Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
In this manuscript a comparative study on Bi<sub>2</sub>O<sub>3</sub>/polystyrene and Bi<sub>2</sub>O<sub>3</sub>/PVDF composites has been executed via analysis of struc...In this manuscript a comparative study on Bi<sub>2</sub>O<sub>3</sub>/polystyrene and Bi<sub>2</sub>O<sub>3</sub>/PVDF composites has been executed via analysis of structural, bonding, surface morphology and dielectric response of composites for energy storage. The composites have been synthesized using solution cast method by varying concentrations of Bi<sub>2</sub>O<sub>3</sub> (BO = 1 - 5 mw%) into polystyrene (PS) and polyvinylidene fluoride (PVDF) polymers respectively. X-ray diffraction confirms the generation of crystallinity, Fourier transform infrared (FT-IR) spectroscopy confirms bonding behavior and scanning electron microscopy (SEM) confirms uniform distribution of Bi<sub>2</sub>O<sub>3</sub> (BO) in PS and PVDF polymers. Impedance spectroscopy has been employed for determination of dielectric response of the fabricated composites. The dielectric constant has been found to be increased as 1.4 times of pristine PS to BO<sub>5%</sub>PS<sub>95%</sub> composites and 1.8 times of pristine PVDF to BO<sub>5%</sub>PVDF<sub>95%</sub> composites respectively. These high dielectric composite electrodes are useful for flexible energy storage devices.展开更多
UPR/Al2O3 composite particles were synthesized from unsaturated polyester resin(UPR) and nanometer/ultra-fine Al2O3 powders by means of suspension polymerization.The effects of Al2O3 with two different particle diamet...UPR/Al2O3 composite particles were synthesized from unsaturated polyester resin(UPR) and nanometer/ultra-fine Al2O3 powders by means of suspension polymerization.The effects of Al2O3 with two different particle diameters on the density and hardness of the composite particles during the synthesis were studied.The results show UPR/Al2O3 composite particles synthesized by suspension polymerization are spherical,smooth,with a yield of 60%～75%(wt),and the particle diameters are 140～250μm;Al2O3 can effectively improves the density and hardness of the composite particles;when the contet is the same,effect of ultra-fine Al2O3 on the density and hardness of the composite particles is better than that of nanometer Al2O3;When the mass fraction of Al2O3 is 55%,the maximum hardness of ultra-fine Al2O3 composite particles and nanometer Al2O3 composite particles are 39.42HV and 25.66HV respectively.展开更多
The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was disc...The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was discussed. Indentation-quench test was conducted to evaluate the effect of thermal fatigue temperature difference （ΔT） and number of thermal cycles （Ⅳ） on fatigue crack growth （Δa）. The mechanical properties and thermal fatigue resistance of TiC/Al203 composites are remarkably improved by the addition of TiC. The thermal shock fatigue of monolithic alumina and TiC/Al2O3 composites is due to a ＂true＂ cycling effect （thermal fatigue）. Crack deflection and bridging are the predominant reasons for the improvement of thermal shock fatigue resistance of the composites.展开更多
In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and micro...In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and microstructures of the sintered composites were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). The process of synthesis was investigated using differential thermal analysis (DTA). The effects of processing parameters and additives on the microstructures of the composites and the development of whisker were examined. It is found that the morphology of the whisker is strongly influenced by the additives, the exothermal reaction process, and the processing parameters.展开更多
Polycrystalline 3Y-TZP/Al2O3 tetragonal zirconia fiber was obtained by the pyrolysis of gel fibers using zirconium oxychloride octahydrate（ZOC） as the raw material. The spinnable zirconia sol was prepared by electro...Polycrystalline 3Y-TZP/Al2O3 tetragonal zirconia fiber was obtained by the pyrolysis of gel fibers using zirconium oxychloride octahydrate（ZOC） as the raw material. The spinnable zirconia sol was prepared by electrolyzing the zirco-nium oxychloride octahydrate（ZOC） solution in the presence of acetic acid and sugar（ sucrose, glucrose or fructose） , in which the molar ratios of CH3 COOH/ZOC and sugar/ZOC were 1.0-4.0 and 0.2-0.4, respectively. The pre- pared tetragonal zireonia fibers sintered at different temperatures showed smooth and crack-free surfaces with diame, ters of 5-10 μm. The addition of Al2O3 enhanced the sintering process and prevented the crystals from growing. Thermogravimetric analysis（TG）, X-ray diffraction （ XRD ）, Fourier transform infrared spectroscopy（FTIR）, and scanning electron microscope（SEM） techniques were used to characterize the prepared fibers.展开更多
