grain size of AZ31 Mg alloy initially decreases and then increases as the MgOp addition temperature is increased from 720 to 810℃,exhibiting a minimum value of 136μm at 780℃.The improved grain refinement efficiency with increasing MgOp addition temperature can be attributed to the reduced Mg melt viscosity and enhanced wettability between MgOp and Mg melt.Furthermore,a corresponding physical model describing the solidification behavior and grain refinement mechanism was proposed.

Refinement Mechanism of Microstructure of Undercooled Nickel Based Alloys

Through the use of purification and recirculation superheating techniques on molten glass,the Ni65Cu33Co2 alloy was successfully undercooled to a maximum temperature of 292 K.High-speed photography was employed to capture the process of interface migration of the alloy liquid,allowing for an analysis of the relationship between the morphological characteristics of the alloy liquid solidification front and the degree of undercooling.Additionally,the microstructure of the alloy was examined using metallographic microscopy,leading to a systematic study of the microscopic morphological characteristics and evolution laws of the refined structure during rapid solidification.The research reveals that the grain refining mechanism of the Ni-Cu-Co ternary alloy is consistent with that of the binary alloy(Ni-Cu).Specifically,under low undercooling conditions,intense dendritic remelting was found to cause grain refinement,while under high undercooling conditions,recrystallization driven by accumulated stress and plastic strain resulting from the interaction between the liquid flow and the primary dendrites caused by rapid solidification was identified as the main factor contributing to grain refinement.Furthermore,the study highlights the significant role of the Co element in influencing the solidification rate and reheat effect of the alloy.The addition of Co was also found to facilitate the formation of non-segregated solidification structure,indicating its importance in the overall solidification process.

Effect of grain refinement induced by wire and arc additive manufacture (WAAM) on the corrosion behaviors of AZ31 magnesium alloy in NaCl solution

Additive manufacturing(AM)of Mg alloys has become a promising strategy for producing complex structures,but the corrosion performance of AM Mg components remains unexploited.In this study,wire and arc additive manufacturing(WAAM)was employed to produce single AZ31 layer.The results revealed that the WAAM AZ31 was characterized by significant grain refinement with non-textured crystallographic orientation,similar phase composition and stabilized corrosion performance comparing to the cast AZ31.These varied corrosion behaviors were principally ascribed to the size of grain,where cast AZ31 and WAAM AZ31 were featured by micro galvanic corrosion and intergranular corrosion,respectively.

Recent advances on grain refinement of magnesium rare-earth alloys during the whole casting processes:A review

High-performance cast magnesium rare-earth(Mg-RE) alloys are one of the most important materials among all developed Mg alloy families, and have shown great potential in military and weapons, aerospace and aviation, orthopedic implants, etc. Controlling grain size and distribution of it is key to the promising mechanical performance of Mg-RE alloy casting components. During the casting of a real component, nearly every procedure in the fabrication process will influence the grain refinement effect. The procedure may include and may not be limited to the chemical inoculations, possibly applied physical fields, the interfere between grain refiner and purifications, and the casting techniques with different processing parameters. This paper reviews the recent advances and proposed future developments in these categories on grain refinement of cast Mg-RE alloys. The review will provide insights for the future design of grain refinement techniques,the choosing of processing parameters, and coping strategies for the failure of coarsening for cast Mg-RE components with high quality and good performance.

Erratum to: Influence of grain refinement on the corrosion behavior of metallic materials: A review

Erratum to:International Journal of Minerals, Metallurgy and MaterialsVolume 28, Number 7, July 2021, Page 1112 The original version of this article unfortunately contained mistakes. Symbols in Table 2 are used incorrectly.