Ti3AlC2/TiC-Al2O3 composite was synthesized by a combustion reaction in TiO2-Al-C system. The effect of the compositions in raw materials on the products was investigated. Ti3AlC2/TiC-Al2O3 composite was obtained at t...Ti3AlC2/TiC-Al2O3 composite was synthesized by a combustion reaction in TiO2-Al-C system. The effect of the compositions in raw materials on the products was investigated. Ti3AlC2/TiC-Al2O3 composite was obtained at the molar ratio of TiO2：Al：C=3.0：5.0～5.1：1.8～2.0. The reaction path for the 3TiO2-5Al- 2C system was proposed. Al3Ti, Ti203, TiO, and 6-Al2O3 are found to be transitional phases. Finally, Ti3AlC2/TiC-Al2O3 composite forms at～900℃ of furnace temperature. The measured Vickers hardness, fracture toughness, and flexural strength of the nearly dense sample from 3TiO2-5Al-2C are 13.3±1.1 GPa, 5.8±0.3 MPa.m^1/2, and 466±39 MPa, respectively.展开更多
Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process...Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process of β-Sialon. The rate of oxidation process is controlled by chemicalreaction at the initial stage and then by diffusion. The apparent activation energies and appar-ent rate constants at different temperatures are determined by treating TG data of the overallprocess.展开更多
The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics...The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.展开更多
Alumina-(0 similar to 20 vol. pct) iron composites were fabricated by hot-pressing of well-mixed-alumina and iron powders at 1400 degreesC and 30 MPa for 30 min. Hot-pressed bodies with nearly theoretical density were...Alumina-(0 similar to 20 vol. pct) iron composites were fabricated by hot-pressing of well-mixed-alumina and iron powders at 1400 degreesC and 30 MPa for 30 min. Hot-pressed bodies with nearly theoretical density were obtained for addition up to 10 vol. pct Fe, but relative density decreased gradually with further increase in Fe addition. The materials exhibit a homogeneous dispersion of Fe. Fracture strength of the composites exhibits a maximum value of 604 MPa at 15 vol. pct Fe, which is 1.5 times that of alumina alone. Fracture toughness increases with the increase in Fe content, reaching 7.5 MPa.m(1/2) at 20 vol. pct Fe. The theoretical values of fracture toughness was calculated and compared with the experimental one. Toughening mechanisms of the composites are also discussed.展开更多
To improve the mechanical properties of alumina particulates reinforced steel matrix composite, Ti powder was added into the alumina preform, a 5140 steel matrix composite was fabricated by squeeze casting, and the in...To improve the mechanical properties of alumina particulates reinforced steel matrix composite, Ti powder was added into the alumina preform, a 5140 steel matrix composite was fabricated by squeeze casting, and the influences of Ti powder on the microstructure, hardness and bending strength of the composite were investigated, compared with the composite without adding Ti powder. Applied Ti powder and alumina particulates were 10-25 μm and 100-180 μm in size, respectively. Both composites were successfully fabricated, however Ti powder addition increased the infiltration thickness of the composite. In the Ti contained composite, a TiC film in micron scale is formed on the surface of alumina particles, many TiC aggregates are dispersed in the steel matrix without obvious remaining Ti powder. The hardness and the three-point bending strength of the composite reach 49.5 HRC and 1 018 MPa, respectively, which are 17.9% and 52.4% higher than those of the composite in the absence of Ti addition. Fracture morphology shows that the debonding of alumina particulates is eliminated for the composite in the presence of Ti addition. Sessile drop test shows the average wetting angle between 5140 steel and that of Ti coated Al2O3 is about 82.15°, much lower than the wetting angle 150° between steel and pure Al2O3. Therefore, the increase in the mechanical properties of the composite is attributed to the improvement of Al2O3 p/steel interface wetting and bonding by adding Ti powder in the preform.展开更多
In-situ Al2O3/TiAl composites were fabricated by pressure-assisted exothermic dispersion （PAXD） method from elemental powder mixtures of Ti, Al, TiO2, and Nb2O5. The microstructures and mechanical properties of the ...In-situ Al2O3/TiAl composites were fabricated by pressure-assisted exothermic dispersion （PAXD） method from elemental powder mixtures of Ti, Al, TiO2, and Nb2O5. The microstructures and mechanical properties of the as-sintered composites are investigated. The results show that the as-sintered products consist of γ-TiAl, α2-Ti3Al, Al2O3, and NbAl3 phases. Microstructure analysis indicates that Al2O3 particles tend to disperse on the grain boundaries. Application of a moderate pressure of 35 MPa at 1200℃ yields Al2O3/TiAl composites with fine Al2O3 reinforcement and a discontinuous network linking by Al2O3 particles. The aluminide component has a fine submicron γ ＋α2 lamellar microstructure. With increasing Nb2O5 content, Al2O3 particles are dispersed uniformly in the matrix. The hardness of the composites increases gradually, and the bending strength and fracture toughness of the composites reach to the maximum value, respectively.展开更多
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
文摘In this manuscript a comparative study on Bi<sub>2</sub>O<sub>3</sub>/polystyrene and Bi<sub>2</sub>O<sub>3</sub>/PVDF composites has been executed via analysis of structural, bonding, surface morphology and dielectric response of composites for energy storage. The composites have been synthesized using solution cast method by varying concentrations of Bi<sub>2</sub>O<sub>3</sub> (BO = 1 - 5 mw%) into polystyrene (PS) and polyvinylidene fluoride (PVDF) polymers respectively. X-ray diffraction confirms the generation of crystallinity, Fourier transform infrared (FT-IR) spectroscopy confirms bonding behavior and scanning electron microscopy (SEM) confirms uniform distribution of Bi<sub>2</sub>O<sub>3</sub> (BO) in PS and PVDF polymers. Impedance spectroscopy has been employed for determination of dielectric response of the fabricated composites. The dielectric constant has been found to be increased as 1.4 times of pristine PS to BO<sub>5%</sub>PS<sub>95%</sub> composites and 1.8 times of pristine PVDF to BO<sub>5%</sub>PVDF<sub>95%</sub> composites respectively. These high dielectric composite electrodes are useful for flexible energy storage devices.
文摘UPR/Al2O3 composite particles were synthesized from unsaturated polyester resin(UPR) and nanometer/ultra-fine Al2O3 powders by means of suspension polymerization.The effects of Al2O3 with two different particle diameters on the density and hardness of the composite particles during the synthesis were studied.The results show UPR/Al2O3 composite particles synthesized by suspension polymerization are spherical,smooth,with a yield of 60%～75%(wt),and the particle diameters are 140～250μm;Al2O3 can effectively improves the density and hardness of the composite particles;when the contet is the same,effect of ultra-fine Al2O3 on the density and hardness of the composite particles is better than that of nanometer Al2O3;When the mass fraction of Al2O3 is 55%,the maximum hardness of ultra-fine Al2O3 composite particles and nanometer Al2O3 composite particles are 39.42HV and 25.66HV respectively.
文摘The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was discussed. Indentation-quench test was conducted to evaluate the effect of thermal fatigue temperature difference （ΔT） and number of thermal cycles （Ⅳ） on fatigue crack growth （Δa）. The mechanical properties and thermal fatigue resistance of TiC/Al203 composites are remarkably improved by the addition of TiC. The thermal shock fatigue of monolithic alumina and TiC/Al2O3 composites is due to a ＂true＂ cycling effect （thermal fatigue）. Crack deflection and bridging are the predominant reasons for the improvement of thermal shock fatigue resistance of the composites.
基金This work was supported by the National Natural Science Foundation of China (No. 50432010, 50372037).
文摘In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and microstructures of the sintered composites were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). The process of synthesis was investigated using differential thermal analysis (DTA). The effects of processing parameters and additives on the microstructures of the composites and the development of whisker were examined. It is found that the morphology of the whisker is strongly influenced by the additives, the exothermal reaction process, and the processing parameters.
基金Supported by National High Technology Research and Development Program of China(No.2002AA2040).
文摘Polycrystalline 3Y-TZP/Al2O3 tetragonal zirconia fiber was obtained by the pyrolysis of gel fibers using zirconium oxychloride octahydrate（ZOC） as the raw material. The spinnable zirconia sol was prepared by electrolyzing the zirco-nium oxychloride octahydrate（ZOC） solution in the presence of acetic acid and sugar（ sucrose, glucrose or fructose） , in which the molar ratios of CH3 COOH/ZOC and sugar/ZOC were 1.0-4.0 and 0.2-0.4, respectively. The pre- pared tetragonal zireonia fibers sintered at different temperatures showed smooth and crack-free surfaces with diame, ters of 5-10 μm. The addition of Al2O3 enhanced the sintering process and prevented the crystals from growing. Thermogravimetric analysis（TG）, X-ray diffraction （ XRD ）, Fourier transform infrared spectroscopy（FTIR）, and scanning electron microscope（SEM） techniques were used to characterize the prepared fibers.