Influence of strain rate on grain refinement and texture evolution under complex shear stress conditions

The effects of different complex shear stress conditions on grain refinement and texture evolution of Mg-13Gd-4Y-2Zn-0.5Zr alloy were investigated.With increasing strain rate,the average grain size of compression-shear(CS)and compression-torsion(CT)samples are decreased,and the grain size of dynamic recrystallization(DRX)grains is also decreased.This is because that the precipitation number ofβphases is increased,and the hindering effect on grain growth can be significantly enhanced.The DRX fractions of CS and CT samples are decreased with increased strain rate.The low DRX fraction at high strain rate is related to the insufficient time for grains to nucleate.The DRX process can be promoted by the PSN mechanism of second phases,and the grain growth can be restricted by the pinning effect.At the same time,the texture strength is enhanced as the strain rate increased.Besides,the kinking degree of lamellar long-period stacking ordered(LPSO)phases is increased.Under complex shear stress conditions,non-basal slip,especially pyramidal slip,is easily activated and the texture is deflected greatly.Compared with the CS samples,CT samples have smaller average grain size,higher DRX fraction,and lower texture strength for a certain strain rate.This is because that the equivalent stress of the CT sample is larger,the stress triaxiality is smaller,so more serious dislocations are piled up near grain boundaries and second phases.At the same time,since CT sample was sheared with torsion,the dislocation movement path can be called“rotational dislocation accumulation”,and the longer distribution path of the CT sample is generated,so more sub-grains and low-angle grain boundaries(LAGBs)are formed.Compared with the CS sample,more huge-angle grain boundaries(HAGBs)and DRX grains are formed from grain boundary to grain interior,so better grain refinement effect is achieved.

Grain refinement and strength enhancement in Mg wrought alloys: A review

Low absolute strength becomes one major obstacle for the wider applications of low/no rare-earth(RE) containing Mg alloys. This review firstly demonstrates the importance of grain refinement in improving strength of Mg alloys by comprehensively comparing with other strategy, e.g., precipitation strengthening. Dynamic recrystallization(DRX) plays a crucial role in refining grain size of Mg wrought alloys.Therefore, secondly, the DRX models, grain nucleation mechanisms and the related grain refinement abilities in Mg alloys are summarized,including phase boundary, twin boundary and general boundary induced recrystallization. Thirdly, the newly developed low-RE containing Mg alloy, e.g., Mg-Ce, Mg-Nd and Mg-Sm based alloys, and the RE-free Mg alloys, e.g., Mg-Al, Mg-Zn, Mg-Sn and Mg-Ca based alloy,are reviewed, with the focus on enhancing the mechanical properties mainly via the grain refinement strategy. At the last section, the perspectives and outstanding issues concerning high-performance Mg wrought alloys are also proposed. This review is meant to promote the deep understanding on the critical role of grain refinement in Mg alloys and provide reference for the development of other high strength and low-cost Mg alloys which are fabricated by the conventional extrusion/rolling processing.

Effect of wide-spectrum pulsed magnetic field on grain refinement of pure aluminium

A wide-spectrum pulsed magnetic field(WSPMF)was obtained by adjusting the number of current pulses and the pulse interval between adjacent pulses.The effect of WSPMF on the grain refinement of pure aluminium was studied.The distribution of electromagnetic force and flow field in the melt under the WSPMF was simulated to reveal the grain refining mechanism.Results show that the grain refinement is attributed to the combined effect of the melt flow and oscillation under a WSPMF.When the pulse interval is 5 ms,the extreme value of electromagnetic force is the highest,and the size of the crystal nucleus is 0.35 mm.In the case of similar flow rates,the grain size gradually decreases as the pulse interval increases.The range of the harmonic frequency of the magnetic field gradually expands with the increase of the pulse interval,which can provide more energy for nucleation at the solid-liquid interface and promote nucleation.