文摘Ti3AlC2/TiC-Al2O3 composite was synthesized by a combustion reaction in TiO2-Al-C system. The effect of the compositions in raw materials on the products was investigated. Ti3AlC2/TiC-Al2O3 composite was obtained at the molar ratio of TiO2：Al：C=3.0：5.0～5.1：1.8～2.0. The reaction path for the 3TiO2-5Al- 2C system was proposed. Al3Ti, Ti203, TiO, and 6-Al2O3 are found to be transitional phases. Finally, Ti3AlC2/TiC-Al2O3 composite forms at～900℃ of furnace temperature. The measured Vickers hardness, fracture toughness, and flexural strength of the nearly dense sample from 3TiO2-5Al-2C are 13.3±1.1 GPa, 5.8±0.3 MPa.m^1/2, and 466±39 MPa, respectively.
文摘Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process of β-Sialon. The rate of oxidation process is controlled by chemicalreaction at the initial stage and then by diffusion. The apparent activation energies and appar-ent rate constants at different temperatures are determined by treating TG data of the overallprocess.
文摘The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.
文摘Alumina-(0 similar to 20 vol. pct) iron composites were fabricated by hot-pressing of well-mixed-alumina and iron powders at 1400 degreesC and 30 MPa for 30 min. Hot-pressed bodies with nearly theoretical density were obtained for addition up to 10 vol. pct Fe, but relative density decreased gradually with further increase in Fe addition. The materials exhibit a homogeneous dispersion of Fe. Fracture strength of the composites exhibits a maximum value of 604 MPa at 15 vol. pct Fe, which is 1.5 times that of alumina alone. Fracture toughness increases with the increase in Fe content, reaching 7.5 MPa.m(1/2) at 20 vol. pct Fe. The theoretical values of fracture toughness was calculated and compared with the experimental one. Toughening mechanisms of the composites are also discussed.
基金Funded by National Natural Science Foundation of China(No.51265019)
文摘To improve the mechanical properties of alumina particulates reinforced steel matrix composite, Ti powder was added into the alumina preform, a 5140 steel matrix composite was fabricated by squeeze casting, and the influences of Ti powder on the microstructure, hardness and bending strength of the composite were investigated, compared with the composite without adding Ti powder. Applied Ti powder and alumina particulates were 10-25 μm and 100-180 μm in size, respectively. Both composites were successfully fabricated, however Ti powder addition increased the infiltration thickness of the composite. In the Ti contained composite, a TiC film in micron scale is formed on the surface of alumina particles, many TiC aggregates are dispersed in the steel matrix without obvious remaining Ti powder. The hardness and the three-point bending strength of the composite reach 49.5 HRC and 1 018 MPa, respectively, which are 17.9% and 52.4% higher than those of the composite in the absence of Ti addition. Fracture morphology shows that the debonding of alumina particulates is eliminated for the composite in the presence of Ti addition. Sessile drop test shows the average wetting angle between 5140 steel and that of Ti coated Al2O3 is about 82.15°, much lower than the wetting angle 150° between steel and pure Al2O3. Therefore, the increase in the mechanical properties of the composite is attributed to the improvement of Al2O3 p/steel interface wetting and bonding by adding Ti powder in the preform.
基金supported by the Special Program for Education Bureau of Shaanxi Province, China(Grant No.08JK240)the Breeding Program for Provincial Level Key Research Base of Shaanxi University of Technology, China (Grant No.SLGJD0806)Scientific Research Start up Program for Introduced Talents of Shaanxi University of Technology, China (Grant No.SLGQD0751).
文摘In-situ Al2O3/TiAl composites were fabricated by pressure-assisted exothermic dispersion （PAXD） method from elemental powder mixtures of Ti, Al, TiO2, and Nb2O5. The microstructures and mechanical properties of the as-sintered composites are investigated. The results show that the as-sintered products consist of γ-TiAl, α2-Ti3Al, Al2O3, and NbAl3 phases. Microstructure analysis indicates that Al2O3 particles tend to disperse on the grain boundaries. Application of a moderate pressure of 35 MPa at 1200℃ yields Al2O3/TiAl composites with fine Al2O3 reinforcement and a discontinuous network linking by Al2O3 particles. The aluminide component has a fine submicron γ ＋α2 lamellar microstructure. With increasing Nb2O5 content, Al2O3 particles are dispersed uniformly in the matrix. The hardness of the composites increases gradually, and the bending strength and fracture toughness of the composites reach to the maximum value, respectively.