Phase field simulation of grain refinement in silver-based filler metal

Numerical simulation is one of the important auxiliary methods for studying materials-related problems. In this study, phase field simulation was employed to investigate the refinement behavior of BAg55CuZn-x B brazing alloys. Simulation and experimental studies were conducted for B contents ranging from 0 wt.% to 0.2 wt.%. The results demonstrated that the addition of 0.05 wt.% B in the brazing alloy leads to a significant refinement effect. As the B content increases, the grain size further reduces, and a refinement stagnation phenomenon occurs after exceeding 0.15 wt.%. The solidification process of brazing alloys with different B content was predicted by simulation, and the simulation results showed that with the increase of B content, the initial number of nucleation increased, and the radius of the dendrite tip decreased. The simulation results are in good agreement with the experimental findings, providing further evidence of the refining effect of the B element and the reliable predictive capability of the phase field model.

Grain refinement in AZ31 magnesium alloy rod fabricated by extrusion-shearing severe plastic deformation process

A new severe plastic deformation （SPD） method that is extrusion-shearing （ES）, which includes initial forward extrusion and shearing process subsequently, was developed to fabricate the fine grained AZ31 Mg alloys. The components of ES die were manufactured and installed to gleeble1500D thermo-mechanical simulator. Microstructure observations were carried out in different positions of ES formed rods. The results show that homogeneous microstructures with mean grain size of 2 μm are obtained at lower temperature as the accumulated true strain is 2.44. Occurring of continuous dynamic recrystallization （DRX） is the main reason for grain refinement during ES process. The experimental results show that the ES process effectively refines the grains of AZ31 magnesium. The production results of ES extrusion with industrial extruder under different extrusion conditions show that the ES extrusion can be applied in large-scale industry.

Structure uniformity and limits of grain refinement of high purity aluminum during multi-directional forging process at room temperature

The effect of forging passes on the refinement of high purity aluminum during multi-forging was investigated. The attention was focused on the structure uniformity due to deformation uniformity and the grain refinement limitation with very high strains. The results show that the fine grain zone in the center of sample expands gradually with the increase of forging passes. When the forging passes reach 6, an X-shape fine grain zone is initially formed. With a further increase of the passes, this X-shape zone tends to spread the whole sample. Limitation in the structural refinement is observed with increasing strains during multi-forging process at the room temperature. The grains size in the center is refined to a certain size （110 μm as forging passes reach 12, and there is no further grain refinement in the center with increasing the forging passes to 24. However, the size of the coarse grains near the surface is continuously decreased with increasing the forging passes to 24.

Grain refinement of as-cast superalloy IN718 under action of low voltage pulsed magnetic field

The grain refinement of superalloy IN718 under the action of low voltage pulsed magnetic field was investigated. The experimental results show that fine equiaxed grains are acquired under the action of low voltage pulsed magnetic field. The refinement effect of the pulsed magnetic field is affected by the melt cooling rate and superheating. The decrease of cooling rate and superheating enhance the refinement effect of the low voltage pulsed magnetic field. The magnetic force and the melt flow during solidification are modeled and simulated to reveal the grain refinement mechanism. It is considered that the melt convection caused by the pulsed magnetic field, as well as cooling rate and superheating contributes to the refinement of solidified grains.

Effects of Al-Ti-B-RE grain refiner on microstructure and mechanical properties of Al-7.0Si-0.55Mg alloy

To investigate the effects of Al-Ti-B-RE grain refiner on microstructure and mechanical properties of Al-7.0Si-0.55Mg （A357） alloy, some novel Al-7.0Si-0.55Mg alloys added with different amount of Al-STi-1B-RE grain refiner with different RE composition were prepared by vacuum-melting. The microstructure and fracture behavior of the AI-7.0Si-0.55Mg alloys with the grain refiners were observed by X-ray diffraction （XRD）, optical microscopy （OM）, scanning electron microscopy （SEM）, and the mechanical properties of the alloys were tested in mechanical testing machine at room temperature. The observation of AI-Ti-B-RE morphology and internal structure of the particles reveals that it exhibits a TiAl3/Ti2Al20RE core-shell structure via heterogeneous TiB2 nuclei. The tensile strength of Al-7.0Si-0.55Mg alloys with Al-5Ti-1B-3.0RE grain refiner reaches the peak value at the same addition （0.2%） of grain refiner.

Grain refinement of Al-5%Cu aluminum alloy under mechanical vibration using meltable vibrating probe

A mechanical vibration technique to refine solidified microstructure was reported. Vibration energy was directly introduced into a molten alloy by a vibrating horn, and the vibrating horn was melted during vibration. Effects of vibration acceleration and mass ratio on the microstructure of Al-5% Cu alloy were investigated. Results show that the present mechanical vibration could provide localized cooling by extracting heat from the interior of molten alloy, and the cooling rate is strongly dependent on vibration acceleration. It is difficult to refine the solidified microstructure when the treated alloy keeps full liquid state within the entire vibrating duration. Significantly refined microstructure was obtained by applying mechanical vibration during the initial stage of solidification. Moreover, mechanisms of grain refinement were discussed.

Numerical simulation of acoustic pressure field for ultrasonic grain refinement of AZ80 magnesium alloy

Ultrasound with different intensities was applied to treating AZ80 alloy melt to improve its solidification structure.The average grain size of the alloy could be decreased from 303 to 148 μm after the ultrasound with intensity of 30.48 W/cm2 was applied.To gain insight into the mechanism of ultrasonic treatment which affected the microstructure of the alloy,numerical simulations were carried out and the effects of different ultrasonic pressures on the behaviors of cavitation bubble in the melt were studied.The ultrasonic field propagation in the melt was also characterized.The results show that samples from different positions are subjected to different acoustic pressures and the effect of grain refinement by ultrasonic treatment for these samples is different.With the increase of ultrasonic intensity,the acoustic pressure is increased and the grain size is decreased generally.

Effect of electrodes and thermal insulators on grain refinement by electric current pulse

The application of electric current pulse（ECP） to a solidification process refers to the immersion of electrodes into the liquid metal and the employment of thermal insulators on the upper surface of metal.In order to ascertain the effects of these two factors on the structure refinement by the ECP technique,three groups of experiments were performed with different types of electrodes or various thermal insulators.By the comparison between solidification structures under different conditions,it is followed that the electrode and the thermal insulator have an obvious influence on the grain refinement under an applied ECP,and further analysis demonstrates that the thermal conditions of the liquid surface play a vital role in the modification of solidification structure.Also,the results support the viewpoint that most of the equiaxed grains originate from the liquid surface subjected to an ECP.

Grain refinement of pure aluminum by direct current pulsed magnetic field and inoculation

The combined effects of direct current pulsed magnetic field （DC-PMF） and inoculation on pure aluminum were investigated, the grain refinement behavior of DC-PMF and inoculation was discussed. The experimental results indicate that the solidification micro structure of pure aluminum can be greatly refined under DC-PMF. Refinement of pure aluminum is attributed to electromagnetic undercooling and forced convection caused by DC-PMF. With single DC-PMF, the grain size in the equiaxed zone is uneven. However, under DC-PMF, by adding 0.05% （mass fraction） Al5Ti-B, the grain size of the sample is smaller, and the size distribution is more uniform than that of single DC-PMF. Furthermore, under the combination of DC-PMF and inoculation, with the increase of output current, the grain size is further reduced. When the output current increases to 100 A, the average grain size can decrease to 113 μn.

Effect of Al_2Ca intermetallic compound addition on grain refinement of AZ31 magnesium alloy

The Al2Ca intermetallic compound was prepared by melting process in a vacuum induction furnace. And the A12Ca compound was added in as-cast AZ31 alloys for grain refinement. The effect of its additional levels on grain refinement of as-cast AZ31 alloy was investigated and the mechanism of the grain refinement was discussed. The results reveal that the addition of 1.1% Al2Ca （mass fraction） decreases the average grain size of as-cast AZ31 alloy from 354 to 198 μm. And the thermal stability of the grains refined by Al2Ca is superior. The grain refining mechanism is attributed to the combined effects of solute and heterogeneous nucleation from the Al2Ca.